FORD ESF-M1L44-A-2006 CABLE-STRANDED VINYL INSULATED EXTRA FLEXIBLE) #19 GAGE TO BE USED WITH FORD WSS-M99P1111-A 《乙烯树脂绝缘的超高柔性绞合电缆》.pdf

《FORD ESF-M1L44-A-2006 CABLE-STRANDED VINYL INSULATED EXTRA FLEXIBLE) #19 GAGE TO BE USED WITH FORD WSS-M99P1111-A 《乙烯树脂绝缘的超高柔性绞合电缆》.pdf》由会员分享，可在线阅读，更多相关《FORD ESF-M1L44-A-2006 CABLE-STRANDED VINYL INSULATED EXTRA FLEXIBLE) #19 GAGE TO BE USED WITH FORD WSS-M99P1111-A 《乙烯树脂绝缘的超高柔性绞合电缆》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 11 06 Revised ESF-M1L44-B Revised 3.2; 3.3 Para 3.6 after the bend test, the cable shall pass the dielectric breakdown test, para 3.5.3. 3.5.5 Cold Resistance A straight specimen shall be reduced to a temperature of -40 C at a rate not to

2、 exceed 50 C/min. After maintaining this temperature for 3 h and while still at this low temperature, the cable shall be wrapped around a mandrel 25 mm in diameter at the uniform rate of one turn in 10 s for 4 full turns. The insulation shall be removed for a distance of 25 mm from each end of the s

3、pecimen and the specimen subjected to the dielectric test, para 3.5.3. 3.5.6 Flame Test A 610 mm specimen shall be suspended in a vertical position within a partial enclosure which allows a flow of sufficient air for complete combustion but is free from drafts. The tip of a 50 mm gas flame with an inner cone one-third its height shall then be applied to the end of the specimen for 15 s. After removal of the flame, the specimen shall not continue to burn for more than 90 s. 3.5.7 Abrasion Resistance, min 508 mm of tape (SAE J1128, 1 lb (0.45 kg) weight)