FORD SK-M1J9554-A-2010 CLEAR TOPCOAT EXTERIOR QUALITY TO BE USED WITH FORD WSS-M99P1111-A 《外观级透明面漆 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD SK-M1J9554-A-2010 CLEAR TOPCOAT EXTERIOR QUALITY TO BE USED WITH FORD WSS-M99P1111-A 《外观级透明面漆 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD SK-M1J9554-A-2010 CLEAR TOPCOAT EXTERIOR QUALITY TO BE USED WITH FORD WSS-M99P1111-A 《外观级透明面漆 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2010 03 16 N-STATUS No replacement named L. Sinclair, NA 2007 12 05 Revised Updated format; no technical change 1973 06 29 Released B/PX 9960 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 1 of 2 CLEAR TOPCO

2、AT, EXTERIOR QUALITY SK-M1J9554-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a clear two component topcoat. 2. APPLICATION In conjunction with hardener SK-M99J9608-A the material is used as clear topcoat on metallic base coat according to SK-M1J9553-A. 3. RE

3、QUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 COMPOSITION 3.1.1 Vehicle Essentially synthetic resin. 3.1.2 Toxicity The use of cadmium is prohibited

4、. Contents of toxic components, e.g. benzene, chlorinated hydrocarbons, lead compounds, etc. shall conform to the safety regulations currently prevailing in the workshop where the material shall be used. 3.1.3 Mixing Ratio Including recommended thinner and spray viscosity as specified by vendor. 3.1

5、.4 Reaction Time Prior to Application As specified by vendor. 3.1.5 Pot Life (ready to spray) Approximately 6 hours at 20 C. ENGINEERING MATERIAL SPECIFICATIONSK-M1J9554-A Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 2 of 2 3.2 PHYSICAL PROPERTIES 3.2.1 Non Vola

6、tile (FLTM BI 102-01) According to the initial sample report +/- 1. 3.2.2 Package Viscosity 75 +/- 10 s FC 4/25 C (FLTM BI 111-01) 3.2.3 Flash Point The flash point shall conform to the safety regulations applicable to the workshop where the material shall be used. 3.2.4 Shelf Stability During a storage of 6 months at room temperature, the material as received shall not gel or liver upon standing. The viscosity of the material shall not increase in excess of 10 s when tested according to FLTM EU-BI 2-3. 3.3 OTHER REQUIREMENTS See SK-M1J9553-A.