ASTM D2918-1999(2005) Standard Test Method for Durability Assessment of Adhesive Joints Stressed in Peel《受撕裂应力的胶粘接头耐用性的标准试验方法》.pdf

《ASTM D2918-1999(2005) Standard Test Method for Durability Assessment of Adhesive Joints Stressed in Peel《受撕裂应力的胶粘接头耐用性的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D2918-1999(2005) Standard Test Method for Durability Assessment of Adhesive Joints Stressed in Peel《受撕裂应力的胶粘接头耐用性的标准试验方法》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 2918 99 (Reapproved 2005)Standard Test Method forDurability Assessment of Adhesive Joints Stressed in Peel1This standard is issued under the fixed designation D 2918; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, t

2、he year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.INTRODUCTIONThe combination of stress and moisture decreases the durability of most adhesive joints. Stresses inthe pr

3、esence of water or water vapor may cause some adhesive joints to fail at some fraction of thestress required to break the dry joint. The time to failure for a given adhesive joint tested under moistconditions generally decreases with increasing stress, temperature, and relative humidity.1. Scope1.1

4、This test method provides data for assessing the dura-bilities of adhesive joints by means of T-peel type specimensstressed in contact with air, air in equilibrium with certainsolutions, water, aqueous solutions, or other environments atvarious temperatures.1.2 The values stated in SI units are to b

5、e regarded as thestandard. The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and

6、determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2B 209 Specification for Aluminum and Aluminum-AlloySheet and PlateD 907 Terminology of AdhesivesD 1828 Practice for Atmospheric Exposure of Adhesive-Bonded Joints and StructuresD 1876 Test

7、Method for Peel Resistance of Adhesives(T-Peel Test)D 2651 Guide for Preparation of Metal Surfaces for Adhe-sive BondingE 104 Practice for Maintaining Constant Relative Humidityby Means of Aqueous Solutions3. Terminology3.1 DefinitionsMany terms in this practice are defined inTerminology D 907.4. Si

8、gnificance and Use4.1 The combination of stress and moisture decreases thedurability of most adhesive joints. Stresses in the presence ofwater or water vapor may cause some adhesive joints to fail atsome small fraction of the stress required to break the dry joint.The time to failure for a given adh

9、esive joint generallydecreases with increasing stress, temperature, and relativehumidity.4.2 This test method may be used as an accelerated screen-ing test for assessing the durability of adhesive joints. It may beused to measure durability of adhesive joints exposed outdoorsor to environmental cond

10、itions experienced by adhesive jointsin service. It may also be used to determine the effects ofvarious surface preparations or substrates on durabilities ofadhesive joints.4.3 The durability performance of various adhesives may becompared by using this test method under uniform sets ofconditions. T

11、o assess the overall durability of a given adhesive,T-peel joints should be tested under a range of stress, relativehumidity, and temperature. For a specific end use it may bepossible to obtain the needed durability data using only one setof test conditions.5. Apparatus5.1 For outdoor exposure the t

12、est location should be in anarea free of or protected from high winds. Standard outdoorweathering racks are suggested (Practice D 1828), but anystable frame may be used (for example galvanized pipe orpainted steel channel). No other special apparatus is requiredfor outdoor tests.5.2 For exposure in

13、environmental cabinets or chambers noadditional special apparatus is necessary. Constant-temperaturebaths may also be used.1This test method is under the jurisdiction of ASTM Committee D14 onAdhesives and is the direct responsibility of Subcommittee D14.80 on MetalBonding Adhesives.Current edition a

14、pproved April 1, 2005. Published April 2005. Originallyapproved in 1971. Last previous edition approved in 1999 as D 2918 99.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information,

15、refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.3 For exposure to distilled or deionized water in thelaboratory it may be convenient to use the apparatus shown inFig.

16、1.5.4 For exposure to constant relative humidities, the speci-men may be placed in a apparatus similar to that shown in Fig.1. A saturated salt solution may be placed in the bottom of theglass tube to provide a constant relative humidity (see PracticeE 104); a stopper having a small glass tube packe

17、d with greasemay be used to seal the upper end of the large glass tube.6. Test Specimens6.1 The successful use of the following test method dependson preparing good quality T-peel joint specimens. Prepare thetest panels carefully according to the adhesive manufacturersdirections or according to some

18、 other specified set of condi-tions agreed upon between the manufacturer and the purchaser.6.2 Use the test-panel construction and the test specimendescribed in Test Method D 1876. To adapt to differing testconditions and constraints due to size or configuration ofvarious test environments and appar

19、atus, dimensions of thespecimen may be varied as long as they are identical whenmaking direct comparisons of different adhesives.NOTE 1For example, test specimens may be cut to 12.7 mm (1 in.)wide to fit more readily into a glass tube as shown in Fig. 1.6.3 The adherend surfaces may be either etched

20、 (see GuideD 2651), solvent wiped, degreased, or treated by some otherspecified method of surface preparation.7. Conditioning7.1 Condition the peel specimens while either stressed orunstressed in the environment of the specific test for aFIG. 1 Apparatus for Measuring Adhesive Peel Rates in WaterD 2

21、918 99 (2005)2minimum of one day before beginning measurements. Carrythis out by discounting measurements made during the firstday.8. Procedure8.1 Clamp one end of the nonbonded part of the T-peel testspecimen as shown in Fig. 1 and attach to a stationary frame orobject relatively free of vibrations

22、. Clamp the other end of thepanel and attach the desired weight (if the apparatus shown inFig. 1 is used, the total force on the adhesive joint is equal tothe sum of the weights of the water, the wet-peel apparatus, andthe applied weight. To avoid possible breaking of the glass tubewhen a joint fail

23、s it is useful to attach a light-weight string fromthe hose clamp or wire around the upper part of the glass tubeto the fixed point of support. If this apparatus is not used, thepeel joints may be tested in series by bolting several jointstogether and attaching the weight at the bottom). The forceex

24、erted on the adhesive joint being tested should be a multipleof 450 g (1.0 lb). Expose the stressed specimen to one of thestandard test environments, and then measure the length of theunpeeled portion of the specimen. Record this length hourly,daily, or weekly depending on the rate of peel of the sp

25、ecimenuntil the specimen has peeled to failure. Make at least sixmeasurements for each specimen. Test a minimum of threespecimens under each set of conditions (test environment andstress). Suggested stress levels are 25, 50, and 75 % of thenormal T-peel strength as measured by Test Method D 1876.9.

26、Calculation9.1 Plot the distance peeled (distance peeled equals initiallength of unpeeled portion minus length of unpeeled portion attime t) versus time. The slope of the curve at any point is thepeel rate at the corresponding time t. Divide the curve into sixequal parts. If the peel rate varies les

27、s than a factor of two overall six parts of the curve, then obtain an average peel rate (slopeof the curve) for the specimen. In order to assess durability,compare the peel rates under different levels of stress andactivities of water (for example, three stresses each for testenvironments 1 and 3) b

28、y plotting the log of peel rate versusstress.10. Report10.1 Report the following information:10.1.1 Complete identification of the adhesive tested, in-cluding type, form, source, and manufacturers code number.10.1.2 Complete identification of the adherends used, in-cluding composition, thickness, an

29、d the temper for metals.NOTE 2The two adherends need not be identical; for example, a thinadherend may be bonded to a thick adherend with peeling occurring at180.10.1.3 Method of preparing the test panel (both adhesiveand adherends) and conditioning treatment.10.1.4 Method of testing (weight in gram

30、s per millimetre(pounds per inch); test environment number from Table 1,including a complete description of any special test environ-ments; location of outdoor test site and time of year, high, low,average temperatures, and sun exposure; angle of peel).10.1.5 Number of specimens tested, average bond

31、 linethickness, initial peel strength of specimens from the same testpanel, average peel rate (or curves of distance peeled versustime) for each specimen, and plot of log of peel rate versusstress when available.11. Keywords11.1 adhesive; durability; exposure; joint; moisture;stressed; T-peelASTM In

32、ternational takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entire

33、ly their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand s

34、hould be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on S

35、tandards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 6

36、10-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).TABLE 1 Standard Test EnvironmentsTest EnvironmentNumberTemperatureAMoisture ConditionsB1 23C (73.4F) immersed in distilled ordeionized water2 23C (73.4F) 50 % RH (relative humidity)3 23C

37、(73.4F) 15 % RH4 35C (95F) 90 % RH5 35C (95F) 100 % RH6 50C (122F) 90 % RH7 50C (122F) 100 % RH8 35C (95F) 5 % salt fog9 ambient (outdoors) ambient (outdoors)10 other (specify) other, including aqueoussolutions or nonaqueousliquids (specify)AThe tolerance for test temperature shall be 61C (1.8F) for environments 1 to8.BThe moisture condition may be provided by controlling the relative humidity ofa box, room, or other chamber by any convenient means.D 2918 99 (2005)3