FORD WRS-M1H1230-A-2016 FABRIC OMNI 100 PATTERN WOVEN 100% PIR PCR UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WRS-M1H1230-A-2016 FABRIC OMNI 100 PATTERN WOVEN 100% PIR PCR UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WRS-M1H1230-A-2016 FABRIC OMNI 100 PATTERN WOVEN 100% PIR PCR UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A .pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 2 2016 05 19 N Status No replacement D. Murtonen, NA 2012 07 13 Revised Revised Sect. 3.2.2 M.Dumitrescu, NA 2011 12 05 Activated M. Dumitrescu, NA Controlled document at www.MATS Copyright 2016, Ford Global Technologies, LLC Page 1 of 2

2、FABRIC, OMNI 100 PATTERN, WOVEN WRS-M1H1230-A 100% PIR/PCR UNLAMINATED NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a woven dobby polyester face fabric. The fabric is made with 100% PIR/PCR (Post industrial/post consumer) recycled yarn. 2. APPLICATION This spe

3、cification was released originally for material used as an interior trim fabric for CD391 2013 seat bolster and/or insert for NA production. The fabric was approved as backcoated and trilaminated with foam and backing fabric/scrim. 3. REQUIREMENTS In addition, to the requirements listed herein, the

4、fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. The fabric must be backcoated. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 Recycled Co

5、ntent This specification must contain 100% recycled content as defined by WRS-M99P42-A2 (Textile Materials, Identification of Recycled Content). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10% tolerance (ASTM D 3775) Warp 909 ends/10 cm Weft 283 picks/10 cm 3.2.2 Fabric Weight, +/-10 % tolerance

6、, (FLTM BN 106-01) Face fabric 320 g/m2 Backcoat 72 g/m2 Total weight 392 g/m2 ENGINEERING MATERIAL SPECIFICATION WRS-M1H1230-A Copyright 2016, Ford Global Technologies, Inc. Page 2 of 2 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoating Acrylic

7、Backing fabric/scrim 100% Polyester, Circ knit 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 167 dtex (100% recycled textured polyester yarn) x 1 Weft 167 dtex (100% recycled textured polyester yarn) x 2 3.5 METHOD OF DYEING Piece dye 3.6 FINISHING OPERATIONS set make, wash, jet dye, coating, brushed 4.

8、GENERAL INFORMATION This information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that the material defined in this specification

9、 and shipped to any one assembly plant will be produced by one supplier only. 4,2 Global strategy is to use Tri-Laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above fabric construction, composition and Yarn construction. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4.