ASTM B252-1992(2014) Standard Guide for Preparation of Zinc Alloy Die Castings for Electroplating and Conversion Coatings《电镀层和转化涂层用锌合金压模铸件的制备的标准指南》.pdf

《ASTM B252-1992(2014) Standard Guide for Preparation of Zinc Alloy Die Castings for Electroplating and Conversion Coatings《电镀层和转化涂层用锌合金压模铸件的制备的标准指南》.pdf》由会员分享，可在线阅读，更多相关《ASTM B252-1992(2014) Standard Guide for Preparation of Zinc Alloy Die Castings for Electroplating and Conversion Coatings《电镀层和转化涂层用锌合金压模铸件的制备的标准指南》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B252 92 (Reapproved 2014) Endorsed by AmericanElectroplaters SocietyEndorsed by NationalAssociation of Metal FinishersStandard Guide forPreparation of Zinc Alloy Die Castings for Electroplatingand Conversion Coatings1This standard is issued under the fixed designation B252; the number i

2、mmediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 T

3、his guide is intended as an aid in establishing andmaintaining a procedure for preparing zinc alloy die castingsfor electroplating and conversion coatings. It is primarilyintended for the preparation of Alloys UNS Z33521 (AG-40A)and UNS Z35530 (AC-41A) (Specification B86) for electro-plating with co

4、pper, nickel, and chromium (SpecificationB456).1.2 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility

5、 of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2B6 Specification for ZincB86 Specification for Zinc and Zinc-Aluminum (ZA) AlloyFoundry and Die Casti

6、ngsB456 Specification for Electrodeposited Coatings of CopperPlus Nickel Plus Chromium and Nickel Plus Chromium2.2 Military Standard:MIL-S-13165C Shot Peening of Metal Parts33. Summary of Practice3.1 The normal sequence of preparation steps is as follows:(1) smoothing of parting lines; (2) smoothing

7、 of rough ordefective surfaces, if necessary; (3) buffing, if necessary; (4)precleaning and rinsing; (5) alkaline electrocleaning and rins-ing; (6) acid dipping and rinsing; and (7) copper striking.4. Significance and Use4.1 The performance and quality of electroplated orconversion-coated zinc alloy

8、 die casting depends upon thesurface cleanliness and condition. Various metals are electro-plated or conversion coatings are established on zinc alloys fordecorative or engineering finish. The common electroplatesapplied are usually copper, nickel, and chromium for decora-tive and functional uses. T

9、he common conversion coatingsapplied are phosphates, chromates, and anodized coatings.Electroplated zinc die castings and conversion coatings on zincdie castings are used in many industries such as the marine,automotive, plumbing fixtures, and appliance industries.5. Composition and Characteristics

10、of Zinc Alloy DieCastings5.1 The alloys used in the manufacture of zinc alloy diecastings are made with special high-grade zinc conforming toSpecification B6, alloyed with about 4 % of aluminum, 0.04 %of magnesium, and either 0.25 (max) or 1.0 % copper (AlloysUNS Z33521 and UNS Z35530). Impurities s

11、uch as lead,cadmium, tin, and iron are held at or below the specified lowlevels in Specification B86.5.2 Die castings made of Alloys UNS 233521 and UNS235530 are usually dense and fine grained but do not alwayshave smooth surfaces. Defects sometimes encountered in thesurface layers include cracks, c

12、revices (cold shut), skin blisters,and hemispherical pores. Burrs are usually left at parting lineswhere fins and gates are removed by die trimming.5.3 Cast surfaces are frequently contaminated with partingcompounds applied at frequent intervals to die surfaces tofacilitate the ejection of the casti

13、ngs and with water-solubleoils added to quenching tanks for corrosion inhibition.1This guide is under the jurisdiction of ASTM Committee B08 on Metallic andInorganic Coatings and is the direct responsibility of Subcommittee B08.02 on PreTreatment.Current edition approved Nov. 1, 2014. Published Nove

14、mber 2014. Originallyapproved in 1951. Last previous edition approved in 2009 as B252 92 (2009).DOI: 10.1520/B0252-92R14.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refe

15、r to the standards Document Summary page onthe ASTM website.3Available from Standardization Documents Order Desk, Bldg. 4 Section D, 700Robbins Ave., Philadelphia, PA 19111-5094, Attn: NPODS.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United St

16、ates15.4 Zinc alloy die castings are chemically active and aredissolved or etched during prolonged contact with concentratedsolutions of many mineral or organic acids or strongly alkalinesolutions with a pH greater than 10. Immersion periods in suchsolutions should be of short duration to avoid roug

17、hening.6. Smoothing of Parting Lines6.1 Parting lines are smoothed by (1) mechanical polishingwith abrasive-coated wheels or belts, (2) tumbling with abra-sive media, or (3) vibration with abrasives.6.2 Abrasives with a size range of 220 to 300 mesh glued oncloth wheels or continuous cloth belts tha

18、t run over flexibleback-up wheels are usually used for mechanical polishing ofparting lines. Wheel diameters range from 5 to 40 cm,depending on the complexity of the shape. Wheels are rotatedwith a minimum peripheral speed of 2500 m/min. A peripheralspeed of 2100 m/min should not be exceeded with be

19、lts. Lowerspeeds of the order of 1100 to 1400 m/min are fairly commonfor small die castings polished on small diameter wheels.Abrasive belts should not be used dry but should be lubricatedwith a small amount of grease. Die castings usually are handledindividually to polish parting lines smooth. This

20、 may require30 s or less for small castings, and sometimes 5 or 6 min forlarger ones.6.3 Tumbling in horizontal barrels, loaded with abrasivestones such as limestone, preformed and fused aluminumoxide, ceramic shapes or abrasive-loaded plastic chips, and alubricant such as soap or detergent solution

21、, removes parting-line burrs from die castings in 4 to 12 h. The barrels may berotated at 4 r/min. Higher speeds reduce the time cycles andcosts, but also increase the danger of impingement of partsagainst zinc surfaces. A hexagonal barrel with a capacity of 0.5m3can be loaded with 450 kg of abrasiv

22、e stones or chips and90 kg of zinc die castings.6.4 Vibration in a bed of resin-bonded abrasive chipsremoves parting-line burrs, typically in 1 to 4 h. Frequenciesrange from 700 to 2100 cpm and amplitudes from 0.8 to 6.4mm. A vibrating tub with a capacity of 0.5 m3can be loadedwith about 900 kg of a

23、brasive media and 180 kg of zinc diecastings. A dilute solution of detergent or soap is continuouslymetered through the bed of media and parts to keep theirsurfaces clean and maximize surface smoothing. Parting linesmay be mechanically polished before vibratory processingwhen a large amount of flash

24、 must be removed.7. Smoothing of Rough or Defective Surfaces7.1 Rough or defective surfaces are smoothed by (1) me-chanical polishing on rotating wheels or continuous, abrasive-coated belts, (2) spin finishing, (3) vibratory finishing, or (4)controlled shot peening. Fissures, skin blisters, and othe

25、rdefects with a depth of 25 to 50 m can usually be erased withthese metal-removal methods. Deeper defects are infrequent.7.2 Mechanical polishing for smoothing rough or defectivesurfaces is similar to mechanical polishing for smoothingparting line areas (see 6.2). Parting lines and rough or defectiv

26、esurfaces are frequently polished by the same operator. Ifpolishing is mechanized to advance die castings attached to aconveyor through successive belts or wheels to polish differentareas, a manual operation may be required later to complete thesmoothing of parting lines if they are too curved. The

27、finishranges from 0.2 to 0.6 m, depending on the abrasive and thepressure.7.3 Smoothing by spinning in abrasives is accomplished byattaching die castings to spindles or drums rotated with aperipheral speed of about 600 m/min in a slurry of abrasivematerial such as ground corn cobs or nut shells mixe

28、d with asmall amount of grease or other lubricant. Times usually rangefrom 5 to 10 min and the finish from 0.1 to 0.2 m, dependingon the abrasive.7.4 Vibrating tubs loaded with plastic chips (such as poly-urethane) impregnated with an abrasive (such as aluminumoxide) smooth the surfaces of die casti

29、ngs in 2 to 4 h whenfrequencies are in the range of 1700 to 2100 cpm andamplitudes are adjusted to 3.2 to 6.4 mm. Vibratory machinesproduce a finish of 0.15 to 0.25 m, with a cutting rate of 5m/h. A smoother finish of 0.075 to 0.125 m can be obtainedwith plastic media containing finer abrasive, whic

30、h removesmetal at a slower rate. Media and zinc parts are usually loadedwith a ratio of 5:1 or 6:1. Surface gouges may occur with asmaller ratio.7.5 Controlled shot peening will plastically deform anddensify the casting surface and near-surface layers. Shotpeening can seal surface pores, which can c

31、reate problems inelectroplating and conversion coating. The process is describedin MIL-S-13165C. The process is also effective in removingfins, burrs, and flash from the surface. The castingconfiguration, including the smallest size radii and wallthickness, as well as the required finish and contami

32、nationlimits, will dictate the proper selection of peening media, shotsize, intensity, and coverage, as is detailed in MIL-S-13165C.8. Buffing8.1 Die castings are buffed to produce a mirror-like finish,suitable for plating with conventional solutions, when goodleveling plating solutions are not avai

33、lable. Buffing can beomitted, however, for die castings which have good surfaces orwhich can be uniformly polished to a finish of 0.25 m, ifsolutions with good leveling power are used for plating copperand nickel.8.2 Die castings are buffed on cloth wheels rotated at aperipheral speed not exceeding

34、2150 m/min. Slower speeds, ofthe order of 1100 to 1600 m/min, are used for small diecastings. Buffing compounds should be made with a binder thatis readily emulsified or saponified during alkaline cleaning.The abrasive may be tripoli (amorphous silica) or lime, mixedwith about 25 % of tallow or othe

35、r lubricants. Compoundssuspended in a liquid are preferred for automatic buffingmachines that advance die castings through a succession ofbuffs of varying diameter and width, which individuallysmooth different surface areas. Buffs are usually made of clothwith a thread count of 34 to 37/cm.Afinish o

36、f 0.025 to 0.05 mcan be produced by buffing. The smoothing rate is influencedby the temperature of the metal surface (faster at approximately150C than at lower temperatures).B252 92 (2014)28.3 After buffing, surfaces with impacted buffing compoundcan be improved by passing them over a dry wheel to r

37、emovebuffing compound. This will reduce the demand placed on theprecleaning solution.9. Precleaning and Rinsing9.1 It is strongly recommended that the preliminary removalof most of the buffing compound and other soil in a precleaningoperation be done as soon as possible after buffing andpolishing. M

38、ost buffing compounds become substantially moredifficult to remove after aging several days.9.2 There are several methods by which soils can beremoved from zinc die castings prior to final alkaline electro-cleaning. Generally speaking, these fall into three main classes:solvent degreasing, emulsion

39、cleaning, and cleaning withaqueous base detergents.9.2.1 Solvent DegreasingBefore considering the use ofsolvent degreasing, federal and state safety and environmentallaws and regulations should be consulted. Many of the com-monly used solvents are now being banned from use. Exposureto their vapors (

40、VOC) is being strictly regulated for health,safety, and environmental reasons. Current safe exposure levelsfor various solvents should be obtained before use. Coldsolvents, such as mineral spirits, methylene chloride,trichloroethylene, perchloroethylene and trichloroethane, areused with brushing to

41、loosen packed buffing compound, butthis method usually is not practical for mass productionconditions. Simple dipping in cold solvent is often ineffective.Vapor degreasing4with trichloroethylene or perchloroethyleneis widely practiced. Often the buffed die castings are sprayedwith, or immersed in, h

42、ot solvent for mechanical removal ofheavy soil deposits. This is followed by condensation of hot,clean solvent vapors on the work; this removes the last tracesof grease and compound. The method is very effective,provided adequate measures are taken to remove the very fineabrasive and metallic partic

43、les from the work. Trichloroethyl-ene and perchloroethylene are nonflammable as used in vapordegreasing and still must be used in systems designed toprotect personnel from inhalation of vapors. Suppliers ofsolvents should be consulted as to the safety of a giveninstallation.9.2.1.1 All federal, stat

44、e, and local regulations for thedisposal of solvents should be followed.9.2.2 Emulsion Cleaning:9.2.2.1 Impacted buffing compound may be loosened, and tosome extent removed, by immersion in various hydrocarbon-water emulsions. These emulsions are available in severalforms, including unstable emulsio

45、ns (diphase cleaners), inverttype emulsions, mixtures of emulsions and alkaline cleaners,and stable emulsions. Such emulsion cleaners usually have asuitable hydrocarbon base such as kerosene or a higherflashpoint solvent to which is added emulsifiers, soaps, andinhibitors to prevent etching of the d

46、ie castings. The pH of theemulsion cleaner should be kept between 7 and 10 to avoiddamage to the castings.9.2.2.2 These emulsions normally are used hot, about 80C,as a soak, sometimes with agitation, for about 2 to 5 min. Awarm water spray rinse should follow the emulsion soakcleaning. Buffing compo

47、und not removed in the emulsion soakis sufficiently softened so that it is easily removed in analkaline spray wash operation that normally follows.9.2.2.3 Emulsion cleaning is an effective method for remov-ing buffing compound. Its principal disadvantage is the dangerof carryover of hydrocarbon solv

48、ent into plating baths becauseof incomplete rinsing. For this reason, it is very important thatproper alkaline cleaning and rinsing follow to ensure solventremoval from blind holes, defects in rack coatings, andrecesses.9.2.2.4 All federal, state, and local regulations for the useand disposal of sol

49、vents should be followed.9.2.3 Aqueous Base DetergentsIn recent years, hot mix-tures of emulsifiers and surfactants (wetting agents), some-times combined with mild alkaline phosphates or borates, areused for soak cleaning to soften and remove buffing compound.Combining soak cleaning with ultrasonics is particularly effec-tive on impacted buffing compound. Such detergent soaksshould be followed by spray cleaning with an alkaline cleaner.If a spray cleaning step is not needed, then the soak cleaningstep should be followed by a spray rinse with warm waterbefore electroclea