ASTM C1437-2013 Standard Test Method for Flow of Hydraulic Cement Mortar《水硬水泥灰浆流动性的标准试验方法》.pdf

《ASTM C1437-2013 Standard Test Method for Flow of Hydraulic Cement Mortar《水硬水泥灰浆流动性的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM C1437-2013 Standard Test Method for Flow of Hydraulic Cement Mortar《水硬水泥灰浆流动性的标准试验方法》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C1437 13Standard Test Method forFlow of Hydraulic Cement Mortar1This standard is issued under the fixed designation C1437; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parenthe

2、ses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This test method covers the determination of flow ofhydraulic cement mortars.1.2 The values stated in SI units are to be regarded as thestandard. Values

3、 in parentheses are for information only.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory

4、 limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2C109/C109M Test Method for Compressive Strength ofHydraulic Cement Mortars (Using 2-in. or 50-mm CubeSpecimens)C185 Test Method for Air Content of Hydraulic CementMortarC230/C230M Specification for Flow Table for Use in Testsof Hyd

5、raulic CementC511 Specification for Mixing Rooms, Moist Cabinets,Moist Rooms, and Water Storage Tanks Used in theTesting of Hydraulic Cements and Concretes3. Significance and Use3.1 This test method is intended to be used to determine theflow of hydraulic cement mortars, and of mortars containingcem

6、entitious materials other than hydraulic cements.3.2 While flow is not usually included in hydraulic cementspecifications, it is commonly used in standard tests thatrequire the mortar to have a water content that provides aspecified flow level.4. Apparatus4.1 Flow Table, Flow Mold, Conforming to the

7、 require-ments of Specification C230/C230M.4.2 Caliper, Conforming to the requirements of Specifica-tion C230/C230M. Alternatively, any outside-measuring cali-per constructed of corrosion-resistant material may be used,provided that it is incremented in millimetres and its maximumextent of measuring

8、 is at least 260 mm (1014 in.).4.3 Tamper, conforming to the requirements of Test MethodC109/C109M.4.4 Trowel, having a steel blade 100 to 150 mm (4 to 6 in.)in length, with straight edges. The edges when placed on aplane surface shall not depart from straightness by more than 1mm (0.04 in.) (Note 1

9、).4.5 Straightedge, made of steel, shall be at least 200 mm (8in.) long and not less than 1.5 mm (0.06 in.) nor more than 3.5mm (0.14 in.) in thickness. Its edge shall not depart from aplane surface by more than 1 mm (0.04-in.) (Note 1).NOTE 1The trowel specified in Test Method C109/C109M and thestr

10、aightedge specified in Test Method C185 may be used for this purpose,providing they comply with the planeness indicated.5. Temperature and Humidity5.1 The temperature and relative humidity of the air in themixing room shall be as prescribed in Specification C511.6. Materials6.1 Hydraulic Cement Mort

11、arA mortar for which thedetermination of flow is specified or desired.7. Procedure7.1 Determination of Flow:7.1.1 Carefully wipe the flow table clean and dry, and placethe flow mold at the center. Place a layer of mortar about 25mm (1 in.) in thickness in the mold and tamp 20 times with thetamper. T

12、he tamping pressure shall be just sufficient to ensureuniform filling of the mold. Tamping should be uniformlydistributed over the cross section of each layer. For the bottomlayer this will necessitate inclining the tamper slightly whentamping near the perimeter. Then fill the mold with mortar andta

13、mp as specified for the first layer. Cut off the mortar to a planesurface flush with the top of the mold by drawing the1This test method is under the jurisdiction of ASTM Committee C01 on Cementand is the direct responsibility of Subcommittee C01.22 on Workability.Current edition June 15, 2013. Publ

14、ished August 2013. Originally approved in1999. Last previous edition approved in 2007 as C1437 - 07. DOI: 10.1520/C1437-13.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, re

15、fer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1straightedge or the edge of the trowel with a sawing motion

16、across the top of the mold. Wipe the table top clean and dry,being especially careful to remove any water from around theedge of the flow mold. Lift the mold away from the mortar 1min after completing the mixing operation. Immediately dropthe table 25 times in 15 s, unless otherwise specified.7.1.2

17、If using the caliper specified in Specification C230/C230M, measure the diameter of the mortar along the fourlines scribed in the table top, recording each diameter as thenumber of caliper divisions, estimated to one tenth of adivision. If some other caliper is being used, measure thediameter of the

18、 mortar along the four lines scribed in the tabletop, recording each diameter to the nearest millimetre.8. Calculation8.1 The flow is the resulting increase in average basediameter of the mortar mass, expressed as a percentage of theoriginal base diameter.8.2 If using the caliper specified in Specif

19、ication C230/C230M, add the four readings, and record the total. This givesthe flow in percent.8.2.1 If using some other caliper, compute the flow inpercent by dividing “A” by the original inside base diameter inmillimetres and multiplying by 100.where:A = average of four readings in millimetres, mi

20、nus theoriginal inside base diameter in millimetres.9. Report9.1 Report the flow to the nearest 1 %.10. Precision and Bias10.1 PrecisionThe single-operator, within-laboratorystandard deviation has been found to be 4 % flow. Therefore,results of two properly conducted tests by the same operator onsim

21、ilar batches should not differ by more than 11 % (Note 2).10.1.1 The multilaboratory standard deviation has beenfound to be 11 %. Therefore, results of two different laborato-ries on similar batches should not differ by more than 31 %flow (Note 2).NOTE 2Data produced when water content is being vari

22、ed to obtain agiven flow is not applicable for this purpose. Only data where flow hasbeen determined using a given cement and fixed water content isapplicable. Consequently, the only data currently available is that ex-tracted from the CCRL Proficiency Sample Program for CS Flow onC109/C109M mortars

23、 (dropping the flow table 25 times in 15 s). The datafor Sample Nos. 109, 110, 111, and 112 have been used to develop theprecision statements given.10.2 BiasSince there is no accepted reference materialsuitable for determining flow available, no statement on bias ismade.11. Keywords11.1 flow; hydrau

24、lic cement; mortarSUMMARY OF CHANGESCommittee C01 has identified the location of selected changes to this test method since the last issue,C1437 07, that may impact the use of this test method. (Approved June 15, 2013)(1) Revised 7.1.1 for clarification.(2) Separated 8.2 for clarification by adding

25、8.2.1.(3) Moved reporting information previously in 8.2 to newSection 9.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of

26、 any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments ar

27、e invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not rec

28、eived a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies)

29、of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).C1437 132