FORD WSD-M10A78-A2-2012 SINTERED IRON CARBON COPPER PHOSPHORUS MANGANESE TO BE USED WITH FORD WSS-M99P1111-A 《烧结铁 碳 铜 磷 锰 与福特WSS-M99P1111-A 一起使用》.pdf

《FORD WSD-M10A78-A2-2012 SINTERED IRON CARBON COPPER PHOSPHORUS MANGANESE TO BE USED WITH FORD WSS-M99P1111-A 《烧结铁 碳 铜 磷 锰 与福特WSS-M99P1111-A 一起使用》.pdf》由会员分享，可在线阅读，更多相关《FORD WSD-M10A78-A2-2012 SINTERED IRON CARBON COPPER PHOSPHORUS MANGANESE TO BE USED WITH FORD WSS-M99P1111-A 《烧结铁 碳 铜 磷 锰 与福特WSS-M99P1111-A 一起使用》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 02 2012 03 06 N Status No usage or replacement G. Weber, NA 2003 10 14 Revised Para 3.0 inserted; para 3.1, 3.7 and 4 deleted 1992 11 25 C10261078 Released G. Lane EAO, J. C. Webster NAAO Controlled document at www.MATS Copyright 2012, Fo

2、rd Global Technologies, Inc. Page 1 of 2 SINTERED IRON, CARBON, COPPER, PHOSPHORUS, WSD-M10A78-A2 MANGANESE NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a sintered carbon, copper, tin, phosphorus manganese steel. 2. APPLICATION This specification was released

3、originally for material used for valve guide bushings. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 CHEMICAL COMPOSITION (Weight %) (ASTM A 75

4、1/ASTM E 1019) Total Carbon 1.5 - 2.5 Combined Carbon 1.0 - 1.8 Copper 3.0 - 6.0 Tin 0.3 - 0.7 Phosphorus 0.1 - 0.35 Manganese 0.1 - 0.5 Sulphur 0.05 - 0.25 Other Elements 2.0 max Iron Remainder Specific composition limits, composition determination procedures, and processing route to meet performan

5、ce and manufacturing requirements will form part of an agreed control plan for each component. 3.3 DENSITY, min 6.4 - 6.9 g/cm3 (ISO 2738/ASTM B 328) For valve guides 55 mm or less, the density variation between the central third and outer third lengths shall be 0.3 g/cm3 max. 3.4 APPARENT HARDNESS

6、HRB 55 - 90 (ISO 4498/1, ASTM E 18) Average of a minimum of five readings along a longitudinal section of the wall on the outside surface a minimum of 5 mm from either end. All individual hardness readings shall conform to the hardness range. ENGINEERING MATERIAL SPECIFICATION WSD-M10A78-A2 Copyrigh

7、t 2012, Ford Global Technologies, Inc. Page 2 of 2 3.5 MICROSTRUCTURE The composite microstructure shall consist of a ternary iron phosphorus carbon eutectic matrix with a discontinuous grain boundary carbide network. Copper-tin alloy, manganese sulphide and graphite are associated with original par

8、ticle boundaries. Inter-connected porosity is distributed throughout. Intra-granular oxide films are not permitted. Phase identification and distribution will be controlled by reference to photomicrographs representing structures of valve guides for which approval is originally given. These photo-mi

9、crographs will form part of the agreed control plan. 3.6 SURFACE CONDITION Surfaces shall be free of scale and rust. Nicks, intrusions, burrs and depressions shall not exceed 0.25 mm in any direction. Visual inspection is to be performed under white light without the aid of magnification. 5. GENERAL

10、 INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 TYPICAL MECHANICAL PROPERTIES Temperature Degree C Room Temperature 200 Youngs Modulus (GPa) 115 125 0.2 Compressive Proof Stress (Mpa) 350 350 Thermal Conductivity (Wm-1K-1) 21 27 Coefficient of Thermal Expansion 11E6/K from 0 - 200 C