BS 3424-14-1985 Testing coated fabrics - Method 16 - Methods for determination of colour fastness to wet and dry rubbing and determination of resistance to printwear《涂覆织物试验 方法16 湿摩.pdf

《BS 3424-14-1985 Testing coated fabrics - Method 16 - Methods for determination of colour fastness to wet and dry rubbing and determination of resistance to printwear《涂覆织物试验 方法16 湿摩.pdf》由会员分享，可在线阅读，更多相关《BS 3424-14-1985 Testing coated fabrics - Method 16 - Methods for determination of colour fastness to wet and dry rubbing and determination of resistance to printwear《涂覆织物试验 方法16 湿摩.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS 3424-14: 1985 Testing coated fabrics Part 14: Method 16: Methods for determination of colour fastness to wet and dry rubbing and determination of resistance to printwear IMPORTANT NOTE. It is recommended that this Part be read in conjunction with the information in Part0 “Forewor

2、d and general introduction”. UDC 677.077.652:678.066.2:677.017.474:535.686.2BS3424-14:1985 This British Standard, having been prepared under the directionof the Fibres, Yarns, Fabrics and Production StandardsCommittee, was published under the authority ofthe Board of BSI and comes intoeffect on 29Ma

3、rch1985 BSI 07-1999 The following BSI references relate to the work on this standard: Committee reference FBM/13 Draft for comment 83/36922 DC ISBN 0 580 14053 9 Amendments issued since publication Amd. No. Date of issue CommentsBS3424-14:1985 BSI 07-1999 i Contents Page Foreword ii 1 Scope 1 2 Meth

4、od 16A. Determination of colour fastness to rubbing 1 3 Method 16B. Determination of printwear 2 Figure 1 Test arrangement for determining fastness of colour to rubbing and printwear 2 Figure 2 Details of typical abrading member A 2 Publications referred to Inside back coverBS3424-14:1985 ii BSI 07-

5、1999 Foreword The methods of test described in this Part of BS3424 are for determining the colour fastness of coated fabrics to wet and dry rubbing and for determining the resistance to wear of print superimposed on the surface of the coating polymer. In each case the apparatus is similar to that de

6、scribed in section X12 of BS1006:1978 and method 310B 1)of BS2782:1970. The differences between the apparatus, materials and methods described in this Part of BS3424 and in BS1006 and BS2782 are as follows. In section X12 of BS1006:1978, the frequency of operation of the apparatus is1Hz (i.e.2 strok

7、es per second; one outward and one return stroke) whereas the methods in this Part of BS3424 and in method310B of BS2782:1970 employ a frequency of0.25Hz (i.e.0.5 strokes per second). In section X12 of BS1006:1978 and in method310B of BS2782:1970, the downward force operating on the abrading finger

8、is9N whereas the methods in this Part of BS3424 employ a downward force on the abrading finger of9.8N in the case of colour fastness testing and14.71N in the case of printwear testing. The number of strokes to end point in section X12 of BS1006:1978 is20 whereas the number of strokes to end point in

9、 this Part of BS3424 is40 in the case of colour fastness testing and1000 in the case of printwear testing. The number of strokes to end point using method310B of BS2782:1970 is indeterminate. In addition, the surface area of the base of the brass peg described in method310B of BS2782:1970 is conside

10、rably less than the16mm diameter specified in this Part of BS3424 and in section X12 of BS1006:1978. These differences in apparatus and end point are considered necessary due to the need to operate the apparatus at a speed, namely0.25Hz and in such a manner, i.e.at9.8N downward force over a larger c

11、ross section of area, as will tend to reduce or eliminate frictional heating of thermoplastic coating polymers, thus avoiding the introduction of uncontrolled testing parameters likely to influence the test results. The abradant described in this Part of BS3424 is one which has been chosen, followin

12、g interlaboratory trials, as providing test results compatible with, and only slightly more severe than the abradant described in method310B of BS2782:1970 and BS5790-1 and BS5790-2, providing a double thickness of abradant cloth is mounted over the peg. In addition, the abradant described in this P

13、art of BS3424 has the advantage of being commercially available in the long term and complies with section X12 of BS1006:1978 and ISO105:1978, published by the International Organization for Standardization (ISO). The abradant described in method310B of BS2782:1970 and BS5790 is no longer available

14、commercially. This Part supersedes method16 of BS3424:1973. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from

15、legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, pages1 to 4, an inside back cover and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment

16、table on the inside front cover. 1) BS2782, method310B is currently under review and it is expected that the revision of this method of BS2782, will, when completed, be renumbered as Method826A.BS3424-14:1985 BSI 07-1999 1 1 Scope This Part of BS3424 describes a method for determining the colour fas

17、tness of coated fabrics to wet and dry rubbing and a method for determining the resistance to printwear of coated fabrics having a line print superimposed over the coating polymer. NOTEThe titles of the publications referred to in this standard are listed on the inside back page. 2 Method 16A. Deter

18、mination of colour fastness to rubbing 2.1 Apparatus NOTEFor information on the availability of the test arrangement (2.1.1) and abradant (2.1.2), apply to Enquiry Section (London), British Standards Institution, enclosing a stamped addressed envelope for reply. 2.1.1 Test arrangement (see Figure 1)

19、, consisting of a platform carrying a smooth rigid plate (e.g. a piece of plate glass), B, and clamps, C and D, to hold the specimen securely in position over the rigid plate. A peg (see Figure 2), A, having a circular base of16mm diameter is fixed to an arm which shall be pivoted at a distance of a

20、pproximately230mm from the centre of the peg. The peg shall be fashioned from a material that is hard and unyielding and does not contaminate the abradant, particularly when the abradant is wet. Weight pieces can be applied to the peg so that a total force of9.8N is brought to bear along the normal

21、to the upper face of the rigid plate, B. Means shall be provided for fixing the abradant (2.1.2) to the base of the peg in such a manner that it does not wrinkle during the test. Means shall be provided for reciprocating the peg or platform in simple harmonic motion in a straight line over a stroke

22、length of100mm at a frequency of0.25 0.033Hz (i.e.0.5 0.067strokes per second). NOTEIf uneven wear of the test specimen and abradant is to be avoided, it is important to ensure that the base of the peg and the surface of the rigid plate are parallel and that the periphery of the base edge of the peg

23、 contains no burrs. Parallelism of the surfaces can be ensured, after any necessary adjustments, by operating the apparatus with a suitable grade of emery cloth mounted in the test specimen position until the base of the peg is uniformly abraded. 2.1.2 Abradant, consisting of cotton fabric, desized,

24、 scoured and bleached and free from fluorescent brightening agents, having a fluidity not greater than8, a mass per unit area of92.8g/m 2and a cloth construction of40 ends per centimetre,39 picks per centimetre, in plain weave, avoiding lumps or neps. 2.1.3 Grey scale for assessing staining, in acco

25、rdance with section A03 of BS1006. 2.1.4 Means for viewing, providing viewing conditions in accordance with BS950. 2.2 Preparation of test specimens Cut three pairs of specimens, each230mm 50mm, with their length parallel to the longitudinal direction, from positions evenly spaced over the area of t

26、he sample. NOTEInitially12 pieces of abradant cotton fabric may have to be cut to enable a double thickness of cotton cloth to be mounted on the peg(s) (see2.4), but only the outermost layer coming into contact with the coated fabric specimen needs to be renewed at each test, and subsequent tests wi

27、ll require only six pieces. 2.3 Conditioning Condition, in accordance with method4 (i.e. Part2 ofBS3424), the test specimens and sufficient abradant(2.1.2), to enable a double layer of abradant to be mounted on the peg for conducting three dry rub fastness tests. 2.4 Procedure 2.4.1 Mounting of test

28、 specimens. Select one test specimen from each of the three pairs and secure it over the rigid plate of the test arrangement (2.1.1) with the coated surface to be evaluated uppermost. Ensure that the test specimen will not be prone to wrinkling during the test by applying a slight strain to the spec

29、imen before securing the mounting grips. To do this with coated fabrics having a knitted base cloth it has been found necessary to stretch the test specimen by approximately9%. 2.4.2 Mounting of abradant 2.4.2.1 Fastness to dry rubbing. Secure a fresh piece of the conditioned abradant, with a backin

30、g of a second layer of the abradant to the base of the peg (see Figure 2). 2.4.2.2 Fastness to wet rubbing. Wet out a fresh piece of abradant and a backing of a second layer of the abradant by dropping evenly on to them approximately their own mass of water and secure to the base of the peg (see Fig

31、ure 2). 2.4.3 Operation (dry). Wipe the coated surface of the test specimen with a clean dry cloth to remove any surface dust. Lower the peg on to the test specimen and set the test arrangement in motion. Stop the test arrangement after20 complete cycles (i.e.40strokes). Repeat the operation with on

32、e specimen from each of the two remaining pairs using a fresh piece of abradant for each test. 2.4.4 Operation (wet). Repeat the operation described in2.4.3 using the three remaining test specimens and a clean wetted piece of abradant for each test. 2.4.5 Examination. Allow the wetted pieces of abra

33、dant to dry at room temperature. Assess the staining of the abradant using the grey scale for assessing staining (2.1.3) and the means for viewing(2.1.4).BS3424-14:1985 2 BSI 07-1999 2.4.6 Test report. Report the numerical rating for dry staining and for wet staining of the pieces of abradant for ea

34、ch of the tests. If the results lie between two contrasts on the grey scale, give an intermediate assessment, e.g. “3-4”. If the pieces of abradant are unstained report “unstained”. 3 Method 16B. Determination of printwear 3.1 Apparatus 3.1.1 Test arrangement, as described in2.1.1, except that addit

35、ional weight pieces shall be added to the peg to enable the total downward force brought to bear on the rigid plate to be14.71N instead of9.8N. 3.1.2 Abradant, as described in2.1.2. NOTEInitially, four pieces of abradant may have to be cut to enable a double thickness of cotton cloth to be mounted o

36、n the peg (see2.4), but only the outermost layer coming into contact with the test specimen needs to be renewed at each test and subsequent tests will require only two pieces. 3.1.3 Grey scale for assessing change in colour in accordance with section A02 of BS1006. 3.1.4 Means for viewing, as descri

37、bed in2.1.4. 3.2 Preparation of test specimens Cut two specimens, each230mm 50mm, one with its length parallel to the longitudinal direction of the sample and the other with its length parallel to the transverse direction. 3.3 Conditioning Condition, in accordance with method4 (i.e. Part2 ofBS3424),

38、 the test specimens and sufficient pieces of abradant to allow a double layer of abradant to be mounted on the peg. 3.4 Procedure 3.4.1 Mounting of coated fabric specimens. Mount the test specimens in accordance with2.4.1. 3.4.2 Mounting of bleached cotton abradant. Secure the bleached cotton fabric

39、 to the base of the peg in accordance with2.4.2.1. Figure 1 Test arrangement for determining fastness of colour to rubbing and printwear Figure 2 Details of typical abrading member ABS3424-14:1985 BSI 07-1999 3 3.4.3 Operation. Wipe the coated surface of the test specimen with a clean dry cloth to r

40、emove any surface dust. Lower the peg on to the test specimen and set the test arrangement in motion. Stop the machine after500 cycles (1000 strokes). Repeat the operation using the second test specimen and fresh piece of abradant. 3.4.4 Examination. Assess the degree of surface printwear on the coa

41、ted fabric specimens using the grey scale for assessing change in colour (3.1.3) and the means for viewing (3.1.4). If one specimen exhibits greater printwear than the other, the worst result of the two shall be taken as the test result. 3.4.5 Test report. Report the numerical rating for change in s

42、hade between the abraded and unabraded portions of the test specimen. If the results lie between contrasts on any grey scale, give an intermediate assessment, e.g.“4-5”.4 blankBS3424-14:1985 BSI 07-1999 Publications referred to BS 950, Artificial daylight for the assessment of colour. BS 1006, Metho

43、ds of test for colour fastness of textiles and leather. BS 2782, Methods of testing plastics 2) . BS 3424, Testing coated fabrics. BS 3424-2, Method 4 Conditioning and selection of test specimens. BS 5790, Coated fabrics for upholstery 2) . BS 5790-1, Specification for PVC coated knitted fabrics. BS

44、 5790-2, Specification for PVC coated woven fabrics. ISO 105, Textiles Tests for colour fastness 2) . 2) Referred to in foreword only.BS 3424-14: 1985 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitution BSI is the independent national body responsible for preparing BritishStandar

45、ds. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments or editions. It is the constant

46、aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel:0208

47、9969000. Fax:02089967400. BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Service

48、s. Tel:02089969001. Fax:02089967001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested. Information on standards BSI provides a wide range of information on national,

49、European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002. Fax:02089967001. Copyright Copyright subsists i