《ASTM D6685-2001(2015) 1082 Standard Guide for the Selection of Test Methods for Fabrics Used for Fabric Formed Concrete (FFC)《选择纤维制混凝土用织物的试验方法的标准指南》.pdf》由会员分享，可在线阅读，更多相关《ASTM D6685-2001(2015) 1082 Standard Guide for the Selection of Test Methods for Fabrics Used for Fabric Formed Concrete (FFC)《选择纤维制混凝土用织物的试验方法的标准指南》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D6685 01 (Reapproved 2015)Standard Guide for theSelection of Test Methods for Fabrics Used for FabricFormed Concrete (FFC)1This standard is issued under the fixed designation D6685; the number immediately following the designation indicates the year oforiginal adoption or, in the case o

2、f revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This guide lists ASTM standards available for thetesting evaluation of fabrics used to form fi

3、ne aggregateconcrete.1.2 This guide identifies the test methods available tomanufacturers, engineers, testing organizations and other re-lated parties.1.3 This guide provides a list of test methods that can beused by the reader to determine the properties of fabric used toform fine aggregate concret

4、e.1.4 This guide is not intended to be used in the establish-ment of performance criteria, but as a guide for productdevelopment and purchasing contracts.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of t

5、his standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.1.6 This guide offers an organized collection of informationor a series of options and does not recommend a specificcourse of action. This document cannot replac

6、e education orexperience and should be used in conjunction with professionaljudgement. Not all aspects of this guide may be applicable inall circumstances. This ASTM standard is not intended torepresent or replace the standard of care of which the ad-equacy of a given professional service must be ju

7、dged, norshould this document be applied without consideration of aprojects many unique aspects. The word “Standard” in thetitle of this document means only that the document has beenapproved through the ASTM consensus process.2. Referenced Documents2.1 ASTM Standards:2D4354 Practice for Sampling of

8、 Geosynthetics and RolledErosion Control Products(RECPs) for TestingD4355 Test Method for Deterioration of Geotextiles byExposure to Light, Moisture and Heat in a Xenon ArcType ApparatusD4439 Terminology for GeosyntheticsD4486 Test Method for Kinematic Viscosity of Volatile andReactive LiquidsD4491

9、Test Methods for Water Permeability of Geotextilesby PermittivityD4533 Test Method for Trapezoid Tearing Strength of Geo-textilesD4595 Test Method for Tensile Properties of Geotextiles bythe Wide-Width Strip MethodD4751 Test Method for DeterminingApparent Opening Sizeof a GeotextileD4759 Practice fo

10、r Determining the Specification Confor-mance of GeosyntheticsD4873 Guide for Identification, Storage, and Handling ofGeosynthetic Rolls and SamplesD4884 Test Method for Strength of Sewn or Bonded Seamsof GeotextilesD5261 Test Method for Measuring Mass per Unit Area ofGeotextilesD5321 Test Method for

11、 Determining the Shear Strength ofSoil-Geosynthetic and Geosynthetic-Geosynthetic Inter-faces by Direct Shear3. Terminology3.1 DefinitionsFor definitions of terms used in thisstandard, refer to the Terminology for Geosynthetics D4439.3.2 Definitions of Terms Specific to This Standard:1This guide is

12、under the jurisdiction ofASTM Committee D18 on Soil and Rockand is the direct responsibility of Subcommittee D18.25 on Erosion and SedimentControl Technology.Current edition approved Feb. 15, 2015. Published March 2015. Originallyapproved in 2001. Last previous edition approved in 2008 as D6685 01(2

13、008).DOI: 10.1520/D6685-01R15.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 1

14、00 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.2.1 Fabric Formed Concrete (FFC) RevetmentA fineaggregate concrete filled woven mattress used to protect soilsfrom erosion. A high strength synthetic fabric is used as a formto cast the fine aggregate concrete.4. Si

15、gnificance and Use4.1 This guide identifies test methods used in the process ofdetermining the characteristics of fabrics used to form fineaggregate concrete for properties such as mass, apparentopening size, tensile strength, water permeability and othermechanical properties.4.2 This guide is inten

16、ded for general use by those whomanufacture, specify or install fabric formed concrete (FFC)revetments.4.3 Consult specific ASTM specifications for evaluationcriteria.4.3.1 A listing of all ASTM geosynthetic performancespecifications may be found in Volume 04.09 of the AnnualBook of Standards.5. Tes

17、t Methods5.1 Recommended test methods for fabric used for formingfine aggregate concrete have been grouped in categories andare listed in the tables as follows:5.1.1 Table 1General Properties for Fabric Used forForming Fine Aggregate Concrete.5.1.2 Table 2Physical Properties for Fabric Used forFormi

18、ng Fine Aggregate Concrete.5.1.3 Table 3Mechanical Properties for Fabric Used forForming Fine Aggregate Concrete.5.1.4 Table 4Hydraulic Properties for Fabric Used forForming Fine Aggregate Concrete.6. Keywords6.1 geotextile; fine aggregate concrete; fabric formed con-crete revetmentTABLE 1 General P

19、roperties for Fabric Used for Forming FineAggregate ConcreteCharacteristic ASTM StandardTerminology for Geosynthetics D4439Practice for Sampling of Geosynthetics for Testing D4354Test Method for Deterioration of Geotextiles from Exposure toUltraviolet And Water (Xenon-Arc Type Apparatus) D4355NOTE 1

20、Fabric Forms fulfill their requirements once the concrete hascured. Since concrete linings rely on the concretes properties for theirlong-term performance, Ultraviolet degradation is not an issue, providedthat the forms have been properly stored at the project site.Practice for Determining the Speci

21、fication Conformance ofGeosynthetics D4759Guide for Identification, Storage, and Handling of Geotextiles D4873TABLE 2 Physical Properties for Fabric Used for Forming FineAggregate ConcreteCharacteristic ASTM StandardTest Method for Abrasion Resistance of Geotextiles(Sand Paper/Sliding Block Method)

22、D4886Test Method for Strength of Sewn Seam or ThermallyBonded Seams of Geotextiles D4884Test Method for Determining Apparent Opening Size of aGeotextile D4751Test Method for Measuring Mass Per Unit Area of Geo-textiles D5261Test Method For Determining the Coefficient of Soil andGeosynthetic or Geosy

23、nthetic and Geosynthetic Fric-tion by the Direct Shear Method D5321D6685 01 (2015)2ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the

24、validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your

25、comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments h

26、ave not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multip

27、le copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Cent

28、er, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 3 Mechanical Properties for Fabric Used for Forming FineAggregate ConcreteCharacteristic ASTM StandardTest Method for Trapezoidal Tearing Strength ofGeotextiles D4533Test Method for Tensile Properties of Geotextiles by theWide Width Strip Method D4595TABLE 4 Hydraulic Properties for Fabric Used for Forming FineAggregate ConcreteCharacteristic ASTM StandardTest Method for Water Permeability of Geotextiles byPermittivity D4491D6685 01 (2015)3