ASTM C845-2004 Standard Specification for Expansive Hydraulic Cement《可膨胀的水硬性水泥标准规范》.pdf

《ASTM C845-2004 Standard Specification for Expansive Hydraulic Cement《可膨胀的水硬性水泥标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM C845-2004 Standard Specification for Expansive Hydraulic Cement《可膨胀的水硬性水泥标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C 845 04Standard Specification forExpansive Hydraulic Cement1This standard is issued under the fixed designation C 845; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses

2、 indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers hydraulic cements that expandduring the early hardening period after setting.2. Referenced Documents2.1 ASTM Standards:2C 33 Spec

3、ification for Concrete AggregatesC 109/C 109M Test Method for Compressive Strength ofHydraulic Cement Mortars (Using 2-in. or 50-mm CubeSpecimens)C 114 Test Methods for Chemical Analysis of HydraulicCementC 183 Practice for Sampling and the Amount of Testing ofHydraulic CementC 185 Test Method for A

4、ir Content of Hydraulic CementMortarC 188 Test Method for Density of Hydraulic CementC 465 Specification for Processing Additions for Use in theManufacture of Hydraulic CementsC 688 Specification for Functional Additions for Use inHydraulic CementsC 806 Test Method for Restrained Expansion of Expans

5、iveCement MortarC 807 Test Method for Time of Setting of Hydraulic Ce-ment Mortar by Modified Vicat Needle3. Terminology3.1 Definitions:3.1.1 expansive cement (K)an expansive cement contain-ing anhydrous calcium aluminosulfate (4CaO3Al2O3SO3),calcium sulfate, and uncombined calcium oxide.3.1.2 expan

6、sive cement (M)an expansive cement contain-ing calcium aluminate cement and calcium sulfate.3.1.3 expansive cement (S)an expansive cement contain-ing tricalcium aluminate (C3A) and calcium sulfate.3.1.4 expansive hydraulic cementa cement composed es-sentially of hydraulic calcium silicates, calcium

7、aluminates andcalcium sulfates, which, upon being mixed with water, forms apaste that increases significantly in volume during the earlyhardening period occurring after setting. This volume increaseis due principally to the reaction of the calcium aluminates andcalcium sulfates.3.1.5 shrinkage-compe

8、nsating concreteconcrete that isinternally restrained with resilient reinforcing and made withexpansive cement which induces both compressive stress in theconcrete and positive steel strain that approximately off-setstensile stresses and negative strains induced by drying shrink-age.4. Classificatio

9、n4.1 The cement covered by this specification is suitable foruse in shrinkage-compensating concrete and shall be desig-nated as Type E-1.NOTE 1Three kinds of expansive cement are identified in Section 3by the letters K, M, and S. The appropriate letter should be used as a suffixto the type designati

10、on when one of these kinds is desired. Expansivecement may also be prepared in other ways.5. Ordering Information5.1 When it is desired that an optional requirement apply orthat the cement be of a particular kind, a specific request to thiseffect should be made by the purchaser.6. Chemical Compositi

11、on6.1 Expansive cement shall conform to the requirements asto chemical composition prescribed in Table 1.6.2 The purchaser has the option of specifying that thealkalies (Na2O + 0.658K2O) shall not exceed 0.60 % (SeeTable 2).NOTE 2This limit should be specified when the cement is to be usedin concret

12、e with aggregates that may be reactive. Reference should bemade to Specification C 33 for suitable criteria of deleterious reactivity.7. Physical Properties7.1 Expansive cement shall conform to the physical require-ments prescribed in Table 3.1This specification is under the jurisdiction of ASTM Com

13、mittee C01 onCement and is the direct responsibility of Subcommittee C01.13 on SpecialCements.Current edition approved July 1, 2004. Published July 2004. Originally approvedin 1976. Last previous edition approved in 1996 as C 84596.2For referenced ASTM standards, visit the ASTM website, www.astm.org

14、, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.8. Additions8.

15、1 The cement covered by this specification shall containno additions except as follows:8.1.1 Water, or a functional addition, or both, that has beenshown to meet the requirements of Specification C 688, may beadded in amounts such that the limits shown in Table 1 for losson ignition shall not be exc

16、eeded.8.1.2 At the option of the manufacturer, processing addi-tions may be used in the manufacture of the cement, providedsuch materials in the amounts used have been shown to be notharmful in accordance with Specification C 465.9. Test Methods9.1 The cement shall be sampled and the properties enum

17、er-ated in this specification shall be determined in accordancewith the following methods:9.1.1 SamplingPractice C 183.9.1.2 Chemical AnalysisTest Methods C 114.9.1.3 Time of SettingTest Method C 807.9.1.4 Air ContentTest Method C 185, using the actualspecific gravity of the cement if it differs fro

18、m 3.15 by morethan 0.05 in calculating the air content.9.1.5 Restrained Expansion of MortarTest Method C 806.9.1.6 Compressive StrengthTest Method C 109/C109M,except that a water-cement ratio of 0.500 shall be used, thespecimens shall be covered with a polyethylene sheet or othersuitable material fo

19、r preventing loss or gain of moisture at thesurface of the specimens during the moist storage period in themolds, and the specimens shall remain in the molds for 3 days.9.1.7 DensityTest Method C 188.10. Inspection10.1 Every facility shall be provided the purchaser forcareful inspection and sampling

20、 of the finished cement. Thefinished cement may be inspected and sampled either at themill or at the site of the work, as may be specified by thepurchaser. The following periods from time of sampling shallbe allowed for completion of testing:7-day test 12 days28-day test 33 days10.2 The manufacturer

21、 shall provide suitable facilities toenable the inspector to check the intergrinding or blendingoperation used to produce cement by either means. The plantfacilities for intergrinding or blending and inspection shall beadequate to ensure compliance with the provisions of thisspecification.11. Reject

22、ion11.1 The cement may be rejected if it fails to meet any of therequirements of this specification.11.2 Cement remaining in bulk storage at the mill prior toshipment for a period greater than 6 months or cement in bagsin local storage in the hands of a vendor for more than 3months, after completion

23、 of the tests, may be retested forexpansion and may be rejected if it fails to conform to therequirements of this specification for expansion.11.3 Packages more than 2 % below the net weight markedthereon, may be rejected. Also, if the average net weight ofpackages in any shipment, as shown by weigh

24、ing 50 packagesat random, is less than that marked on the packages, the entireshipment may be rejected.12. Certification12.1 At the request of the purchaser, the manufacturer shallstate in writing the composition of a finished cement.12.2 The composition of any cement shall conform to thatshown in t

25、he statement of the manufacturer within the follow-ing tolerances:Tolerance, 6 %Silicon dioxide (SiO2)3Aluminum oxide (Al2O3)2Calcium oxide (CaO) 312.3 At the request of the purchaser, the manufacturer shallstate in writing the nature, amount, and identity of anyprocessing or functional addition tha

26、t may have been used.Also, if requested, the manufacturer shall supply test datashowing compliance of any processing addition with theprovisions of Specification C 465, and any functional additionwith the provisions of Specification C 688.12.4 Upon request of the purchaser in the contract or order,a

27、 manufacturers certification that the material during produc-tion was tested in accordance with this specification togetherwith a report of the test results shall be furnished at the time ofshipment.13. Packaging and Package Marking13.1 When the cement is delivered in packages, the words“expansive c

28、ement,” the type, the kind (if the cement is one ofthe three kinds defined in Section 3), the name and brand of themanufacturer, and the net weight shall be plainly marked oneach package. Similar information shall be provided in theshipping documents accompanying the shipment of packagedor bulk ceme

29、nt. All packages shall be in good condition at thetime of inspection.TABLE 1 Standard Chemical RequirementsComposition, %Magnesium oxide (MgO), max 6.0Insoluble residue, max 1.0Loss on ignition, max 4.0TABLE 2 Optional Chemical RequirementsAlkalies (Na2O + 0.658 3 K2O) max, % 0.60TABLE 3 Physical Re

30、quirementsTime of setting, min, minutes 75Air content, max, vol % 12.0Restrained expansion of mortar:7-day expansion:min, % 0.04max, % 0.1028-day, percentage of 7-dayexpansion, max 115Compressive strength, min:7-day, psi(MPa) 2100(14.7)28-day, psi(MPa) 3500(24.5)C84504214. Storage14.1 The cement sha

31、ll be stored in a manner such as topermit easy access for proper inspection and identification ofeach shipment and in a suitable weathertight building that willprotect the cement from dampness and minimize warehouseset.15. Keywords15.1 calcium aluminate; calcium aluminosulfate; calciumoxide; calcium

32、 silicate; calcium sulfate; cement; expansive;hydraulic; shrinkage-compensated; tricalcium aluminateASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that dete

33、rmination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or

34、 withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel tha

35、t your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).C845043