ASTM A822 A822M-2004(2010) Standard Specification for Seamless Cold-Drawn Carbon Steel Tubing for Hydraulic System Service《液压系统设备用冷拉碳素无缝钢管的标准规范》.pdf

《ASTM A822 A822M-2004(2010) Standard Specification for Seamless Cold-Drawn Carbon Steel Tubing for Hydraulic System Service《液压系统设备用冷拉碳素无缝钢管的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A822 A822M-2004(2010) Standard Specification for Seamless Cold-Drawn Carbon Steel Tubing for Hydraulic System Service《液压系统设备用冷拉碳素无缝钢管的标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A822/A822M 04 (Reapproved 2010)Standard Specification forSeamless Cold-Drawn Carbon Steel Tubing for HydraulicSystem Service1This standard is issued under the fixed designation A822/A822M; the number immediately following the designation indicates the yearof original adoption or, in the

2、 case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers nominal wall thickness, seam-less, cold-drawn carbon steel tu

3、bing intended for use inhydraulic systems and in other similar applications whereforming operations require tight radius bending and flaring.1.2 Tubing sizes and thicknesses usually furnished to thisspecification are18 to 3 in. 3.2 to 88.9 mm in outsidediameter and 0.035 to 0.134 in. 0.9 to 3.4 mm i

4、nclusive, innominal wall thickness. Tubing having other dimensions maybe furnished, provided such tubing complies with all otherrequirements of this specification.1.3 Mechanical property requirements do not apply totubing smaller than18 in. 3.2 mm in inside diameter or 0.015in. 0.4 mm in thickness.1

5、.4 Optional supplementary requirements are provided and,when desired, shall be so stated in the order.1.5 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. Within the text, theSI units are shown in brackets. The values stated in eachsystem may not be

6、exact equivalents; therefore, each systemshall be used independently of the other. Combining valuesfrom the two systems may result in non-conformance with thestandard.2. Referenced Documents2.1 ASTM Standards:2A450/A450M Specification for General Requirements forCarbon and Low Alloy Steel TubesA751

7、Test Methods, Practices, and Terminology for Chemi-cal Analysis of Steel Products3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 lotfor tension and hardness test requirementstheterm “lot” applies to all tubes, prior to cutting, of the samenominal diameter and wall thickness wh

8、ich are produced fromthe same heat of steel. When final heat treatment is in abatch-type furnace, a lot shall include only those tubes of thesame size and the same heat which are heat treated in the samefurnace charge.When the final heat treatment is in a continuousfurnace, a lot shall include all t

9、ubes of the same size and heat,heat treated in the same furnace at the same temperature, timeat heat, and furnace speed.4. Ordering Information4.1 Orders for material to this specification should includethe following, as required, to describe the desired materialadequately:4.1.1 Quantity (feet, metr

10、es, or number of lengths),4.1.2 Name of material (seamless tubing),4.1.3 Manufacture (cold-drawn),4.1.4 Tube size (outside diameter and nominal wall thick-ness),4.1.5 Length (specific or random),4.1.6 Test report required (see Certified Test Report sectionin Specification A450/A450M),4.1.7 Specifica

11、tion designation, and4.1.8 End use of material.5. General Requirements5.1 Material furnished under this specification shall con-form to the applicable requirements of the latest edition ofSpecification A450/A450M, unless otherwise provided herein.6. Manufacture6.1 Tubes shall be made by the seamless

12、 process and shallbe cold drawn to size.7. Heat Treatment7.1 Tubes shall be heated after the final cold workingoperation to a temperature of at least 1200 F 650 C.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct respons

13、ibility of SubcommitteeA01.09 on Carbon Steel Tubular Products.Current edition approved April 1, 2010. Published August 2010. Originallyapproved in 1984. Last previous edition approved in 2004 as A822/A822M04.DOI: 10.1520/A0822_A0822M-04R10.2For referenced ASTM standards, visit the ASTM website, www

14、.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.8. Ch

15、emical Composition8.1 Steel shall conform to the chemical composition re-quirements prescribed in Table 1.9. Mechanical Properties9.1 Tensile PropertiesMaterial shall conform to the ten-sile properties prescribed in Table 2.9.2 Hardness RequirementsFinished tubes shall have ahardness not exceeding 6

16、5 HRB. The hardness test shall not berequired on tubing having a nominal wall thickness of less than0.065 in. 1.7 mm.9.3 Flattening TestA section of finished tubing, not lessthan 3 in. 75 mm in length shall not crack or exhibit flawswhen flattened between parallel plates to a distance equal tothree

17、times the tubing nominal wall thickness. Superficialruptures resulting from minor surface imperfections shall notbe considered cause for rejection.10. Permissible Variations in Dimensions10.1 Permissible variations in the outside diameter of thetubing shall not exceed the values given in Table 3.10.

18、2 Permissible variations in the wall thickness of thetubing shall not exceed 610 % for tubing having 0.50 in. 12.7mm or larger nominal outside diameter or more than 615 %for tubing having a smaller nominal outside diameter.11. Workmanship, Finish, and Appearance11.1 Finished tubes shall be free of s

19、cale but may have asuperficial oxide film on the surfaces.11.2 Finished tubes shall be reasonably straight and havesmooth ends free of burrs. Tubes shall have a workmanlikefinish and shall be free of surface imperfections that cannot beremoved within the allowable wall tolerances. Removal ofsurface

20、imperfections, such as handling marks, straighteningmarks, light mandrel and die marks, shallow pits, and scalepattern, will not be required provided they are within theallowable tolerances.11.3 Finished tubes shall be protected both on the outsideand the inside diameter to prevent corrosion in tran

21、sit. If acorrosion preventive compound is applied, it shall be such thatafter normal storage periods it can be readily removed bycleaning.12. Number of Tests12.1 One tension test, flaring test, flattening test, and hard-ness test shall be made on each lot of tubes.13. Hydrostatic Proof Test13.1 Tubi

22、ng supplied under this specification shall havebeen tested hydrostatically, with no evidence of failure orpermanent deformation, at a pressure that will subject thematerial to a hoop stress of 20 000 psi 140 MPa. Testpressures shall be determined as follows:P 52TSDwhere:D = outside diameter of tubin

23、g, in. mm,P = hydrostatic pressure, psi MPa,S = allowable stress = 20 000 psi 140 MPa, andT = minimum wall thickness of tubing, in. mm.13.2 No tube shall be tested beyond a hydrostatic pressureof 5000 psi 35 MPa, unless so specified on the purchaseorder.14. Packaging and Package Marking14.1 Tubing s

24、hall be packaged or bundled in such a manneras to prevent damage in ordinary handling and transportation.14.2 Tubing shall be identified by a tag with the name of themanufacturer, purchase order number, specification designa-tion, and size.15. Keywords15.1 carbon; pressure-containing parts; seamless

25、 steel tube;steel tubeTABLE 1 Chemical RequirementsElement Composition, %Carbon 0.18 maxManganese 0.27 to 0.63Phosphorus 0.048 maxSulfur 0.058 maxTABLE 2 Tensile RequirementsTensile strength, min., ksi MPa 45 310Yield strength, min., ksi MPa 25 170Elongation, in 2 in. or 50 mm, min., % 35TABLE 3 Tub

26、ing Outside Diameter TolerancesNominal Tubing Outside Diameter,Ain. mmOutside Diameter Tolerance,in. mmUp to 1 25 60.004 0.101to112 25to38 60.006 0.15Over 112 to 2 38 to 50, inclusive 60.008 0.20Over 2 to 312 50 to 90, inclusive 60.010 0.25AThe actual outside diameter shall be the average of the max

27、imum andminimum outside diameters as determined at any one cross-section through thetubing.A822/A822M 04 (2010)2SUPPLEMENTARY REQUIREMENTSThe following supplementary requirement may become a part of the specification when specified inthe inquiry or invitation to bid, and purchase order or contract.

28、These requirements shall not beconsidered, unless specified in the order, in which event the necessary tests shall be made by themanufacturer prior to shipment of the tubing.S1. Product AnalysisS1.1 Product analysis shall be made by the supplier fromone tube per heat of steel. If the original test f

29、or productanalysis fails, retests of two additional lengths of tubes shall bemade. Both retests shall meet the requirements of this specifi-cation for the elements in question; otherwise, all remainingmaterial in the heat shall be rejected or, at the option of theproducer, each length of tube may be

30、 individually tested foracceptance. Lengths of tubes which do not meet the require-ments of this specification shall be rejected.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard ar

31、e expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not

32、revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which yo

33、u may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United

34、 States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A822/A822M 04 (2010)3