《ASTM C990M-2006 Standard Specification for Joints for Concrete Pipe Manholes and Precast Box Sections Using Preformed Flexible Joint Sealants (Metric)《使用预制柔性接头缝密封件的混凝土管道、人孔和预制箱型部件用.pdf》由会员分享，可在线阅读，更多相关《ASTM C990M-2006 Standard Specification for Joints for Concrete Pipe Manholes and Precast Box Sections Using Preformed Flexible Joint Sealants (Metric)《使用预制柔性接头缝密封件的混凝土管道、人孔和预制箱型部件用.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C 990M 06METRICStandard Specification forJoints for Concrete Pipe, Manholes, and Precast BoxSections Using Preformed Flexible Joint Sealants Metric1This standard is issued under the fixed designation C 990M; the number immediately following the designation indicates the year oforiginal

2、adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers joints for precast concrete pipeand box a

3、nd other sections using preformed flexible jointsealants for use in storm sewers and culverts which are notintended to operate under internal pressure, or are not subjectto infiltration or exfiltration limits. Joint material used inhorizontal applications is intended to prevent the flow of solidsthr

4、ough the joint.1.2 Precast concrete manhole sections and other verticalstructures that are subject to internal or external pressure,infiltration, or exfiltration limits are not prohibited from beingspecified. Joints in vertical structures covered by this specifi-cation are intended mainly to prevent

5、 the flow of solids orfluids through the joint.1.3 This specification is to be used with pipe and structuresconforming in all respects to Specifications C 14M, C 76M,C 478M, C 506M, C 507M, C 655M, C 985M, C 1504, andC 1433M, provided that if there is a conflict in permissiblevariations in dimension

6、s, the requirements of this specificationshall govern.1.4 This specification is the metric companion of Specifica-tion C 990.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish app

7、ro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.NOTE 1This specification covers the material and performance of thejoint and sealant only. Infiltration and exfiltration quantities for installedsections are dependent on factors other than

8、the joints which must becovered by other specifications and suitable testing of the installedpipeline.2. Referenced Documents2.1 ASTM Standards:2C 14M Specification for Nonreinforced Concrete Sewer,Storm Drain, and Culvert Pipe MetricC 76M Specification for Reinforced Concrete Culvert,Storm Drain, a

9、nd Sewer Pipe MetricC 478M Specification for Precast Reinforced ConcreteManhole Sections MetricC 506M Specification for Reinforced Concrete Arch Cul-vert, Storm Drain, and Sewer Pipe MetricC 507M Specification for Reinforced Concrete EllipticalCulvert, Storm Drain, and Sewer Pipe MetricC 655M Specif

10、ication for Reinforced Concrete D-LoadCulvert, Storm Drain, and Sewer Pipe MetricC 822 Terminology Relating to Concrete Pipe and RelatedProductsC 972 Test Method for Compression-Recovery of TapeSealantC 985M Specification for Nonreinforced Concrete Speci-fied Strength Culvert, Storm Drain, and Sewer

11、 Pipe Met-ricC 1433M Specification for Precast Reinforced ConcreteBox Sections for Culverts, Storm Drains, and SewersMetricC 1504 Specification for Manufacture of Precast ReinforcedConcrete Three-Sided Structures for Culverts and StormDrainsD4 Test Method for Bitumen ContentD6 Test Method for Loss o

12、n Heating of Oil and AsphalticCompoundsD36 Test Method for Softening Point of Bitumen (Ring-and-Ball Apparatus)D71 Test Method for Relative Density of Solid Pitch and1This specification is under the jurisdiction of ASTM Committee C13 onConcrete Pipe and is the direct responsibility of Subcommittee C

13、13.08 on Joints forPrecast Concrete Structures.Current edition approved Nov. 1, 2006. Published November 2006. Originallyapproved in 1992. Last previous edition approved in 2003 as C 990M 03a.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at ser

14、viceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Asphalt (Displacement Method)D92 Test Method for Flash

15、 and Fire Points by ClevelandOpen Cup TesterD113 Test Method for Ductility of Bituminous MaterialsD 217 Test Methods for Cone Penetration of LubricatingGreaseD 297 Test Methods for Rubber ProductsChemicalAnalysis2.2 AASHTO Standards:3T47 Test for Loss of Heating of Oil and Asphaltic Com-poundsT48 Te

16、st for Flash and Fire Points by Cleveland Open CupT51 Test for Ductility of Bituminous MaterialT111 Test for Inorganic Matter or AshT229 Test for Specific Gravity of Asphalts and Tar PitchesSufficiently Solid to be Handled in Fragments3. Terminology3.1 DefinitionsFor definitions of terms relating to

17、 con-crete pipe, see Terminology C 822.4. Basis of Acceptance4.1 The acceptability of the pipe joint and sealant shall bedetermined by the results of the physical tests prescribed in thisspecification, if and when required, and by inspection todetermine whether the pipe joint and the sealant conform

18、 tothis specification as to design and freedom from defects.5. Materials and Manufacture for Sealants5.1 Bitumen sealants shall be produced from asphalts,hydrocarbon resins and plasticizing compounds reinforcedwith inert mineral filler and shall contain no solvents. Butylrubber sealants shall be pro

19、duced from blends of butyl rubberand refined hydrocarbon resins and plasticizing compoundsreinforced with inert mineral filler and shall contain nosolvents.5.2 Blends of material used in the manufacture of flexiblejoint sealants shall be approved by the owner and meet thecomposition and physical req

20、uirements prescribed in Section 6.The joint sealant shall not depend on oxidizing, evaporating, orchemical action for its adhesive or cohesive strength and shallbe supplied preformed and of suitable cross section and size toseal the joint annular space when the sections are joined. For agiven joint

21、size, the sealing material, as furnished, shall be suchso as to encircle the outside circumference of the spigot ortongue of the joint or the inside circumference of the bell orgroove and shall not be stretched when seated in the joint.Sealant material shall be furnished in the required length andcr

22、oss-sectional dimensions, and the dimensions shall be clearlymarked. Sealant material shall be preformed to the followingspecified tolerances:ToleranceLength, % +5, 0Cross sectional area, % +10, 5Volume (mm3/linear m),% +10, 5Cross-sectional dimensions (mm), % +10, 5*Dimensions in the field may vary

23、 from preformed dimensions6. Physical Requirements for Sealants6.1 Bitumen Sealants:6.1.1 Bitumen sealants shall comply with the followingcomposition and physical requirements. Testing shall be inaccordance with the methods prescribed in Section 9.Hydrocarbon Blends, % by weight 50 minAsh-Inert Mine

24、ral Matter, % by weight 25 minVolatile matter, % by weight 3 maxSpecific gravity at 25C 1.151.40Ductility at 25C, cm 5 minFlash Point, C.O.C. 177C minFire Point, C.O.C., 191C minSoftening Point, 160C minCompression Index at 25C 27 N/cm3Compression Index at 0C 95 N/cm3Cone Penetration at 25C, 150g, 5

25、s, dmm 50120Cone Penetration at 0C, 150g, 5s, dmm 15 minChemical Resistance No deterioration, no cracking,no swelling6.2 Butyl Rubber Sealant:6.2.1 Butyl rubber sealants (elastomeric polymer shall bebutyl rubber only) shall comply with the following composi-tion and physical requirements. Testing sh

26、all be in accordancewith the methods prescribed in Section 9.Butyl Rubber (hydrocarbon blends), % by mass 50 % minAsh-Inert Mineral Matter, % by mass 30 % minVolatile Matter, % by mass 3 % maxSpecific Gravity at 25C 1.15 min1.40 maxDuctility at 25C, cm 5.0 minFlash Point, C.O.C. 177C minFire Point,

27、C.O.C. 191C minCompression Index at 25C 27 N/cm3maxCompression Index at 0C 54 N/cm3maxCone Penetration at 25C, 150 g, 5 s, dmm 50120Cone Penetration at 0C, 150 g, 5 s, dmm 30 minChemical Resistance No deterioration, nocracking, no swelling7. Design of Joints7.1 The pipe manufacturer shall furnish th

28、e owner with thedetailed design of the joint. The sealant manufacturer shallfurnish a complete list of joint sizes showing the minimum sizeof material to be used with each size joint, along with completeinstructions on recommended installation procedures.7.1.1 The joint design shall consist of a bel

29、l or groove onone end of the section and a spigot or tongue on the adjacentend of the joining section.7.1.2 All surfaces of the joint upon or against which thesealant will bear shall be free of spalls, cracks or fractures, andimperfections that would adversely affect the function of thejoint.7.1.3 T

30、he joints of the sections shall be of such design thatthey will withstand the forces caused by the compression of thesealant when joined, without cracking or fracturing whentested, in accordance with Section 10.7.1.4 For horizontal installations, the angle of taper on theconic surfaces of the inside

31、 of the bell or groove and the outersurface of the spigot or tongue where the sealant seats shall be3Available from American Association of State Highway and TransportationOfficials (AASHTO), 444 N. Capitol St., NW, Suite 249, Washington, DC 20001,http:/www.transportation.org.C990M062not more than 1

32、0 measured from the pipe axis. Alternatetapers are permitted if proven adequate by the plant testsspecified in Section 10 and approved by the owner.7.1.5 The annular space measured perpendicular to thesealant bearing surfaces of the assembled and centered jointshall not exceed 12 mm at any point or

33、the maximum specifiedby the sealant manufacturer, whichever is the lesser. The jointdesign shall provide for the deflection of a section by openingone side of the outside perimeter of the joint 12 mm wider thanthe assembled position. Where greater deflections are requiredthan provided by the joint d

34、esign, beveled joints or elbows areacceptable if approved by owner.7.1.6 The sealant shall be the sole element depended upon tomake the joint flexible and meet the test requirements set forthin Section 10. The sealant is not prohibited from beingcomposed of one or more pieces and shall be applied as

35、 acontinuous ring in installation.7.2 Alternative Joint Designs:7.2.1 When agreed upon by the owner, manufacturers arenot prohibited from submitting to the owner, detailed designsfor joints other than those described in 7.1.7.2.2 Design submissions shall include joint dimensions,tolerances, proposed

36、 plant tests, and such other information asrequired by the owner to evaluate the joint design for fieldperformance.7.2.3 Joints of alternative designs shall meet all test require-ments of this specification unless waived by the owner.Alternative joint designs shall be acceptable provided thedesigns

37、are approved by the owner prior to manufacture andprovided the test pipe joints comply with the tests as describedin Section 10.8. Permissible Variations in Dimensions8.1 The planes formed by the ends of nonbeveled pipesections shall not vary from the perpendicular to the longitu-dinal axis by more

38、than 4.5 mm for internal horizontal spans of750 mm and smaller; or by more than 6 mm for internalhorizontal spans of 825 mm to 1350 mm inclusive; or by morethan 9 mm for internal horizontal spans of 1500 mm and larger.9. Test Methods for Sealants9.1 The composition and physical properties of bitumen

39、 orbutyl sealants shall be determined in accordance with thefollowing test methods:9.1.1 Bitumen (hydrocarbon blends)Test Method D4,and Butyl Rubber (hydrocarbon blends)Test Methods D 297.9.1.2 Ash-Inert Mineral MatterAASHTO T111.9.1.3 Volatile Matter Test Method D6or AASHTO T47.9.1.4 Specific Gravi

40、ty Test Method D71 or AASHTOT229.9.1.5 DuctilityTest Method D113or AASHTO T51.9.1.6 Softening Point Test Method D36.9.1.7 Penetration Test Method D 217.9.1.8 Flash Point and Fire PointTest Method D92. Thecup shall be heated by an electric heater or oven.9.1.9 Chemical ResistanceChemical resistance s

41、hall bedetermined by 30-day separate immersion in 5 % solutions atambient room temperature of HCl (hydrochloride acid),H2SO4(sulfuric acid), NaOH (sodium hydroxide), KOH (po-tassium hydroxide), H2S (saturated hydrogen sulfide solution).9.1.10 Compression-Recovery of Tape SealantTestMethod C 972.9.2

42、The sealant manufacturer shall, if required, furnishcertified copies of test reports specified under this specification.10. Performance Requirements for Joints10.1 The sections shall be tested hydrostatically in verticalalignment and a sufficient number of sections shall be as-sembled in straight al

43、ignment to develop a pressure of at least70 kPa for 10 minutes at the test joint. Alternate test methodsare acceptable as long as the designated internal hydrostaticpressure is achieved at the joint. No mortar or concretecoatings, fillings or packing shall be placed prior to watertightness tests. Th

44、ere shall be no visible leakage. Moisture orbeads of water appearing on the joint will not be considered asleakage.10.2 The user of this specification is advised that hydrostatictest is intended only for use as a quality control test, and not asa simulated service test. The 70 kPa pressure criterion

45、 forsections should not be considered an indication of the hydro-static pressure capability of the joint and sealant under installedconditions. Field tests for completed portions of concrete pipeand structures are not covered by this specification, but shall beincluded in the specifications for inst

46、allation.11. Storage11.1 The sealant shall be stored in as cool and as clean aplace as practicable, preferably at a temperature between 10Cand 21C.12. Inspection12.1 The quality of the materials and the joint and sealantshall be subject to inspection and approval by the owner.13. Rejection13.1 Pipe

47、joints and sealants shall be subject to rejectionupon failure to conform to any of the requirements of thisspecification.13.2 Sealants shall be subject to rejection whenever theyshow surface checking, weathering, or other deterioration priorto installation in the work.13.3 Joints that are damaged be

48、cause of carelessness orcontinuing failure to prevent recurrent imperfections in manu-facturing or damage during handling shall be subject torejection.14. Repairs14.1 Spalled areas, manufacturing imperfections, or damageduring handling of a pipe or box or other section that willadversely affect the

49、joint, are not prohibited from beingrepaired. The repairs will be acceptable if, in the opinion of theowner, the repairs are sound, properly finished and cured,provided the length of a single area to be repaired does notexceed 10 % of the total perimeter length, and the length ofseveral areas to be repaired does not exceed 20 % of the totalperimeter length. The finished repair shall conform to therequirements of 7.1.2.At the option of the owner, the pipe jointC990M063that has been repaired shall be subjected to the designate