ASTM G60-2001(2018) Standard Practice for Conducting Cyclic Humidity Exposures.pdf

《ASTM G60-2001(2018) Standard Practice for Conducting Cyclic Humidity Exposures.pdf》由会员分享，可在线阅读，更多相关《ASTM G60-2001(2018) Standard Practice for Conducting Cyclic Humidity Exposures.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: G60 01 (Reapproved 2018)Standard Practice forConducting Cyclic Humidity Exposures1This standard is issued under the fixed designation G60; the number immediately following the designation indicates the year of originaladoption or, in the case of revision, the year of last revision. A nu

2、mber in parentheses indicates the year of last reapproval. A superscriptepsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice covers procedures for conducting cyclichumidity exposures with a corrosive dip.2It sets forth theconditions required in cyc

3、lic humidity testing.1.2 This practice does not prescribe the type of exposurespecimen or exposure periods nor the interpretation to be givento the results.1.3 The values stated in SI units are to be regarded asstandard. The values given in parentheses are for informationonly.1.4 This standard does

4、not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to consult andestablish appropriate safety, health, and environmental prac-tices and determine the applicability of regulatory limitationsprior to use.1.5 This inte

5、rnational standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT)

6、Committee.2. Referenced Documents2.1 ASTM Standards:3D1193 Specification for Reagent WaterG1 Practice for Preparing, Cleaning, and Evaluating Corro-sion Test Specimens3. Significance and Use3.1 The procedure described is used to observe the behaviorof steels under exposure conditions that retard the

7、 formation ofa protective type of rust. It is also used to evaluate seal coat oninsulation.3.2 This practice should not be used to rank steels that forma protective type of rust under atmospheric exposure condi-tions.4. Apparatus4.1 The apparatus required for cyclic humidity exposuresconsists of a t

8、est chamber, provisions for heating the chamber,a humidifying tower, a drying train, a dip mechanism, provi-sions for introducing and draining the solution, a supply ofcompressed air, specimen supports, and necessary means ofcontrol.4.2 The size and detailed construction of the apparatus areoptional

9、, provided the conditions obtained meet the require-ments of this practice.4.3 Aschematic diagram of the apparatus is shown in Fig. 1.4.4 The apparatus should be capable of providing an 8-hhumidity cycle three times per day, as shown in Fig. 2, and adip cycle once a day.4.4.1 The cyclic variation of

10、 humidity can be obtained byvariation of the temperature of the water in the humidifyingtower. The temperature of the water is cycled thermostaticallysuch that the relative humidity of air bubbling through thewater at a minimum rate of 1 L min (0.04 ft3/min) will varybetween 100 and 50 % when the te

11、mperature of the air in thetest chamber is brought to 52 6 1C (125 6 2F).4.4.2 The range of relative humidity can be extended byadding a drying period to the humidity cycle described above.The minimum relative humidity shall be 20 % and themaximum relative humidity shall be 95 % for each cycle.4.4.3

12、 Drops of solution which accumulate on the ceiling orcover of the chamber shall not be permitted to fall on thespecimens being exposed.NOTE 1Instruments to continuously record temperature and humidityare not mandatory, but these provide the most reliable and economical1This practice is under the jur

13、isdiction of ASTM Committee G01 on Corrosionof Metals and is the direct responsibility of Subcommittee G01.05 on LaboratoryCorrosion Tests.Current edition approved Oct. 1, 2018. Published November 2018. Originallyapproved in 1979. Last previous edition approved in 2013 as G60 01 (2013). DOI:10.1520/

14、G0060-01R18.2Opinsky, A. J., Thomson, R. F., and Boegehold, A. L., “A Cyclic HumidityAccelerated Corrosion Test for Sheet Steel,” ASTM Bulletin, January 1953.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of A

15、STMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized pr

16、inciples on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1way of recording such information. In the absence of suchinstrumentation

17、, temperature and humidity measurement shall be made, atleast twice a day, at the maximum and minimum humidity in a cycle.4.5 Materials of Construction:4.5.1 The test chamber should be made of inert materialssuch as plastics, glass, or metals lined with impervious plastics,rubber or epoxy-type mater

18、ials, or materials exhibiting equiva-lent corrosion resistance. Material of construction shall be suchthat it will not affect the corrosiveness of the exposureatmosphere.4.5.2 The dip solution container should not be affected by orcause contamination of the dip solution.4.6 Specimen Supports:4.6.1 T

19、he specimen-supporting device should not be af-fected by or cause contamination of the dip solution. See Note2.4.6.2 The method of supporting specimens will vary withthe apparatus used for conducting the tests, but should bedesigned to insulate the specimens from each other physicallyand electricall

20、y and to insulate the specimens from any metalliccontainer or supporting device used within the apparatus. Thespecimens shall not contact any material capable of acting as awick.NOTE 2Suitable materials for the construction or coating of racks andsupports are glass, rubber, plastic, or suitably coat

21、ed wood. Bare metalshall not be used. Specimens shall preferably be supported from theFIG. 1 Main Parts of the Cyclic Humidity Corrosion Exposure Apparatus (Schematic)FIG. 2 Humidity Cycle (Schematic)G60 01 (2018)2bottom or the side. Slotted wooden strips are suitable for the support of flatpanels.

22、Suspension from glass hooks or waxed string may be used as longas the specified position of the specimens is obtained, if necessary, bymeans of secondary support at the bottom of the specimens.4.6.3 Shape and form of the specimen support should assurefree contact of the specimen with the corrosive s

23、olution, theliquid line, or the vapor phase. In a stacked rack, the first andlast specimens should be dummy specimens so that theoutermost exposure specimens are shielded by their neighborsin the same manner as specimens in the middle of the stack.5. Reagents and Materials5.1 Purity of ReagentsReage

24、nt grade chemicals shall beused in all tests. Unless otherwise indicated, it is intended thatall reagents shall conform to the specifications of the Commit-tee on Analytical Reagents of the American Chemical Society,where such specifications are available.45.2 Purity of WaterUnless otherwise indicat

25、ed, referenceto water shall be understood to mean distilled or deionizedwater conforming to Type IV reagent water described inSpecification D1193 except that for this test method the limitsfor chlorides and sodium may be ignored.5.3 Dip SolutionThe dip solution should be prepared bydissolving 1 % so

26、dium chloride (NaCl), 1 % calcium chloride(CaCl2), and 0.1 % sulfuric acid (H2SO4) by solution weight inwater. The solution volume to specimen surface area ratioshould be a minimum of 250 mL/cm2.6. Air Supply6.1 The compressed air supply shall be free of oil and dirt.7. Exposure Specimens7.1 The typ

27、e and number of test specimens to be used, aswell as the criteria for the evaluation of the test results, shall bedefined in the specifications covering the material or productbeing exposed or shall be mutually agreed upon between thepurchaser and the seller.7.2 Strip coupons 75 by 38 by 2 mm (3 by

28、112 by116 in.)may be preferred as corrosion specimens.7.3 Six to eight identical specimens should be exposed.7.4 Specimens should be prepared, cleaned, and evaluatedin accordance with Practice G1.8. Position of Specimens During Exposure8.1 The position of the specimens in the cyclic humiditychamber

29、during the exposure shall be such that the followingconditions are met:8.1.1 Unless otherwise specified, the specimens shall besupported or suspended between 15 and 30 from the vertical.8.1.2 Each specimen shall be so placed as to permit freesettling of the humidity atmosphere on all specimens.9. Pr

30、ocedure9.1 Place specimens in the test chamber when the humidityis 100 %.9.2 Keep the chamber shut for the remainder of the expo-sure. Start the first dip cycle immediately after placing thespecimens in the chamber.9.2.1 One dip cycle shall consist of three 5-min immersionperiods. Drain the dip solu

31、tion from the test chamber for a1-min period between each immersion period.9.2.2 Maintain the dip solution at 52 6 1C (125 6 2F).9.3 Cycle the humidity as shown in Fig. 2 during theexposure period.9.3.1 Maintain the temperature in the test chamber at 52 61C (1256 2F).9.3.2 Operate the dip cycle once

32、 a day at a point in thehumidity cycle when the relative humidity is close to 100 %.9.4 The duration of the exposure should be a minimum of20 days. Longer exposure times may be used depending uponthe purpose of the test. Use fresh dip solution for each test, andchange the dip solution at least every

33、 90 days during extendedexposure periods.10. Report10.1 Data for the exposed specimens should include physi-cal dimensions, chemical composition, metallurgical history,surface preparation, and after-exposure cleaning methods.10.2 The report should include the exposure period and themethod of support

34、ing the specimens in the test chamber.10.3 The results of the exposure should be expressed ascorrosion rate (Practice G1) such as penetration per unit time(for example, millimetre per year), loss in thickness over theexposure period, or plotted as mass loss per unit area versustime.10.4 Any disturba

35、nces that significantly alter the prescribedtest conditions invalidate the test. Do not report results fromsuch exposure.11. Keywords11.1 cyclic exposure; exposure cycles; humidity; steels; testequipment4Reagent Chemicals, American Chemical Society Specifications, AmericanChemical Society, Washingto

36、n, DC. For suggestions on the testing of reagents notlisted by the American Chemical Society, see Analar Standards for LaboratoryChemicals, BDH Ltd., Poole, Dorset, U.K., and the United States Pharmacopeiaand National Formulary, U.S. Pharmacopeial Convention, Inc. (USPC), Rockville,MD.G60 01 (2018)3

37、ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are

38、 entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standar

39、dsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committ

40、ee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 01 (2018)4