BS 2S 205-2004 Austenitic chromium-nickel steel wire rod wire and springs - Specification《奥氏体铬镍钢盘条 金属丝和弹簧 规格》.pdf
《BS 2S 205-2004 Austenitic chromium-nickel steel wire rod wire and springs - Specification《奥氏体铬镍钢盘条 金属丝和弹簧 规格》.pdf》由会员分享,可在线阅读,更多相关《BS 2S 205-2004 Austenitic chromium-nickel steel wire rod wire and springs - Specification《奥氏体铬镍钢盘条 金属丝和弹簧 规格》.pdf(8页珍藏版)》请在麦多课文档分享上搜索。
1、BRITISH STANDARD AEROSPACE SERIESBS 2S 205:2004(Superseding BS S 205:1969)Austenitic chromium-nickel steel wire rod, wire and springs SpecificationICS 49.025.10g49g50g3g38g50g51g60g44g49g42g3g58g44g55g43g50g56g55g3g37g54g44g3g51g40g53g48g44g54g54g44g50g49g3g40g59g38g40g51g55g3g36g54g3g51g40g53g48g44
2、g55g55g40g39g3g37g60g3g38g50g51g60g53g44g42g43g55g3g47g36g58Incorporating um No. 1 CorrigendCommittees responsible for this British StandardThe preparation of this British Standard was entrusted by ACE/61, Metallic materials for aerospace to Technical Committee ACE/61/-/15, Steels, upon which the fo
3、llowing bodies were represented:Cast Metals FederationCivil Aviation Authority AirworthinessConfederation of British MetalformingInstitute of Spring TechnologyMinistry of Defence UK Defence StandardizationSociety of British Aerospace Companies Ltd.UK Steel AssociationBS 2S 205:2004This British Stand
4、ard waspublished under the authorityof the Standards Policy andStrategy Committee on14 December 2004 BSI 2011The following BSI referencesrelate to the work on this British Standard:Committee reference ACE/61/-/15Draft for comment 03/316693 DCAmendments/corrigenda issued since publicationAmd. No. Dat
5、e Comments C1 31 March 2011 Normative references: “BS 5S 100” changed to “BS S 100”Throughout: “the latest edition of British Standard S 100” changed to “BS S 100”ISBN 978 0 580 72678 1BS 2S 205:2004 BSI 2011iContentsPageCommittees responsible Inside front coverForeword ii1Scope 12 Inspection and te
6、sting procedure 13 Normative references 14 Process of manufacture 15 Chemical composition 16 Surface dressing 17 Condition 28 Freedom from defects 29 Final heat treatment 210 Mechanical properties 211 Dimensional tolerances 3Table 1 Chemical composition 1Table 2 Condition of supply 2Table 3 Tensile
7、test strengths 3BS 2S 205:2004ii BSI 2011ForewordThis British Standard has been prepared by Technical Committee ACE/61/-/15. It supersedes BS S 205:1969, which is withdrawn. The original standard was based on Ministry of Technology Specification DTD 5006.This standard covers the specification of aus
8、tenitic chromium-nickel steel wire rod, wire and springs. In this revision units of measurement have been brought into line with SI.This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application.Compliance with a British Sta
9、ndard cannot confer immunity from legal obligations.Summary of pagesThis document comprises a front cover, an inside front cover, pages i and ii, pages 1 to 3 and a back cover.The BSI copyright notice displayed in this document indicates when the document was last issued.BS 2S 205:2004 BSI 201111 Sc
10、opeThis standard specifies austenitic chromium-nickel steel wire rod, wire and springs for aerospace purposes.2 Inspection and testing procedure2.1 GeneralThis British Standard shall be used in conjunction with BS S 100.2.2 Sulfur printing or deep etching testsSamples shall be selected in accordance
11、 with BS S 100.3 Normative referencesThe following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.BS S 100, Pro
12、cedure for inspection, testing and acceptance of wrought steels (other than plate, sheet, strip and tube).BS EN 10270-3, Steel wire for mechanical springs Part 3: Stainless spring steel wire.4 Process of manufactureThe material shall be manufactured by an electric process unless otherwise agreed bet
13、ween the manufacturer and the purchaser in accordance with BS S 100.5 Chemical compositionThe steel shall contain the chemical levels shown in Table 1.Table 1 Chemical composition6 Surface dressingThe material from which the rods are rolled shall be overall dressed in accordance with the requirement
14、s of BS S 100.Element PercentageMin. Max.Carbon 0.15Silicon 0.20 1.0Manganese 0.50 2.0Phosphorus 0.035Sulfur 0.025Chromium 17.0 19.0Nickel 7.5 9.0BS 2S 205:20042 BSI 20117 ConditionThe material shall be supplied in the appropriate condition stated in Table 2 unless otherwise agreed between the manuf
15、acturer and the purchaser, in which case the condition in which the material is to be supplied shall be stated on the order. Table 2 Condition of supply8 Freedom from defects8.1 Surface defects Visual examinationThe rod and wire shall be visually examined in accordance with BS S 100.8.2 Surface defe
16、cts Deep etching testsSamples of rod and wire, selected and prepared for examination in accordance with BS S 100,shall be immersed in a solution containing 10 % by volume of concentrated nitric acid and 3.5 % by volume of hydrofluoric acid (40 % HF) in water at approximately 60 C. The time of immers
17、ion shall be approximately two seconds for every 0.025 mm of diameter, but shall not be less than two minutes nor more than ten minutes. An alternative solution may be used if agreed by the Inspecting Authority 8.3 Alternatively to 8.2, for wire of less than 2.0 mm diameter the deep etching test sha
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- BS2S2052004AUSTENITICCHROMIUMNICKELSTEELWIRERODWIREANDSPRINGSSPECIFICATION 奥氏体 镍钢 金属丝 弹簧 规格 PDF
链接地址:http://www.mydoc123.com/p-543476.html