《FORD ESB-M2E3-B-2003 FIBERBOARD (PANEL) LAMINATED - POLYETHYLENE LINED TO BE USED WITH FORD WSS-M99P1111-A (Shown on ESB-M2E3-A)《聚乙烯衬里的涂层层压纤维板(壁板) 与标准FORD WSS-M99P1111-A一起使用 列于.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M2E3-B-2003 FIBERBOARD (PANEL) LAMINATED - POLYETHYLENE LINED TO BE USED WITH FORD WSS-M99P1111-A (Shown on ESB-M2E3-A)《聚乙烯衬里的涂层层压纤维板(壁板) 与标准FORD WSS-M99P1111-A一起使用 列于.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2003 01 31 Revised Para 3.0 inserted ; Para 3.1, 3.14, 4 deleted 1978 09 15 Metricated, Renumbered & Retyped CAHI-RD572066-93 1971 08 17 Released ESB-M2E3-B,4-C,5-B AB1-302-14 Printed copies are uncontrolled

2、 Page 1 of 3 Copyright 2003, Ford Global Technologies, Inc. FIBERBOARD (PANEL), LAMINATED-POLYETHYLENE LINED ESB-M2E3-A ESB-M2E3-B ESB-M2E4-A ESB-M2E4-C ESB-M2E5-A ESB-M2E5-B 1. SCOPE The material defined by these specifications is a laminated, polyethylene lined panel board of good quality and unif

3、orm construction. 2. APPLICATION These specifications were released originally for material used as a trim foundation for door panels or as a base board to which a coating is applied for headlining or package tray applications. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Mater

4、ial suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 CONSTRUCTION The board shall be constructed of a core of kraft and mixed fibers. The core shall be free of residual asphalt and other contaminants which might cause sew

5、line stains. Laminated to each side of the core shall be a film of polyethylene which is also laminated to a kraft paper liner. The kraft paper liners shall form the outer faces of the board. 3.3 THICKNESS (SAE J 315b) ESB-M2E3-A & ESB-M2E3-B 0.060 +/ 0.005 in (1.52 +/- 0.13 mm) ESB-M2E4-A & ESB-M2E

6、4-C 0.08 +/- 0.005 in (2.03 +/- 0.13 mm) ESB-M2E5-A & ESB-M2E5-B 0.100 +/- 0.005 in (2.54 +/- 0.13 mm) ENGINEERING MATERIAL SPECIFICATION ESB-M2E3-A ESB-M2E3-B ESB-M2E4-A ESB-M2E4-C ESB-M2E5-A ESB-M2E5-B Page 2 of 3 Copyright 2003, Ford Global Technologies, Inc. 3.4 MOISTURE CONTENT, max 7 % (SAE J

7、315b) Based on original weight 3.5 WATER ABSORPTION, max 20 % (SAE J 315b, 24 h immersion) 3.6 WARP, max 4 % (FLTM BS 2-1, 24 h water immersion) 3.7 BURSTING STRENGTH, min (SAE J 315b) ESB-M2E3-A & ESB-M2E3-B 235 psi (1.62 MPa) ESB-M2E4-A & ESB-M2E4-C 325 psi (2.24 MPa) ESB-M2E5-A & ESB-M2E5-B 425 p

8、si (2.93 MPa) 3.8 TENSILE STRENGTH, lb/in (N/mm), min (ASTM D 828) WMD AMD ESB-M2E3-A & ESB-M2E3-B 350 (61) 125 (22) ESB-M2E4-A & ESB-M2E4-C 450 (79) 150 (26) ESB-M2E5-A & ESB-M2E5-B 500 (88) 200 (35) 3.9 DIMENSIONAL STABILITY (SAE J 315b, 24 h, water) WMD AMD 3.9.1 Expansion, max 0.7% 0.7% 3.9.2 Co

9、ntraction, max 0.7% 0.7% 3.10 ADHESION, min 1 lb/in (176 N/m) of width (FLTM BN 113-01) The polyethylene films and adhesives employed shall result in a firm bond between the plies to hold the assembly together, during production handling and for the normal life of the assembly, at various extreme te

10、mperatures and humidity conditions encountered under service operating conditions. 3.11 STAINING (FLTM AN 101-03, Method “A“) The material shall contain no asphalt or other resins that shall cause staining of the contact fabric. ENGINEERING MATERIAL SPECIFICATION ESB-M2E3-A ESB-M2E3-B ESB-M2E4-A ESB

11、-M2E4-C ESB-M2E5-A ESB-M2E5-B Page 3 of 3 Copyright 2003, Ford Global Technologies, Inc. 3.12 ESB-M2E3-A, 4-A, and 5-A FLAMMABILITY, max 4 in (101 mm)/min (FLTM BN 24-2, without the lot sampling plan) In addition, the test specimen shall not exhibit any flashing or sudden flaming on either surface i

12、n excess of the above max value. 3.13 ESB-M2E3-B, 4-C and 5-B FLAMMABILITY 3.13.1 In order to comply with Federal Motor Vehicle Safety Standard No. 302, the materials, portions of components, and composites shall not burn, or transmit a flame across its surface, at a rate of more than 4 in (101 mm)

13、per min. To demonstrate compliance, the sample size and method of testing shall be in accordance with FLTM BN 24-2. 3.13.2 Performance - Environmental Aging All materials, portions of components, and composites defined by this specification that have not been treated, modified or reformulated and ex

14、ceed a max burn rate of 3.0 in (76 mm) per min as specified by the Flammability Lot Sampling Plan of FLTM BN 24-2, must be evaluated for permanency of the materials flame retardant properties per ESB-M25P3-A according to the accelerated environmental aging requirements applicable to the basic materi

15、al category of this particular specification. Any material, portions of components, and composites defined by this specification that have been treated, modified or reformulated to conform to Flammability Lot Sampling Plan of FLTM BN 24-2, regardless of max burn rate, must be evaluated for both perm

16、anency of materials flame retardant properties and changes in mechanical, chemical and physical properties per ESB-M25P3-A applicable to the basic materials category of this particular specification. 3.13.3 Flammability Test Program Materials, portions of components, and composites governed by this specification must also comply with the requirements of ES-D3AB-11014-AA. Procedure I-A.