ASTM B490-1992(2003) Standard Practice for Micrometer Bend Test for Ductility of Electrodeposits《用测微计弯曲试验法测定电解沉积物的延展性》.pdf
《ASTM B490-1992(2003) Standard Practice for Micrometer Bend Test for Ductility of Electrodeposits《用测微计弯曲试验法测定电解沉积物的延展性》.pdf》由会员分享,可在线阅读,更多相关《ASTM B490-1992(2003) Standard Practice for Micrometer Bend Test for Ductility of Electrodeposits《用测微计弯曲试验法测定电解沉积物的延展性》.pdf(2页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: B 490 92 (Reapproved 2003)Standard Practice forMicrometer Bend Test for Ductility of Electrodeposits1This standard is issued under the fixed designation B 490; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year o
2、f last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice describes a procedure for measuring theductility of electrodeposited foils.21.2 This practice is suit
3、able only for the evaluation ofelectrodeposits having low ductility.1.3 The obtained ductility values must only be consideredsemi-quantitative because this test has a significant operatordependence.1.4 This practice is best used for in-house process controlwhere measurements are always made by the s
4、ame operator. Achange in ductility value can be used as an indication ofpossible changes in the electroplating solution.1.5 This standard does not purport to address the safetyproblems, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate saf
5、ety andhealth practices and determine the applicability of regulatorylimitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B 177 Guide for Engineering Chromium Electroplating3. Summary of Practice3.1 This practice consists of measuring the bend of a foilheld between the jaws of a micro
6、meter; these are closed untilfracture or cracks appear.4. Significance and Use4.1 This practice is useful as one method of controllingsome electroplating solutions. It serves to indicate the presenceof contamination or some other adverse condition.4.2 Ductility measurements are of particular value w
7、henelectroplated parts are to be subjected to moderate stress suchas that involved in bolting an electroplated bumper to anautomobile.NOTE 1The foils used in this practice are typically 25 to 40 m thick.Foils in this thickness range do not have the same properties as bulk metal.For example, a nickel
8、 electrodeposit 0.5 mm thick, prepared in purifiedbright nickel electroplating solutions for which this test is being used, hadless than 3 % elongation in a tension test, and could not be bent to a 90angle without complete fracture. However, foils 25 to 40 m thick,electroplated at the same time, had
9、 micrometer ductility values in the 10to 25 % range.5. Apparatus5.1 Micrometer, 25-mm with flat jaws to measure thethickness and to compress the foil.5.2 Hand or Power Shear, grinding wheel, or hack saw, totrim the edges of the electroplated panel and to separate the foilfrom the basis metal.5.3 Pai
10、r of Sharp Scissors to cut the test specimens.6. Test Specimens6.1 An electrodeposit shall be prepared using a basis metalwith a smooth surface from which the electrodeposit can bereadily separated. A stainless steel or nickel electroplated steelpanel may be used for this purpose, prepared as in 6.2
11、.6.2 Apiece of cold-rolled steel, of any convenient size, suchas 100 by 150 mm, shall be properly cleaned, acid dipped, andelectroplated with approximately 7.5 m of nickel. Afterrinsing, the specimen shall be cleaned anodically for 15 s in ahot alkaline cleaner, rinsed, acid dipped in about 1 N sulf
12、uricacid (about 27 mL of concentrated sulfuric acid added to about900 mL of cold water, mixed, and diluted with cold water to 1L), and immediately placed in the electroplating solution of themetal to be tested. An electrodeposit 25 to 40 m thick shall beelectroplated on the prepared surface. The dep
13、osit shall beplated at an average current density and under conditions(agitation, temperature, etc.) approximating those used on partsplated in the solution being tested.1This practice is under the jurisdiction of ASTM Committee B08 on Metallicand Inorganic Coatings and is the direct responsibility
14、of Subcommittee B08.10 onTest Methods.Current edition approved Oct. 1, 2003. Published October 2003. Originallyapproved in 1968. Last previous edition approved in 1998 as B 490 92 (1998).2For a discussion of this test see Mohrnheim, A. F., “The Bend Test forMeasuring the Strain Limit of Surfaces,” P
15、lating, Vol 50, 1963, pp. 10941099.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM Internatio
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMB49019922003STANDARDPRACTICEFORMICROMETERBENDTESTFORDUCTILITYOFELECTRODEPOSITS 测微计 弯曲 试验 测定 电解 沉积物
链接地址:http://www.mydoc123.com/p-461373.html