FORD WSS-M4G370-A-2010 SEALANT ANAEROBIC PRE-APPLIED THREADED TO BE USED WITH FORD WSS-M99P1111-A 《厌氧的预先使用螺纹的密封剂 与福特WSS-M99P1111-A 一起使用》.pdf

《FORD WSS-M4G370-A-2010 SEALANT ANAEROBIC PRE-APPLIED THREADED TO BE USED WITH FORD WSS-M99P1111-A 《厌氧的预先使用螺纹的密封剂 与福特WSS-M99P1111-A 一起使用》.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M4G370-A-2010 SEALANT ANAEROBIC PRE-APPLIED THREADED TO BE USED WITH FORD WSS-M99P1111-A 《厌氧的预先使用螺纹的密封剂 与福特WSS-M99P1111-A 一起使用》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions Rev. 0 2010 10 19 Activated R. Verde, SA Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 1 of 2 SEALANT, ANAEROBIC, PRE-APPLIED THREADED WSS-M4G370-A 1. SCOPE The material defined by this specification is one

2、 component, paste-like, curing anaerobic material, which sets between closely fitted metal surfaces and prevents loosening and leakage from shock and vibration. 2. APPLICATION This material was originally released for materials used to seal threaded plugs, gaskets, and joints in the engine and chass

3、is. This material is designed for the locking and sealing of metal tapered threads and fittings, low strength; 150 C continuous use temperature and pressure to 2.5 bar; solvent resistance. Not recommended for use on thermoplastic materials where stress cracking of the plastic could result. Users are

4、 recommended to confirm compatibility of the product with such substrates. Prior to the release for a particular application and in addition to the requirements specified herein, full evaluation with the assembled part must be ensured by the affected Component Engineering activity. 3. REQUIREMENTS M

5、aterial specification requirements are to be used for initial qualification of materials. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 VISCOSITY 250.000 a 800

6、0.000 mPa.s (ASTM D 1084, Method A, Brookfield RVF, # 7 spindle, 2 rpm at 25 C) 3.3 SPECIFIC GRAVITY 1.10 +/- 0.10 (ASTM D 792, Method A) 3.4 FLASH POINT above 93 (ASTM D 56) 3.5 SEALING PRODUCTS PERFORMANCE 3.5.1 Breakaway torque, 1.5 N.m min (ISO 10964), After 24h cure at 23+/-2 ENGINEERING MATERI

7、AL SPECIFICATIONWSS-M4G370-A Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 2 of 2 3.6 COMPATIBILITY (ASTM D 471, 166h at 150 +/- 2) After conditioned as above repeat breakaway torque. 4. APPROVAL OF MATERIAL Materials defined by this specification must have prior

8、 approval by the responsible Materials Engineering activity. Suppliers desiring approval of their materials shall first obtain an expression of interest from the affected Purchasing, design and Materials Engineering activity. Upon request, the Supplier shall submit to the affected Materials Engineering activity its own laboratory report to the specification (test results, not nominal values), the material designation and code number, and test specimens for Ford evaluation. Upon approval, the material will be added to the Engineering Material approved Source List.