ASTM A1049 A1049M-2006 Standard Specification for Stainless Steel Forgings Ferritic Austenitic (Duplex) for Pressure Vessels and Related Components《压力容器和相关元件用铁素体 奥氏体(双重)不锈钢锻件的标准规范》.pdf

《ASTM A1049 A1049M-2006 Standard Specification for Stainless Steel Forgings Ferritic Austenitic (Duplex) for Pressure Vessels and Related Components《压力容器和相关元件用铁素体 奥氏体(双重)不锈钢锻件的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A1049 A1049M-2006 Standard Specification for Stainless Steel Forgings Ferritic Austenitic (Duplex) for Pressure Vessels and Related Components《压力容器和相关元件用铁素体 奥氏体(双重)不锈钢锻件的标准规范》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A 1049/A 1049M 06Standard Specification forStainless Steel Forgings, Ferritic/Austenitic (Duplex), forPressure Vessels and Related Components1This standard is issued under the fixed designation A 1049/A 1049M; the number immediately following the designation indicates theyear of origina

2、l adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers ferritic/austenitic (duplex)stainless s

3、teel forgings for boilers, pressure vessels, and asso-ciated equipment in grades that are also found in SpecificationA 182/A 182M.1.2 The purchaser may specify in the order or contract anyappropriate supplementary requirements that are provided inSpecification A 788/A 788M.1.3 Unless the order speci

4、fies the applicable “M” specifica-tion designation the material shall be furnished to the inch-pound units.1.4 The values stated in either inch-pound or SI (metric)units are to be regarded separately as standard. Within the textand tables, the SI units are shown in brackets. The values statedin each

5、 system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in nonconformancewith the specification.2. Referenced Documents2.1 ASTM Standards:2A 182/A 182M Specification for Forged or Rolled Alloyand Stainless

6、Steel Pipe Flanges, Forged Fittings, andValves and Parts for High-Temperature ServiceA 370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA 388/A 388M Practice for Ultrasonic Examination ofHeavy Steel ForgingsA 745/A 745M Practice for Ultrasonic Examination ofAus-tenitic Steel F

7、orgingsA 788/A 788M Specification for Steel Forgings, GeneralRequirementsA 923 Test Methods for Detecting Detrimental IntermetallicPhase in Duplex Austenitic/Ferritic Stainless SteelsE 165 Test Method for Liquid Penetrant ExaminationG48 Test Methods for Pitting and Crevice Corrosion Re-sistance of S

8、tainless Steels and Related Alloys by Use ofFerric Chloride Solution2.2 Other Standards:ASME Boiler and Pressure Vessel Code3NACE MR0175/ISO15156 Petroleum and Natural GasIndustriesMaterials for Use in H2SContaining Envi-ronments in Oil and Gas Production43. Ordering Information and General Requirem

9、ents3.1 Material supplied to this specification shall conform tothe requirements of Specification A 788/A 788M, which out-lines additional ordering information, manufacturing require-ments, testing and retesting methods and procedures, marking,certification, product analysis variations, and addition

10、al supple-mentary requirements.3.1.1 If the requirements of this specification are in conflictwith the requirements of Specification A 788/A 788M, therequirements of this specification shall prevail.3.1.2 The purchaser may require that the forging be ma-chined to an approved heat treatment drawing i

11、ndicating theproposed configuration of the forging at the time of thespecified solution heat treatment.3.1.3 The purchaser may approve the use of an alternateliquid quenching medium for cooling from the solution treat-ment temperature.3.2 The purchaser shall specify the acceptance criteria foreither

12、 Methods B or C of Test Methods A 923, if supplemen-tary requirement S1 is selected.3.3 The purchaser shall specify the required minimumpitting resistance equivalent number (PREN) value determinedaccording to the applicable equation in Table 1.3.4 When Practice A 745/A 745M is the basis for ultrason

13、icexamination in accordance with 7.1, the purchaser shall specifywhether Quality levels 1 or 2 form the basis for acceptance.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.06 on Steel

14、 Forgings and Billets.Current edition approved Sept. 1, 2006. Published September 2006.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summar

15、y page onthe ASTM website.3Available from American Society of Mechanical Engineers (ASME), ASMEInternational Headquarters, Three Park Ave., New York, NY 10016-5990.4Available from National Association of Corrosion Engineers (NACE), 1440South Creek Dr., Houston, TX 77084-4906.1Copyright ASTM Internat

16、ional, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Supplementary requirement S4 permits the purchaser tospecify Practice A 388/A 388M in lieu of Practice A 745/A 745M, in which case the purchaser must also specify theacceptance criteria.3.5 When Supplementary

17、requirement S3, for pitting corro-sion testing, of Test Methods G48is specified, the purchasershall identify the method and test temperature to be used.3.6 When Supplementary requirement S5 for the liquidpenetrant examination of forgings in the final machined con-figuration is specified, the purchas

18、er shall specify the necessaryacceptance criteria, if the requirements of S19 in SpecificationA 788/A 788M are not sufficient.4. Materials and Manufacture4.1 Steel melting and forging shall be in accordance withSpecification A 788/A 788M.4.2 Heat Treatment:4.2.1 Forgings may be machined before solut

19、ion annealingat the manufacturers option, unless the purchaser requires thatmachining to a prescribed configuration be done before heattreatment (see 3.2).4.2.2 All forgings shall be reheated to the required tempera-ture for solution treatment followed, unless otherwise agreedwith the purchaser, by

20、water quenching. With the purchasersconsent (see 3.1.3) some other liquid quenching medium maybe used to rapidly cool the forging.4.2.3 The solution treatment temperature is dependant onthe ordered Grade or composition (UNS number) and shall beas listed in Table 2.4.2.4 The forgings shall be held at

21、 the specified solutiontreatment temperature for a minimum of 30 min per inch ofmaximum heat-treated section thickness.5. Chemical Requirements5.1 The heat analysis taken in accordance with SpecificationA 788/A 788M shall comply with Table 1 for the orderedGrade.5.2 A PREN value is included as a req

22、uirement in Table 1depending on the specified Grade and this will further restrictthe chemical requirements.5.3 The manufacturer shall use the product analysis provi-sions of Specification A 788/A 788M to obtain a productanalysis from a forging representing each heat or multiple heat.5.4 Dual markin

23、g is permitted when the actual values of thelisted elements match two or more of the Grades in Table 1;however, grade substitution such as combining a tungstenbearing Grade with one that has no requirement for tungsten isnot permitted.6. Mechanical Properties6.1 RequirementsThe material shall confor

24、m to the re-quirements for mechanical properties prescribed in Table 3.The mechanical testing requirements of Test Methods A 370and Specification A 788/A 788M apply.6.2 Number of Tension TestsThe number and location oftension tests are based on the solution-treated weight of theforging(s) from the s

25、ame heat and solution treated in the samefurnace charge.6.2.1 For forgings weighing less than 5000 lb 2250 kg asheat treated one tension test shall be required. This may betaken from an integral prolongation from one forging or froma forged test bar. Separate forged test bars shall have beenforged i

26、n the same manner, and with equivalent forgingreduction as the forgings they represent, and shall not be lessthan the represented forgings in heat-treated section thickness.6.2.1.1 When solution treatment is performed in acontinuous-type furnace, equipped with recording pyrometers,TABLE 1 Chemical R

27、equirementsGrade F50AF51AF52AF53AF54BF55BF57BF59AF60AF61AUNS No. S31200AS31803AS32950AS32750AS39274BS32760BS39277BS32520AS32205AS32550ACarbon, max 0.030 0.030 0.030 0.030 0.030 0.030 0.025 0.030 0.030 0.04Manganese, max 2.00 2.00 2.00 1.20 1.00 1.00 0.80 1.50 2.00 1.50Phosphorous, max 0.045 0.030 0.

28、035 0.035 0.030 0.030 0.025 0.035 0.030 0.040Sulfur, max 0.030 0.020 0.010 0.020 0.020 0.010 0.002 0.020 0.020 0.030Silicon, max 1.00 1.00 0.60 0.80 0.80 1.00 0.80 0.80 1.00 1.00Nickel 5.5-6.5 4.5-6.5 3.5-5.2 6.0-8.0 6.0-8.0 6.0-8.0 6.5-8.0 5.5-8.0 4.5-6.5 4.5-6.5Chromium 24.0-26.0 21.0-23.0 26.0-29

29、.0 24.0-26.0 24.0-26.0 24.0-26.0 24.0-26.0 24.0-26.0 22.0-23.0 24.0-27.0Molybdenum 1.20-2.00 2.5-3.5 1.00-2.50 3.0-5.0 2.5-3.5 3.0-4.0 3.0-4.0 3.0-5.0 3.0-3.5 2.9-3.9Nitrogen 0.14-0.20 0.08-0.20 0.15-0.35 0.240.32 0.24-0.32 0.20-0.30 0.23-0.33 0.20-0.35 0.14-0.20 0.10-0.25Copper . . . . . . . . . 0.

30、50 max 0.20-0.80 0.50-1.00 1.20-2.00 0.50-3.00 . . . 1.50-2.50Tungsten . . . . . . . . . . . . 1.50-2.50 0.50-1.00 0.80-1.20 . . . . . . . . .APREN = Cr + 3.3(Mo) + 16(N)BPREN = Cr + 3.3(Mo +12 W) + 16(N)NOTEThe required PREN value for both the tungsten bearing forging Grades with the superscript B

31、and the non-tungsten bearing Grades with thesuperscript A frequently lies between 33 and 40 depending on service experience, so that the Purchaser shall specify the required minimum PREN value(see 3.3).TABLE 2 Solution Heat TreatmentUNSDesignationGradeSolution TemperatureF CWater QuenchAto Below F C

32、S31200 F 50 1925 1050 min 200 95S31803 F 51 1870 1020 min 200 95S32950 F 52 1825-1875 1000-1025 200 95S32750 F 53 1880 1025 min 200 95S39274 F 54 1920-2060 1050-1125 200 95S32760 F 55 2010-2085 1100-1140 200 95S39277 F 57 1940 1060 min 200 95S32520 F 59 1975-2050 1080-1120 200 95S32205 F 60 1870 102

33、0 min 200 95S32550 F 61 1920-2060 1050-1125 200 95AWater quenching is required unless the use of another liquid quenchingmedium is approved by the purchaser (see 3.1.3).A 1049/A 1049M 062such that complete heating records are available, a solutionannealing charge may be considered as any continuous

34、run forforgings from the same heat not exceeding 8 h.6.2.2 For forgings weighing over 5000 lb 2250 kg as heattreated, one tension test shall be taken from each forging froman integral prolongation.6.3 Test OrientationTension tests shall be oriented in thelongitudinal direction, that is, parallel to

35、the direction ofmaximum working. For upset forged disks the test specimenaxis may be oriented tangentially to the radius of the forging.6.4 Test LocationThe location of the longitudinal axis ofthe tension test specimen shall be located midway between theparallel surfaces of the test extension if add

36、ed to the peripheryof disks, or midway between the center and surface of solidforgings. For bored or hollow forgings the specimen shall belocated at midwall. For the special case of forgings that are heattreated solid, but are subsequently bored, the specimen may betaken at the location of the minim

37、um inside diameter afterboring instead of the mid-radius position. For tube sheetsintended for construction to Section VIII of the ASME Boilerand Pressure Vessel Code, the tension test shall be located inaccordance with Supplementary requirement S12 of Specifica-tion A 788/A 788M.6.5 Hardness:6.5.1

38、For the Grades in Table 3 that have hardness limits,one hardness test per forging shall be taken after solution heattreatment.6.5.2 Supplementary requirement S6 may be specified whenthe application comes under the rules of NACE MR0175/ISO15156.7. Nondestructive Examination7.1 Ultrasonic Examination:

39、7.1.1 After solution treatment and the necessary machiningto comply with the test practice requirements, the forging shallbe examined in accordance with Practice A 745/A 745M,except that when Supplementary Requirement S5 has beenspecified, Practice A 388/A 388M shall be employed.7.1.2 When Practice

40、A 745/A 745M is used, acceptanceshall be based on Quality Level 1 or 2, as specified by thepurchaser.8. Rejection, Certification, and Marking8.1 Rejection, certification, and marking of forgings shall bein accordance with Specification A 788/A 788M.9. Keywords9.1 austenitic/ferritic stainless steel;

41、 duplex stainless steel;forgings; PREN value; pressure vesselsSUPPLEMENTARY REQUIREMENTSThe following supplementary requirement(s) shall apply only when specified by the purchaser in thecontract or order. Additional supplementary requirements that may be applicable are included inSpecification A 788

42、/A 788M.S1. Detrimental Intermetallic Phase DetectionS1.1 Forgings in Grades F51 (S31803), F52 (S32950), andF60 (S32205) shall be subject to detrimental intermetallicphase detection in accordance with Test Methods A 923.S1.2 Method A of Test Methods A 923 shall be followed byeither Charpy impact tes

43、ting to Method B or a ferric chloridecorrosion test to Method C at the purchasers option.S1.3 The location of the test specimens for testing tomethods B or C of Test Methods A 923 shall be as specified in6.4 unless otherwise denoted by the purchaser.S1.4 Unless otherwise specified by the purchaser a

44、ccep-tance shall be as specified in Test Methods A 923 for thechosen test method.S2. Charpy Impact TestingS2.1 One set of three Charpy V-Notch specimens, preparedand tested in accordance with Test Methods A 370 shall betaken from each tension test location and tested to therequirements of the applic

45、able construction code, or as re-quired by the purchaser.TABLE 3 Tensile Strength and Hardness RequirementsUNSDesignationGradeTensile Strengthksi MPaMinimum or RangeYield Strength0.2 % Offsetksi MPaMinimumElongation %in 2 in. or 50 mmMinimumReduction of Area% MinimumBrinell HardnessHBMaximumS31200 F

46、 50 100-130 690-900 65 450 25 50 . . .S31803 F 51 90 620 65 450 25 45 . . .S32950 F 52 100 690 70 485 15 45 . . .S32750 F 53 116 800 80 550 15 45 310S39274 F 54 116 800 80 550 15 30 310S32760 F 55 109-130 750-900 80 550 25 45 . . .S39277 F 57 118 815 85 585 25 50 . . .S32520 F 59 112 770 80 550 25 4

47、0 . . .S32205 F 60 95 655 70 485 25 45 . . .S32550 F 61 109 750 80 550 25 50 . . .A 1049/A 1049M 063S2.2 Test reporting shall include absorbed energy, lateralexpansion, fracture appearance, and test temperature.S3. Corrosion ResistanceS3.1 Testing for resistance to pitting and crevice corrosionshall

48、 be carried out in accordance with Test Methods G48. Thetest temperature shall be as specified by the purchaser (see 3.5)within the guidelines of Test Methods G48, and the actual testtemperature shall be reported.S3.2 The purchaser shall indicate which of the test methodsare to be used as well as th

49、e acceptance criteria.S4. Ultrasonic ExaminationS4.1 At the purchasers option PracticeA 388/A 388M shallbe used instead of A 745/A 745M for ultrasonic examination.S4.2 The purchaser shall specify the examination criteriaincluding the reference hole size for the DAC curve and theacceptance criteria.S5. Liquid Penetrant ExaminationS5.1 For forgings in the final machined configuration aliquid penetrant examination done in accordance with TestMethod E 165 shall be carried out on a