ASTM B973-2010(2014) Standard Specification for Tin-Coated Braid and Ribbon Flat Copper Wire intended for use in Electronic Application《预用作电子设施的镀锡织带和缎带扁铜线的标准规格》.pdf

《ASTM B973-2010(2014) Standard Specification for Tin-Coated Braid and Ribbon Flat Copper Wire intended for use in Electronic Application《预用作电子设施的镀锡织带和缎带扁铜线的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B973-2010(2014) Standard Specification for Tin-Coated Braid and Ribbon Flat Copper Wire intended for use in Electronic Application《预用作电子设施的镀锡织带和缎带扁铜线的标准规格》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B973 10 (Reapproved 2014)Standard Specification forTin-Coated Braid and Ribbon Flat Copper Wire intended foruse in Electronic Application1This standard is issued under the fixed designation B973; the number immediately following the designation indicates the year oforiginal adoption or,

2、 in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers tin-coated hard-drawn copperbraid and ribbon flat wire

3、 intended for electronic application(Explanatory Note 1).1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.2.1 ExceptionsThe SI value

4、s for density, resistivity, andvolume are to be regarded as standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the

5、applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2B1 Specification for Hard-Drawn Copper WireB3 Specification for Soft or Annealed Copper WireB49 Specification for Copper Rod Drawing Stock for Elec-trical PurposesB193 Test Method for Resistivity of Elec

6、trical ConductorMaterialsB258 Specification for Nominal Diameters and Cross-SectionalAreas ofAWG Sizes of Solid Round Wires Usedas Electrical Conductors2.2 Other Standards:3NBS Handbook 100 Copper Wire Tables3. Ordering Information3.1 Orders for material under this specification shall includethe fol

7、lowing information:3.1.1 Quantity of each size,3.1.2 Wire size-thickness and width in inches (see 5.3),3.1.3 Type of copper, if special (see 4.2),3.1.4 Package size (see 10.1),3.1.5 Special packaging marking, if required, and3.1.6 Place of inspection (see 7.1).4. Material4.1 Tin for CoatingThe tin s

8、hall be electroplated for thecoating and shall be commercially pure (Explanatory Note 1).For purposes of this specification, the tin shall be consideredcommercially pure if the total of other elements, exclusive ofcopper, does not exceed 1 %. Not withstanding the previoussentence, chemical analysis

9、of the tin coating or of the tin usedfor coating shall not be required under this specification.4.2 Copper-Base MetalThe base metal shall be copper ofsuch quality and purity that the finished product shall haveproperties and characteristics prescribed in this specification.NOTE 1Specifications B1, B

10、3,orB49 defines copper suitable for use.5. General Requirements (See Section 8)5.1 Tensile and ElongationThe tin-coated copper flat wirein the hard drawn condition shall conform to elongationrequirements of 1 % minimum to 5 % maximum. The tensilestrength shall be 55 000 psi (379 MPa) minimum.5.2 Res

11、istivity (Explanatory Note 3)The electrical resis-tivity of the coated wire at a temperature of 20C shall notexceed the values prescribed in Table 1.5.3 Dimensions and Permissible VariationsThe flat wiresizes shall be expressed as the thickness and width of the wirein decimal fractions of an inch to

12、 the nearest 0.0001 in. (0.0025mm). The tin-coated flat wire shall not vary from the specifiedthickness and width by more than the amounts specified inTable 2 and Table 3, respectively.5.4 Continuity of CoatingThe tin coating shall be continu-ous. The continuity of coating on the flat wire shall bed

13、etermined on representative samples taken before braiding1This specification is under the jurisdiction of ASTM Committee B01 onElectrical Conductors and is the direct responsibility of Subcommittee B01.04 onConductors of Copper and Copper Alloys.Current edition approved Oct. 1, 2014. Published Octob

14、er 2014. Originallyapproved in 2010. Last previous edition approved in 2010 as B973 10. DOI:10.1520/B0973-10R14.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the

15、standards Document Summary page onthe ASTM website.3Available from National Technical Information Service (NTIS), 5301 ShawneeRd., Alexandria, VA 22312, http:/www.ntis.gov.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1applications o

16、r insulating. The continuity of coating shall bedetermined by the hydrochloric acid-sodium polysulfide test inaccordance with 6.4.5.5 JointsNecessary joints in the wire and rods prior tofinal coating and drawing shall be made in accordance with thebest commercial practice. There shall be no uncoated

17、 joints inthe final product.5.6 FinishThe coating shall consist of a smooth continu-ous layer, firmly adherent to the surface of the copper. The wireshall be free of all imperfections not consistent with the bestcommercial practice.6. Test Methods6.1 Tensile Strength and Elongation (Explanatory Note

18、 4):6.1.1 The tensile strength, expressed in pounds per squareinch, shall be obtained by dividing the maximum load carriedby the specimen during the tension test by the originalcross-sectional area of the specimen. Tensile strength andelongation may be determined simultaneously on the samespecimen.6

19、.1.2 The elongation of the flat wire may be determined bymeasurements made between the jaws of the tensile testingmachine. The zero length shall be the distance between thejaws at the start of the tension test and be as near 10 in. (254mm) as practicable. The final length shall be the distancebetwee

20、n the jaws at the time of rupture. The fracture shall bebetween the jaws of the testing machine and not closer than 1in. (25.4 mm) to the jaw.6.2 Resistivity (Explanatory Note 3)The electrical resis-tivity of the material shall be determined in accordance withTest Method B193. The purchaser may acce

21、pt certification thatthe wire was drawn from rod stock meeting the internationalstandard for annealed copper instead of resistivity tests on thefinished wire.6.3 Dimensional MeasurementsDimensional measure-ments for width and thickness shall be made with a micrometercaliper equipped with a vernier g

22、raduated in 0.0001 in. (0.0025mm). Measurements shall be made on at least three places oneach unit selected for this test. Any measurement takenexceeding the dimensions and permissible variation require-ments in 5.4 shall constitute failure to meet the dimensionalconformance criterion.6.4 Continuity

23、 of Coating:6.4.1 Specimens:6.4.1.1 Length of SpecimensTest specimens shall have alength of about 6 in. (152 mm). They shall be tagged or markedto correspond with the coil, spool, or reel from which they werecut.6.4.1.2 Treatment of SpecimensThe specimens shall bethoroughly cleaned by immersion in a

24、 suitable organic solventfor at least 3 min; then removed and wiped dry with a clean,soft cloth ( Caution-see Explanatory Note 5). The specimensthus cleaned shall be kept wrapped in a clean, dry cloth untiltested. That part of the specimen to be immersed in the testsolution shall not be handled. Car

25、e shall be taken to avoidabrasion by the cut ends.6.4.2 Special Solutions Required:6.4.2.1 Hydrochloric Acid Solution (HCl) (sp gr 1.088)Commercial HCl (sp gr 1.12) shall be diluted with distilledwater to a specific gravity of 1.088 measured at 15.6C (60F).A portion of HCl solution having a volume o

26、f 180 mL shall beconsidered to be exhausted when the number of test specimensprescribed in Table 4 of a size as indicated in 6.4.3 have beenimmersed in it for two cycles.6.4.2.2 Sodium Polysulfide Solution (sp gr 1.142) (Explana-tory Note 6)A concentrated solution shall be made bydissolving sodium s

27、ulfide crystals (cp) in distilled water untilTABLE 1 Electrical Resistivity RequirementsThickness Range,Inch (mm)Resistivity at 20Clb/mile20.0008 to 0.0012 (0.020 to 0.031), incl 1006.00.0013 to 0.0016 (0.033 to 0.041), incl 972.450.0017 to 0.0024 (0.043 to 0.061), incl 961.760.0025 to 0.0048 (0.064

28、 to 0.122), incl 951.310.0049 to 0.0100 (0.125 to 0.254), incl 941.08TABLE 2 Permissible Variations in ThicknessNominal Thickness Range,Inch (mm)Tolerance,Inch (mm)0.0010 to 0.0014 (0.025 to 0.036) +/- 0.0002 (0.005)0.0015 to 0.0019 (0.038 to 0.048) +/- 0.0003 (0.008)0.0020 to 0.0049 (0.051 to 0.124

29、) +/- 0.0004 (0.010)0.0050 to 0.0100 (0.127 to 0.254) +/- 0.0005 (0.013)TABLE 3 Permissible Variations in WidthNominal Width Range,Inch (mm)Tolerance,Inch (mm)0.0100 to 0.0499 (0.254 to 1.27) +/- 0.0013 (0.033)0.0500 to 0.0699 (1.27 to 1.78) +/- 0.0015 (0.038)0.0700 to 0.0999 (1.78 to 2.54) +/- 0.00

30、20 (0.051)0.1000 to 0.1249 (2.54 to 3.17) +/- 0.0030 (0.076)0.1250 to 0.1500 (3.18 to 3.81) +/- 0.0040 (0.102)TABLE 4 Limiting Number of Test Specimens for Coating TestAEquivalent RoundNominal DiameterMaximum Number ofSpecimensto be Tested for 2Cyclesin 180 mL of AcidSolutionin. mmUnder 0.0851 to0.0

31、501,inclUnder 2.2 to 1.3,incl6Under 0.0501 to0.0381,inclUnder 1.3 to 0.97,incl10Under 0.0381 to0.0301,inclUnder 0.97 to 0.76,incl12Under 0.0301 to0.0030,inclUnder 0.76 to 0.076,incl14ASee Explanatory Note 2 for equivalent round calculation.B973 10 (2014)2the solution is saturated at about 21C (70F),

32、 and addingsufficient flowers of sulfur (in excess of 250 g/L of solution) toprovide complete saturation, as shown by the presence in thesolution of an excess of sulfur after the solution has beenallowed to stand for at least 24 h. The test solution shall bemade by diluting a portion of the concentr

33、ated solution withdistilled water to a specific gravity of 1.135 to 1.145 at 15.6C(60F). The sodium polysulfide test solution should havesufficient strength to blacken thoroughly a piece of cleanuntinned copper wire in 5 s. The test solution used for testingsamples shall be considered exhausted if i

34、t fails to blacken apiece of clean copper as described above.6.4.3 Procedure:6.4.3.1 Immersion of SpecimensImmerse a length of atleast 4.5 in. (114 mm) from each of the clean specimens, inaccordance with the following cycles, in test solutions main-tained at a temperature between 15.6 and 21C (60 an

35、d 70F):(1) Immerse the specimen for 1 min in the HCl solutiondescribed in 6.4.2, wash, and wipe dry; (2) immerse thespecimen for 30 s in the sodium polysulfide solution describedin 6.4.2, wash, and wipe dry; (3) immerse the specimen for 1min in the HCl solution, wash, and dry; (4) immerse thespecime

36、n for 30 s in the sodium polysulfide solution, wash, andwipe dry.6.4.3.2 Washing SpecimensAfter each immersion, imme-diately wash the specimens thoroughly in clean water and wipedry with a clean, soft cloth.6.4.3.3 Examination of SpecimensAfter immersion andwashing, examine the specimens to ascertai

37、n if copper exposedthrough openings in the tin coating has been blackened byaction of the sodium polysulfide. The specimens shall beconsidered to have failed if, by such blackening, exposedcopper is revealed. No attention shall be paid to blackeningwithin 0.5 in. (12.7 mm) of the cut end. A grayish

38、brownappearance of the coating shall not constitute failure.6.5 FinishSurface-finish inspection shall be made with theunaided eye (normal spectacles excepted).7. Inspection7.1 General (Explanatory Note 7)Unless otherwise speci-fied in the contract or purchaser order, the manufacturer shallbe respons

39、ible for the performance of all inspection and testrequirements specified.7.1.1 All inspections and tests shall be made at the place ofmanufacture unless otherwise especially agreed upon betweenthe manufacturer and the purchaser at the time of purchase.7.1.2 The manufacturer shall afford the inspect

40、or represent-ing the purchaser all reasonable manufacturers facilities tosatisfy him that the material is being furnished in accordancewith this specification.7.1.3 Unless otherwise agreed upon between the purchaserand the manufacturer, conformance of the wire to the variousrequirements listed in Se

41、ction 5 shall be determined on samplestaken from each lot of wire presented for acceptance.7.1.4 The manufacturer shall, if requested prior toinspection, certify that all wire in the lot was made under suchconditions that the product as a whole conforms to therequirements of this specification as de

42、termined by regularlymade and recorded tests.7.2 Definitions Applicable to Inspection:7.2.1 lotany amount of wire of one type and size pre-sented for acceptance at one time.7.2.2 samplea quantity of production units (coils reels,and so forth) selected at random from the lot for the purpose ofdetermi

43、ning conformance of the lot to the requirements of thisspecification.7.2.3 specimena length of wire removed for test purposesfrom any individual production unit of the sample.7.3 Sample Size (Explanatory Note 7)The number ofproduction units in a sample shall be as follows:7.3.1 A full (100 % inspect

44、ion) will be completed at everyset-up prior to running the order.7.3.2 For elongation, resistivity, dimensional measurements,and continuity of coating determinations, the sample shallconsist of sequential production units from the lot.7.3.3 For surface-finish inspection and for packaging in-spection

45、 (when specified by the purchaser at the time of placingthe order) the sample shall consist of sequential productionunits from the lot.8. Conformance Criteria (Explanatory Note 7)8.1 Any lot of wire, the samples of which comply with theconformance criteria of Section 5, shall be considered ascomplyi

46、ng with the requirements of this standard. Individualproduction units that fail to meet one or more of the require-ments shall be rejected. If a failure of an individual productionunit occurs, material which was made between the non-conforming unit and the last production unit which passed theconfor

47、mance criteria must be inspected for the non-conformingcharacteristic.9. Density (Explanatory Note 8)9.1 For the purpose of calculating linear densities, crosssections, etc., the density of the copper shall be taken as 8.89g/cm3(0.32117 lb/in.3) at 20C.10. Packaging and Shipping10.1 Package sizes sh

48、all be agreed upon by the manufac-turer and the purchaser in the placing of individual orders.10.2 The flat wire shall be protected against damage inordinary handling and shipping.11. Keywords11.1 copper flat wire tin-coated; tin-coated annealed copperflat wire; tin-coated copper electrical equipmen

49、t flat wire;tin-coated copper flat wireB973 10 (2014)3EXPLANATORY NOTESNOTE 1(1) It has been found that the tin coating on copper wireconsists of two parts, an envelope of pure tin on the outside, with anintermediate layer of copper-tin alloy. This tin alloy, as well as the amountof tin present, has an effect on the resistivity of the wire. Since the relativeamount of tin coating and alloy is greater as the size decreases, theresistivity of the wire increases as the size decreases.(2) The manufacturer and user of the standard should also g