FORD WSS-M2F212-A1-2015 FABRIC PREMIUM VINYL (PVC) COATED WITH ENHANCED HAPTIC TOP COAT TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WSS-M2F212-A1-2015 FABRIC PREMIUM VINYL (PVC) COATED WITH ENHANCED HAPTIC TOP COAT TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M2F212-A1-2015 FABRIC PREMIUM VINYL (PVC) COATED WITH ENHANCED HAPTIC TOP COAT TO BE USED WITH FORD WSS-M99P1111-A .pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2015 03 02 Released D. Murtonen, FNA Controlled document at www.MATS Copyright 2015, Ford Global Technologies, LLC Page 1 of 2 FABRIC, PREMIUM VINYL (PVC) COATED, WITH ENHANCED WSS-M2F212-A1 HAPTIC TOP COAT 1. SCOPE The material define

2、d by this specification is an expanded polyvinyl chloride film laminated to a knitted polyester or polyester/cotton fabric. These materials can be used laminated with foam and/or a backing fabric/scrim, based on the application. 2. APPLICATION WSS-M2F212-A1 was released originally for material used

3、in interior trim as a covering for seating applications. Any other applications must be evaluated by the appropriate product engineer with functional testing and approved by Materials Engineering. . 2.1 LIMITATIONS Product grain will be used to determine and classify the usage of this premium enhanc

4、ed haptic top coat polyvinyl chloride for Ford and Lincoln vehicles. Not recommended for usage in areas where anti-squeak properties are required. Not to be used for truck or commercial vehicle, in any A surface. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers a

5、nd part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A) 3.1.1 Materials used in interior applications must meet the requirements outlined in WSS-M99P2222-D1 / latest, Performance, Vehicle Interior Environmental Quality Material/Component Require

6、ments. Data must be included in material submission package. 3.1.2 In addition to the requirements listed herein, this material shall meet the specification requirements of WSS-M8P3-E1/E3/latest, Performance, Flexible Polymeric Film, Interior Quality. 3.2 APPEARANCE (FLTM BI 109-01) The color, patte

7、rn, grain, gloss level and finish shall match the approved corporate design master sample or shall be as specified on the engineering drawing. 3.3 COMPOSITION 3.3.1 Vinyl Coated Fabric Composite ENGINEERING MATERIAL SPECIFICATION WSS-M2F212-A1 Copyright 2015, Ford Global Technologies, LLC Page 2 of

8、2 3.3.1.1 Weight (ASTM D 751, Sample Method) Total (vinyl and supported fabric) 820 - 945 g/m2 3.3.1.2 Thickness 1.0min. - 1.7max/mm 3.3.2 Supported Fabric (ASTM D 276) 3.3.2.1 Fabric Composition Warp Knit made of 100% Polyester or 65% Polyester/35% Cotton Blend 3.3.2.2 Weight 125-135 g/m2 (ASTM D 7

9、51, Sample Method) 3.4 PHYSICAL PROPERTIES 3.4.1 Breaking Strength (ASTM D751, Grab Method) WMD 480 N min AMD 455 N min 3.4.2 Tear Strength (ASTM D751, Trapezoid Tear) WMD 145 N min AMD 145 N min 3.4.3 Seam Strength (FLTM BN 119-01) WMD 500 N min AMD 480 N min 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 5. SUMMARY OF REVISIONS