1、Designation: B824 16Standard Specification forGeneral Requirements for Copper Alloy Castings1This standard is issued under the fixed designation B824; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A num

2、ber in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This specification establishes general requirements

3、 com-mon to ASTM copper alloy casting specifications B22/B22M,B61, B62, B66, B67, B148, B176, B271/B271M, B369, B427,B505/B505M, B584, B763/B763M, B770, and B806. Theserequirements apply to the casting specifications to the extentreferenced therein.1.1.1 In the event of conflict between this specifi

4、cation anda casting specification, the requirements of the casting speci-fication shall take precedence.1.2 The chemical composition and other requirements notincluded in this specification shall be prescribed in the castingproduct specifications.1.3 UnitsThe values stated in inch-pound units are to

5、 beregarded as standard. The values given in parentheses aremathematical conversions to SI units that are provided forinformation only and are not considered standard.1.4 No precise quantitative relationship can be stated be-tween the properties of the metal in various locations of thesame casting o

6、r between the properties of castings and those ofa test bar casting from the same metal. (See Appendix X1.)22. Referenced Documents2.1 The following documents, of the issue in effect on dateof casting purchase, form, part of this specification to the extentreferenced herein:2.2 ASTM Standards:3B22/B

7、22M Specification for Bronze Castings for Bridgesand TurntablesB61 Specification for Steam or Valve Bronze CastingsB62 Specification for Composition Bronze or Ounce MetalCastingsB66 Specification for Bronze Castings for Steam Locomo-tive Wearing PartsB67 Specification for Car and Tender Journal Bear

8、ings,LinedB148 Specification for Aluminum-Bronze Sand CastingsB176 Specification for Copper-Alloy Die CastingsB193 Test Method for Resistivity of Electrical ConductorMaterialsB194 Specification for Copper-BerylliumAlloy Plate, Sheet,Strip, and Rolled BarB208 Practice for Preparing Tension Test Speci

9、mens forCopper Alloy Sand, Permanent Mold, Centrifugal, andContinuous CastingsB271/B271M Specification for Copper-Base Alloy Centrifu-gal CastingsB369 Specification for Copper-Nickel Alloy CastingsB427 Specification for Gear Bronze Alloy CastingsB505/B505M Specification for Copper Alloy ContinuousCa

10、stingsB584 Specification for Copper Alloy Sand Castings forGeneral ApplicationsB763/B763M Specification for Copper Alloy Sand Castingsfor Valve ApplicationsB770 Specification for Copper-Beryllium Alloy Sand Cast-ings for General ApplicationsB806 Specification for Copper Alloy Permanent Mold Cast-ing

11、s for General ApplicationsB846 Terminology for Copper and Copper AlloysE8/E8M Test Methods for Tension Testing of Metallic Ma-terialsE10 Test Method for Brinell Hardness of Metallic MaterialsE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE29 Practice for Using Significant Digits in Tes

12、t Data toDetermine Conformance with SpecificationsE54 Test Methods for Chemical Analysis of Special Brassesand Bronzes (Withdrawn 2002)41This specification is under the jurisdiction ofASTM Committee B05 on Copperand Copper Alloys and is the direct responsibility of Subcommittee B05.05 onCastings and

13、 Ingots for Remelting.Current edition approved Oct. 15, 2016. Published October 2016. Originallyapproved in 1992. Last previous edition approved in 2014 as B824 14. DOI:10.1520/B0824-16.2For ASME Boiler and Pressure Vessel Code application, see related specifica-tion in Section II of that code.3For

14、referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4The last approved version of this historical standard is referenc

15、ed onwww.astm.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1E62 Test Methods for Chemical Analysis of Copper andCopperAlloys (Photometric Methods) (Withdrawn 2010)

16、4E76 Test Methods for Chemical Analysis of Nickel-CopperAlloys (Withdrawn 2003)4E255 Practice for Sampling Copper and Copper Alloys forthe Determination of Chemical CompositionE478 Test Methods for Chemical Analysis of Copper AlloysE581 Test Methods for Chemical Analysis of Manganese-Copper Alloys2.

17、3 JIS Standard:5JIS H 1068:2005 Methods for Determination of Bismuth inCopper and CopperAlloys (Japanese Industrial Standards)3. Terminology3.1 For definitions of terms related to copper and copperalloys, refer to Terminology B846.3.2 Definitions of Terms Specific to this Standard:3.2.1 lota collect

18、ion of like final product (same alloy,temper, dimensions, as applicable) produced under the same oridentical conditions from which samples were drawn forinspection or testing, or both.4. Materials and Manufacture4.1 ManufactureMechanical properties of Copper AlloyUNS Nos. C94700, C95300, C95400, C95

19、410, C95500,C95520, and C96800 can be changed by heat treatment.Suggested heat treatments are given in the casting specifica-tions containing these alloys.5. Chemical Composition5.1 The casting material shall conform to the chemicalrequirements of the casting product specification involved.5.2 These

20、 composition limits do not preclude the presenceof other elements. Limits may be established and analysisrequired for unnamed elements by agreement between themanufacturer and the purchaser.6. Mechanical Property Requirements6.1 When tension testing is required by the casting productspecification, t

21、he results shall conform to the requirements ofthat specification, when tested in accordance with Test Meth-ods E8/E8M.6.2 When Brinell Hardness testing is required by the castingproduct specification, the results shall conform to the require-ments of that specification, when tested in accordance wi

22、th theTest Method E10.6.3 When Rockwell Hardness testing is required by thecasting product specification, the results shall conform to therequirements of that specification, when tested in accordancewith the Test Methods E18.7. Other Requirements7.1 Hydrostatic TestWhen specified in the purchase ord

23、er,a hydrostatic test shall be performed on the castings. Thedetails of the test and acceptance criteria shall be established byagreement between the manufacturer and the purchaser.7.2 SoundnessWhen specified in the purchase order, cast-ings shall meet soundness requirements furnished or referencedb

24、y the purchaser. In the absence of standards for soundness, therequirement shall be as agreed upon between the manufacturerand the purchaser.7.3 When Electrical Resistivity testing is required by thecasting product specification, the results shall conform to therequirements of that specification, wh

25、en tested in accordancewith the Test Method B193.8. Dimensions, Mass, and Permissible Variations8.1 The manufacturer shall be responsible for conforming tothe dimensional requirements of the castings as related to thedrawing when the pattern equipment is produced by themanufacturer.8.2 When the patt

26、ern equipment is provided by thepurchaser, the manufacturer shall be responsible for conform-ing to the dimensional requirements of the castings, but withany mutually agreed to exceptions relating to the providedpattern equipment.8.3 Where thick and thin sections of the casting adjoin, themanufactur

27、er shall be permitted to add fillets of adequate size,where not previously provided, subject to approval of thepurchaser.9. Workmanship, Finish, and Appearance9.1 The surface of the casting shall be free of adhering sand,cracks, and hot tears. Other surface discontinuities shall meetvisual acceptanc

28、e standards agreed upon between the manu-facturer and the purchaser.10. Sampling10.1 Lot SizeA lot shall consist of: (1) all of the metalpoured from a single furnace or crucible melt, or (2) all themetal poured from two or more furnaces into a single ladle, or(3) all of the metal poured from a conti

29、nuous melting furnacebetween charges, or (4) all of the metal poured from anindividual melting furnace or group of melting furnaces havinga uniform melting stock, operating during the course ofone-half shift, not to exceed 5 h.10.2 Chemical Analysis:10.2.1 The sample for chemical analysis shall be t

30、aken inaccordance with Practice E255 for product in the final formfrom the pieces selected in 10.1 and combined into onecomposite sample. The minimum weight of the compositesample shall be 150 g.10.2.2 Instead of sampling as directed in 10.2.1, the manu-facturer shall have the option of sampling at

31、the time castingsare poured or from the semifinished product. When samples aretaken during the course of manufacture, sampling of thefinished product by the manufacturer is not required. Thenumber of samples taken for the determination of compositionshall be as follows:5Available from Japanese Stand

32、ards Association (JSA), Mita MT Bldg., 3-13-12Mita, Minato-ku, Tokyo 108-0073, Japan, http:/www.jsa.or.jp.B824 16210.2.2.1 When samples are taken at the time the castings arepoured, at least one sample shall be taken for each group ofcastings poured from the same source of molten metal.10.3 Tension-

33、test bars used in meeting the requirements of6.1 shall be separately cast for the sand, permanent mold, andcentrifugal casting processes. The results represent the proper-ties of the metal going into castings poured from the same heat.The mechanical properties may not be the same as theproperties of

34、 the corresponding castings because of the solidi-fication effects of varying size, section, and design. Test barsfor continuous castings are taken from the castings andtherefore represent the properties of the casting.10.3.1 When the requirements of 6.1 have been compliedwith using separately cast

35、test bars, additional tests may beperformed using test bars removed from the casting with testbar location and mechanical properties agreed upon betweenthe manufacturer and the purchaser. It should be noted that theminimum requirements, listed in applicable specifications,were obtained using data fr

36、om separately cast coupons. Testspecimens machined from castings may not achieve theseresults.11. Number of Tests and Retests11.1 Tests:11.1.1 A chemical analysis of each element with a specifiedlimiting value shall be made on each lot. Chemical analysis forresidual elements is not required unless s

37、pecified in thepurchase order.11.1.2 One tension test shall be performed on each lot.11.1.3 Should the percent elongation of any tensile-testspecimen be less than that specified and any part of the fractureis outside the middle two-thirds of the gage length or in apunched or scribed mark within the

38、reduced section, thespecimen may be discarded and replaced by another from thesame lot.11.1.4 If the result of any test fails to conform to thespecified requirements, two retests shall be performed. If eitherretest fails to meet the specified requirements, the lot shall berejected.11.1.5 Should any

39、of the properties be less than thatspecified and there is a discontinuity in the cross-sectional areaof the fracture, the specimen may be discarded and replaced byanother of the same lot.11.2 Retests:11.2.1 When requested by the manufacturer, a retest shall bepermitted when test results obtained by

40、the purchaser fail toconform to the casting specification requirements.11.2.2 Retesting shall be as prescribed in the casting speci-fication for the initial test, except the number of test specimensshall be twice that normally required for the test. Test resultsfor all specimens shall comply with th

41、e casting specificationrequirements. Failure to comply shall be cause for rejection.11.2.3 Chemical AnalysisIf one or more of the elementswith specified limits fail to meet the compositional requirementof the product specification when determined from the sampleprepared in accordance with Practice E

42、255, one retest cycleshall be permitted with a second composite sample prepared inaccordance with Practice E255.12. Specimen Preparation12.1 The specimen for chemical analysis shall be takenfrom the lot in such a manner as to avoid contamination and berepresentative of the molten metal. Sample prepa

43、ration shall bein accordance with Practice E255. Analytical specimen prepa-ration shall be the responsibility of the reporting laboratory.12.2 Tension-test specimens shall be prepared in accordancewith Practice B208.12.2.1 If any specimen is machined improperly or if flawsare revealed by machining o

44、r during testing, the specimen shallbe discarded and replaced by another from the same lot.13. Test Methods13.1 Chemical Composition:13.1.1 The chemical analysis methods used for the routinedetermination of specification compliance and preparation oftest reports shall be at the discretion of the lab

45、oratory perform-ing the analysis.13.1.2 In case of disagreement on chemical composition,referee analytical methods for copper alloys other than copper-beryllium alloys (Specification B770) are given in Table 1.Referee analytical methods for copper-beryllium alloys aregiven in the Annex of Specificat

46、ion B194.13.1.3 The determination of magnesium, niobium,zirconium, and titanium, for which no recognized test methodis known to be published, shall be subject to agreementbetween the manufacturer and the purchaser.13.1.4 Analytical methods for elements with ranges beyondthose given in Table 1 shall

47、be subject to agreement betweenthe manufacturer and the purchaser.13.1.5 Analytical methods for the determination of elementsrequired by the purchase order agreement shall be as agreedupon between the manufacturer and the purchaser.TABLE 1 Referee Chemical Analytical MethodsElement Range or % max Te

48、st MethodsAluminum (Al) 0.00513.5 E478Antimony (Sb) 0.05-0.70 E62Arsenic (As) 0.0-0.50 E62Bismuth (Bi) 0.16 JIS H 1068Carbon (C) 0.0-0.50 E76Copper (Cu) 50.0-99.75 E478Iron (Fe) 0.003-1.250.0-5.0E478E54Lead (Pb) 0.002-15.02.0-30.0E478;Atomic AbsorptionE478; TitrimetricManganese (Mn) 0.10-12.012.0-23

49、.0E62E581Nickel (Ni)(incl Cobalt (Co)0.0-5.0 E478; PhotometricPhosphorus (P) 0.01-1.0 E62Silicon (Si) 0.005-5.50 E54;Perchloric AcidDehydrationSulfur (S) 0.05-0.08 E76:Direct CombustionTin (Sn) 0.01-1.00.50-20.0E478; PhotometricE478; TitrimetricZinc (Zn) 0.02-2.02.0-40.0E478;Atomic AbsorptionE478; TitrimetricB824 16313.2 Mechanical Properties:13.2.1 Tension testing shall be performed in accordancewith Test Methods E8/E8M.14. Significance of Numerical Limits14.1 For the purpose of determining compliance with thespecified limits for requirements of the properties listed i