ASTM D2152-1995(2010) Standard Test Method for Adequacy of Fusion of Extruded Poly(Vinyl Chloride) (PVC) Pipe and Molded Fittings by Acetone Immersion《用丙酮浸渍法测定挤压制聚氯乙烯管(PVC)和模制配件溶合度.pdf

《ASTM D2152-1995(2010) Standard Test Method for Adequacy of Fusion of Extruded Poly(Vinyl Chloride) (PVC) Pipe and Molded Fittings by Acetone Immersion《用丙酮浸渍法测定挤压制聚氯乙烯管(PVC)和模制配件溶合度.pdf》由会员分享，可在线阅读，更多相关《ASTM D2152-1995(2010) Standard Test Method for Adequacy of Fusion of Extruded Poly(Vinyl Chloride) (PVC) Pipe and Molded Fittings by Acetone Immersion《用丙酮浸渍法测定挤压制聚氯乙烯管(PVC)和模制配件溶合度.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D2152 95 (Reapproved 2010)An American National StandardStandard Test Method forAdequacy of Fusion of Extruded Poly(Vinyl Chloride) (PVC)Pipe and Molded Fittings by Acetone Immersion1This standard is issued under the fixed designation D2152; the number immediately following the designati

2、on indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agen

3、cies of the Department of Defense.1. Scope1.1 This test method covers the determination of the ad-equacy of fusion of extruded rigid poly(vinyl chloride) (PVC)pipe and molded fittings as indicated by reaction to immersionin anhydrous acetone.1.2 The values stated in inch-pound units are to be regard

4、edas the standard except where instruments are calibrated in SIunits.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the

5、applica-bility of regulatory limitations prior to use. Specific hazardsstatements are given in Annex A1.2. Referenced Documents2.1 ASTM Standards:2D618 Practice for Conditioning Plastics for Testing3. Significance and Use3.1 This test method is applicable only for distinguishingbetween inadequately

6、fused and adequately fused PVC. Thedifference between thermally degraded and adequately fusedPVC cannot be detected by this test method. Acetone immer-sion is not a substitute for burst, impact, or other physical orchemical tests on PVC pipe or fittings and it, therefore, shallnot be used as the onl

7、y test specification for purchasing of PVCpipe and fittings. This test only detects inadequate fusion anddoes not determine the over-all quality of the PVC pipe orfittings.3.2 This test method is useful in determining whetherinadequate fusion contributed to failure of PVC pipe or fittingsin other ph

8、ysical or chemical tests, or in service.3.3 This test method is useful in evaluating the adequacy ofPVC fusion obtained in process or materials trials.3.4 This test method determines adequacy of fusion on asingle, relatively small specimen. This test method requires theuse of a hazardous reagent whi

9、ch must be properly handled anddisposed. Therefore, this test method may not be cost-effectiveto employ as a routine quality control test.4. Apparatus4.1 ContainerEither individual, sealable containers foreach specimen or one large, airtight container capable ofholding several specimens without touc

10、hing one another.4.2 Hydrometer and CylinderPrecision hydrometer,graduated in thousandths, with a minimum range of 0.780 to0.790 g/mL and a cylinder large enough to immerse thehydrometer.4.3 ThermometerASTM 12C total immersion thermom-eter, range from 20C to 102C accurate to 0.2C, orequivalent.5. Re

11、agent5.1 AcetoneAmerican Chemical Society Reagent Grade,having a maximum density of 0.7857 g/mL at 25C.NOTE 1SeeAnnexA1 for the safety and health precautions to be usedwith acetone.5.2 Prior to conducting the test, check the density of theacetone with a precision hydrometer to determine its dryness.

12、If the density of the acetone is greater than 0.7890 g/mL at23C, (corresponding to approximately 1 % water by mass (seeFig. X1.1), use fresh acetone or dry the wet acetone with adrying agent. Recheck the density of the fresh or dried acetonebefore using.NOTE 2Wet acetone can be dried by thoroughly a

13、gitating it with atleast 15 g of anhydrous calcium sulfate (CaSO4) for each gram of waterpresent.NOTE 3The presence of water in the acetone reduces its sensitivity todifferences in the degree of fusion of rigid poly(vinyl chloride) (PVC). It1This test method is under the jurisdiction of ASTM Committ

14、ee F17 on PlasticPiping Systems and is the direct responsibility of Subcommittee F17.25 on VinylBased Pipe.Current edition approved April 1, 2010. Published May 2010. Originallyapproved in 1963T. Last previous edition approved in 2003 as D2152 95 (2003).DOI: 10.1520/D2152-95R10.2For referenced ASTM

15、standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohock

16、en, PA 19428-2959, United States.is important to dry the acetone properly and conduct the test in a sealedcontainer, because acetone rapidly absorbs moisture from the atmosphere.NOTE 4Round-robin testing between four laboratories showed thattest results are not significantly altered with up to 2 % w

17、ater by weight inthe acetone.6. Sampling6.1 Specimens shall be taken from individual pipe sections,fittings, or remnant portions of pipe or fittings. Specimens shallbe taken from locations which are to be evaluated for adequacyof fusion, or immediately adjacent to them.6.2 The number of individual s

18、pecimens to be tested andtheir locations shall be chosen to be representative of the pipeor fittings being evaluated for adequacy of fusion.7. Test Specimens7.1 Size of SpecimenSpecimen shall be a size that isconvenient to immerse in the test container but not less than12in. (13 mm) in height. For s

19、mall diameter pipe, the specimenshall be a complete circumferential section of the pipe. Forlarge diameter pipe, the specimen shall be a full pipe sectionbut it may be cut into smaller pieces to facilitate testing. Smallmolded parts shall be immersed as a single item. For largemolded fittings, the s

20、pecimen shall be a complete circumfer-ential section which may be cut into segments before beingimmersed. If the pipe or fitting to be evaluated has fractured orfragmented in other tests or in service, specimens of any shapeand size may be tested.7.2 Specimen PreparationFor pipe having a wall thick-

21、ness greater than 0.125 in. (3.2 mm) the wall thickness shall bereduced by at least one-half its thickness for a minimum ofone-half the height of the specimen at six or more intervalsaround the circumference of one end of the specimen. Removalshall be effected by filing, wet sanding, or other means

22、that willminimize localized heating of the surface. It is not necessary toreduce the wall thickness on molded fittings.8. Conditioning8.1 Unless otherwise specified, condition the specimens inairfor1hat236 2C (73.4 6 3.6F) prior to testing. Thespecimens shall not be conditioned in water because of t

23、heeffect water has on the acetone. For referee purposes condi-tioning shall be in accordance with Procedure A of PracticeD618.9. Procedure9.1 Conduct the tests in a Standard Laboratory Atmosphereof 23 6 2C unless otherwise specified.9.2 Place sufficient dried acetone into the container toensure comp

24、lete immersion of the specimen.9.3 Place the test specimen in the acetone, seal the con-tainer, and do not agitate. Allow specimen to stand immersedfor 20 min.9.4 After 20 min, remove the specimen from the containerand inspect for signs of attack.9.5 Attack is described as a lifting, raising, or rem

25、oving, orboth, of any material outside surface, inside surface, ormid-wall, of the specimen. Swelling or softening of the testspecimen shall not be considered attack.10. Fusion Criteria10.1 At least 50 % attack of the inside, outside, or mid-wallsurface or at least 10 % attack on more than one surfa

26、ce shallbe considered to be indicative of inadequate fusion.11. Report11.1 The report shall include the following:11.1.1 Complete identification of the PVC compound,11.1.2 Production code number of the pipe or fittings,11.1.3 Nominal dimensions of the pipe or fittings,11.1.4 Observations after 20 mi

27、n immersion shall be re-ported indicating attack or no attack,11.1.5 The area attacked, inside, outside, or mid-wall, andthe estimated percentage of that area attacked, and11.1.6 Date of test.12. Precision and Bias12.1 This test method is subjective, based on operatorjudgement. Therefore a statement

28、 on precision and bias is notapplicable.13. Keywords13.1 acetone; fusion; pipe; poly(vinyl chloride); PVCANNEX(Mandatory Information)A1. RECOMMENDED SAFETY PRECAUTIONS TO BE USED WITH ACETONEA1.1 Safety Requirements:A1.1.1 No source of ignition is to be permitted whereacetone is used.A1.1.2 Dispense

29、 acetone only from approved safety con-tainers.A1.1.3 Dispose of used acetone, or acetone-impregnatedcloths only in an approved safety waste receptacle.A1.1.4 Avoid prolonged breathing of acetone. Use acetoneonly in a well ventilated area.A1.1.5 Use proper eye protection such as chemical-workers gog

30、gles or a face shield when handling acetone.A1.1.6 Avoid prolonged exposure to the skin. If prolongedexposure to the skin cannot be avoided, use protective clothing.A1.2 Health Hazards:A1.2.1 Acetone is a mild irritant to eyes, nose and throat butonly minor residual injury will occur if no medical t

31、reatment isgiven.D2152 95 (2010)2A1.2.2 Prolonged or continuous exposure of acetone to theskin may cause acute or chronic dermatitis. Exposed skin areasshould be washed and dried. Consult a physician if a rashdevelops.A1.3 Fire Hazard:A1.3.1 Acetone is a very flammable liquid having a flashpoint of

32、18C (0F). Use dry chemical, alcohol foam, orcarbon dioxide to fight a fire. Use water to keep fire-exposedcontainers cool or to wash away or dilute spills which have notignited.APPENDIX(Nonmandatory Information)X1. DENSITY OF ACETONE VERSUS PERCENT WATER AT FOUR TEMPERATURESASTM International takes

33、no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own respo

34、nsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed

35、 to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the a

36、ddress shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).FIG. X1.1 Density of Acetone versus Percent Water at Four TemperaturesD2152 95 (2010)3