ASTM F441 F441M-2013e1 Standard Specification for Chlorinated Poly(Vinyl Chloride) (CPVC) Plastic Pipe Schedules 40 and 80《氯化聚氯乙烯(CPVC)塑料管 计划表40和80的标准规范》.pdf

《ASTM F441 F441M-2013e1 Standard Specification for Chlorinated Poly(Vinyl Chloride) (CPVC) Plastic Pipe Schedules 40 and 80《氯化聚氯乙烯(CPVC)塑料管 计划表40和80的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM F441 F441M-2013e1 Standard Specification for Chlorinated Poly(Vinyl Chloride) (CPVC) Plastic Pipe Schedules 40 and 80《氯化聚氯乙烯(CPVC)塑料管 计划表40和80的标准规范》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F441/F441M 131An American National StandardStandard Specification forChlorinated Poly(Vinyl Chloride) (CPVC) Plastic Pipe,Schedules 40 and 801This standard is issued under the fixed designation F441/F441M; the number immediately following the designation indicates the yearof original ad

2、option or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1

3、NOTEX1.7 was editorially revised in September 2013.1. Scope*1.1 This specification covers chlorinated poly(vinyl chlo-ride) (CPVC) pipe made in Schedule 40 and 80 sizes andpressure-rated for water (see appendix). Included are criteriafor classifying CPVC plastic pipe materials and CPVC plasticpipe,

4、a system of nomenclature for CPVC plastic pipe, andrequirements and test methods for materials, workmanship,dimensions, sustained pressure, burst pressure, flattening, andextrusion quality. Methods of marking are also given.NOTE 1The CPVC pipe covered by this specification was coveredpreviously in S

5、pecification D1785.NOTE 2The sustained and burst pressure test requirements, and thepressure ratings in the appendix, are calculated from stress values obtainedfrom tests made on pipe 2 in. 50 mm and smaller. However, tests onlarger pipe have shown these stress values to be valid.1.2 The products co

6、vered by this specification are intendedfor use with the distribution of pressurized liquids only, whichare chemically compatible with the piping materials. Due toinherent hazards associated with testing components and sys-tems with compressed air or other compressed gases somemanufacturers do not a

7、llow pneumatic testing of their products.Consult with specific product/component manufacturers fortheir specific testing procedures prior to pneumatic testing.NOTE 3Pressurized (compressed) air or other compressed gasescontain large amounts of stored energy which present serious safteyhazards should

8、 a system fail for any reason.1.3 The text of this specification references notes, footnotes,and appendixes which provide explanatory material. Thesenotes and footnotes (excluding those in tables and figures) shallnot be considered as requirements of the specification.1.4 The values stated in either

9、 SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.5 The following

10、safety hazards caveat pertains only to thetest methods portion, Section 8, of this specification: Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety and healthpracti

11、ces and determine the applicability of regulatory limita-tions prior to use. A specific precautionary statement is givenin Note 7.2. Referenced Documents2.1 ASTM Standards:2D618 Practice for Conditioning Plastics for TestingD1598 Test Method for Time-to-Failure of Plastic PipeUnder Constant Internal

12、 PressureD1599 Test Method for Resistance to Short-Time HydraulicPressure of Plastic Pipe, Tubing, and FittingsD1600 Terminology forAbbreviated Terms Relating to Plas-ticsD1784 Specification for Rigid Poly(Vinyl Chloride) (PVC)Compounds and Chlorinated Poly(Vinyl Chloride)(CPVC) CompoundsD1785 Speci

13、fication for Poly(Vinyl Chloride) (PVC) PlasticPipe, Schedules 40, 80, and 120D2122 Test Method for Determining Dimensions of Ther-moplastic Pipe and FittingsD2837 Test Method for Obtaining Hydrostatic Design Basisfor Thermoplastic Pipe Materials or Pressure Design Basisfor Thermoplastic Pipe Produc

14、tsF412 Terminology Relating to Plastic Piping Systems1This specification is under the jurisdiction of ASTM Committee F17 on PlasticPiping Systems and is the direct responsibility of Subcommittee F17.25 on VinylBased Pipe.Current edition approved June 1, 2013. Published June 2013. Originallyapproved

15、in 1974. Last previous edition approved in 2012 as F441 12. DOI:10.1520/F0441_F0441M-13.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summa

16、ry page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States12.2 Federal Standard:Fed. Std. No. 123 Marking for Shipment (Civil Agencies)32.3 Military Stan

17、dard:MIL-STD-129 Marking for Shipment and Storage32.4 NSF Standards:Standard No. 14 for Plastic Piping Components and RelatedMaterials4Standard No. 61 for Drinking Water Systems ComponentsHealth Effects43. Terminology3.1 DefinitionsDefinitions are in accordance with Termi-nology F412, and abbreviati

18、ons are in accordance with Termi-nology D1600, unless otherwise specified. The abbreviation forchlorinated poly(vinyl chloride) is CPVC.3.2 Definitions of Terms Specific to This Standard:3.2.1 hydrostatic design stressthe estimated maximumtensile stress the material is capable of withstanding contin

19、u-ously with a high degree of certainty that failure of the pipewill not occur. This stress is circumferential when internalhydrostatic water pressure is applied.3.2.2 pressure rating (PR)the estimated maximum waterpressure the pipe is capable of withstanding continuously witha high degree of certai

20、nty that failure of the pipe will not occur.3.2.3 relation between dimensions, design stress, and pres-sure ratingThe following expression, commonly known asthe ISO equation,5is used in this specification to relatedimensions, hydrostatic design stress, and pressure rating:2 S/P 5 DO/t! 2 1where:S =

21、hydrostatic design stress, psi MPa,P = pressure rating, psi MPa,DO= average outside diameter, in. mm, andt = minimum wall thickness, in. mm.3.2.4 standard thermoplastic pipe materials designationcodeThe pipe materials designation code shall consist of theabbreviation CPVC for the type of plastic, fo

22、llowed by theASTM type and grade inArabic numerals and the design stressat 73F 23C in units of 100 psi 0.7 MPa with any decimalfigures dropped, followed by the design stress at 180F 82Cin units of 100 psi 0.7MPa with any decimal figures dropped.When the design stress code contains less than two figu

23、res, acipher shall be used before the number. Thus a completematerial code shall consist of four letters and six figures forCPVC plastic pipe materials (see Section 5).4. Classification4.1 GeneralThis specification covers CPVC pipe madefrom one (see X1.2) CPVC plastic pipe material in Schedule 40and

24、 80 sizes.4.2 Hydrostatic Design StressesThis specification coversCPVC pipe made from CPVC plastic as defined by hydrostaticdesign stresses which have been developed on the basis oflong-term tests (see appendix).NOTE 4This specification does not include requirements for pipefittings intended to be u

25、sed to vent combustion gases.5. Materials5.1 GeneralChlorinated poly(vinyl chloride) plastics usedto make pipe meeting the requirements of this specification arecategorized by means of two criteria, namely, (1) short-termstrength tests and (2) long-term hydrostatic strength tests atboth 73 and 180F

26、23 and 82C.5.2 Basic Materials:5.2.1 Basic Materials Short-term TestsThis specificationcovers pipe made from CPVC plastics having certain physicalproperties as described in Specification D1784.5.2.1.1 CompoundThe CPVC compounds used for thispipe shall equal or exceed the classification 23447 describ

27、ed inSpecification D1784.5.2.2 Basic Materials Long-term TestThis specificationconvers pipe made from CPVC plastics having certain Hydro-static Design Bases (HDB) and Hydrostatic Design Stresses(HDS) described in Test Method D28375.2.2.1 CompoundThe CPVC compounds used for thispipe shall have a Hydr

28、ostatic Design Basis at 73F 23C of4000 psi 28 MPa, , and a Hydrostatic Design Basis at 180F82C of either 1000 psi 7.0 MPa or 1250 psi 8.6 MPawhen evaluated in accordance with Test Method D28375.2.3 Standard thermoplastic pipe materials designationThe pipe materials designation shall consist of the m

29、aterialdesignation code CPVC 4120-05 or CPVC 4120-06 for thetype of plastic.NOTE 5As per Terminology F412 (see, “code, thermoplastic pipematerials designation”) the pipe materials designation code CPVC 4120 isas follows: CPVC is the abbreviation for chlorinated poly(vinyl chloride)as per Terminology

30、 D1600, 41 represents Cell Classification 23447 perSpecification D1784, and 20 represents a HDS of 2000 psi 14 MPa forwater at 73F (23C) per Test Method D2837. In addition, the -05 or -06suffix represents a HDS of 500 psi 3.4 MPa or 625 psi 4.3 MParespectively for water at 180F 82C per Test Method D

31、2837.5.3 Rework MaterialThe manufacturers shall use onlytheir own clean rework pipe material and the pipe producedshall meet all the requirements of this specification.6. Requirements6.1 Dimensions and Tolerances:6.1.1 Dimensions and tolerances shall be as shown in Table1 and Table 2 when measured i

32、n accordance with Test MethodD2122. The tolerances for out-of-roundness shall apply only topipe prior to shipment.6.1.2 Wall Thickness RangeThe wall thickness range shallnot exceed 12 % when measured in accordance with TestMethod D2122.6.2 Sustained PressureThe pipe shall not fail, balloon,burst, or

33、 weep as defined in Test Method D1598, at the testpressures given in Table 3, when tested in accordance with 8.4.3Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.dodssp.daps.mil.4Available from NSF International

34、, P.O. Box 130140, 789 N. Dixboro Rd., AnnArbor, MI 48113-0140, http:/www.nsf.org.5ISO R 161-1960, Pipes of Plastics Materials for the Transport of Fluids(Outside Diameters and Nominal Pressures) Part 1, Metric Series.F441/F441M 13126.2.1 Accelerated Regression TestThe accelerated regres-sion test s

35、hall be used in place of both the sustained and burstpressure tests at the option of the manufacturer. The test shallbe conducted in accordance with 8.4.1. The pipe shall demon-strate a hydrostatic design basis projection at the 100 000 hintercept that meets the hydrostatic design basis categoryrequ

36、irement (see Table 1, Test Method D2837) for the CPVCmaterial used in its manufacture. If the lower confidence valueat 100 000 h differs from the extrapolated LTHS value by morethan 15 % of the latter; or M in Appendix X2 (Test MethodD2837) is zero or negative; or b in the equation h = a + bf inAppe

37、ndix X1 (Test Method D2837) is positive, consider thedata unsuitable.6.3 Burst PressureThe minimum burst pressures forCPVC plastic pipe shall be as given in Table 4, whendetermined in accordance with Test Method D1599.6.4 FlatteningThere shall be no evidence of splitting,cracking, or breaking when t

38、he pipe is tested in accordancewith 8.5.7. Workmanship, Finish, and Appearance7.1 The pipe shall be homogeneous throughout and freefrom visible cracks, holes, foreign inclusions, or other defects.The pipe shall be as uniform as commercially practicable incolor, opacity, density, and other physical p

39、roperties.TABLE 1 Outside Diameters and Tolerances for CPVC Plastic Pipe, Schedules 40 and 80, in. mmTolerancesMaximum Out-of-Roundness(maximum minus minimum diameter)Nominal Pipe Size Outside Diameter Schedule 40 sizes312 in. and over;Schedule 80sizes 8 in. and overSchedule 40 sizes3 in. and less;S

40、chedule 80 sizes6 in. and less14 8 0.540 13.7 0.004 0.10 . 0.016 (0.41)38 10 0.675 17.1 0.004 0.10 . 0.016 (0.41)12 15 0.840 21.3 0.004 0.10 . 0.016 (0.41)34 20 1.050 26.7 0.004 0.10 . 0.020 (0.51)1 25 1.315 33.4 0.005 0.13 . 0.020 (0.51)114 32 1.660 42.2 0.005 0.13 . 0.024 (0.61)112 40 1.900 48.3 0

41、.006 0.15 . 0.024 (0.61)2 50 2.375 60.3 0.006 0.15 . 0.024 (0.61)212 65 2.875 73.0 0.007 0.18 . 0.030 (0.76)3 80 3.500 88.9 0.007 0.18 . . . 0.023 (0.58)312 90 4.000 101.6 0.008 0.20 0.100 (2.54) 0.030 (0.76)4 100 4.500 114.3 0.008 0.20 0.100 (2.54) 0.023 (0.58)5 125 5.563 141.3 0.010 0.25 0.100 (2.

42、54) 0.060 (1.52)6 150 6.625 168.3 0.011 0.28 0.100 (2.54) 0.070 (1.78)8 200 8.625 219.1 0.015 0.38 0.150 (3.81) 0.090 (2.29)10 250 10.750 273.1 0.015 0.38 0.150 (3.81) 0.100 (2.54)12 300 12.750 323.9 0.015 0.38 0.150 (3.81) 0.120 (3.05)14 350 14.000 355.6 0.015 0.380 0.200 (5.08) .16 400 16.000 406.

43、4 0.019 0.480 0.320 (8.13) .TABLE 2 Wall Thicknesses and Tolerances for CPVC Plastic Pipe, Schedules 40 and 80, in.A,BmmNominal PipeSizeWall ThicknessASchedule 40 Schedule 80Min Tolerance Min Tolerance14 8 0.088 2.24 +0.020 0.51 0.119 3.02 +0.020 0.5138 10 0.091 2.31 +0.020 0.51 0.126 3.20 +0.020 0.

44、5112 15 0.109 2.77 +0.020 0.51 0.147 3.73 +0.020 0.5134 20 0.113 2.87 +0.020 0.51 0.154 3.91 +0.020 0.511 25 0.133 3.38 +0.020 0.51 0.179 4.55 +0.021 0.53114 32 0.140 3.56 +0.020 0.51 0.191 4.85 +0.023 0.58112 40 0.145 3.68 +0.020 0.51 0.200 5.08 +0.024 0.612 50 0.154 3.91 +0.020 0.51 0.218 5.54 +0.

45、026 0.66212 65 0.203 5.16 +0.024 0.61 0.276 7.01 +0.033 0.843 80 0.216 5.49 +0.026 0.66 0.300 7.62 +0.036 0.91312 90 0.226 5.74 +0.027 0.68 0.318 8.08 +0.038 0.964 100 0.237 6.02 +0.028 0.71 0.337 8.56 +0.040 1.025 125 0.258 6.55 +0.031 0.79 0.375 9.52 +0.045 1.146 150 0.280 7.11 +0.034 0.86 0.432 1

46、0.97 +0.052 1.328 200 0.322 8.18 +0.039 0.99 0.500 12.70 +0.060 1.5210 250 0.365 9.27 +0.044 1.12 0.593 15.06 +0.071 1.8012 300 0.406 10.31 +0.049 1.24 0.687 17.45 +0.082 2.0814 350 0.437 11.10 +0.053 +1.35 0.750 19.05 +0.090 +2.2916 400 0.500 12.70 +0.060 +1.52 0.843 21.14 +0.101 +2.57AThe minimum

47、is the lowest wall thickness of the pipe at any cross section. All tolerances are on the plus side of the minimum requirement.BThese dimensions conform to nominal IPS dimensions.F441/F441M 1313NOTE 6Color and transparency or opacity should be specified in thecontract or purchase order.8. Test Method

48、s8.1 ConditioningCondition the test specimens at 73.4 63.6F 23 6 2C and 50 6 5 % relative humidity for not lessthan 40 h prior to test in accordance with Procedure A ofPractice D618, for those tests where conditioning is required.8.2 Test ConditionsConduct tests in the standard labora-tory atmosphere of 73 6 3.6F 23 6 2C and 50 6 5%relative humidity, unless otherwise specified in the test meth-ods or in this specification.8.3 SamplingThe