ASTM A810-2001(2008) Standard Specification for Zinc-Coated (Galvanized) Steel Pipe Winding Mesh.pdf

《ASTM A810-2001(2008) Standard Specification for Zinc-Coated (Galvanized) Steel Pipe Winding Mesh.pdf》由会员分享，可在线阅读，更多相关《ASTM A810-2001(2008) Standard Specification for Zinc-Coated (Galvanized) Steel Pipe Winding Mesh.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A 810 01 (Reapproved 2008)Standard Specification forZinc-Coated (Galvanized) Steel Pipe Winding Mesh1This standard is issued under the fixed designation A 810; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year o

2、f last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers various designs of welded wiremesh or twisted (woven) hexagonal wire mesh, zinc coatedbefo

3、re fabrication, to be used as reinforcement for the concreteapplied in the manufacture of negative buoyancy pipe neededfor laying pipe in marshes or in water. The mesh is also usedas reinforcement for concrete applied to pipe as a bendable ornonbendable mechanical protective coating when laying pipe

4、in a harsh environment.1.2 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forinformation only.1.3 The text of this standard references notes and footnotesthat provide explanatory material. These notes and footnotes(excluding those in tabl

5、es and figures) shall not be consideredas requirements of the standard.2. Referenced Documents2.1 ASTM Standards:2A 90/A 90M Test Method for Weight Mass of Coating onIron and Steel Articles with Zinc or Zinc-Alloy CoatingsA 370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA 64

6、1/A 641M Specification for ZincCoated (Galvanized)Carbon Steel WireA 902 Terminology Relating to Metallic Coated Steel Prod-uctsB6 Specification for Zinc3. Terminology3.1 DefinitionsFor definitions of terms used in this speci-fication, see Terminology A 902.4. Classification4.1 The steel pipe windin

7、g mesh is classified by type, basedon method of manufacture, and by design number, related towidth, number of longitudinal wires, and wire sizes.4.2 Types of Fabric:4.2.1 Type TWFabric manufactured by twisting wires toform a mesh with a series of hexagonal openings, as shown inFig. 1. One of the edg

8、es of the fabric includes a straight selvagewire. Additional longitudinal reinforcing wires are includedwhen specified.4.2.2 Type WWFabric manufactured by welding a seriesof longitudinal wires to transverse wires to form a mesh withrectangular openings.4.2.2.1 Type WW-CType WW fabric having uniforms

9、pacing of longitudinal wires, with the longitudinal wirescrimped as indicated in Fig. 2.4.2.2.2 Type WW-NType WW fabric having nonuniformspacing of longitudinal wires, by having the space between theedge wire and adjacent longitudinal wire double the spacing ofthe intermediate longitudinal wires. Al

10、l longitudinal wires arecrimped as indicated in Fig. 3.4.2.2.3 Type WW-SType WW fabric having straight lon-gitudinal wires (without crimping), with uniform spacing asindicated in Fig. 4.4.3 Design NumbersThe design number is in the form ofA 3 B 3 C 3 D.4.3.1 For Type TW fabric, where1This specificat

11、ion is under the jurisdiction of ASTM Committee A05 onMetallic-Coated Iron and Steel Products and is the direct responsibility ofSubcommittee A05.12 on Wire Specifications.Current edition approved Nov. 1, 2008. Published December 2008. Originallyapproved in 1983. Last previous edition approved in 20

12、01 as A 810 - 01.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harb

13、or Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.A = nominal width of wire mesh fabric, in inches (milli-metres),B = number of straight reinforcing wires, not including thestraight selvage wire,C = nominal diameter of wire in hexagonal mesh andstraight selvage wire, in inches (

14、millimetres), andD = nominal diameter of straight reinforcing wires, notincluding straight selvage wire, in inches (millimetres).(Example: 7.5 3 1 3 0.054 3 0.048.)4.3.2 For Type WW fabric, whereA = nominal overall width of wire mesh fabric, in inches(millimetres),B = number of longitudinal wires,C

15、= nominal diameter of longitudinal wires, in inches(millimetres), andD = nominal diameter of transverse wires, in inches (mil-limetres). (Example: 7.5 3 8 3 0.063 3 0.063.)5. Ordering Information5.1 Orders for zinc-coated steel pipe winding mesh underthis specification shall include the following in

16、formation, asnecessary to adequately describe the desired product:5.1.1 Name of material (steel pipe winding mesh),FIG. 1 Type TWTwisted Hexagonal Mesh (Design Number 7.5 30 3 0.054 3 0)FIG. 2 Type WW-CCrimped Welded Mesh with UniformLongitudinal Wire SpacingFIG. 3 Type WW-NCrimped Welded Mesh with

17、Non-UniformLongitudinal Wire SpacingFIG. 4 Type WW-SWelded Mesh with Straight LongitudinalWiresA 810 01 (2008)25.1.2 ASTM designation and year of issue,5.1.3 Type of fabric (see 4.2),5.1.4 Design number (see 4.3 and Tables 1 and 2),5.1.4.1 Mesh dimensions for welded mesh (see 9.3 andTable 3),5.1.5 Z

18、inc coating class (see 8.1),5.1.6 Quantity (number of rolls),5.1.7 Width of fabric and length of rolls, and5.1.8 Packaging (see Section 14).6. Materials6.1 The steel from which the wire is produced shall be madeby any commercially accepted steelmaking process.6.1.1 The base metal shall be a steel ha

19、ving composition topermit drawing to a finished size and also to ensure freedomfrom zinc flaking during weaving or welding into mesh.6.1.2 Wire for Welded MeshBefore welding the galva-nized wire shall have a minimum tensile strength of 70 000 psi(483 MPa),6.1.3 Wire for Hexagonal Woven MeshBefore we

20、avingthe galvanized wire shall have a maximum tensile strength of75 000 psi (515 MPa),6.2 Slab zinc used for the coating shall be any grade of zincconforming to Specification B6.7. Manufacture7.1 Hexagonal Woven MeshThis fabric is manufacturedby twisting wires to form a series of openings, hexagonal

21、 inshape, as specified in Table 1 and Fig. 1. One of the edges ofthe fabric shall be constructed to include a selvage wire. Inaddition to those specified in Table 1 and Fig. 1, other designs(width and other reinforcing wire configurations) are subject toagreement between the purchaser and manufactur

22、er.7.2 Welded MeshThis fabric is manufactured by weldinga series of parallel longitudinal wires to transverse wires toform rectangular openings. The longitudinal wires shall becrimped or not crimped as indicated for the type specified.Crimping shall be as indicated in Fig. 2. In addition to thosespe

23、cified in Table 2, and Figs. 2-4, other designs (width andlongitudinal wire configurations) are subject to agreementbetween the purchaser and manufacturer.8. Coating Requirements Coating Requirements8.1 The zinc coating shall be Class 1 coating, or shall be“regular coating”, whichever is specified i

24、n the purchase order.8.1.1 Class 1 zinc coating shall be as specified in Specifi-cation A 641/A 641M.8.1.2 Zinc-coated wire produced as “regular coating” shallhave the full surface covered with zinc, but there is no specifiedminimum weight of coating.8.2 Slight burning of the zinc coating at welded

25、intersec-tions of welded mesh shall not be cause for rejection.9. Dimensions and Permissible Variations9.1 Width of FabricHexagonal mesh fabric is usuallyavailable in 712-in. (190-mm) width. Welded mesh fabric,crimped, is usually available in 7-in. (178-mm) width having amaximum width of 712 in. (19

26、0 mm) including crimp. Non-crimped welded mesh fabric is usually available in 8-in.(203-mm) width. Other widths of woven and welded fabricsare available. Nominal width of fabric shall be as agreed uponbetween the purchaser and manufacturer.9.2 Length of RollNominal length of rolls shall be asagreed

27、upon between the purchaser and manufacturer.9.3 Standard openings in Type TW mesh, between adjacentwires parallel to the selvage wire, is shown in Fig. 1. Standardspacing for longitudinal wires in Type WW-C, Type WW-N,and Type WW-S mesh is shown in Figs. 2-4, respectively.Standard spacing for transv

28、erse wires in Type WW fabrics isshown in Table 3. All measurements are center to center ofwires. Spacing other than indicated are subject to agreementbetween the purchaser and manufacturer.9.4 Tolerances:9.4.1 Width:9.4.1.1 Hexagonal MeshActual width between outerwires shall not be more than12 in. (

29、13 mm) under the specifiedwidth.9.4.1.2 Welded MeshActual width between outer wiresshall not be more than1364 in. (5 mm) under the specifiedwidth.9.4.2 LengthActual length shall be ordered length 0,+3 %.9.4.3 Mesh Size:9.4.3.1 For hexagonal mesh, the tolerance shall be 618 in.(63.2 mm).9.4.3.2 Welde

30、d mesh size tolerances shall be in accordancewith Table 3.9.4.4 Wire Size:TABLE 1 Standard Sizes and Constructions for Type TW Woven Hexagonal MeshDesign NumbersPrevious DesignNumbersNominal Width,in. (mm)Nominal Diameter ofZinc-Coated Wire,in. (mm)Nominal Cross SectionalArea Per Nominal Width,in.2(

31、mm2)ANominal Cross SectionalArea Per Foot (Meter) ofWidth,in.2(mm2)AB7.5 3 0 3 0.054 3 0 10712 3 112 3 17 712 (190) 0.054 (1.37) 0.0252 (16.26) 0.0430 (91.02)7.5 3 1 3 0.054 3 0.048C20712 3 112 3 1718C712 (190) 0.054 (1.37)/0.048 (1.22) 0.0270 (17.42) 0.0489 (103.51)7.5 3 2 3 0.054 3 0.048D30712 3 1

32、12 3 1718D712 (190) 0.054 (1.37)/0.048 (1.22) 0.0287 (18.52) 0.0519 (109.86)7.5 3 4 3 0.054 3 0.048E50712 3 112 3 1718E712 (190) 0.054 (1.37)/0.048 (1.22) 0.0323 (20.84) 0.0580 (122.77)14.25 3 4 3 0.054 3 0.048F51414 3 112 3 1718F1414 (362) 0.054 (1.37)/0.048 (1.22) 0.0529 (34.13) 0.0475 (100.55)ABa

33、sed on nominal diameter.BIncludes minimum12-in. (12.70-mm) lap of mesh as applied.CPlus 0.048 in. (1.22 mm) line wire placed 412 in. (114.30 mm) from selvage.DPlus 0.048 in. (1.22 mm) line wires placed 3 in. (76.20 mm) and 6 in. (152.40 mm) from selvage.EPlus 0.048 in. (1.22 mm) line wires placed 11

34、2 in. (38.10 mm), 3 in. (76.20 mm), 412 in. (114.30 mm), and 6 in. (152.40 mm) from selvage.FPlus 0.048 in. (1.22 mm) line wires placed 3 in. (76.20 mm), 6 in. (152.40 mm), 9 in. (228.60 mm), and 12 in. (304.80 mm) from selvage.A 810 01 (2008)39.4.4.1 Permissible variation of the nominal diameter of

35、wire shall be as follows:0.035 in. (0.89 mm) to under 0.076 in. (1.93 mm) 6 0.002 in. (0.05 mm)0.076 in. (1.93 mm) and over 6 0.003 in. (0.08 mm)10. Sampling and Testing10.1 For test purposes, one sample shall be taken from oneroll selected at random from each 200 rolls or fraction thereof.10.1.1 De

36、velopment of cross-sectional area data shall comefrom these samples.10.1.2 Because of the distortion inherent in the manufactur-ing of the mesh, it is normal to test for coating weight andtensile compliance on samples of wire before fabrication. Thenumber of test specimens will vary with the quality

37、 controlprocedures and facilities of each manufacturer.10.2 Determine the weight of zinc coatings for wire speci-fied to have a Class 1 coating, by the stripping test inaccordance with Test Method A 90/A 90M. Inspect wire speci-fied to have a “regular coating” to verify that the wire iscompletely co

38、ated (except for slight burning at welded inter-sections for wire inspected after fabrication).10.2.1 For wire tested before fabrication, the minimum testspecimen length shall be 24 in. (600 mm).10.2.2 For wire tested after fabrication, cut short lengths ofwire from between twists or welds, such tha

39、t the total lengthequals at least 24 in. (600 mm).10.3 Tensile testing shall be as described in Test Methodsand Definitions A 370.11. Retests and Rejection11.1 If one or more of the samples fail to show compliancewith any of the requirements of this specification, the lot shallbe subjected to retest

40、.11.2 Retesting of the lot shall be on the basis of a samplingfrequency of one sample for each 50 rolls. If any sample failsto show compliance with the requirements of this specification,the entire lot shall be rejected.12. Inspection12.1 The manufacturer shall afford the inspector represent-ing the

41、 purchaser all reasonable facilities to satisfy the inspec-tor that the material is being furnished in accordance with thisspecification. All tests and inspections shall be made at theplace of manufacture before shipment, unless otherwise speci-fied, and be conducted so as not to interfere unnecessa

42、rily withthe operation of the works.13. Certification13.1 When specified in the purchase order or contract, thepurchaser shall be furnished certification that the samplesrepresenting each lot have been either tested or inspected asdirected in this specification and that the requirements havebeen met

43、. When specified in the purchase order or contract, areport of the test results shall be furnished.14. Packaging, Marking, and Loading14.1 Packaging will be based on negotiations between thepurchaser and the manufacturer. Banding or strapping with orwithout pallets represents a common form of packag

44、e.14.2 A tag shall be securely attached to each bundle andshall be marked with the type, design number, wire sizes,ASTM designation, and name or mark of the manufacturer.15. Keywords15.1 concrete reinforcement; mesh (for steel pipe/tube);steel wire; zinc-coated steel wireTABLE 2 Standard Sizes and C

45、onstructions For Type WW Welded Wire MeshDesign NumbersPrevious DesignNumbersNominal Diameter of Zinc-CoatedWire, in. (mm)Nominal Cross Sectional Area PerNominal Width, in.2(mm2)ANominal Cross Sectional Area perFoot (Metre) of Width, in.2(mm2)ABType WW-CUniform SpacingCrimped7.5 3 8 3 0.059 3 0.059

46、1.50 3 1.50 0.059 (1.50)/0.059 (1.50) 0.0219 (14.13) 0.0373 (78.96)7.5 3 8 3 0.063 3 0.063 1.60 3 1.60 0.063 (1.60)/0.063 (1.60) 0.0249 (16.06) 0.0426 (90.17)7.5 3 8 3 0.079 3 0.063 2.00 3 1.60 0.079 (2.00)/0.063 (1.60) 0.0392 (25.29) 0.0669 (141.61)7.5 3 8 3 0.079 3 0.079 2.00 3 2.00 0.079 (2.00)/0

47、.079 (2.00) 0.0392 (25.29) 0.0669 (141.61)7.5 3 8 3 0.098 3 0.079 2.50 3 2.00 0.098 (2.50)/0.079 (2.00) 0.0603 (38.90) 0.1030 (218.03)7.5 3 8 3 0.118 3 0.079 3.00 3 2.00 0.118 (3.00)/0.079 (2.00) 0.0875 (56.45) 0.1493 (316.03)Type WW-NNon-uniform SpacingCrimped7.5 3 6 3 0.063 3 0.063 . . . 0.063 (1.

48、60)/0.063 (1.60) 0.0187 (12.06) 0.0374 (79.16)7.5 3 6 3 0.079 3 0.063 . . . 0.079 (2.00)/0.063 (1.60) 0.0294 (18.97) 0.0588 (124.46)7.5 3 6 3 0.098 3 0.079 . . . 0.098 (2.50)/0.079 (2.00) 0.0453 (29.23) 0.0905 (191.56)7.5 3 6 3 0.118 3 0.079 . . . 0.118 (3.00)/0.079 (2.00) 0.0656 (42.32) 0.1312 (277

49、.71)Type WW-SUniform SpacingNot Crimped8 3 9 3 0.079 3 0.079 14 3 14 0.079 (2.00)/0.079 (2.00) 0.0446 (28.80) 0.0685 (145.06)ABased on nominal diameter.BIncludes minimum12-in. (12.70-mm) lap of mesh for Types WW-C and WW-S, and 1-in. (25.4-mm) lap of mesh for Type WW-N, as applied.TABLE 3 Welded Mesh Sizes and TolerancesNOTE 1Mesh sizes are measured from center to center and alwaysindicated by two figures, L 3 S, where L = the distance between thelongitudinal wires, in. (mm).NOTE 2Crimp depth12 in. (12.7 mm), tolerance 618 i