ASTM A392-2011 Standard Specification for Zinc-Coated Steel Chain-Link Fence Fabric《镀锌钢链节栅栏结构的标准规格》.pdf

《ASTM A392-2011 Standard Specification for Zinc-Coated Steel Chain-Link Fence Fabric《镀锌钢链节栅栏结构的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A392-2011 Standard Specification for Zinc-Coated Steel Chain-Link Fence Fabric《镀锌钢链节栅栏结构的标准规格》.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、Designation:A39207 Designation: A392 11Standard Specification forZinc-Coated Steel Chain-Link Fence Fabric1This standard is issued under the fixed designation A392; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last r

2、evision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers zinc-coated steel chain-link fence fabric, zinc coated either before or after weaving.1.2The value

3、s stated in inch-pound units are to be regarded as the standard.1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not considered standard.2. Referenced Docum

4、ents2.1 ASTM Standards:2A90/A90M Test Method for Weight Mass of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy CoatingsA370 Test Methods and Definitions for Mechanical Testing of Steel ProductsA700 Practices for Packaging, Marking, and Loading Methods for Steel Products for ShipmentA817

5、Specification for Metallic-Coated Steel Wire for Chain-Link Fence Fabric and Marcelled Tension WireB6 Specification for Zinc2.2 Federal Standard:Fed. Std. No. 123 Marking for Shipments (Civil Agencies)32.3 Military Standards:MIL-STD-129 Marking for Shipment and Storage3MIL-STD 163 Steel Mill Product

6、s, Preparation for Shipment and Storage33. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 chain-link fence fabrica fencing material made from steel wire helically wound and interwoven in such a manner as toprovide a continuous mesh without knots or ties except in the form of knu

7、ckling or of twisting the ends of the wires to form theselvage of the fabric. Variations to knuckled or twisted selvages are permissible.3.1.2 diamond countthe number of diamond openings from one edge of the fabric to the other. The diamond count of a givenfabric shall begin at the first completed d

8、iamond at one edge and continue to the unfinished (12) or full opening at the other edge.3.1.3 knucklingthe type of selvage obtained by interlocking adjacent pairs of wire ends and then bending the wire ends backinto a loop. The loop shall be closed or nearly closed to a measurement less than the di

9、ameter of the wire.3.1.4 twistingthe type of selvage obtained by twisting adjacent pairs of wire ends together in a close helix of 112 machineturns, which is equivalent to 3 full twists, and cutting the wire ends at an angle. The wire ends beyond the twist shall be at least14 in. 6.4 mm(6.4 mm) long

10、. This type of selvage is not used on fabric with a mesh size of less than 2 in. 50.8 mm. (50.8 mm).4. Ordering Information4.1 Orders for chain-link fence fabric purchased to this specification shall include the following information:4.1.1 Quantity (Section 14),4.1.2 Zinc coated after weaving or bef

11、ore weaving (Section 5),4.1.3 Size of mesh (Section 7),4.1.4 Size of wire (Section 8),4.1.5 Height of fabric (Section 9),1This specification is under the jurisdiction of ASTM Committee F14 on Fences and is the direct responsibility of Subcommittee F14.40 on Chain Link Fence and WireAccessories.Curre

12、nt edition approved JulyFeb. 1, 2007.2011. Published July 2007.March 2011. Originally approved in 1955. Last previous edition approved in 20062007 asA392 - 067. DOI: 10.1520/A0392-07.10.1520/A0392-11.2For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Servi

13、ce at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.3Available from Standardization Documents Order Desk, Bldg. 4 Section D, 700 Robbins Ave., Philadelphia, PA 19111-5094, Attn: NPODS.1This document is not an AS

14、TM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In a

15、ll cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.1.6 Diamond count, if specified (Section 6),4.1.7 Type of selvage (Secti

16、on 10),4.1.8 Class of coating (Section 11),4.1.9 ASTM designation and year of issue, and4.1.10 Certification if required (Section 17).4.2 All rolls of fencing accepted by the purchaser shall be billed on the basis of the original footage of the rolls before sampling,unless changed by contractual arr

17、angement.NOTE 1Atypical ordering description is as follows: 25 rolls, 50 ft each, chain-link fence fabric, zinc coated after weaving, 2-in. mesh, 0.148-in. wire,60 in. high, knuckled both selvages, Class 2 coating to ASTM A392 - XX.5. Materials5.1 If zinc-coated before weaving, the wire from which t

18、he fabric is woven shall conform to all requirements of SpecificationA817 for Type II coating, in the class of coating specified (Class 4 or Class 5).5.2 If zinc-coated after weaving, the base metal shall be steel of such quality and purity that, when drawn to the size of wirespecified and coated wi

19、th zinc after fabrication, the finished fencing shall be of uniform quality and have the properties andcharacteristics as prescribed in this specification.5.3 Zinc for CoatingThe slab zinc, when used for the coating, shall be any grade of zinc conforming to Specification B6.6. Weave6.1 The wire shal

20、l be woven throughout in the form of approximately uniform square mesh, having parallel sides and horizontaland vertical diagonals of approximately uniform dimensions. The top and bottom of the fabric shall be knuckled or twisted asspecified in Section 10.6.2 A typical diamond count for each standar

21、d height is shown in Table 1. Other diamond counts are permissible provided thatthey are consistent within a lot. The purchaser has the option to specify the diamond count (see 4.1.6).7. Size of Mesh7.1 The size of mesh shall be as indicated in Table 4.7.2 The permissible variation from the specifie

22、d size of mesh shall be 618 in. 3.2 mm(3.2 mm) for all mesh sizes larger than114 in. 31.75 mm,(31.75 mm), and 6116 in. 61.6 mm(61.6 mm) for all mesh sizes 114 in. 31.75 mm(31.75 mm) and smaller.7.3 The size of mesh shall be determined by measuring the minimum clear distance between the wires forming

23、 the parallel sidesof the mesh, and determined as the average of two readings taken at right angles to each other.8. Size of Wire8.1 Chain-link fabric shall be fabricated from wire diameters as listed in Specification A817, with a permissible variation fromthe specified diameter of the coated wire o

24、f 60.005 in. 60.13 mm. (60.13 mm).9. Height of Fabric9.1 Chain-link fabric shall be furnished in the standard heights shown in Table 4. Custom order fabric is available in heightsto and including 20 ft. 6.10 m.(6.10 m). The height of fabric shall be the overall dimension from ends of twists or knuck

25、les.Permissible variation from the specified height shall be 61 in. 625 mm(625 mm) for standard selvage on fabric with mesh sizes1 in. 25.4 mm(25.4 mm) and over 612 in. 613 mm(613 mm) for all fabric with mesh sizes less than 1 in. 25.4 mm. (25.4mm).TABLE 1 Typical Diamond CountANOTE 1Other diamond c

26、ounts are permitted (see 6.2).NOTE 2 For fabric heights over 144 in., see 6.2.NOTE 3Variations to knuckled or twisted selvage may affect diamond count (see 6.2).NominalDiameterCoatedWire, in.Size ofMesh,in.Height of Fence Fabric, in.36 42 48 60 72 84 96 108 120 1440.192 2 1012 1212 1312 1712 2012 24

27、12 2712 3112 3412 41120.148 2 1012 1212 1312 1712 2012 2412 2712 3112 3412 41120.148 114 . . . . . . 23 29 35 41 46 52 58 700.148 1 20 23 27 33 39 45 53 61 67 790.120 2 1012 1212 1412 1712 2012 2412 . . . .0.120 134 . . . . . . 3112 3512 3912 47120.120 1 20 23 27 33 39 45 53 61 67 790.113 218 912 11

28、12 1312 1612 1912 . . . . .ASee Appendix X1 for metric equivalents and Fig. 1 for mesh sizes less than 1 in. (25.4 mm).A392 11210. Selvage10.1 Unless otherwise specified by the purchaser, fabrics with 2 or 218 in. 50(50 or 54 mmmm) mesh, in heights 60 in. 1520mm(1520 mm) and under shall be knuckled

29、at both selvages. Fabric 72 in. 1830 mm(1830 mm) high and over shall be knuckledat one selvage and twisted at the other. (WarningTwisted selvages for fence fabric under 72 in. 1830 mm(1830 mm) in heightare not recommended because of consumer safety considerations.)10.2 The selvages of fabrics with m

30、eshes of less than 2 in. 50 mm(50 mm) shall be knuckled.11. Weight of Zinc Coating11.1 The weight of zinc coating on the fabric may be ordered in two coating weight classes as follows:TABLE 2 Available Mesh Sizes and Zinc Coating WeightsASpecified Diameter of Coated Wire, in. mm Mesh Sizes with a Cl

31、ass 12.00 oz/ft2(610) coating, in.Mesh Sizes with a Class 21.20 oz/ft2(366) coating, in.Specified Diameter of Coated Wire, in. (mm) Mesh Sizes with a Class 12.00 oz/ft2(610) coating, in.Mesh Sizes with a Class 21.20 oz/ft2(366) coating, in.0.192 4.88 134 and 2 20.192 (4.88) 134 and 2 20.148 3.7612 ,

32、58 ,1,114 ,134 , and 2 134 and 20.148 (3.76)12 ,58 ,1,114 ,134 , and 2 134 and 20.120 3.0538 ,12 ,58 ,1,114 ,134 , and 2 .0.120 (3.05)38 ,12 ,58 ,1,114 ,134 , and 2 .0.113 2.87 218 .0.113 (2.87) 218 .AMesh sizes of 114 in. or smaller are typically produced with Galvanized before Weave product.TABLE

33、3 Breaking StrengthSpecified Diameter ofCoated Wire, in. mmBreaking Strength,min, lbf NSpecified Diameter ofCoated Wire, in. (mm)Breaking Strength,min, lbf (N)0.192 4.88 2170 96500.192 (4.88) 2170 (9650)0.148 3.76 1290 57400.148 (3.76) 1290 (5740)0.135 3.43 1290 57400.135 (3.43) 1290 (5740)0.120 3.0

34、5 850 37800.120 (3.05) 850 (3780)0.113 2.87 750 33400.113 (2.87) 750 (3340)TABLE 4 Sizes of Wire and MeshANOTE 1 For fabrics heights over 144 in., see 9.1.SpecifiedDiameterofCoatedWire, in.Size,CoatedWireGaugeSize ofMesh,in.BHeight of Fence Fabric, in.0.192 6 2 36 42 48 60 72 84 96 108 120 1440.148

35、9 2 36 42 48 60 72 84 96 108 120 1440.148 9 114C. . . . . . 23 29 35 41 46 52 58 700.148 9 1 36 42 48 60 72 84 96 108 120 1440.148 912 36 42 48 60 72 84 96 108 120 1440.120 11 2 36 42 48 60 72 84 . . . .0.120 11 134 . . . . . . 96 108 120 1440.120 11 114C. . . . . . 48 60 72 84 96 108 120 1440.120 1

36、1 1 36 42 48 60 72 84 96 108 120 1440.120 1138D36 42 48 60 72 84 96 108 120 1440.120 1112D36 42 48 60 72 84 96 108 120 1440.120 1158 36 42 48 60 72 84 96 108 120 1440.113 1112 218 36 42 48 60 72 . . . . .ASee Appendix X1 for metric equivalents.BSee Fig. 1 for mesh dimensions for58 in.,12 in., and38

37、in. fence fabric. Thesesizes are typically used for high security requirements.CThis mesh and smaller is recommended for swimming pools.DThese sizes are designed for security purposes.A392 11311.1.1 Class 1The weight of zinc coating shall not be less than 1.2 oz/ft2366 g/m(366 g/m2) of uncoated wire

38、 surface asdetermined from the average of two or more specimens, and not less than 1.08 oz/ft2330 g/m(330 g/m2) of uncoated wire surfacefor any individual specimen.11.1.2 Class 2The weight of zinc coating shall not be less than 2 oz/ft2610 g/m(610 g/m2) of uncoated wire surface asdetermined from the

39、 average of two or more specimens, and not less than 1.8 oz/ft2500 g/m(500 g/m2) of uncoated wire surfacefor any individual specimen.NOTE 2Fabric galvanized after fabrication is normally not produced with a Class 2 coating on 0.120-in. 3.05-mm(3.05-mm) or 0.113-in.2.87-mm(2.87-mm) wire or with mesh

40、sizes smaller than 2 inches.11.2 On fabric galvanized after weaving, the weight of coating shall be determined on one or more pieces of wire removed fromthe fabric. These specimens may be of any length over 12 in. 300 mm(300 mm) and shall include both bends and straight sections,but shall not includ

41、e either twists or knuckles.11.3 The weight of coating shall be determined in accordance with Test Method A90/A90M.12. Breaking Strength12.1 Wire constituting the fabric shall meet the minimum breaking strength listed in the Breaking Strength table of SpecificationA817 when tested in accordance with

42、 Test Methods and DefinitionsA370. Specimens to establish conformance to this requirementshall consist of individual pickets from a section of the fence fabric. The specimens shall be of sufficient length so as to be firmlygripped in the testing machine after straightening. The actual gage length (d

43、istance between jaws) of the specimen shall be limitedto the undeformed length of wire between the two adjacent straightened bends.13. Workmanship13.1Chain-link fence fabric shall be produced by methods recognized as good commercial practices. The zinc coating ongalvanized-after-weaving fabric shall

44、 be applied in a continuous process and shall not be applied to the fabric in roll form.13.2Excessive roughness, blisters, sal ammoniac spots, bruises, and flaking shall be noted. These and other defects, if presentto any considerable extent, shall provide a basis for rejection.13.1 Chain-link fence

45、 fabric shall be produced by methods recognized as good commercial practices. The zinc coating ongalvanized-after-weaving fabric shall be applied in a continuous process and shall not be applied to the fabric in roll form. Thegalvanized before-weaving fabric shall be woven using proven industry proc

46、edures to ensure a smooth consistent surface withoutpenetrating to the substrate, except at the selvage cut ends, see Note 3.13.2 Excessive roughness, blisters, sal ammoniac spots, bruises, flaking, and white rust shall be noted. The Galvanized AfterWeaving (GAW) process shall include the use of app

47、ropriate apparatus for producing galvanized fabric so as to prevent excessmaterial in the elbow joints that form the diamond mesh. The finished product shall exhibit free independent motion of overlappingwires that form the diamond mesh when in a free or installed state of tension. Any of the above

48、described defects listed in 13.1and 13.2 that will compromise the function of the product shall provide a basis for rejection.NOTE 3On fabric that is zinc-coated before weaving, rust formations on the cut ends of the wire at the fabric selvages are inherent characteristicsof this material and do not

49、 warrant rejection of the fabric.14. Standard Length of Rolls14.1 The standard length of roll shall be 50 ft 15.24 m(15.24 m) 6 1 % except as otherwise agreed upon at the time ofpurchase.14.2 The length of roll shall be determined by unrolling a roll of fabric on a flat surface and exerting tension by appropriatemeans to remove all slack. The tension applied shall not reduce the actual height of t