ASTM B599-1992(2014) Standard Specification for Nickel-Iron-Chromium-Molybdenum-Columbium Stabilized Alloy &40 UNS N08700&41 Plate Sheet and Strip《镍铁铬钼铌稳定合金 (UNS N08700) 板材 薄板材和带材.pdf
《ASTM B599-1992(2014) Standard Specification for Nickel-Iron-Chromium-Molybdenum-Columbium Stabilized Alloy &40 UNS N08700&41 Plate Sheet and Strip《镍铁铬钼铌稳定合金 (UNS N08700) 板材 薄板材和带材.pdf》由会员分享,可在线阅读,更多相关《ASTM B599-1992(2014) Standard Specification for Nickel-Iron-Chromium-Molybdenum-Columbium Stabilized Alloy &40 UNS N08700&41 Plate Sheet and Strip《镍铁铬钼铌稳定合金 (UNS N08700) 板材 薄板材和带材.pdf(9页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: B599 92 (Reapproved 2014)Standard Specification forNickel-Iron-Chromium-Molybdenum-Columbium StabilizedAlloy (UNS N08700) Plate, Sheet, and Strip1This standard is issued under the fixed designation B599; the number immediately following the designation indicates the year oforiginal adop
2、tion or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers nickel-iron-chromium-molybdenum-columbium stab
3、ilized alloy (UNS N08700)2plate, sheet, and strip in the solution-annealed condition.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.
4、1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas
5、 provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3A262 Practices for Detecting Susceptibility to IntergranularAttack in Austenitic Stainless SteelsE8/E8M
6、 Test Methods for Tension Testing of Metallic Ma-terialsE10 Test Method for Brinell Hardness of Metallic MaterialsE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE55 Practice for Sampling W
7、rought Nonferrous Metals andAlloys for Determination of Chemical CompositionE140 Hardness Conversion Tables for Metals RelationshipAmong Brinell Hardness, Vickers Hardness, RockwellHardness, Superficial Hardness, Knoop Hardness, Sclero-scope Hardness, and Leeb HardnessE350 Test Methods for Chemical
8、Analysis of Carbon Steel,Low-Alloy Steel, Silicon Electrical Steel, Ingot Iron, andWrought IronE353 Test Methods for Chemical Analysis of Stainless,Heat-Resisting, Maraging, and Other Similar Chromium-Nickel-Iron Alloys3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 The terms
9、plate, sheet, and strip as used in thisspecification are described as follows:3.1.2 plate, nmaterial 0.1875 in. (4.76 mm) and over inthickness and over 10 in. (254 mm) in width.3.1.3 sheet, nmaterial under 0.1875 in. (4.76 mm) inthickness and over 24 in. (610 mm) in width.3.1.4 strip, nmaterial unde
10、r 0.1875 in. (4.76 mm) inthickness and under 24 in. (610 mm) in width.4. Ordering Information4.1 Orders for material under this specification shouldinclude the following information:4.1.1 Quantity (weight or number of pieces).4.1.2 Name of material or UNS N08700.4.1.3 Form (plate, sheet, or strip).4
11、.1.4 Dimensions.4.1.5 Type of edge required (for strip only, see 9.4).4.1.6 Finish (Section 10)For sheet ordered with No. 4finish, specify whether one or both sides are to be polished.4.1.7 ASTM designation and year of issue.4.1.8 Corrosion TestState if intergranular corrosion test isrequired (Secti
12、on 8).4.1.9 MarkingState if metal die identification is requiredon plate14 in. (6.35 mm) or thicker (Section 17).4.1.10 Certification or Test ReportsState if certification ortest reports are required (Section 16).1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals
13、 and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved Oct. 1, 2014. Published October 2014. Originallyapproved in 1980. Last previous edition approved in 2009 as B599 92 (2009)1.DOI: 10.1520/B0599-92R14.2New designat
14、ion established in accordance with ASTM E527 and SAE J1086,Practice for Numbering Metals and Alloys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standa
15、rds Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15. Materials and Manufacture5.1 Heat TreatmentThe final heat treatment shall be asolution anneal. Minor cold working such as flattening ortem
16、per rolling may be performed after the final solutionannealing treatment.NOTE 1This recommended solution anneal consists of heating to aminimum temperature of 2000F (1090C) and cooling rapidly to roomtemperature.6. Chemical Composition6.1 The material sampled, in accordance with 11.2, shallconform t
17、o the composition limits prescribed in Table 1.6.2 If a product analysis is subsequently made, the materialshall conform to the composition limits with the productanalysis variation prescribed in Table 2.7. Mechanical Requirements7.1 The material shall conform to the requirements as to themechanical
18、 property prescribed in Table 3.8. Intergranular Corrosion Test8.1 All material supplied to this specification shall becapable of passing the intergranular corrosion test, but the testneed not be performed on any given lot unless it is specified onthe purchase order. If the test is specified, it sha
19、ll be performedby the manufacturer on specimens taken in the as-shippedcondition. Specimens shall be tested in the sensitized condition(1 h at 1250F (677C), and tested in accordance with PracticeC of Practices A262. The corrosion rate shall not exceed 2.5mils/month (165 mg/dm2day).9. Dimensions and
20、Permissible Variations9.1 SheetThe material referred to as sheet shall conformto the variations in dimensions prescribed in Tables 4-9,inclusive.9.2 Cold-Rolled StripThe material referred to as cold-rolled strip shall conform to the permissible variations indimensions prescribed in Tables 10-13, inc
21、lusive.9.3 PlateThe material referred to as plate shall conform tothe permissible variations in dimensions prescribed in Tables14-20, inclusive.9.4 Edges for Cold-Rolled Strip:9.4.1 The various types of edges procurable shall be asfollows:9.4.1.1 No. 1 EdgeRolled edge, contour as specified.9.4.1.2 N
22、o. 3 EdgeAn edge produced by slitting.9.4.1.3 No. 5 EdgeApproximately square edge producedby rolling or filing, or both, after slitting.10. Workmanship, Finish, and Appearance10.1 The material shall be free of injurious imperfectionsand shall correspond to the designated finish as described asfollow
23、s:10.1.1 SheetThe various types of finish procurable onsheet products shall be as follows:10.1.1.1 No. 1 FinishHot rolled, annealed, and descaled;produced by hot rolling to specified thicknesses followed byannealing and descaling (see 10.2).10.1.1.2 No. 2D FinishDull, cold-rolled finish; producedby
24、cold rolling to the specified thickness, annealing, anddescaling. The dull finish results from the descaling andpickling operations.10.1.1.3 No. 2B FinishBright, cold-rolled finish; producedby giving a final light cold-rolled pass with polished rolls, to asheet that has been annealed and descaled.10
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMB59919922014STANDARDSPECIFICATIONFORNICKELIRONCHROMIUMMOLYBDENUMCOLUMBIUMSTABILIZEDALLOY40UNSN0870041PLATESHEETANDSTRIP

链接地址:http://www.mydoc123.com/p-461683.html