DIN EN 13523-5-2014 Coil coated metals - Test methods - Part 5 Resistance to rapid deformation (impact test) German version EN 13523-5 2014《涂覆金属卷材 试验方法 第5部分 耐快速变形(冲击试验) EN 13523-5 .pdf

《DIN EN 13523-5-2014 Coil coated metals - Test methods - Part 5 Resistance to rapid deformation (impact test) German version EN 13523-5 2014《涂覆金属卷材 试验方法 第5部分 耐快速变形(冲击试验) EN 13523-5 .pdf》由会员分享，可在线阅读，更多相关《DIN EN 13523-5-2014 Coil coated metals - Test methods - Part 5 Resistance to rapid deformation (impact test) German version EN 13523-5 2014《涂覆金属卷材 试验方法 第5部分 耐快速变形(冲击试验) EN 13523-5 .pdf（11页珍藏版）》请在麦多课文档分享上搜索。

1、August 2014 Translation by DIN-Sprachendienst.English price group 7No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS

2、25.220.60!%:;6“2232419www.din.deDDIN EN 13523-5Coil coated metals Test methods Part 5: Resistance to rapid deformation (impact test);English version EN 13523-5:2014,English translation of DIN EN 13523-5:2014-08Bandbeschichtete Metalle Prfverfahren Teil 5: Widerstandsfhigkeit gegen schnelle Verformun

3、g (Schlagprfung);Englische Fassung EN 13523-5:2014,Englische bersetzung von DIN EN 13523-5:2014-08Tles prlaques Mthodes dessai Partie 5: Rsistance la dformation rapide (essai de choc);Version anglaise EN 13523-5:2014,Traduction anglaise de DIN EN 13523-5:2014-08SupersedesDIN EN 13523-5:2001-12www.be

4、uth.deDocument comprises 11 pagesIn case of doubt, the German-language original shall be considered authoritative.07.14DIN EN 13523-5:2014-08 2 A comma is used as the decimal marker. National foreword This document (EN 13523-5:2014) has been prepared by Technical Committee CEN/TC 139 “Paints and var

5、nishes”, (Secretariat: DIN, Germany), Working Group WG 9 “Testing of coil coated metals” (Secretariat: DIN, Germany). The responsible German body involved in its preparation was the Normenausschuss Beschichtungsstoffe und Beschichtungen (DIN Standards Committee Coatings and Coating Materials), Worki

6、ng Committee NA 002-00-07 AA Allgemeine Prfverfahren fr Beschichtungsstoffe und Beschichtungen. Amendments This standard differs from DIN EN 13523-5:2001-12 as follows: a) the limitation in the scope to coatings having a thickness of 60 m maximum has been deleted; b) an information concerning the co

7、nditioning of the specimen has been added; c) details on the brands of the tape used have been added; d) in addition to the use of a magnifying glass 10, the evaluation is to be carried out with normal corrected vision. Previous editions DIN EN 13523-5: 2001-12 EUROPEAN STANDARD NORME EUROPENNE EURO

8、PISCHE NORM EN 13523-5 June 2014 ICS 25.220.60 Supersedes EN 13523-5:2001English Version Coil coated metals - Test methods - Part 5: Resistance to rapid deformation (impact test) Tles prlaques - Mthodes dessai - Partie 5: Rsistance la dformation rapide (essai de choc) Bandbeschichtete Metalle - Prfv

9、erfahren - Teil 5: Widerstandsfhigkeit gegen schnelle Verformung (Schlagprfung) This European Standard was approved by CEN on 7 May 2014. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a nationa

10、l standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A versio

11、n in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Cze

12、ch Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. E

13、UROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2014 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 13523-5:2014

14、EEN 13523-5:2014 (E) 2 Contents Page Foreword 3 1 Scope 5 2 Normative references 5 3 Terms and definitions .5 4 Principle 5 5 Apparatus and materials .5 6 Sampling .5 7 Test panels .6 8 Procedure .6 9 Expression of results 6 10 Precision .6 11 Test report 6 Annex A (informative) Conversion of units

15、8 Bibliography 9 DIN EN 13523-5:2014-08EN 13523-5:2014 (E) 3 Foreword This document (EN 13523-5:2014) has been prepared by Technical Committee CEN/TC 139 “Paints and varnishes”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either b

16、y publication of an identical text or by endorsement, at the latest by December 2014, and conflicting national standards shall be withdrawn at the latest by December 2014. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or

17、 CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 13523-5:2001. The main technical changes are: a) the limitation in the scope to coatings having a thickness of 60 m maximum was deleted; b) a remark on preconditioning was added; c) deta

18、ils on the brands of the tape used were added; d) in addition to use a 10 magnifying glass, the evaluation shall be carried out with normal corrected vision. EN 13523, Coil coated metals Test methods, consists of the following parts: Part 0: General introduction Part 1: Film thickness Part 2: Gloss

19、Part 3: Colour difference Instrumental comparison Part 4: Pencil hardness Part 5: Resistance to rapid deformation (impact test) Part 6: Adhesion after indentation (cupping test) Part 7: Resistance to cracking on bending (T-bend test) Part 8: Resistance to salt spray (fog) Part 9: Resistance to water

20、 immersion Part 10: Resistance to fluorescent UV radiation and water condensation Part 11: Resistance to solvents (rubbing test) Part 12: Resistance to scratching Part 13: Resistance to accelerated ageing by the use of heat DIN EN 13523-5:2014-08EN 13523-5:2014 (E) 4 Part 14: Chalking (Helmen method

21、) Part 15: Metamerism Part 16: Resistance to abrasion Part 17: Adhesion of strippable films Part 18: Resistance to staining Part 19: Panel design and method of atmospheric exposure testing Part 20: Foam adhesion Part 21: Evaluation of outdoor exposed panels Part 22: Colour difference Visual comparis

22、on Part 23: Resistance to humid atmospheres containing sulfur dioxide Part 24: Resistance to blocking and pressure marking Part 25: Resistance to humidity Part 26: Resistance to condensation of water Part 27: Resistance to humid poultice (Cataplasm test) Part 29: Resistance to environmental soiling

23、(Dirt pick-up and striping) According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republ

24、ic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. DIN EN 13523-5:2014-08EN 13523-5:2014 (E) 5 1 Scope This pa

25、rt of EN 13523 specifies the procedure for determining the resistance to cracking and/or pick-off on rapid deformation of an organic coating on a metallic substrate in terms of energy which the specimen will withstand. 2 Normative references The following documents, in whole or in part, are normativ

26、ely referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 13523-0:2014, Coil coated metals Test methods Part 0: General

27、introduction EN 23270, Paints and varnishes and their raw materials Temperatures and humidities for conditioning and testing (ISO 3270) EN 60454-2, Pressure-sensitive adhesive tapes for electrical purposes Part 2: Methods of test (IEC 60454-2) EN ISO 6272-1, Paints and varnishes Rapid-deformation (i

28、mpact resistance) tests Part 1: Falling-weight test, large-area indenter (ISO 6272-1) 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN 13523-0:2014 apply. 4 Principle The test specimen is deformed (indentation in the form of a dome), using a falling we

29、ight. Usually, the deformation is carried out from the reverse side but can occasionally be carried out directly on the coated surface under test. The resistance of the coating to cracking and/or pick off is then determined. 5 Apparatus and materials 5.1 Apparatus in accordance with EN ISO 6272-1, e

30、quipped with a hemispherical striker, of diameter 20 mm and having two scales, one of which corresponding to a mass of 1 000 g, the other to a mass of 2 000 g. 5.2 Magnifying glass 10. 5.3 Transparent pressure-sensitive adhesive tape, 25 mm wide, with an adhesion strength of (10 1) N per 25 mm width

31、 when tested in accordance with EN 60454-2. 6 Sampling See EN 13523-0. DIN EN 13523-5:2014-08EN 13523-5:2014 (E) 6 7 Test panels See EN 13523-0. 8 Procedure Measure the resistance to rapid deformation at ambient temperature. For more accurate measurements, as required for instance in case of dispute

32、, the temperature shall be (23 2) C and the relative humidity (50 5) % in accordance with EN 23270. Conditioning is carried out in accordance with EN 13523-0:2014, Clause 6. Place the test panel in the apparatus (5.1) with the coated surface to be tested facing downward (reverse impact test). The te

33、st may occasionally be carried out for forward impact. Drop the mass from the required height to provide the appropriate energy of impact. Assess the resistance to cracking with normal corrected vision and the 10 magnifying glass (5.2). If resistance to pick-off is to be evaluated, remove two comple

34、te laps from a reel of the adhesive tape (5.3) and discard. Remove an additional length at a steady rate and cut a piece, approximately 75 mm long. Place the centre of the tape over the deformation and smooth the tape into place over a distance of at least 20 mm either side with a finger. To ensure

35、good contact with the coating, rub the tape firmly with a fingertip. The colour of the coating seen through the tape is a useful indication of overall contact. Within 5 min of applying the tape, remove the tape by holding the free end and pulling it off steadily in 0,5 s to 1 s at an angle that is a

36、s close as possible to 60 to the panel. Resistance to pick-off is evaluated after removal of tape: no loss of adhesion is allowed. Retain the tape for reference purposes, for example by attaching it to a sheet of transparent film. 9 Expression of results Record the resistance to no cracking and/or n

37、o loss of adhesion in Joules. State whether resistance to cracking and/or loss of adhesion has been measured. 10 Precision No precision data are currently available. 11 Test report The test report shall contain at least the following information: a) all details necessary to identify the product test

38、ed; b) a reference to this part of EN 13523 (EN 13523-5); c) the results of the test, as indicated in Clause 9; DIN EN 13523-5:2014-08EN 13523-5:2014 (E) 7 d) any deviation from the test method specified; e) any unusual features (anomalies) observed during the test; f) the date of the test. DIN EN 1

39、3523-5:2014-08EN 13523-5:2014 (E) 8 Annex A (informative) Conversion of units For the purpose of this test, the following approximations may be used: 1 J (or 1 Nm) = 0,1 kgf m = 0,1 kp m = 8,8 lbf in 1 kgf m = 1 kp m = 9,8 J = 87 lbf in 1 lbf in = 0,113 J = 0,011 kgf m where J is Joule; Nm is Newton

40、 metre; kgf m is kilogramme-force metre; kp m is kilopond metre; lbf in is pound-force inch (inch pound). DIN EN 13523-5:2014-08EN 13523-5:2014 (E) 9 Bibliography 1 EN 1396, Aluminium and aluminium alloys Coil coated sheet and strip for general applications Specifications 2 EN 10169, Continuously organic coated (coil coated) steel flat products Technical delivery conditions DIN EN 13523-5:2014-08