ASTM D3530-1997(2015) Standard Test Method for Volatiles Content of Composite Material Prepreg《合成材料预浸料坯中挥发物含量的标准试验方法》.pdf
《ASTM D3530-1997(2015) Standard Test Method for Volatiles Content of Composite Material Prepreg《合成材料预浸料坯中挥发物含量的标准试验方法》.pdf》由会员分享,可在线阅读,更多相关《ASTM D3530-1997(2015) Standard Test Method for Volatiles Content of Composite Material Prepreg《合成材料预浸料坯中挥发物含量的标准试验方法》.pdf(3页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: D3530 97 (Reapproved 2015)Standard Test Method forVolatiles Content of Composite Material Prepreg1This standard is issued under the fixed designation D3530; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of l
2、ast revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This test method covers the deter
3、mination of the vola-tiles content, in weight percent of composite material prepregs.This standard focuses on composites with thermosetting resinsthat tend to lose a few percent of the matrix mass when heateddue to loss of both retained water and low molecular weightmatrix constituents that volatili
4、ze during heating.1.2 Use of this test method is limited to maximum tempera-ture of circulating air ovens (approximately 300C).1.3 Use of this test method is limited to temperatures belowwhich the matrix flows from the reinforcement.1.4 The values stated in SI units are to be regarded asstandard.1.5
5、 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use. Specific precau-t
6、ionary statements are given in Section 8.2. Referenced Documents2.1 ASTM Standards:2D3878 Terminology for Composite MaterialsE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE1309 Guide for Identification of Fiber-ReinforcedPolymer-Matrix Composite Materials in Databases (Wit
7、h-drawn 2015)32.2 NFPA Standard:NFPA 86 Standard for Ovens and Furnaces43. Terminology3.1 DefinitionsTerminology D3878 defines terms relatingto composite materials. Terminology D883 defines termsrelating to plastics. Practice E177 defines terms relating tostatistics. In the event of a conflict betwe
8、en terms, TerminologyD3878 shall have precedence over other documents.3.1.1 prepreg, nthe admixture of fibrous reinforcementand polymeric matrix used to fabricate composite materials. Itsform may be sheet, tape, or tow. See Terminology D3878.3.2 Definitions of Terms Specific to This Standard:3.2.1 V
9、olatiles Content, nthe amount of volatiles presentin a prepreg expressed as a weight percent.3.3 Symbols:3.3.1 Mithe initial mass of the sample.3.3.2 Mfthe mass of the sample after oven exposure.3.3.3 Vcthe weight percent volatiles content.4. Summary of Test Method4.1 Specimens of prepreg are weighe
10、d and then exposed toelevated temperature, equal to the nominal cure or consolida-tion temperature of the material, in an air circulating oven toremove the volatiles. The exposed samples are reweighed andthe percent change in weight expressed as volatiles content.5. Significance and Use5.1 This test
11、 method is used to obtain the volatiles contentof composite material prepreg. Knowledge of the volatilescontent is useful in developing optimum manufacturing pro-cesses.5.2 The volatiles content is determined after exposure to thenominal cure or consolidation temperature.6. Interferences6.1 AirflowT
12、he amount of measured volatiles may beincreased or decreased by changing the velocity of airflow.1This test method is under the jurisdiction of ASTM Committee D30 onComposite Materials and is the direct responsibility of Subcommittee D30.03 onConstituent/Precursor Properties.Current edition approved
13、 Nov. 1, 2015. Published December 2015. Originallyapproved in 1976. Last previous edition approved in 2008 as D3530/D3530M 97(2008)2. DOI: 10.1520/D3530_D3530M-97R15.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual B
14、ook of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.4Available from National Fire Protection Association (NFPA), 1 BatterymarchPark, Quincy, MA 02269-9101.Copyrigh
15、t ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1Since airflow in most ovens is not linear in each part, avelometer should be used to measure airflow where samplesare placed. Samples should be placed only in positions ofknown airflow so that r
16、esults may be repeatable. Use of baffleshas been found to even airflow between samples.6.2 Sample ExposureThe geometric shape and positioningof the sample have an effect on the measured volatiles content.Samples placed horizontally in a rack will not be exposed tothe same amount of airflow as sample
17、s hung vertically. Aribbon wound in a 150 mm diameter hoop may give slightlydifferent results than the same ribbon wound in a 50 mmdiameter hoop. A thinner sample will be exposed to moreairflow at its surface than a thicker sample.6.3 Time of ExposureFor any given temperature, sampleplacement, and a
18、irflow, the sample will lose volatiles at a setinitial rate, that decreases over time. After some time period,volatiles lost in the test will approach the true volatiles contentof the sample. If the time period is not sufficient to show a truevolatiles content of the material, the volatiles content
19、isrepresentative of only the condition of the test.6.4 Time of Ambient ExposureVolatiles content varies dueto prolonged exposure of temperatures exceeding prepreg glasstransition temperature or exposure to humidity. This change isassociated with matrix crosslinking and change in tack.7. Apparatus7.1
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMD353019972015STANDARDTESTMETHODFORVOLATILESCONTENTOFCOMPOSITEMATERIALPREPREG 合成 材料 预浸料坯中 挥发物 含量 标准
链接地址:http://www.mydoc123.com/p-514952.html