ASTM D2287-2011 Standard Specification for Nonrigid Vinyl Chloride Polymer and Copolymer Molding and Extrusion Compounds《非刚性氯乙烯聚合物和共聚物模制及挤压化合物的标准规格》.pdf

《ASTM D2287-2011 Standard Specification for Nonrigid Vinyl Chloride Polymer and Copolymer Molding and Extrusion Compounds《非刚性氯乙烯聚合物和共聚物模制及挤压化合物的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM D2287-2011 Standard Specification for Nonrigid Vinyl Chloride Polymer and Copolymer Molding and Extrusion Compounds《非刚性氯乙烯聚合物和共聚物模制及挤压化合物的标准规格》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D2287 11Standard Specification forNonrigid Vinyl Chloride Polymer and Copolymer Moldingand Extrusion Compounds1This standard is issued under the fixed designation D2287; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision,

2、the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification cover

3、s nonrigid vinyl chloride poly-mer and copolymer classes in which the resin portion of thecomposition contains at least 90 % vinyl chloride. The remain-ing 10 % can include one or more monomers copolymerizedwith vinyl chloride or consist of other resins mechanicallyblended with polyvinyl chloride or

4、 copolymers thereof.1.2 These nonrigid vinyl compounds are defined by ahardness range and include the necessary stabilizers, plasticiz-ers, fillers, dyes, and pigments to meet the designated require-ments.1.3 This specification includes nonrigid vinyl chloride com-pounds recommended for compression

5、molding, injectionmolding, and extrusion, but it must be recognized that particu-lar compounds are not suitable for all these means of fabrica-tion.NOTE 1This standard and ISO 2898-1 and ISO 2898-2 address thesame subject matter, but differ in technical content.1.4 The values stated in SI units are

6、to be regarded as thestandard. The values given in parentheses are for informationonly.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices

7、and determine the applica-bility of regulatory limitations prior to use.1.6 The text of this specification references notes andfootnotes which provide explanatory material. These notes andfootnotes (excluding those in tables and figures) shall not beconsidered as requirements of this specification.1

8、.7 Recycle PVC plastics meeting the requirements of thisspecification may be used in some applications. Refer to thespecific requirements in the Materials and Manufacture sectionof the applicable product standard.2. Referenced Documents2.1 ASTM Standards:2D257 Test Methods for DC Resistance or Condu

9、ctance ofInsulating MaterialsD618 Practice for Conditioning Plastics for TestingD635 Test Method for Rate of Burning and/or Extent andTime of Burning of Plastics in a Horizontal PositionD638 Test Method for Tensile Properties of PlasticsD746 Test Method for Brittleness Temperature of Plasticsand Ela

10、stomers by ImpactD792 Test Methods for Density and Specific Gravity (Rela-tive Density) of Plastics by DisplacementD883 Terminology Relating to PlasticsD1203 Test Methods for Volatile Loss From Plastics UsingActivated Carbon MethodsD1600 Terminology for Abbreviated Terms Relating toPlasticsD2240 Tes

11、t Method for Rubber PropertyDurometerHardnessD3182 Practice for RubberMaterials, Equipment, andProcedures for Mixing Standard Compounds and Prepar-ing Standard Vulcanized SheetsD3892 Practice for Packaging/Packing of Plastics2.2 ISO Standards:3ISO 2898-1 PlasticsPlasticide Compounds of Homopoly-mers

12、 and Copolymers of Vinyl Chloride (PVC-P)ISO 2898-2 PlasticsPlasticide Compounds of Homopoly-mers and Copolymers of Vinyl Chloride (PVC-P)Part 2Preparation of Test Specimens and Determination ofProperties3. Terminology3.1 GeneralDefinitions are in accordance with Terminol-ogy D883 and abbreviations

13、with Terminology D1600, unlessotherwise indicated.1This specification is under the jurisdiction of ASTM Committee D20 onPlastics and is the direct responsibility of Subcommittee D20.15 on ThermoplasticMaterials.Current edition approved Sept. 1, 2011. Published September 2011. Originallyapproved in 1

14、964. Last previous edition approved in 2010 as D2287 - 96(2010).DOI: 10.1520/D2287-11.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary

15、 page onthe ASTM website.3Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohock

16、en, PA 19428-2959, United States.4. Classification4.1 Provision is made in this specification for the identifi-cation of vinyl chloride polymers and copolymers by use ofTerminology D1600. Additionally, there is provision for dis-tinguishing electrical grades and burning rate by suffix. Thesystem of

17、classification provided in Table 1 permits character-ization and identification of all compounds having propertieswithin the ranges of the combinations that may be selectedfrom the table. Following type identification in accordancewith Terminology D1600, grades are designated by the cellnumber for e

18、ach property in the order in which they are listedin Table 1, including the suffixes identifying electrical gradesand flammability when required. When a property is notspecified, a “0” is entered as the cell number unless identifi-cation is terminated prior to that point.NOTE 2The manner in which se

19、lected materials are identified isillustrated by the examples given below:NOTE 3The cell-type format provides means for close characteriza-tion and specification of material properties, alone or in combination, fora broad range of materials. This format, however, is subject to possiblemisapplication

20、 since unobtainable property combinations can be selectedif the user is not familiar with commercially available materials. Themanufacturer should be consulted.5. General Requirements5.1 Material shall be of uniform composition and be socompounded as to meet the requirements designated for it.5.2 Th

21、e designated material shall contain the ingredientsnecessary to permit satisfactory processing with appropriateequipment under recommended or commercially acceptableconditions. There shall be no separation of components underconditions of application normal for these compounds.TABLE 1 Detail Grade R

22、equirementsDesignationOrder No.Property and UnitCell Limits0 1234567891 Durometer hardness, A scale unspecified 1.5973F/23C 1.24 1.29 1.34 1.39 1.44 1.49 1.593 Tensile strength, min:MPa 24.1psi 35004 Volatile loss at 105C, max, % unspecified 1.0 2.0 3.0 4.0 5.0 6.0 7.0 7.05 Brittleness temperature,

23、max, C unspecified 0 5 10 15 20 30 40 50 60E Volume resistivity at 50C, min, V-cm unspecified 101110121013. . . . . .X Burning rate unspecified .A. . . . . . . .AWhen tested in accordance with Test Method D635, the compounds of this cell unit designation shall yield the following results: average ex

24、tent of burning of 25 mm;average time of burning of 10 s.D2287 1126. Significance and Use6.1 Means for selecting and identifying nonrigid vinylchloride compounds are provided in Table 1. The propertiesenumerated in this table and the tests defined are expected toprovide identification of the compoun

25、ds selected. They are notnecessarily suitable for direct application in design because ofdifferences in shape of part, size, loading, environmentalconditions, etc. Only when specimens are molded in accor-dance with 11.1.1 can comparative data be expected. The testsselected can also be used for inspe

26、ction or quality controlprovided that they are performed strictly in accordance with theinstructions given herein and in the designated methods so thatextraneous variables are minimized and results are reproducedwithin the limits of variability of the material being examinedand of the tests used for

27、 its examination.7. Detail Requirements7.1 Compliance with the designated requirements shall bedetermined with test specimens prepared of sheets molded inaccordance with 11.1.1 of this specification.7.2 Test values for specimens so prepared shall comply withthe designated requirements as given in Ta

28、ble 1.7.3 Subject to agreement between the purchaser and theseller, testing on specimens prepared of finished moldedarticles is permitted. It is possible results of such tests will notagree with the values given in Table 1. Therefore, in reports ofsuch tests, methods, and conditions of preparation,

29、dimensions,and all other pertinent information shall be included.8. Contractual Requirements8.1 Nonrigid vinyl chloride plastics ordinarily are suppliedin either diced, pelletized, or granulated form. Particle sizeshall be as agreed between the purchaser and the seller. Otherforms are acceptable whe

30、n agreed upon by the seller andpurchaser.8.2 Color and transparency or opacity of the materials, whenmolded under the conditions recommended by the seller, shallbe comparable within commercial tolerances with a standardspecimen of the same thickness furnished in advance by theseller.9. Number of Tes

31、ts9.1 One set of test specimens as needed to verify therequirements selected in Table 1 and as prescribed in Section11 shall be considered sufficient for testing the material.10. Sampling10.1 Adequate statistical sampling before packaging is anacceptable procedure. A batch or lot of material shall b

32、econsidered as a unit of manufacture prepared for shipment andis permitted to consist of a blend of two or more productionruns of material.10.2 Material shall be free of foreign matter to such a levelof contamination that is agreed upon between the purchaserand the seller.11. Test Methods11.1 The pr

33、operties enumerated herein shall be determinedin accordance with the following methods:11.1.1 Test SpecimensUnless otherwise specified, testspecimens shall be prepared of sheets 1.9 6 0.2 mm (0.075 60.010 in.) thick molded by compression as described inPractice D3182. The conditions of molding shall

34、 be either asrecommended by the seller or in keeping with acceptedcommercial practice for the material being used. Specimensshall be of the shape and dimensions specified in the individualtest methods.11.1.2 ConditioningTest specimens of nonrigid vinylchloride plastics shall be conditioned in accord

35、ance withPractice D618, Procedure A.11.1.3 Test ConditionsTests shall be conducted in theStandard Laboratory Atmosphere of 23 6 2C (73 6 4F) and50 6 10 % relative humidity unless otherwise specified hereinor in the individual test methods.11.1.4 Durometer HardnessTest Method D2240 using a15-s interv

36、al as described in 10.2 of that method.11.1.5 Specific GravityTest Methods D792, Method A.Alternative methods of equal accuracy is permitted except forreferee tests.11.1.6 Tensile StrengthTest Method D638, Type IV. Testspeed shall be 50 mm/min (2 in./min) 6 10 %.11.1.7 Volatile LossTest Methods D120

37、3, Method A. Testtemperature shall be 105C.11.1.8 Brittleness TemperatureTest Method D746.11.1.9 Volume ResistivityTest Methods D257. Test speci-mens shall be of any uniform thickness between 0.5 mm (0.020in.) and 2.2 mm (0.085 in.), test temperature shall be 50 61.0C, and electrodes are either merc

38、ury, conductive paints, orsprayed or evaporated metal as described in the section onElectrode Systems of Test Methods D257 and mounted asshown in the figures illustrating a flat specimen for measuringvolume and surface resistances or conductances and mercuryelectrodes for flat, solid specimens in th

39、at method. Appliedvoltage within the range 100 to 500 V is recommended.11.1.10 Burning RateTest Method D635.12. Retest and Rejection12.1 If any failure occurs, the materials shall be retested toestablish conformity in accordance with agreement betweenthe purchaser and the seller.13. Packaging and Pa

40、ckage Marking13.1 PackagingThe material shall be packaged in stan-dard commercial containers so constructed as to ensure accep-tance by common or other carriers for safe transportation at thelowest rate to the point of delivery, unless otherwise specifiedin the contract or order.13.2 Package Marking

41、Unless otherwise agreed betweenthe seller and the purchaser, shipping containers shall bemarked with the name of the material, the batch or lot number,and the quantity contained therein, as defined by the contract ororder under which shipment is made, the name of the seller,and the number of the con

42、tract or order.13.3 All packing, packaging, and marking provisions ofPractice D3892 shall apply to this specification.D2287 11314. Keywords14.1 compounds; nonrigid; poly(vinyl chloride); recycleplastics; vinyl chloride copolymersSUMMARY OF CHANGESCommittee D20 has identified the location of selected

43、 changes to this standard since the last issue(D2287 - 96(2010) that may impact the use of this standard. (September 1, 2011)(1) Corrected ISO statement in Note 1to be in accordance withGuide D4968.(2) Removed non-mandatory language from 1.1, 1.3, 6.1, 7.3,8.1, 10.1, 10.2, 11.1.9, and 12.1.(3) Delet

44、ed D412 and D1898; and added D638 in 2.1.(4) Deleted year dates from ISO references in 2.2.(5) Removed PVC from examples in Note 2.(6) Removed reference to D1898 in 10.1 since it has beendiscontinued.(7) Revised 11.1.2, 11.1.5, 11.1.7, and 11.1.8.(8) Increased humidity deviation to 6 10 % from 5 % i

45、n11.1.3.(9) Revised 11.1.6: Reference D638, Type IV specimen. Settest speed.(10) Added nonrigid to Keywords.(11) Corrected Specific Gravity temperature (F) in Table 1.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin th

46、is standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must b

47、e reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theres

48、ponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, W

49、est Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D2287 114