ASTM D7349 D7349M-2015 red 1923 Standard Test Method for Determining the Capability of Roofing and Waterproofing Materials to Seal around Fasteners《测定屋顶和防水材料与周围紧固件接合能力的标准试验方法》.pdf

《ASTM D7349 D7349M-2015 red 1923 Standard Test Method for Determining the Capability of Roofing and Waterproofing Materials to Seal around Fasteners《测定屋顶和防水材料与周围紧固件接合能力的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D7349 D7349M-2015 red 1923 Standard Test Method for Determining the Capability of Roofing and Waterproofing Materials to Seal around Fasteners《测定屋顶和防水材料与周围紧固件接合能力的标准试验方法》.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D7349/D7349M 11D7349/D7349M 15Standard Test Method forDetermining the Capability of Roofing and WaterproofingMaterials to Seal around Fasteners1This standard is issued under the fixed designation D7349/D7349M; the number immediately following the designation indicates theyear of origina

2、l adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This qualitative test method determines the capability of asphalt-

3、based roofing or waterproofing material to seal around afastener that penetrates the material and prevent transmission of liquid water through the material at the penetration under definedconditions.1.2 This test method is provided for adoption by ASTM or other consensus-based roofing and waterproof

4、ing productspecifications as a standardized means to evaluate capability to seal around a fastener. Performance of this test method aftersubjecting the product to conditioning intended to simulate environmental stresses and strains is not prohibited.1.3 The text of this test method references notes

5、and footnotes which provide explanatory material. These notes and footnotes(excluding those in tables and figures) shall not be considered as requirements of the standard.1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each

6、system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from thetwo systems may result in non-conformance with the standard.1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is

7、the responsibilityof the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatorylimitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D1079 Terminology Relating to Roofing and WaterproofingD3462D3462/D3462M Specification

8、for Asphalt Shingles Made from Glass Felt and Surfaced with Mineral GranulesD5147D5147/D5147M Test Methods for Sampling and Testing Modified Bituminous Sheet MaterialF1667 Specification for Driven Fasteners: Nails, Spikes, and Staples3. Terminology3.1 DefinitionsFor definitions of terms used in this

9、 test method, refer to Terminology D1079.4. Summary of Test Method4.1 The capability of asphalt-based roofing or waterproofing materials to seal around a penetrating fastener and prevent thepassage of liquid water at the fastener/material interface is determined by penetrating the material with a fa

10、stener, erecting a watercolumn over that penetration, and monitoring the assembly for water passage for a period of time.4.2 The test method includes protocols that establish levels for the test method parameters. The protocol used to evaluate amaterial is designated in a standard specification for

11、the material or by the user of this test method.5. Significance and Use5.1 In some situations, penetration through asphalt-based roofing or waterproofing materials by fasteners is a required part ofthe material installation process or occurs during installation of other system components. When faste

12、ners penetrate the material1 This test method is under the jurisdiction of ASTM Committee D08 on Roofing and Waterproofing and is the direct responsibility of Subcommittee D08.02 on SteepRoofing Products and Assemblies.Current edition approved May 1, 2011Dec. 15, 2015. Published May 2011December 201

13、5. Originally approved in 2008. Last previous edition approved in 20102011 asD7349/D7349M 10.D7349/D7349M 11. DOI: 10.1520/D7349_D7349M-11.10.1520/D7349_D7349M-15.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book

14、of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technica

15、lly possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box

16、C700, West Conshohocken, PA 19428-2959. United States1as a purposeful and planned part of the construction process, it is reasonable to expect that materials designed to limit migrationof liquid water at the interface between the penetrating fastener and the material will do so. This qualitative tes

17、t method providesa means to evaluate the ability of a material to limit water migration at fastener penetrations when tested under defined conditions.6. Apparatus6.1 Specimen RollerA roller having a mass of 11.8 kg 26 lb 60.5 %, diameter of 125 mm 5 in. 65 %, and width of 125mm 5 in. 65 %.6.2 Water

18、Column ContainerA4A 4 L 1 gal can with the bottom cut out.6.3 SealantAny commercially-available sealant suitable for sealing the water column container to the roofing or waterproof-ing material that will not adversely affect the roofing or waterproofing material.6.4 FastenerThe item that penetrates

19、the test specimen. Use one fastener for each test specimen. Refer to Table 1.6.5 SubstrateThe material to which the test specimen is attached prior to penetration with the fastener. One piece 255 by 255mm 10 by 10 in. 65 % is required for each test specimen. Refer to Table 1.6.6 Intervening Material

20、A material placed between the test specimen and the fastener. Refer to Table 1.7. Sampling7.1 From each lot of roofing or waterproofing material, select sample rolls in accordance with Test Methods D5147D5147/D5147M.7.2 The rolls so selected shall constitute the representative sample used for all te

21、sts pertaining to the lot of material beingexamined.8. Test Specimens8.1 Each test specimen shall consist of one piece of roofing or waterproofing material, 255 by 255 mm 10 by 10 in. 65 %65 % in size, selected at random from a sample roll.8.2 At least one test specimen shall be selected from each s

22、ample roll.8.3 Condition test specimens at 23 6 2C 73.4 6 3.6F and 50 6 10 % relative humidity for at least four hours prior to testassembly preparation.9. Test Assembly Preparation9.1 Select a protocol from Table 1 for the material to be evaluated (see Appendix X1) or use the protocol designated by

23、 thestandard specification for the material. Specify the number of specimens to be selected from each sample roll.9.2 Prepare one test assembly for each test specimen, assembling the materials in accordance with these instructions and asillustrated in Fig. 1. Use the substrate, intervening material,

24、 fastener, and fastener driving method specified by the selected protocol(see Table 1).9.3 Apply the test specimen to the substrate specified in the selected protocol (see Table 1, Substrate) as follows:9.3.1 Self-adhesive materialsPeel the release paper or film off the roofing or waterproofing spec

25、imen and lightly place thespecimen on the substrate, centering the specimen on the substrate with the edges of the specimen and substrate aligned. Pressdown the edges of the specimen just hard enough to keep the edges from lifting. Roll the specimen to promote adhesion to thesubstrate using the spec

26、imen roller, completing a total of three back-and-forth cycles. Each cycle shall be completed in 4 to 6 s.9.3.2 Non-self-adhesive materialsPlace the specimen on the substrate, centering the specimen on the substrate with the edgesof the specimen and substrate aligned.9.4 Place two pieces of lumber,

27、oriented parallel to each other and spaced 50 6 10 mm 2 6 0.5 in. apart, underneath thesubstrate for support.9.5 Place the intervening material specified in the selected protocol (see Table 1, Intervening Material) on top of the testspecimen, centering it in both directions.9.6 Drive one fastener sp

28、ecified in the selected protocol (see Table 1, Fastener) through the intervening material (if present),test specimen, and substrate near the center of the specimen in the area between the two pieces of supporting lumber in the mannerspecified in the selected protocol (see Table 1, Fastener Driving M

29、ethod).9.7 Place the water column container on the specimen, centered over the fastener. Apply a 6 to 10-mm 0.25 to 0.375-in. beadof sealant completely around the outside rim of the water column container to bond it to the specimen. Allow a minimum of 2 hfor the sealant to set, then apply another be

30、ad around the inside rim of the water column container.9.8 Maintain the test assembly at 23 6 2C 73.4 6 3.6F and 50 6 10 % 10 % relative humidity for 24 hours to allow thesealant to cure.D7349/D7349M 152TABLE 1 ProtocolsPROTOCOL 1Substrate APA Rated Sheathing, 3216, Exposure 1 plywood,12 mm 1532 in.

31、 thickIntervening Material NoneFastener ASTM F1667 NLRFSS-53Z smooth shank steel roofing nail32 mm 1.25 in. long with a shank diameter of 3.05 mm0.120 in., a head diameter of 9.52 mm 0.375 in.,and a zinc coatingFastener Driving Method With a hammer, perpendicular to the specimen, until the fastenerh

32、ead is flush with the surface of the specimenTest Assembly Conditioning 4 0.25 h at 40 2C 104 3.6F, followed by20 0.25 h at 23 2C 73.4 3.6FWater Depth 125 6 mm 5 0.25 in.Test Temperature 4 2C 39.2 3.6FTest Period 72 0.25 hPROTOCOL 2Substrate APA Rated Sheathing, 3216, Exposure 1 plywood,12 mm 1532 i

33、n. thickIntervening Material NoneFastener ASTM F1667 NLRFSS-53Z smooth shank steel roofing nail32 mm 1.25 in. long with a shank diameter of 3.05 mm0.120 in., a head diameter of 9.52 mm 0.375 in.,and a zinc coatingFastener Driving Method With a hammer, perpendicular to the specimen, until the fastene

34、rhead is flush with the surface of the specimenTest Assembly Conditioning 4 0.25 h at 40 2C 104 3.6F, followed by20 0.25 h at 23 2C 73.4 3.6FWater Depth 25 1 mm 1.0 0.05 in.Test Temperature 4 2C 39.2 3.6FTest Period 8 0.25 hPROTOCOL 3Substrate APA Rated Sheathing, 3216, Exposure 1 oriented strand bo

35、ard,12 mm 1532 in. thickIntervening Material 75 by 75 mm 3 by 3 in. single-thickness piece ofD3462-labeled asphalt shingleIntervening Material 75 by 75 mm 3 by 3 in. single-thickness piece ofD3462/D3462M-labeled asphalt shingleFastener ASTM F1667 NLRFSR-53Z ring shank steel roofing nail32 mm 1.25 in

36、. long with a shank diameter of 3.05 mm0.120 in., a head diameter of 9.52 mm 0.375 in.,and a zinc coatingFastener Driving Method With a hammer, perpendicular to the specimen, until the fastenerhead is flush with the surface of the intervening materialTest Assembly Conditioning 24 0.25 h at 23 2C 73.

37、4 3.6FWater Depth 125 6 mm 5 0.25 in.Test Temperature 4 2C 39.2 3.6FTest Period 72 0.25 hPROTOCOL 4Substrate APA Rated Sheathing, 3216, Exposure 1 plywood,12 mm 1532 in. thickIntervening Material 75 by 75 mm 3 by 3 in. single-thickness piece ofD3462-labeled asphalt shingleIntervening Material 75 by

38、75 mm 3 by 3 in. single-thickness piece ofD3462/D3462M-labeled asphalt shingleFastener ASTM F1667 NLRFSS-53Z smooth shank steel roofing nail32 mm 1.25 in. long with a shank diameter of 3.05 mm0.120 in., a head diameter of 9.52 mm 0.375 in.,and a zinc coating; hot dipped galvanizedFastener Driving Me

39、thod With a hammer, perpendicular to the specimen, until the fastenerhead is flush with the surface of the intervening materialTest Assembly Conditioning 24 0.25 h at 23 2C 73.4 3.6FWater Depth 125 6 mm 5 0.25 in.Test Temperature 4 2C 39.2 3.6FTest Period 72 0.25 hD7349/D7349M 1539.9 After the seala

40、nt has cured, condition the test assembly as specified in the selected protocol (see Table 1, Test AssemblyConditioning).PROTOCOL 5Substrate APA Rated Sheathing, 3216, Exposure 1 oriented strand board,12 mm 1532 in. thickIntervening Material 75 by 75 mm 3 by 3 in. single-thickness piece ofD3462-labe

41、led asphalt shingleIntervening Material 75 by 75 mm 3 by 3 in. single-thickness piece ofD3462/D3462M-labeled asphalt shingleFastener ASTM F1667 NLRFSS-53Z smooth shank steel roofing nail32 mm 1.25 in. long with a shank diameter of 3.05 mm0.120 in., a head diameter of 9.52 mm 0.375 in.,and a zinc coa

42、ting; electrogalvanized; coil gun nailFastener Driving Method With a coil-fed pneumatic tool (nail gun), perpendicularto the specimen, pneumatic tool pressure set to ensurethe fastener head is flush with the surface ofthe intervening materialTest Assembly Conditioning 24 0.25 h at 23 2C 73.4 3.6FWat

43、er Depth 125 6 mm 5 0.25 in.Test Temperature 4 2C 39.2 3.6FTest Period 72 0.25 hNoteThere is a possibility of increased variability in test results when pneumatically-driven coil nails are used instead of hand-driven nails.FIG. 1 Test ArrangementD7349/D7349M 15410. Procedure10.1 Conduct the test usi

44、ng the water depth, test temperature, and test period specified in the selected protocol (see Table 1).10.2 Place the test assembly atop a 4 L 1-gal can from which the lid has been removed.10.3 Fill the water column container to the depth specified in the selected protocol (see Table 1, Water Depth)

45、 with deionizedor distilled water.10.4 Place the test assembly and 4 L 1-gal bottom can in a temperature controlled chamber maintained at the temperaturespecified by the selected protocol (see Table 1, Test Temperature).10.5 Maintain the test assembly at the test temperature for the test period spec

46、ified by the selected protocol (see Table 1, TestPeriod).10.6 At the conclusion of the test period, remove the test assembly from the 4 L 1-gal bottom can, carefully pour the waterfrom the water column container without splashing onto the substrate, and blot the inside of the water column container

47、dry.Examine the assembly and note any water in the 4 L 1-gal bottom can, on the shank of the fastener, or on the underside of thesubstrate.10.7 Carefully remove the water column container from the roofing or waterproofing material. Peel the roofing or waterproofingmaterial back to the fastener and i

48、nspect the underside of the material and top side of the substrate for any signs of water.11. Interpretation of Results11.1 A specimen is considered to pass the test if no water is present in the 4 L 1-gal bottom can, on the underside of thesubstrate, on the shank of the fastener, or between the mat

49、erial and the substrate.12. Report12.1 Report the following information:12.1.1 Identifying information about the roofing or waterproofing material being tested, including the manufacturer and productname.12.1.2 The number of sample rolls.12.1.3 The number of specimens tested per sample roll.12.1.4 The protocol use