ASTM A917-2008(2015) Standard Specification for Steel Sheet Coated by the Electrolytic Process for Applications Requiring Designation of the Coating Mass on Each Surface (General R.pdf
《ASTM A917-2008(2015) Standard Specification for Steel Sheet Coated by the Electrolytic Process for Applications Requiring Designation of the Coating Mass on Each Surface (General R.pdf》由会员分享,可在线阅读,更多相关《ASTM A917-2008(2015) Standard Specification for Steel Sheet Coated by the Electrolytic Process for Applications Requiring Designation of the Coating Mass on Each Surface (General R.pdf(3页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: A917 08 (Reapproved 2015)Standard Specification forSteel Sheet, Coated by the Electrolytic Process forApplications Requiring Designation of the Coating Mass onEach Surface (General Requirements)1This standard is issued under the fixed designation A917; the number immediately following t
2、he designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification cove
3、rs hot-rolled and cold-rolled steelsheet coated by the electrolytic process. Coatings can becomprised of pure metals or metal alloys. For specific coatings,refer to Specifications A879/A879M and A918.1.2 The product shall be coated on one or both surfaces withequal or differential coating masses on
4、the two surfaces.Sheet-coated with equal coating masses on each surface hassimilar levels of corrosion protection on each surface. Often,however, a higher level of corrosion protection is required onone surface than is required on the other. In these situations,one surface shall be specified with a
5、heavier coating mass thanthe other. Either surface, when specified to be painted, willprovide additional corrosion protection as compared to anunpainted surface.1.3 This coating process has essentially no effect on the basemetal mechanical properties, and use is permitted on any gradeof hot-rolled o
6、r cold-rolled steel sheet. The coated sheet isavailable as Commercial Steel (CS), Drawing Steel (DS), DeepDrawing Steel (DDS), Extra-Deep Drawing Steel (EDDS),Structural Steel (SS) High-Strength Low-Alloy Steel(HSLAS), High-Strength Low-Alloy Steel with ImprovedFormability (HSLAS-F), Solution-Harden
7、ed Steel (SHS), orBake-Hardenable Steel (BHS).1.4 The values stated in SI units are to be regarded as thestandard.2. Referenced Documents2.1 ASTM Standards:2A90/A90M Test Method for Weight Mass of Coating onIron and Steel Articles with Zinc or Zinc-Alloy CoatingsA370 Test Methods and Definitions for
8、 Mechanical Testingof Steel ProductsA754/A754M Test Method for Coating Weight (Mass) ofMetallic Coatings on Steel by X-Ray FluorescenceA879/A879M Specification for Steel Sheet, Zinc Coated bythe Electrolytic Process for Applications Requiring Des-ignation of the Coating Mass on Each SurfaceA902 Term
9、inology Relating to Metallic Coated Steel Prod-uctsA918 Specification for Steel Sheet, Zinc-Nickel AlloyCoated by the Electrolytic Process for Applications Re-quiring Designation of the Coating Mass on Each SurfaceA1008/A1008M Specification for Steel, Sheet, Cold-Rolled,Carbon, Structural, High-Stre
10、ngth Low-Alloy, High-Strength Low-Alloy with Improved Formability, SolutionHardened, and Bake HardenableA1011/A1011M Specification for Steel, Sheet and Strip,Hot-Rolled, Carbon, Structural, High-Strength Low-Alloy, High-Strength Low-Alloy with ImprovedFormability, and Ultra-High StrengthB504 Test Me
11、thod for Measurement of Thickness of Metal-lic Coatings by the Coulometric Method3. Terminology3.1 Definitions For definitions of terms and abbreviationsused in this specification, see Terminology A902.4. Ordering Information4.1 Ordering information for all products is shown in theindividual product
12、 specifications.5. Coating Designation (Mass and Type)5.1 The following seven-character format shall be used toidentify the coating mass required:5.1.1 First and Second Characters Minimum coatingmass of the surface with the less critical surface qualityrequirements;5.1.2 Third Character A letter, as
13、 designated in theappropriate product specification, to denote the kind of coating;G for pure zinc and N for zinc-nickel alloy;1This specification is under the jurisdiction of ASTM Committee A05 onMetallic-Coated Iron and Steel Products and is the direct responsibility ofSubcommittee A05.11 on Sheet
14、 Specifications.Current edition approved May 1, 2015. Published May 2015. Originallyapproved in 1993. Last previous edition approved in 2008 as A917 - 08. DOI:10.1520/A0917-08R15.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org.
15、 For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15.1.3 Fourth and Fifth Characters Minimum coatingmass of the surface
16、 with the more critical surface qualityrequirements;5.1.4 Sixth Character A letter, as designated in the appro-priate product specification, to denote the kind of coating; Gfor pure zinc and N for zinc-nickel alloy;5.1.5 Seventh CharacterEither E or U, designating anexposed or unexposed application,
17、 respectively.Example: 60 G 20 G ESee Section: 5.1.1 5.1.2 5.1.3 5.1.4 5.1.5NOTE 1The terms “exposed” and “unexposed” describe the intendedapplication as either hidden or exposed to view and is an indicator of thedegree of freedom from surface imperfections that affect the cosmeticcharacteristics of
18、 the coated surface.6. Chemical Requirements6.1 The heat analysis of the steel shall conform to therequirements of the specification for the steel ordered or asspecified by negotiations.7. Base Metal Requirements7.1 The steel shall conform to all of the requirements of theappropriate specification l
19、isted as follows for the steel ordered.Where reference is made to a combined standard (such asSpecification A1011/A1011M), conformance shall be to themetric portion, using SI units of measurement as standard.7.1.1 Hot Rolled:7.1.1.1 Commercial Steel (CS), Drawing Steel (DS), Struc-tural Steel (SS),
20、High-Strength Low-Alloy Steel (HSLAS), andHigh-Strength Low-Alloy Steel with Improved Formability(HSLAS-F)Specification A1011/A1011M.7.1.2 Cold Rolled:7.1.2.1 Commercial Steel (CS), Drawing Steel (DS), DeepDrawing Steel (DDS), Extra-Deep Drawing Steel (EDDS),Structural Steel (SS), High-Strength Low-
21、Alloy Steel (HSLAS),High-Strength Low-Alloy Steel with Improved Formability(HSLAS-F), Solution-Hardened Steel (SHS), and Bake-Hardenable Steel (BHS)Specification A1008/A1008M.7.2 Base Metal Specimens:7.2.1 Test specimens shall be prepared from finished mate-rial and tested in accordance with Test Me
22、thods and DefinitionsA370.7.2.2 In determining the base metal mechanical properties,one of the following methods shall be used. Unless specified inthe order, the producer shall determine the method to be used;however, in the event of a dispute the method in 7.2.2.1 shallbe used.7.2.2.1 The base meta
23、l thickness shall be measured afterstripping the coating from the ends of the specimen contactingthe grips of the tension testing machine before testing.7.2.2.2 The base metal thickness shall be determined bysubtracting the coating thickness from the measured thicknessof the tension test specimen. T
24、he coating thickness shall becalculated from the coating mass test.7.2.3 When the percent elongation in the tension test is lessthan the specified minimum and any part of the fracture isoutside the middle half of the gage length as scribed before thetest, the test shall be discarded and a retest sha
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMA91720082015STANDARDSPECIFICATIONFORSTEELSHEETCOATEDBYTHEELECTROLYTICPROCESSFORAPPLICATIONSREQUIRINGDESIGNATIONOFTHECOATINGMASSONEACHSURFACEGENERALRPDF
链接地址:http://www.mydoc123.com/p-459961.html