ASTM D6873 D6873M-2017 red 3131 Standard Practice for Bearing Fatigue Response of Polymer Matrix Composite Laminates《聚合物基复合层压制品轴承疲劳响应的标准实施规程》.pdf
《ASTM D6873 D6873M-2017 red 3131 Standard Practice for Bearing Fatigue Response of Polymer Matrix Composite Laminates《聚合物基复合层压制品轴承疲劳响应的标准实施规程》.pdf》由会员分享,可在线阅读,更多相关《ASTM D6873 D6873M-2017 red 3131 Standard Practice for Bearing Fatigue Response of Polymer Matrix Composite Laminates《聚合物基复合层压制品轴承疲劳响应的标准实施规程》.pdf(13页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: D6873/D6873M 08 (Reapproved 2014)D6873/D6873M 17Standard Practice forBearing Fatigue Response of Polymer Matrix CompositeLaminates1This standard is issued under the fixed designation D6873/D6873M; the number immediately following the designation indicates theyear of original adoption or
2、, in the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice provides instructions for modifying static bearing test methods t
3、o determine the fatigue behavior of compositematerials subjected to cyclic bearing forces. The composite material forms are limited to continuous-fiber reinforced polymermatrix composites in which the laminate is both symmetric and balanced with respect to the test direction. The range of acceptable
4、test laminates and thicknesses are described in 8.2.1.2 This practice supplements Test Method D5961/D5961M with provisions for testing specimens under cyclic loading. Severalimportant test specimen parameters (for example, fastener selection, fastener installation method, and fatigue force/stress ra
5、tio) arenot mandated by this practice; however, repeatable results require that these parameters be specified and reported.1.3 This practice is limited to test specimens subjected to constant amplitude uniaxial loading, where the machine is controlledso that the test specimen is subjected to repetit
6、ive constant amplitude force (stress) cycles. Either engineering stress or applied forcemay be used as a constant amplitude fatigue variable. The repetitive loadings may be tensile, compressive, or reversed, dependingupon the test specimen and procedure utilized.1.4 The values stated in either SI un
7、its or inch-pound units are to be regarded separately as standard. Within the text theinch-pound units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system mustbe used independently of the other. Combining values from the two systems may result in
8、 nonconformance with the standard.1.4.1 Within the text the inch-pound units are shown in brackets.1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate safety and healt
9、h practices and determine the applicability of regulatorylimitations prior to use.1.6 This international standard was developed in accordance with internationally recognized principles on standardizationestablished in the Decision on Principles for the Development of International Standards, Guides
10、and Recommendations issuedby the World Trade Organization Technical Barriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2D883 Terminology Relating to PlasticsD3878 Terminology for Composite MaterialsD5229/D5229M Test Method for Moisture Absorption Properties and Equilibrium C
11、onditioning of Polymer Matrix CompositeMaterialsD5961/D5961M Test Method for Bearing Response of Polymer Matrix Composite LaminatesE4 Practices for Force Verification of Testing MachinesE6 Terminology Relating to Methods of Mechanical TestingE122 Practice for Calculating Sample Size to Estimate, Wit
12、h Specified Precision, the Average for a Characteristic of a Lot orProcessE177 Practice for Use of the Terms Precision and Bias in ASTM Test MethodsE456 Terminology Relating to Quality and Statistics1 This practice is under the jurisdiction of ASTM Committee D30 on Composite Materials and is the dir
13、ect responsibility of Subcommittee D30.05 on Structural TestMethods.Current edition approved Aug. 1, 2014April 1, 2017. Published September 2014April 2017. Originally approved in 2003. Last previous edition approved in 20082014 asD6873/D6873M 08.D6873/D6873M 08(2014). DOI: 10.1520/D6873_D6873M-08R14
14、.10.1520/D6873_D6873M-17.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standar
15、d and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases o
16、nly the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1E467 Practice for Verification of Constant Amplitude Dynamic Forces in an Axial Fati
17、gue Testing SystemE739 Practice for Statistical Analysis of Linear or Linearized Stress-Life (S-N) and Strain-Life (-N) Fatigue DataE1309 Guide for Identification of Fiber-Reinforced Polymer-Matrix Composite Materials in Databases (Withdrawn 2015)3E1434 Guide for Recording Mechanical Test Data of Fi
18、ber-Reinforced Composite Materials in Databases (Withdrawn 2015)3E1823 Terminology Relating to Fatigue and Fracture Testing3. Terminology3.1 DefinitionsTerminology D3878 defines terms relating to high-modulus fibers and their composites. Terminology D883defines terms relating to plastics. Terminolog
19、y E6 defines terms relating to mechanical testing. Terminology E1823 defines termsrelating to fatigue. Terminology E456 and Practice E177 define terms relating to statistics. In the event of a conflict between terms,Terminology D3878 shall have precedence over the other standards.NOTE 1If the term r
20、epresents a physical quantity, its analytical dimensions are stated immediately following the term (or letter symbol) infundamental dimension form, using the following ASTM standard symbology for fundamental dimensions, shown within square brackets: M for mass,L for length, T for time, for thermodyn
21、amic temperature, and nd for non-dimensional quantities. Use of these symbols is restricted to analyticaldimensions when used with square brackets, as the symbols may have other definitions when used without the brackets.3.2 Definitions of Terms Specific to This Standard:3.2.1 bearing force, P MLT-2
22、, nthe total force carried by a bearing coupon.3.2.2 constant amplitude loading, nin fatigue, a loading in which all of the peak values of force (stress) are equal and all ofthe valley values of force (stress) are equal.3.2.3 fatigue loading transition, nin the beginning of fatigue loading, the numb
23、er of cycles before the force (stress) reachesthe desired peak and valley values.3.2.4 force (stress) ratio, R nd, nin fatigue loading, the ratio of the minimum applied force (stress) to the maximum appliedforce (stress).3.2.5 frequency, f T-1, nin fatigue loading, the number of force (stress) cycle
24、s completed in 1 s (Hz).3.2.6 hole elongation, D L, nthe permanent change in hole diameter in a bearing coupon caused by damage formation,equal to the difference between the hole diameter in the direction of the bearing force after a prescribed loading and the holediameter prior to loading.3.2.7 nom
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
5000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMD6873D6873M2017RED3131STANDARDPRACTICEFORBEARINGFATIGUERESPONSEOFPOLYMERMATRIXCOMPOSITELAMINATES
链接地址:http://www.mydoc123.com/p-523828.html