1、Designation: D3530M 97 (Reapproved 2008)1Standard Test Method forVolatiles Content of Composite Material Prepreg1This standard is issued under the fixed designation D3530M; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year o
2、f last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1NOTEThis standard was corrected to a single-de
3、signation standard editorially in October 2013.1. Scope1.1 This test method covers the determination of the vola-tiles content, in weight percent of composite material prepregs.This standard focuses on composites with thermosetting resinsthat tend to lose a few percent of the matrix mass when heated
4、due to loss of both retained water and low molecular weightmatrix constituents that volatilize during heating.1.2 Use of this test method is limited to maximum tempera-ture of circulating air ovens (approximately 300C).1.3 Use of this test method is limited to temperatures belowwhich the matrix flow
5、s from the reinforcement.1.4 The values stated in SI units are to be regarded asstandard.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practice
6、s and determine the applica-bility of regulatory limitations prior to use. Specific precau-tionary statements are given in Section 8.2. Referenced Documents2.1 ASTM Standards:2D3878 Terminology for Composite MaterialsE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE1309 Guid
7、e for Identification of Fiber-ReinforcedPolymer-Matrix Composite Materials in Databases2.2 NFPA Standard:NFPA 86 Standard for Ovens and Furnaces33. Terminology3.1 DefinitionsTerminology D3878 defines terms relatingto composite materials. Terminology D883 defines termsrelating to plastics. Practice E
8、177 defines terms relating tostatistics. In the event of a conflict between terms, TerminologyD3878 shall have precedence over other documents.3.1.1 prepreg, nthe admixture of fibrous reinforcementand polymeric matrix used to fabricate composite materials. Itsform may be sheet, tape, or tow. See Ter
9、minology D3878.3.2 Definitions of Terms Specific to This Standard:3.2.1 Volatiles Content, nthe amount of volatiles presentin a prepreg expressed as a weight percent.3.3 Symbols:3.3.1 Mithe initial mass of the sample.3.3.2 Mfthe mass of the sample after oven exposure.3.3.3 Vcthe weight percent volat
10、iles content.4. Summary of Test Method4.1 Specimens of prepreg are weighed and then exposed toelevated temperature, equal to the nominal cure or consolida-tion temperature of the material, in an air circulating oven toremove the volatiles. The exposed samples are reweighed andthe percent change in w
11、eight expressed as volatiles content.5. Significance and Use5.1 This test method is used to obtain the volatiles contentof composite material prepreg. Knowledge of the volatilescontent is useful in developing optimum manufacturing pro-cesses.5.2 The volatiles content is determined after exposure to
12、thenominal cure or consolidation temperature.1This test method is under the jurisdiction of ASTM Committee D30 onComposite Materials and is the direct responsibility of Subcommittee D30.03 onConstituent/Precursor Properties.Current edition approved April 1, 2008. Published April 2008. Originallyappr
13、oved in 1976. Last previous edition approved in 2008 as D3530/D3530M 97(2008). DOI: 10.1520/D3530M-97R08E01.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the stan
14、dards Document Summary page onthe ASTM website.3Available from National Fire Protection Association (NFPA), 1 BatterymarchPark, Quincy, MA 02269-9101.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16. Interferences6.1 AirflowThe amoun
15、t of measured volatiles may beincreased or decreased by changing the velocity of airflow.Since airflow in most ovens is not linear in each part, avelometer should be used to measure airflow where samplesare placed. Samples should be placed only in positions ofknown airflow so that results may be rep
16、eatable. Use of baffleshas been found to even airflow between samples.6.2 Sample ExposureThe geometric shape and positioningof the sample have an effect on the measured volatiles content.Samples placed horizontally in a rack will not be exposed tothe same amount of airflow as samples hung vertically
17、. Aribbon wound in a 150 mm diameter hoop may give slightlydifferent results than the same ribbon wound in a 50 mmdiameter hoop. A thinner sample will be exposed to moreairflow at its surface than a thicker sample.6.3 Time of ExposureFor any given temperature, sampleplacement, and airflow, the sampl
18、e will lose volatiles at a setinitial rate, that decreases over time. After some time period,volatiles lost in the test will approach the true volatiles contentof the sample. If the time period is not sufficient to show a truevolatiles content of the material, the volatiles content isrepresentative
19、of only the condition of the test.6.4 Time of Ambient ExposureVolatiles content varies dueto prolonged exposure of temperatures exceeding prepreg glasstransition temperature or exposure to humidity. This change isassociated with matrix crosslinking and change in tack.7. Apparatus7.1 Cutting BladeDie
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMD3530M19972008E1STANDARDTESTMETHODFORVOLATILESCONTENTOFCOMPOSITEMATERIALPREPREG 复合材料 预浸料中 挥发物 含量
![提示](http://www.mydoc123.com/images/bang_tan.gif)
链接地址:http://www.mydoc123.com/p-514953.html