ASTM A915 A915M-1993(2003) Standard Specification for Steel Castings Carbon and Alloy Chemical Requirements Similar to Standard Wrought Grades.pdf
《ASTM A915 A915M-1993(2003) Standard Specification for Steel Castings Carbon and Alloy Chemical Requirements Similar to Standard Wrought Grades.pdf》由会员分享,可在线阅读,更多相关《ASTM A915 A915M-1993(2003) Standard Specification for Steel Castings Carbon and Alloy Chemical Requirements Similar to Standard Wrought Grades.pdf(3页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: A 915/A 915M 93 (Reapproved 2003)Standard Specification forSteel Castings, Carbon, and Alloy, Chemical RequirementsSimilar to Standard Wrought Grades1This standard is issued under the fixed designation A 915/A 915M; the number immediately following the designation indicates the yearof o
2、riginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers carbon and low alloy steelcasting
3、s having chemical analyses similar to that of thestandard wrought grades.1.2 Several grades are covered and are designated bychemical composition shown in Table 1.1.3 The values stated in either inch-pound units or SI unitsare to be regarded separately as standard. Within the text, theSI units are s
4、hown in brackets. The values stated in eachsystem are not exact equivalents; therefore, each system mustbe used independently of the other. Combining values from thetwo systems may result in nonconformance with the specifi-cation. Inch-pound units are applicable for material ordered toSpecification
5、A 915 and SI units for material ordered toSpecification A 915M.2. Referenced Documents2.1 ASTM Standards:A 370 Test Methods and Definitions for Mechanical Testingof Steel Products2A 781/A 781M Specification for Castings, Steel and Alloy,Common Requirements, for General Industrial Use33. Ordering Inf
6、ormation3.1 Orders for material under this specification shouldinclude the following information:3.1.1 Quantity,3.1.2 Specification, including year, date, and grade,3.1.3 Description of the casting by pattern number ordrawing. Dimensional tolerances shall be included on thecasting drawing,3.1.4 Opti
7、ons in the specification, and3.1.5 Supplementary requirements desired, including stan-dards of acceptance.4. Heat Treatment4.1 Grades SC 1020 and SC 1025 may be supplied unheattreated or heat treated as described in 4.2.4.2 Castings shall be heat treated either by full annealing,normalizing, normali
8、zing and tempering, or quenching andtempering. Unless otherwise specified in the inquiry, contract,or order, the castings may be heat treated by any of these heattreatments or combination of these heat treatments at the optionof the manufacturer.4.3 Heat treatment shall be performed after the castin
9、gshave been allowed to cool below the transformation range.4.4 The furnace temperature for heat treating shall beeffectively controlled by the use of recording-type pyrometers.5. Chemical Composition5.1 The steel shall conform to the requirements of chemicalcomposition as prescribed in Table 1.5.2 T
10、he product analysis tolerances given in SpecificationA 781/A 781M shall apply to all product analysis performed oncastings supplied to this specification.6. General Conditions for Delivery6.1 Material furnished to this specification shall conform tothe applicable requirements of Specification A 781/
11、A 781M,including the supplementary requirements indicated on thepurchasers order.7. Repair by Welding7.1 Weld repairs shall be inspected to the same qualitystandards used to inspect the castings. When castings areproduced with Supplementary Requirement S1 specified, weldrepairs shall be inspected by
12、 magnetic particle examination tothe same standards used to inspect the castings. When castingsare produced with Supplementary Requirement S2specified,weld repairs in which the depth of the cavity prepared forrepair welding exceeds 20 % of the wall thickness or 1 in. 25mm, whichever is smaller, or i
13、n which the cavity prepared forwelding is greater than approximately 10 in.265 cm2, shall beradiographed to the same standards used to inspect the cast-ings.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel, and Related Alloys and is the direct responsibili
14、ty of SubcommitteeA01.18 on Castings.Current edition approved April 10, 2003. Published April 2003. Originallyapproved in 1993. Last previous edition approved in 1998 as A 915/A 915M 93(1998).2Annual Book of ASTM Standards, Vol 01.03.3Annual Book of ASTM Standards, Vol 01.02.1Copyright ASTM Internat
15、ional, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.7.2 Weld repairs shall be considered major when the depthof the cavity prepared for welding exceeds 20 % of the wallthickness or 1 in. 25 mm, whichever is smaller, or when theextent of the cavity exceeds 10 in
16、.265 cm2. Castingsproduced from Grades SC 1020, SC 1025, or SC 1030 whichcontain major weld repairs shall receive a postweld heattreatment. Castings produced from any of the other grades shallreceive a postweld heat treatment regardless of weld repairsize. Postweld heat treatment shall consist of a
17、thermal stressrelief or a complete reheat treatment. The postweld heattreatment shall be in accordance with the qualified weldprocedure used.8. Rejection and Rehearing8.1 Subsequent to acceptance at the manufacturers works,material which is found to be unacceptable as determined byrequirements speci
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMA915A915M19932003STANDARDSPECIFICATIONFORSTEELCASTINGSCARBONANDALLOYCHEMICALREQUIREMENTSSIMILARTOSTANDARDWROUGHTGRADESPDF

链接地址:http://www.mydoc123.com/p-459955.html