FORD ESA-M4G294-A-1988 SEALER SILICONE RUBBER - NEUTRAL CURE《中性固化的硅橡胶密封剂》.pdf

《FORD ESA-M4G294-A-1988 SEALER SILICONE RUBBER - NEUTRAL CURE《中性固化的硅橡胶密封剂》.pdf》由会员分享，可在线阅读，更多相关《FORD ESA-M4G294-A-1988 SEALER SILICONE RUBBER - NEUTRAL CURE《中性固化的硅橡胶密封剂》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONMaterial Name Specification NumberDate Action Changes1988 07 01 RD-226350-C9 Revised87 10 14 CDR2-171150-C9 ReleasedWP 3948-a Page 1 of 3 SEALER, SILICONE RUBBER - NEUTRAL CURE ESA-M4G294-A1. SCOPEThe mate rial defined by this specification is a one component silic

2、onerubber adhesive/sealer which wi ll cure at room temperature in the presenceof moisture. Vapors given off during the cure are non-acidic.2. APPLICATIONThis specification was released originally for material used to attachmolded acrylic medallions to wheel covers or ornaments.3. REQUIREMENTS3.1 The

3、 following tests are to be conducted on each lot of material.3.1.1 Viscosity 6.5 +/- 2.0(FLTM BV 3-1, except use 345 kPa airpressure and a 3.18 mm diameter opening.)3.1.2 Cure Rate PassTe st Method: Apply a 3.18 mm diameter bead of sealer to asteel plate and allow to cure for 5 h at 25 +/- 3 C and 5

4、0+/- 5 % relative humidity. After 5 h, compress the sealerbead to a height of 1.0 mm maximum for 1 min. Spacer barsmay b e used for proper dimensioning. Sealer must besufficiently cured so the skin does not break, s plit or crackduring compression.3.1.3 Specific Gravity 1.04 +/- 0.03(ASTM D 792, Met

5、hod A)3.2 The following tests plus the tests required in para 3.1, are to beconducted at the time of initial material approv al and as directed byQuality Control. Requirements are to be fulfille d using approximately1.8 mm thick slabs prepared in accordance with the manufacturersrecommendations.3.2.

6、1 Tensile Strength, MPa, min 1.2(ASTM D 412, dumbbell specimen)3.2.2 Elongation, % min 240(ASTM D 412, dumbbell specimen)ENGINEERING MATERIAL SPECIFICATIONESA-M4G294-AWP 3948-b Page 2 of 3 3.2.3 Hardness, Durometer A 20-40(ASTM D 2240)3.2.4 QualityTh e material shall be a smooth homogeneous mixture,

7、 free fromforeign materials and properties detrimental to normalprodu ction applications. It shall not contain particles orsolid spots o f sufficient size to cause blockage of an 0.05 mmdiameter orifice.3.2.5 Infrared SpectrophotometryFord Motor Company, at its option, may conduct infraredanalysis o

8、f material/parts supplied to this specification. Thespec tra established for initial approval shall constitute thereference sta ndard and shall be kept on file at the designatedmate rial laboratory. All samples shall produce spectra thatcorrespond to the reference standard w hen tested under the sam

9、econditions as those specified on the master spectrum.3.3 STATISTICAL PROCESSSupp liers must conform to the requirements of Ford Quality SystemStandard Q-101. A mutually acceptable Control Plan as describe d thereinis required for material/source approval. Appropriate statisti cal toolsmust be used

10、to analyze process/product data so that variation in thefinal product is continuously reduced.3.4 SUPPLIERS RESPONSIBILITYAll materials supplied to this specification must be equivalent in allcharact eristics to the material upon which approval was originallygranted.Prior to making any change in the

11、 properties, composition, cons truction,color, processing or labeling of the m aterial originally approved underthi s specification, whether or not such changes affect the materialsability to meet the specification requirements, the Supplier shallno tify Purchasing, Toxicology and the affected Mater

12、ials Engineeringactivity of the proposed changes and o btain the written approval of theMaterials Engineering activity. Test data, test samples and a new codeidentification are to be submitted with the request.Substance restrictions imposed by law, regulations or Ford, app ly to thematerials add res

13、sed by this document. The restrictions are defined inEngineering M aterial Specification WSS-M99P9999-A1, unless a differentsuffix (e.g., A2 or A3) is specified on the engineering documen t for theapplication.ENGINEERING MATERIAL SPECIFICATIONESA-M4G294-AWP 3948-b Page 3 of 3 4. APPROVAL OF MATERIAL

14、SMat erials defined by this specification must have prior approval by theresponsible Materials Engineering activity. Suppliers desiring approval oftheir materials shall first obtain an expression of interest from the a ffectedPurchasi ng, Design and Materials Engineering activity. Upon request, theS

15、upplier shall submit to the affected Materials Engineering activity its ownlaboratory report to the specification (test results, not nominal value s), thematerial designation and code number, and test specimens for Ford evaluation.Upon approval, the material will be added to the Engineering Material

16、 A pprovedSource List.5. GENERAL INFORMATIONThis information is for direction of the user and is not a requirement for thesupplier.5.1 STORAGE STABILITYMaterial shall retain original propert ies for a period of 6 months fromthe date of s hipment when stored in unopened container at temperaturesbetween 20 C-30 C.5.2 SAFETYThis material may release MeOH during cure. Adequate ventilati on shouldbe provided in the work environment to prevent build up of fumes.