FORD WSB-M99C120-A-2009 LUBRICANT DRY FILM PTFE IN WATER BASED POLYURETHANE BINDER TO BE USED WITH FORD WSS-M99P1111-A 《水基聚氨酯胶粘剂中的聚四氟乙烯（PTFE）、干膜润滑油 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD WSB-M99C120-A-2009 LUBRICANT DRY FILM PTFE IN WATER BASED POLYURETHANE BINDER TO BE USED WITH FORD WSS-M99P1111-A 《水基聚氨酯胶粘剂中的聚四氟乙烯（PTFE）、干膜润滑油 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD WSB-M99C120-A-2009 LUBRICANT DRY FILM PTFE IN WATER BASED POLYURETHANE BINDER TO BE USED WITH FORD WSS-M99P1111-A 《水基聚氨酯胶粘剂中的聚四氟乙烯（PTFE）、干膜润滑油 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 11 17 N-STATUS No known use. No replacement named D. DiGregorio, NA 2003 12 10 Revised Para 3.0 inserted; paras 3.1, 3.2, 3.3, 3.12 and 4 deleted; para 3.9 revised 1992 07 22 Released NB00I10043054194 R. D. Moore Printed copies are uncont

2、rolled Copyright 2009, Ford Global Technologies, LLC. Page 1 of 2 LUBRICANT, DRY FILM, PTFE IN WATER BASED WSB-M99C120-A POLYURETHANE BINDER NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a dry film lubricant, which consists of PTFE in water based polyurethane b

3、inder. The lubricant was designed for applications where EPA or OSHA regulations restrict emissions of volatile organic compounds. The material provides good wear, low coefficient of friction, solvent resistance, and resistance to chalking in U.V. exposure. After dip or spray application, the materi

4、al can be air dried or force dried with heat. 2. APPLICATION This specification was released originally as a spray lubricant applied onto the Ranger bucket seat back polyester fabric, which creaked against backlite glass. For other applications the material could be used over phosphated steel, stain

5、less steel, anodized aluminum, copper alloys, rubber and plastics. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 COLOR Opaque 3.5 ODOR Slight,

6、not objectionable 3.6 BOILING POINT 85 100 C (ASTM D 92) 3.7 DENSITY 1.07 - 1.09 kg/L (ASTM D 1475) 3.8 VOLATILES, % by weight, max 77 (FLTM BI 102-01) 3.9 NON-VOLATILES, % by weight, min 24 (FLTM BI 102-01) 3.9.1 Fluorocarbon, min 7.0 3.9.2 Modified Polyester Urethane, min 17.0 3.9.3 Other, min 0.5

7、 ENGINEERING MATERIAL SPECIFICATIONWSB-M99C120-A Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 2 3.10 WATER CONTENT, % by weight, min 70.0 (ASTM D 95) 3.11 EFFECT ON PLASTIC (ASTM D 2716) Dip or spray lubricant on ESB-M4D483-A1, A2 or WSK-M4D827-A (ABS) plas

8、tic panels. Prior to testing, air dry at 23 C for 24 h. 3.11.1 Heat Resistance None (2 h at 100 C) 3.11.2 Water Resistance None (24 h at 82 C) 5. GENERAL INFORMATION The information below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 SPECIFIC GRAVITY 23.0 (ASTM D 4052) 5.2 VAPOR PRESSURE 17.5 mm Hg (Calculated)