FORD ESF-M1P13-A-2008 PLATING SILVER TO BE USED WITH FORD WSS-M99P1111-A 《电镀银(和FORD WSS-M99P1111-A一起使用)》.pdf

《FORD ESF-M1P13-A-2008 PLATING SILVER TO BE USED WITH FORD WSS-M99P1111-A 《电镀银(和FORD WSS-M99P1111-A一起使用)》.pdf》由会员分享，可在线阅读，更多相关《FORD ESF-M1P13-A-2008 PLATING SILVER TO BE USED WITH FORD WSS-M99P1111-A 《电镀银(和FORD WSS-M99P1111-A一起使用)》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Ver. 4 2008 07 22 N-STATUS No Replacement Named 2003 07 25 Revised Para 3.0 inserted 1963 07 20 Released F6-1092 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 1 of 2 PLATING, SILVER ESF-M1P13-A NOT TO BE

2、USED FOR NEW DESIGN 1. SCOPE This specification defines the performance of silver electroplating. 2. APPLICATION This specification was released originally for silver plating of electrical connecting devices. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and p

3、art producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 PLATING METHOD This specification is not intended to limit the procedure of plating. Any process resulting in a satisfactory adherent and durable plate will be satisfactory. A nickel under

4、plate is required when specified on engineering drawing. 3.1.1 Cleaning Requirements Carburized parts, case depths in excess of 0.012 in (0.30 mm), cold worked parts such as hard drawn spring wire parts, steel bolts having a Rockwell hardness of “C“ 27 and over and all other parts having a hardness

5、of Rockwell “C“ 32 and over are considered susceptible to hydrogen embrittlement. Any standard cleaning method is acceptable providing the following restrictions are observed. . Carburized parts must have been stress relieved for 1 h at 135 C minimum before cleaning. . None of the parts mentioned ab

6、ove shall be cleaned by acid solution unless specifically approved. 3.1.2 Hydrogen Embrittlement After plating, all of the above mentioned parts shall be heated to 175 C and held at this temperature for 1 h minimum. This draw operation must be performed within 4 h (1 h preferred) after plating opera

7、tion. 3.2 THICKNESS, min 0.00012 in (3.0 m) (ASTM A 219) 3.3 WEIGHT, min 2.95 g/ft (31.9 g/m) ENGINEERING MATERIAL SPECIFICATION ESF-M1P13-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 2 of 2 3.4 QUALITY Plated parts shall be free from surface imperfections such as rough or orange peel conditions, cold shuts, pits, slivers, dullness, stains, discoloration, break in the plate and wheel marks or buff lines to the extent required by specifications for the visual inspection of appearance items established by Product Engineering. Note: Similar to P-23-B.