DIN EN 15973-2011 Rubber- or plastic-coated fabrics - Upholstery fabrics - Resistance to soiling German version EN 15973 2011《橡胶或塑料涂层织物 家具布 耐污性 德文版本EN 15973-2011》.pdf

《DIN EN 15973-2011 Rubber- or plastic-coated fabrics - Upholstery fabrics - Resistance to soiling German version EN 15973 2011《橡胶或塑料涂层织物 家具布 耐污性 德文版本EN 15973-2011》.pdf》由会员分享，可在线阅读，更多相关《DIN EN 15973-2011 Rubber- or plastic-coated fabrics - Upholstery fabrics - Resistance to soiling German version EN 15973 2011《橡胶或塑料涂层织物 家具布 耐污性 德文版本EN 15973-2011》.pdf（13页珍藏版）》请在麦多课文档分享上搜索。

1、May 2011 Translation by DIN-Sprachendienst.English price group 9No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 59.

2、080.40!$p_c“1776064www.din.deDDIN EN 15973Rubber- or plastic-coated fabrics Upholstery fabrics Resistance to soilingEnglish translation of DIN EN 15973:2011-05Mit Kautschuk oder Kunststoff beschichtete Textilien Mbelstoffe Verhalten gegenber AnschmutzenEnglische bersetzung von DIN EN 15973:2011-05Su

3、pports textiles revtus de caoutchouc ou de plastique toffes dameublement Rsistance la salissureTraduction anglaise de DIN EN 15973:2011-05www.beuth.deDocument comprises pagesIn case of doubt, the German-language original shall be considered authoritative.1304.11 DIN EN 15973:2011-05 A comma is used

4、as the decimal marker. National foreword This standard has been prepared by Technical Committee CEN/TC 248 “Textiles and textile products” (Secretariat: BSI, United Kingdom). The responsible German body involved in its preparation was the Normenausschuss Kunststoffe (Plastics Standards Committee), W

5、orking Committee NA 054-04-04 AA Kunststoff-Folien und kunststoffbeschichtete Flchengebilde (Kunstleder); allgemeine Eigenschaften. 2 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 15973 March 2011 ICS 59.080.40 English Version Rubber- or plastic-coated fabrics Upholstery fabrics Resistance to

6、 soiling Supports textiles revtus de caoutchouc ou de plastique toffes dameublement Rsistance la salissure Mit Kautschuk oder Kunststoff beschichtete Textilien Mbelstoffe Verhalten gegenber Anschmutzen This European Standard was approved by CEN on 15 January 2011. CEN members are bound to comply wit

7、h the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Manage

8、ment Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same stat

9、us as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland,Portugal,

10、Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2011 CEN All rights of exploitation in any form and by any means reser

11、ved worldwide for CEN national Members. Ref. No. EN 15973:2011: EEN 15973:2011 (E) 2 Contents Page Foreword 31 Scope 42 Normative references 43 Terms and definitions .44 Principle 55 Apparatus and materials .56 Preparation and conditioning of test specimens .67 Procedure .68 Test report 9Annex A (in

12、formative) Example for report of results 10Bibliography . 11DIN EN 15973:2011-05 EN 15973:2011 (E) 3 Foreword This document (EN 15973:2011) has been prepared by Technical Committee CEN/TC 248 “Textiles and textile products”, the secretariat of which is held by BSI. This European Standard shall be gi

13、ven the status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 2011, and conflicting national standards shall be withdrawn at the latest by September 2011. Attention is drawn to the possibility that some of the elements of this documen

14、t may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Aus

15、tria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom.

16、 DIN EN 15973:2011-05 EN 15973:2011 (E) 4 1 Scope This European standard specifies a test method for assessing resistance to soiling and cleanability of coated fabrics for upholstery. This European standard is applicable to upholstery fabrics with a coating on the wear face. 2 Normative references T

17、he following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 20105-A03, Textiles Tests for colour fastness P

18、art A03: Grey scale for assessing staining (ISO 105-A03:1993) EN ISO 2231, Rubber- or plastics-coated fabrics Standard atmospheres for conditioning and testing (ISO 2231:1989) EN ISO 12945-2, Textiles Determination of fabric propensity to surface fuzzing and to pilling Part 2: Modified Martindale me

19、thod (ISO 12945-2:2000) EN ISO 12947-1, Textiles Determination of the abrasion resistance of fabrics by the Martindale method Part 1: Martindale abrasion testing apparatus (ISO 12947-1:1998) ISO 105-F09, Textiles Tests for colour fastness Part F09: Specification for cotton rubbing cloth 3 Terms and

20、definitions For the purposes of this document, the following terms and definitions apply. 3.1 coated fabric fabric with an adherent, discrete continuous layer of rubber and/or plastic based material on one or both surfaces (see EN 13360) 3.2 soiling process of transferring one or more unwanted subst

21、ances to the surface of a material NOTE The term “staining“: a special case of soiling caused by one or more dyes or pigments. 3.3 cleanability property of the coated fabric to be restored to its original appearance after cleaning DIN EN 15973:2011-05 EN 15973:2011 (E) 5 4 Principle This method prov

22、ides a procedure for exposing test specimens to the influence of soiling material under defined conditions, their cleaning and following visual assessment. For soiling three different types of soiling substances are used: a) solid soil and dyes transferred by a soiling cloth; b) an aqueous soil and

23、c) an oily soil. After soiling and a conditioning period the specimens are cleaned. The specimens are visually assessed before and after cleaning. 5 Apparatus and materials 5.1 Martindale apparatus, according to EN ISO 12947-1. 5.2 Pilling specimen holder heads, for the Martindale apparatus (5.1), i

24、ncluding the auxiliary mandrel device for specimen mounting, as defined in EN ISO 12945-2. Pilling specimen holder fitted with ring weight and the nominal 12 kPa loading piece (sum of the mass of the applied load and the mass of the specimen holder assembly of (1 010 15) g). NOTE 1 This exerts a nom

25、inal pressure of 1,6 kPa on the test specimen during the test. NOTE 2 The use of the mandrel is necessary to correctly mount the soiling cloth on the holder and to avoid contact with the soiling surface of the cloth. Use the option that forms a Lissajous figure with a (60 1) mm stroke. It should be

26、noted that this stroke differs from the standard machine setting for the textile pilling test. WARNING Some Martindale apparatus have been designed such as the clamping ring is fastened around the abradant table with protuberant screws. Such screws do not allow mechanically the free movement of the

27、pilling specimen holder heads, and then, such apparatus are not available to perform this test method. 5.3 Wool felt underlay, according to EN ISO 12945-2, cut to a diameter of (90 1) mm, for the pilling holder (5.2). 5.4 Wool felt underlay, according to EN ISO 12947-1, cut to a diameter of (140 1)

28、mm, for the abrading table of the Martindale apparatus (5.1). 5.5 Circular sample cutters, for the specimen and soiling cloth, one cutter with a diameter of at least 140 mm. 5.6 Pipettes, for application of the liquids, accurate to at least 0,1 ml. 5.7 Glass plates, size at least 150 mm x 150 mm. 5.

29、8 Cotton cloth, according to ISO 105-F09, dimension: 70 mm x 70 mm pieces for soiling and pieces of about 150 mm square for cleaning. DIN EN 15973:2011-05 EN 15973:2011 (E) 6 5.9 Soil for dry soiling Soiling cloth1)cut to a diameter 140 mm with following properties: denim with 100 % cotton, 450 g/m

30、(24,5 threads per cm in warp direction, 19,5 threads per cm in weft direction), dyeing with 2,3% indigo blue and 0,5% sulphuric black, soiled with carbon black / olive oil, both at (4 1) g/m. 5.10 Aqueous soil, “instant“ coffee (freeze dried) without sugar2), mixed (2,5 0,1) g coffee to (240 5) ml w

31、ater at 60 C to 80 C and cooled to 40 C. 5.11 Oily soil, paraffin oil (liquid, pure grade, CAS 8012-95-1) containing 0,1 % -carotin (CAS 7235-40-7; purity 95 %). 5.12 Cleaning agent, sodium lauryl ether sulphate (CAS 9004-82-4), 0,5 % solution in water. 5.13 Grey scale, in accordance with EN 20105-A

32、03. 5.14 Other soils and cleaning solutions can be used if requested by the customer, information to be reported. 5.15 Hot air woven, set up to maintain (80 2)C. 6 Preparation and conditioning of test specimens Cut the following specimens for the different procedures: a) for dry soiling: two specime

33、ns 140 mm diameter b) for aqueous soiling: two specimens 100 mm x 100 mm c) for oily soiling: two specimens 100 mm x 100 mm d) for assessment: one specimen about 50 mm x 100 mm Condition the specimens at least 24 h at 20 C and 65 % relative humidity or at 23 C and 50 % relative humidity (according t

34、o EN ISO 2231 respectively, climate A or B). 7 Procedure Perform all described tests in duplicate. 1) “EMPA 128“ is the trade-name of a product supplied by EMPA. This information is given for the convenience of users of this European Standard and does not constitute an endorsement by CEN of the prod

35、uct named. Equivalent products may be used if they can be shown to lead to the same results. 2) “Nescaf Classic“ is the brand-name of a product which has been found suitable. This information is given for the convenience of users of this European Standard and does not constitute an endorsement by CE

36、N of the product named. Equivalent products may be used if they can be shown to lead to the same results. DIN EN 15973:2011-05 EN 15973:2011 (E) 7 7.1 Dry soiling 7.1.1 Carry out the soiling procedure on the abrading table of the Martindale abrasion machine (5.1). Fit the coated textile test specime

37、n backed with the wool felt underlay (5.4) on the abrading table (lower position) with the test side facing upwards as described in EN ISO 12945-2. Check the specimens and backing wool felt are centrally positioned in the clamp of the abrading table. 7.1.2 Fit the soiling cloth (5.9), backed with wo

38、ol felt underlay (5.3), to the pilling holder head (5.2) of the Martindale abrasion machine (5.1) using the auxiliary mandrel device for specimen mounting as described in EN ISO 12945-2. Check for the soiling side of the soiling cloth being on the outside and the cloth and the wool felt underlay are

39、 centrally positioned in the clamp of the holder. The soiling cloth is normally prepared by printing the soiling preparation to one side of the cloth. Be careful that the soiling side is used to rub against the surface of the coated textile. 7.1.3 Adjust the Martindale machine settings for the Lissa

40、jous figure with stroke of (60 1) mm. 7.1.4 Mount the pilling holder with the soiling cloth on the Martindale apparatus. Add immediately the loading piece and run 1000 rubs as defined in EN ISO 12947-1. 7.1.5 Remove the pilling holder with the soiling cloth immediately after finishing 1000 rubs. The

41、 soiling cloth can be discarded. Remove the specimen from the Martindale table. 7.1.6 Place the specimen in the dark for (24 4) h at 20 C and 65 % relative humidity or at 23C and 50 % relative humidity (according to EN ISO 2231 respectively, climate A or B). If required, a part of the soiled specime

42、n can be aged, directly after soiling, (24 0,5) h at (80 2) C in a hot air oven (5.15). After ageing the specimens shall be placed 1 h at 20 C and 65 % relative humidity or at 23 C and 50 % relative humidity (according to EN ISO 2231 respectively, climate A or B) before cleaning. 7.1.7 Clean the spe

43、cimen as described in 7.4, allow it to dry and condition the specimen in the dark for at least 16 h at 20 C and 65 % relative humidity or at 23 C and 50 % relative humidity (according to EN ISO 2231 respectively, climate A or B). Assess the soiled and cleaned specimen as described in 7.5. 7.2 Aqueou

44、s soiling 7.2.1 Place the specimen flat on a glass plate (5.7). Place a 70 mm x 70 mm piece of cotton cloth (5.8) in the centre of the specimen surface. Apply (2,0 0,1) ml of aqueous soil so that all liquid remains uniformly on the cotton cloth. NOTE For mesh fabrics or perforated materials, apply (

45、1,0 0,1) ml, if necessary. This quantity should be reported. 7.2.2 Store the specimen on a glass plate together with the soil and the cotton cloth for (4 0,5) h at 20 C and 65 % relative humidity or at 23 C and 50 % relative humidity (according to EN ISO 2231 respectively, climate A or B). 7.2.3 Rem

46、ove the cotton cloth. Remove carefully any excess soil using a new dry cotton cloth patting the surface of the specimen dry without rubbing. 7.2.4 Clean the specimen as described in 7.4, allow it to dry and condition the specimen in the dark for at least 16 h at 20 C and 65 % relative humidity or at

47、 23 C and 50 % relative humidity (according to EN ISO 2231 respectively, climate A or B). 7.2.5 Assess the soiled and cleaned specimen as described in 7.5. DIN EN 15973:2011-05 EN 15973:2011 (E) 8 7.3 Oily soiling 7.3.1 Place the specimen flat on a glass plate (5.7). Place a 70 mm x 70 mm piece of c

48、otton cloth (5.8) in the centre of the specimen surface. Apply (2,0 0,1) ml of oily soil slowly on the cotton cloth. Take care that all liquid remains on the cotton cloth. NOTE For mesh fabrics or perforated materials, apply (1,0 0,1) ml, if necessary. This quantity shall be reported. 7.3.2 Store the specimen on a glass plate together with the soil and the cotton cloth in the dark for (4 0,5