ASTM F2179-2014 Standard Specification for Annealed Soda-Lime-Silicate Glass Containers That Are Produced for Use as Candle Containers《用作蜡烛台而生产的退火钠钙硅酸盐玻璃容器的标准规范》.pdf

《ASTM F2179-2014 Standard Specification for Annealed Soda-Lime-Silicate Glass Containers That Are Produced for Use as Candle Containers《用作蜡烛台而生产的退火钠钙硅酸盐玻璃容器的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM F2179-2014 Standard Specification for Annealed Soda-Lime-Silicate Glass Containers That Are Produced for Use as Candle Containers《用作蜡烛台而生产的退火钠钙硅酸盐玻璃容器的标准规范》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F2179 14Standard Specification forAnnealed Soda-Lime-Silicate Glass Containers That AreProduced for Use as Candle Containers1This standard is issued under the fixed designation F2179; the number immediately following the designation indicates the year oforiginal adoption or, in the case

2、 of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the minimum requirements forannealed soda-lime-silicate glass cont

3、ainers when the producerknows the containers are to be used as candle containers.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and de

4、termine the applica-bility of regulatory requirements prior to use.2. Referenced Documents2.1 Reference to these documents shall be the latestrevision, unless otherwise specified by the authority applyingthis specification.2.2 ASTM Standards:2C148 Test Methods for Polariscopic Examination of GlassCo

5、ntainersC149 Test Method for Thermal Shock Resistance of GlassContainersC162 Terminology of Glass and Glass ProductsC224 Practice for Sampling Glass ContainersF1972 Guide for Terminology Relating to Candles andAssociated Accessory Items3. Terminology3.1 For definitions of glass and glass products te

6、rms used inthis specification, refer to Terminology C162.3.2 For definitions of candle related terms used in thisspecification, refer to Guide F1972.4. Performance Requirements4.1 Annealing:4.1.1 Transparent GlassContainers examined under po-larized light in accordance with Test Methods C148 shall,

7、afterannealing, show no greater than real temper number 4. Thisperformance requirement will also apply to containers that arefurther processed (such as ceramic enamel decorations), fol-lowing the original manufacture, by reheating the containerabove the strain point and cooling to room temperature.

8、TheScratch Test (Section 5) can be used as an alternative to TestMethods C148. Containers tested in accordance with theScratch Test shall show no fractures.4.1.2 Non-transparent GlassIf glass condition (color,decoration, etc.) prohibits sufficient light transmission for useof Test Methods C148, anne

9、aling shall be qualified through theuse of the Scratch Test (Section 5). Containers tested inaccordance with the Scratch Test shall show no fractures. Thisperformance requirement will also apply to containers that arefurther processed (such as ceramic enamel decorations), fol-lowing the original man

10、ufacture, by re-heating the containerabove the strain point and cooling to room temperature.4.2 Thermal Shock:4.2.1 Containers shall not crack or break when tested, withthe water retained in the container from the first immersionthrough the second immersion, at a thermal shock temperaturedifferentia

11、l (T) of 50C (90F) during continuous productionin accordance with Test Method C149.4.2.2 Containers shall be tested at a thermal shock tempera-ture differential (T) of 50C (90F) during lot sampling inaccordance with Practice C224.5. Test Methods5.1 ScopeThis Scratch Test Method is designed to ensure

12、that residual stress is reduced to a commercially acceptablelevel in annealed soda-lime-silicate glass containers that areintended for use as candle containers. It provides an alternativemethod to Test Methods C148. Two methods of performing theScratch Test are covered:5.1.1 Test Method AScratch Tes

13、t using a tungsten carbidescribe, 5.4.2.1, and5.1.2 Test Method BScratch Test using fifty-grit emerypaper/cloth, 5.4.2.2.NOTE 1Independent test results showed no significant statisticaldifference between using tungsten carbide scribe and fifty-grit emerypaper/cloth.1This specification is under the j

14、urisdiction of ASTM Committee F15 onConsumer Products and is the direct responsibility of Subcommittee F15.45 onCandle Products.Current edition approved Jan. 15, 2014. Published February 2014. Originallyapproved in 2002. Last previous edition approved in 2013 as F2179 02 (2013).DOI: 10.1520/F2179-14

15、.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box

16、C700, West Conshohocken, PA 19428-2959. United States15.2 Significance and UseThis test method can be used inthe quality control of soda-lime-silicate glass candlecontainers, where the degree of annealing must be verified toensure quality products. This procedure can be used whereglass cannot be rea

17、d by polariscope (color, decoration, etc.) oras an alternative method for transparent glass containers.5.3 SamplingMethods of sampling for a group of contain-ers of a given type are given in Practice C224 for annealing.5.4 Test Procedure:5.4.1 Allow the ware to cool evenly through the entirethicknes

18、s of the container to room temperature before usingeither Method A or B.NOTE 2Failure to cool the container completely may result in a falseresult.5.4.2 Scratch Procedure:5.4.2.1 Using Method AWith a tungsten carbide scribe,scratch once around the inside knuckle of the article. Thenscratch an “X” ac

19、ross the entire inside bottom surface of thearticle. All scratches are to be made using sufficient pressure topenetrate the surface of the glass.5.4.2.2 Using Method BWith fifty-grit emery paper/cloth,abrade the inside surface of each article using sufficient force topenetrate the surface of the gla

20、ss. Ensure that all sharp corners,dimples, indentations are abraded. A new piece of emerypaper/cloth is to be used for every piece tested.5.4.3 After using either method A or B, fill each article withwater at the same room temperature as the glass. Wait fifteenminutes, then empty the water and exami

21、ne each piece forfractures.5.5 ReportReport the number of fractures, if any for eachtest.5.6 Precision and BiasNo information is presented abouteither the precision or bias of the scratch test method since thetest result (fracture versus no fracture) is nonquantitative.6. Keywords6.1 annealing; attr

22、ibutes; candle containers; glass; nontransparent glass; scratch test; soda-lime-silicate; thermalshock; transparent glassASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expres

23、sly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised,

24、 either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may at

25、tend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States.

26、 Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).F2179 142