ASTM B249 B249M-2016 Standard Specification for General Requirements for Wrought Copper and Copper-Alloy Rod Bar Shapes and Forgings《锻造铜和铜合金杆材 棒材 型材和锻件通用要求的标准规格》.pdf

《ASTM B249 B249M-2016 Standard Specification for General Requirements for Wrought Copper and Copper-Alloy Rod Bar Shapes and Forgings《锻造铜和铜合金杆材 棒材 型材和锻件通用要求的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B249 B249M-2016 Standard Specification for General Requirements for Wrought Copper and Copper-Alloy Rod Bar Shapes and Forgings《锻造铜和铜合金杆材 棒材 型材和锻件通用要求的标准规格》.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B249/B249M 16Standard Specification forGeneral Requirements for Wrought Copper and Copper-Alloy Rod, Bar, Shapes and Forgings1This standard is issued under the fixed designation B249/B249M; the number immediately following the designation indicates the yearof original adoption or, in th

2、e case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1

3、 This specification2establishes the general requirementscommon to wrought copper and copper alloy rod, bar, shapes,and forgings which shall apply to Specifications B16/B16M,B21/B21M, B98/B98M, B124/B124M, B138/B138M, B139/B139M, B140/B140M, B150/B150M, B151/B151M, B187/B187M, B196/B196M, B283/B283M,

4、 B301/B301M, B371/B371M, B411/B411M, B441, B453/B453M, B455, B570,B870, B927/B927M, B929, B967/B967M, and B974/B974Mto the extent referenced therein.1.2 The chemical composition, physical and mechanicalproperties, and all other requirements not included in thisspecification are prescribed in the pro

5、duct specification.1.3 UnitsThe values stated in either SI units or inch-pound units are to be regarded separately as standard. Thevalues stated in each system may not be exact equivalents;therefore, each system shall be used independently of the other.Combining values from the two systems may resul

6、t in non-conformance with the standard.1.3.1 Within the text the SI values are given in brackets.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health

7、practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B16/B16M Specification for Free-Cutting Brass Rod, Barand Shapes for Use in Screw MachinesB21/B21M Specification for Naval Brass Rod, Bar, andShapesB98/B98M Specification for

8、Copper-Silicon Alloy Rod, Barand ShapesB124/B124M Specification for Copper and Copper AlloyForging Rod, Bar, and ShapesB138/B138M Specification for Manganese Bronze Rod, Bar,and ShapesB139/B139M Specification for Phosphor Bronze Rod, Bar,and ShapesB140/B140M Specification for Copper-Zinc-Lead (RedBr

9、ass or Hardware Bronze) Rod, Bar, and ShapesB150/B150M Specification for Aluminum Bronze Rod, Bar,and ShapesB151/B151M Specification for Copper-Nickel-Zinc Alloy(Nickel Silver) and Copper-Nickel Rod and BarB154 Test Method for Mercurous Nitrate Test for CopperAlloysB187/B187M Specification for Coppe

10、r, Bus Bar, Rod, andShapes and General Purpose Rod, Bar, and ShapesB193 Test Method for Resistivity of Electrical ConductorMaterialsB194 Specification for Copper-BerylliumAlloy Plate, Sheet,Strip, and Rolled BarB196/B196M Specification for Copper-BerylliumAlloy Rodand BarB283/B283M Specification for

11、 Copper and Copper-AlloyDie Forgings (Hot-Pressed)B301/B301M Specification for Free-Cutting Copper Rod,Bar, Wire, and ShapesB371/B371M Specification for Copper-Zinc-Silicon AlloyRodB411/B411M Specification for Copper-Nickel-Silicon AlloyRod and BarB441 Specification for Copper-Cobalt-Beryllium, Copp

12、er-Nickel-Beryllium, and Copper-Nickel-Lead-BerylliumRod and Bar (UNS Nos. C17500, C17510, and C17465)B453/B453M Specification for Copper-Zinc-Lead Alloy(Leaded-Brass) Rod, Bar, and Shapes1This specification is under the jurisdiction ofASTM Committee B05 on Copperand CopperAlloys and is the direct r

13、esponsibility of Subcommittee B05.02 on Rod,Bar, Wire, Shapes and Forgings.Current edition approved Oct. 1, 2016. Published October 2016. Originallyapproved in 1951. Last previous edition approved in 2015 as B249/B249M 15a.DOI: 10.1520/B0249_B0249M-16.2For ASME Boiler and Pressure Vessel Code applic

14、ations see related Specifi-cations SB-249 in Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM

15、website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1B455 Specification for Copper-Zinc-Lead Alloy (Leaded-Brass) Extruded ShapesB570 Specification for Copper-Berylli

16、um Alloy (UNS Nos.C17000 and C17200) Forgings and ExtrusionsB577 Test Methods for Detection of Cuprous Oxide (Hydro-gen Embrittlement Susceptibility) in CopperB846 Terminology for Copper and Copper AlloysB858 Test Method for Ammonia Vapor Test for DeterminingSusceptibility to Stress Corrosion Cracki

17、ng in CopperAlloysB870 Specification for Copper-Beryllium Alloy Forgingsand Extrusions Alloys (UNS Nos. C17500 and C17510)B900 Practice for Packaging of Copper and Copper AlloyMill Products for U.S. Government AgenciesB927/B927M Specification for Brass Rod, Bar, and ShapesB929 Specification for Copp

18、er-Nickel-Tin Spinodal AlloyRod and BarB967/B967M Specification for Copper-Zinc-Tin-BismuthAlloy Rod, Bar and WireB974/B974M Specification for Free-Cutting Bismuth BrassRod, Bar and WireD4855 Practice for Comparing Test Methods (Withdrawn2008)4E3 Guide for Preparation of Metallographic SpecimensE8/E

19、8M Test Methods for Tension Testing of Metallic Ma-terialsE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE53 Test Method for Determination of Copper in UnalloyedCopper by GravimetryE54 Tes

20、t Methods for Chemical Analysis of Special Brassesand Bronzes (Withdrawn 2002)4E62 Test Methods for Chemical Analysis of Copper andCopperAlloys (Photometric Methods) (Withdrawn 2010)4E75 Test Methods for Chemical Analysis of Copper-Nickeland Copper-Nickel-Zinc Alloys (Withdrawn 2010)4E76 Test Method

21、s for Chemical Analysis of Nickel-CopperAlloys (Withdrawn 2003)4E112 Test Methods for Determining Average Grain SizeE118 Test Methods for Chemical Analysis of Copper-Chromium Alloys (Withdrawn 2010)4E121 Test Methods for Chemical Analysis of Copper-Tellurium Alloys (Withdrawn 2010)4E255 Practice for

22、 Sampling Copper and Copper Alloys forthe Determination of Chemical CompositionE290 Test Methods for Bend Testing of Material for Ductil-ityE478 Test Methods for Chemical Analysis of Copper AlloysE581 Test Methods for Chemical Analysis of Manganese-Copper Alloys3. Terminology3.1 For definitions of t

23、erms related to copper and copperalloys, refer to Terminology B846.3.2 Definitions of Terms Specific to This Standard:3.2.1 lengths, mill, nstraight lengths, including ends, thatcan be conveniently manufactured in the mill. Full lengthpieces are usually 10 or 12 ft 3000 or 3600 mm.3.2.2 lengths, sto

24、ck, nstraight lengths that are mill cut andstored in advance of orders. They are usually 10 or 12 ft 3000or 3600 mm and subject to established length tolerances.4. Materials and Manufacture4.1 Materials:4.1.1 The material of manufacture shall be a form of theCopper or Copper Alloy UNS No. designatio

25、n specified in theordering information of such purity and soundness as to besuitable for processing into the products described in theproduct specification.4.1.2 When specified in the contract or purchase order, thatheat identification or traceability is required, the purchasershall specify the deta

26、ils desired.NOTE 1Due to the discontinuous nature of the processing of castingsinto wrought products, it is not always practical to identify specific castinganalysis with a specific quantity of finished product.4.2 ManufactureThe product shall be manufactured bysuch hot working, cold working, and an

27、nealing processes as toproduce a uniform wrought structure in the finished product.4.2.1 The product shall be hot or cold worked to the finishedsize and subsequently annealed or heat treated when required,and straightened to meet the properties specified.4.2.2 EdgesThe edge shall be drawn, extruded,

28、 or rolled;refer to Edge Contours in Section 6.5. Chemical Composition5.1 The material shall conform to the chemical compositionrequirements prescribed in the product specification.5.1.1 Results of analysis on a product (check) sample shallconform to the composition requirements within the permitted

29、analytical variance given in the product specification.5.2 The composition limits established for the Copper orCopper Alloy UNS No. designation specified in the productspecification do not preclude the presence of other elements.By agreement between the manufacturer or supplier and thepurchaser. Lim

30、its may be established and analysis required forunnamed elements.5.3 When material composition has been determined duringthe course of manufacture, analysis of the finished product bythe manufacturer is not required.6. Dimensions, Mass and Permissible Variations6.1 GeneralFor the purpose of determin

31、ing conformancewith the dimensional requirements, any measured value out-side the specified limiting values for any dimension may because for rejection.6.1.1 The dimensions and tolerances for products refer-enced to this specification, shall be as noted in the followingparagraphs and tables, where t

32、he product specification is notedin the table heading.NOTE 2Blank spaces in the tolerance tables indicate either that thematerial generally is not available or that no tolerances are established.4The last approved version of this historical standard is referenced onwww.astm.org.B249/B249M 1626.2 Dia

33、meter or Distance Between Parallel SurfacesThediameter of round sections or the distance between parallelsurfaces in the case of other sections, except shapes, shall notvary from that specified by more than the amounts specified inTables 1-12, incl, for the product, specification indicated:Table 1 a

34、nd Table 2List the tolerances for diameter ordistance between parallel surfaces of cold-drawn rod in round,hexagonal and octagonal cross sections. Applicable productspecifications and alloys are shown in the table titles.Table 3Lists the diameter tolerances for piston finish rodapplicable to product

35、 specifications shown in the table title.Table 4 and Table 5List the tolerances for diameter ordistance between parallel surfaces of as-extruded rod and barapplicable to the specifications and alloys shown in the tabletitles. These tolerances are applicable to round, hexagonal, andoctagonal rod as w

36、ell as square and rectangular bar.Table 6Lists the diameter tolerances for hot-rolled roundrod applicable to the product specification shown in the tabletitle.Table 7, Table 8 and Table 9List the thickness tolerancesfor rectangular and square bar applicable to the productspecifications and alloys sh

37、own in the table titles.Table 10 and Table 11List the width tolerances forrectangular bar applicable to the product specifications andalloys shown in the table titles.Table 12Lists the diameter or distance between parallelsurfaces tolerances for hot-forged rod and bar applicable to theproduct specif

38、ication shown in the title.6.3 LengthRod, bar, and shapes shall be furnished in stocklengths with ends, unless the order specifies stock lengths,specific lengths, or specific lengths with ends as specified inTable 13, Table 14, and Table 15 for the product specificationindicated:Table 13Length toler

39、ances for full-length pieces appli-cable to product specifications shown in the table title.Table 14 and Table 15Lists the schedule of lengths(specific and stock) with ends applicable to product specifica-tions and alloys shown in the table titles.6.4 Straightness:6.4.1 Unless otherwise specified, d

40、rawn rod, bar, andshapes, other than shafting rod, piston-finish rod shall befurnished in straight lengths. The deviation from straightnessshall not exceed the limitations specified in Table 16 for eithergeneral or automatic screw machine use for the productspecifications and alloys shown in the tab

41、le titles. To determinecompliance with this tolerance, the lengths shall, in case ofdisagreement, be checked by the following method:6.4.1.1 Place the lengths on a level table so that the arc ordeparture from straightness is horizontal. Measure the depth ofTABLE 1 Tolerances for Diameter or Distance

42、 Between ParallelSurfaces of Cold-Drawn Rod(Applicable to Specifications B16/B16M, B21/B21M, B98/B98M (Cop-per Alloy UNS No. C65100), B124/B124M (Copper Alloy UNS Nos.C11000, C14500, C14700, C46400, C46750, C48200, C48500,C49250, C49255, C49260, C49265, C49300, C49340, C49345,C49350, and C49360), B1

43、40/B140M, B301/B301M, B453/B453M,B927/B927M, B967/B967M, and B974/B974M)Diameter or Distance BetweenParallel Surfaces, in. mmTolerances, Plus and Minus,Ain. mmRoundHexagonal,OctagonalUp to 0.150 3.8, incl 0.0013 0.035 0.0025 0.06Over 0.150 to 0.500 3.8 to 12, incl 0.0015 0.04 0.003 0.08Over 0.500 to

44、 1.00 12 to 25, incl 0.002 0.05 0.004 0.10Over 1.00 to 2.00 25 to 50, incl 0.0025 0.06 0.005 0.13Over 2.00 50 0.15B0.15B0.30B0.30BAWhen tolerances are specified as all plus or all minus, double the values given.BPercent of specified diameter or distance between parallel surfaces expressed tothe near

45、est 0.001 in. 0.01 mm.TABLE 2 Tolerances for Diameter or Distance Between ParallelSurfaces of Cold-Drawn Rod(Applicable to Specifications B98/B98M (Copper Alloy UNS No.C65500 and C66100), B124/B124M (Copper Alloy UNS Nos. C27450,C36500, C37000, C37700, C61900, C62300, C63000, C63200,C64200, C64210,

46、C65500, C67500, C67600, C69240, C69300,C70620, C71520, and C77400), B138/B138M, B139/B139M, B150/B150M, B151/B151M, B196/B196M, B371/B371M, B411/B411M, andB441)Diameter or Distance BetweenParallel Surfaces, in. mmTolerances, Plus and Minus,Ain. mmRoundHexagonal,OctagonalUp to 0.150 3.8, incl 0.002 0

47、.050 . . .Over 0.150 to 0.500 3.8 to 12, incl 0.002 0.050 0.004 0.10Over 0.500 to 1.00 12 to 25, incl 0.003 0.08 0.005 0.13Over 1.00 to 2.00 25 to 50, incl 0.004 0.10 0.006 0.15Over 2.00 50 0.20B0.20B0.40B0.40BAWhen tolerances are specified as all plus or all minus, double the values given.BPercent

48、of specified diameter or distance between parallel surfaces expressed tothe nearest 0.001 in. 0.01 mm.TABLE 3 Diameter Tolerances for Piston-Finish Rod(Applicable to Specifications B21/B21M, B138/B138M, B139/B139M,and B150/B150M)Diameter, in. mm Tolerances, Plus and Minus,Ain. mmOver 0.500 to 1.00 1

49、2 to 25, incl 0.0013 0.35Over 1.00 to 2.00 25 to 50, incl 0.0015 0.04Over 2.00 50 0.10B0.10BAWhen tolerances are specified as all plus or all minus, double the values given.BPercent of specified diameter expressed to the nearest 0.0005 in. 0.01 mm.TABLE 4 Tolerances for Diameter or Distance Between ParallelSurfaces of As-Extruded Rod and Bar(Applicable to Specifications B21/B21M, B124/B124M (Copper AlloyUNS Nos. C27450, C36500, C37000, C37700, C46400, C46750,C48200, C48500,