《ASTM F2179-2002(2013) Standard Specification for Annealed Soda-Lime-Silicate Glass Containers That Are Produced for Use as Candle Containers《用作蜡烛台而生产的退火钠钙硅酸盐玻璃容器的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM F2179-2002(2013) Standard Specification for Annealed Soda-Lime-Silicate Glass Containers That Are Produced for Use as Candle Containers《用作蜡烛台而生产的退火钠钙硅酸盐玻璃容器的标准规范》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F2179 02 (Reapproved 2013)Standard Specification forAnnealed Soda-Lime-Silicate Glass Containers That AreProduced for Use as Candle Containers1This standard is issued under the fixed designation F2179; the number immediately following the designation indicates the year oforiginal adopti

2、on or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the minimum requirements forannealed soda-lime-s

3、ilicate glass containers when the producerknows the containers are to be used as candle containers.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and healt

4、h practices and determine the applica-bility of regulatory requirements prior to use.2. Referenced Documents2.1 Reference to these documents shall be the latestrevision, unless otherwise specified by the authority applyingthis specification.2.2 ASTM Standards:2C148 Test Methods for Polariscopic Exam

5、ination of GlassContainersC149 Test Method for Thermal Shock Resistance of GlassContainersC162 Terminology of Glass and Glass ProductsC224 Practice for Sampling Glass ContainersF1972 Guide for Terminology Relating to Candles andAssociated Accessory Items3. Terminology3.1 For definitions of glass and

6、 glass products terms used inthis specification, refer to Terminology C162.3.2 For definitions of candle related terms used in thisspecification, refer to Guide F1972.4. Performance Requirements4.1 Annealing:4.1.1 Transparent GlassContainers examined under po-larized light in accordance with Test Me

7、thods C148 shall, afterannealing, show no greater than real temper number 4. Thisperformance requirement will also apply to containers that arefurther processed (such as ceramic enamel decorations), fol-lowing the original manufacture, by reheating the containerabove the strain point and cooling to

8、room temperature. TheScratch Test (Section 5) can be used as an alternative to TestMethods C148. Containers tested in accordance with theScratch Test shall show no fractures.4.1.2 Non-transparent GlassIf glass condition (color,decoration, etc.) prohibits sufficient light transmission for useof Test

9、Methods C148, annealing shall be qualified through theuse of the Scratch Test (Section 5). Containers tested inaccordance with the Scratch Test shall show no fractures. Thisperformance requirement will also apply to containers that arefurther processed (such as ceramic enamel decorations), fol-lowin

10、g the original manufacture, by re-heating the containerabove the strain point and cooling to room temperature.4.2 Thermal Shock:4.2.1 Containers shall not crack or break when tested at athermal shock temperature differential (T) of 50C (90F)during continuous production in accordance with Test Method

11、C149.4.2.2 Containers shall be tested at a thermal shock tempera-ture differential (T) of 50C (90F) during lot sampling inaccordance with Practice C224.5. Test Methods5.1 ScopeThis Scratch Test Method is designed to ensurethat residual stress is reduced to a commercially acceptablelevel in annealed

12、soda-lime-silicate glass containers that areintended for use as candle containers. It provides an alternativemethod to Test Methods C148. Two methods of performing theScratch Test are covered:5.1.1 Test Method AScratch Test using a tungsten carbidescribe, 5.4.2.1, and5.1.2 Test Method BScratch Test

13、using fifty-grit emerypaper/cloth, 5.4.2.2.NOTE 1Independent test results showed no significant statisticaldifference between using tungsten carbide scribe and fifty-grit emerypaper/cloth.1This specification is under the jurisdiction of ASTM Committee F15 onConsumer Products and is the direct respon

14、sibility of Subcommittee F15.45 onCandle Products.Current edition approved July 1, 2013. Published September 2013. Originallyapproved in 2002. Last previous edition approved in 2007 as F2179 02 (2007).DOI: 10.1520/F2179-02R13.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orco

15、ntact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15.2 Significance and

16、UseThis test method can be used inthe quality control of soda-lime-silicate glass candlecontainers, where the degree of annealing must be verified toensure quality products. This procedure can be used whereglass cannot be read by polariscope (color, decoration, etc.) oras an alternative method for t

17、ransparent glass containers.5.3 SamplingMethods of sampling for a group of contain-ers of a given type are given in Practice C224 for annealing.5.4 Test Procedure:5.4.1 Allow the ware to cool evenly through the entirethickness of the container to room temperature before usingeither Method A or B.NOT

18、E 2Failure to cool the container completely may result in a falseresult.5.4.2 Scratch Procedure:5.4.2.1 Using Method AWith a tungsten carbide scribe,scratch once around the inside knuckle of the article. Thenscratch an “X” across the entire inside bottom surface of thearticle. All scratches are to b

19、e made using sufficient pressure topenetrate the surface of the glass.5.4.2.2 Using Method BWith fifty-grit emery paper/cloth,abrade the inside surface of each article using sufficient force topenetrate the surface of the glass. Ensure that all sharp corners,dimples, indentations are abraded. A new

20、piece of emerypaper/cloth is to be used for every piece tested.5.4.3 After using either method A or B, fill each article withwater at the same room temperature as the glass. Wait fifteenminutes, then empty the water and examine each piece forfractures.5.5 ReportReport the number of fractures, if any

21、 for eachtest.5.6 Precision and BiasNo information is presented abouteither the precision or bias of the scratch test method since thetest result (fracture versus no fracture) is nonquantitative.6. Keywords6.1 annealing; attributes; candle containers; glass; nontransparent glass; scratch test; soda-

22、lime-silicate; thermalshock; transparent glassASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, a

23、nd the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revis

24、ion of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you s

25、houldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).F2179 02 (2013)2