1、Designation: B666/B666M 08B666/B666M 15Standard Practice forIdentification Marking of Aluminum and MagnesiumProducts1This standard is issued under the fixed designation B666/B666M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, th

2、e year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This practice establi

3、shes the physical item marking requirements for identification purposes for aluminum and magnesiumproducts. Package marking for shipment and inspection acceptance is not within the scope of this standard.1.2 The values stated in either SI units or inch-pound units are to be regarded separately as st

4、andard. The values stated in eachsystem may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from thetwo systems may result in non-conformance with the standard.1.3 This standard does not purport to address all of the safety concerns, if any

5、, associated with its use. It is the responsibilityof the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatorylimitations prior to use.2. Referenced Documents2.1 The following documents of the issue in effect on the date of material

6、 purchase form a part of this specification to the extentreferenced herein:2.2 ASTM Standards:2B361 Specification for Factory-Made Wrought Aluminum and Aluminum-Alloy Welding FittingsB404/B404M Specification for Aluminum and Aluminum-Alloy Seamless Condenser and Heat-Exchanger Tubes with IntegralFin

7、s (Withdrawn 2006)3B547/B547M Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round TubeB881 Terminology Relating to Aluminum- and Magnesium-Alloy Products2.3 ANSI Standards:H35.1/H35.1(M) Alloy and Temper Designation Systems for Aluminum42.4 Military Standards:MIL-STD-409 Alloy

8、Nomenclature and Temper Designation System for Magnesium Base Alloys53. Terminology3.1 DefinitionsRefer to Terminology B881 for definitions of product terms used in this specification.3.2 Definitions of Terms Specific to This Standard:3.2.1 Marking:3.2.2 spot markingmarking the identification only o

9、nce on the product.1 This practice is under the jurisdiction ofASTM Committee B07 on Light Metals andAlloys and is the direct responsibility of Subcommittee B07.03 on AluminumAlloyWrought Products.Current edition approved July 15, 2008Oct. 1, 2015. Published August 2008October 2015. Originally appro

10、ved in 1980. Last previous edition approved in 20012008 asB666/B666M 01.B666/B666M 08. DOI: 10.1520/B0666_B0666M-08.10.1520/B0666_B0666M-15.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume

11、 information, refer to the standards Document Summary page on the ASTM website.3 The last approved version of this historical standard is referenced on www.astm.org.4 Available from Aluminum Association, Inc., 1525 Wilson Blvd., Suite 600,1400 Crystal Drive, Suite 430 Arlington, VA 22209, http:/www.

12、aluminum.org.22202(http:/www.aluminum.org).5 Available from Standardization Documents Order Desk, DODSSP, Bldg. 4, Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.dodssp.daps.mil.19111-5098 (http:/www.dodssp.daps.mil).This document is not an ASTM standard and is intended only to

13、provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof

14、the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.2.3 continuous markingrecurring marking of

15、the identification in intervals not greater than 40 in. 1000 mm throughout thelength of the product.3.2.4 perimeter markingmarking continuously the identification in one or two rows adjacent to the four edges of the product.3.2.5 taggingattaching tags bearing the required identification markings to

16、coils, bundles, or containers of items which are toosmall to mark or whose configuration preclude marking otherwise.4. Basic Marking Requirements and Application4.1 When this practice is required by the material specification or specified in the contract or purchase order, wrought aluminumand magnes

17、ium mill products shall be marked for identification purposes only with the following information on the product oron tags attached to the product:4.1.1 Name or Registered Trademark of the Company, which performs the final processing or finishing operation such as rolling,stretching, thermal treatme

18、nt, etc., prior to marketing the product;NOTE 1The company that performs nothing more than a simple shearing or sawing operation may be excluded from marking the product with itsname.4.1.2 Alloy and Temper of the ProductDesignations shall be in accordance with ANSI H35.1/H35.1M for aluminum andMIL-S

19、TD-409 for magnesium;4.1.3 Basic Number of the Specification to which the Product was ProducedThe basic number does not include the revisionindicator;4.1.4 Specified (Ordered) Dimensions of the Following Products:4.1.4.1 Sheet and PlateThickness in inches millimetres,4.1.4.2 Coiled Wire and Spooled

20、WireDiameter in inches millimetres,4.1.4.3 Tube:(1) Straight LengthsOutside diameter and wall thickness, in inches millimetres,(2) CoiledWall thickness, in inches millimetres,4.1.4.4 PipeNominal pipe size and ANSI schedule number;4.1.5 Lot number shall be included in the product marking. The definit

21、ion of lot shall be that as defined in the materialspecification.4.1.6 For magnesium products, the applicable lot number shall be marked on each piece in at least one location.4.1.7 When required by the material specification, the word “seamless” on certain tube or pipe.NOTE 2The requirements specif

22、ied in 4.1 are minimum; marking systems that involve additional information shall be as agreed upon between theproducer and the purchaser.4.2 When this practice is required by the material specification or specified in the contract or purchase order, marking of castaluminum products shall be in acco

23、rdance with Section 6.4.3 Product marking shall be such that it shall not rub off or be otherwise obliterated by contact arising from normal handling,exposure to the elements, shipment, and storage. The height of the characters shall be commensurate with the size of the productbeing marked; for exam

24、ple, not less than 0.375 in. 9 mm for flat sheet and plate, not less than 0.250 in. 6 mm for hand forgingsand not less than 0.125 in. 3 mm for tubular products. Legibility of all markings shall be such as required for ready readabilityand the required permanency of identification.4.4 Product marking

25、 shall be accomplished in a manner that will not adversely affect the subsequent fabrication of the material,or produce stresses that would be deleterious to the functioning of the finished product. Marking on the product shall be withmarking fluid applied by printing, stamping, or stenciling. Ghost

26、 images of the characters may remain upon the removal of markingapplied. Impression stamping is considered detrimental and shall not be used except on ingot, castings, forging, and certain tubeproducts, or when required by prior agreement between the producer and purchaser.5. Marking of Wrought Alum

27、inum and Magnesium Mill Products5.1 When this practice is required by the material specification or specified in the contract or purchase order, wrought aluminumand magnesium mill products shall be marked as follows:5.1.1 Lot Number, All ProductsSpot marking the product.5.1.2 Coiled SheetSpot markin

28、g in one or more rows near the outside end as shown in Fig. 1 1M.Fig. 1M.5.1.3 Flat Sheet and Plate:5.1.3.1 Flat sheet less than 0.012 in. up through 0.30 mm (for O temper, less than 0.020 in. up through 0.50 mm) inthicknessSpot marking near one end,5.1.3.2 Plate and flat sheet 0.012 in. and over ov

29、er 0.30 mm (for O temper, 0.020 in. and over over 0.50 mm) in thicknessand less than 6 in. up through 150 mm wideContinuous marking in one row,5.1.3.3 Plate up through 0.375 in. 10 mm and flat sheet 0.012 in. and over over 0.30 mm (for O temper, 0.020 in. and overover 0.50 mm) in thickness, 6 throug

30、h 60 in. over 150 through 1500 mm in width, and 36 through 200 in. over 1000 throughB666/B666M 1525000 mm in lengthContinuous marking in rows running the direction of rolling on 6 in. 150 mm centers across the width onone surface as shown in Fig. 2 2M Fig. 2M and Fig. 33M. Fig. 3M. Using the marking

31、 pattern of Fig. 2 2M, Fig. 2M,every third row shall contain the producers name or trademark and the ordered thickness. The other two rows shall each containthe alloy and temper and the specification number, and shall be staggered. Using the marking pattern of Fig. 33M, Fig. 3M,there are two alterna

32、ting rows. One row shall contain the producers name or trademark and the ordered thickness, and thealternating row shall contain the alloy and temper and the specification number. Both the marking patterns shown in Fig. 22MFig. 2M and Fig. 33M Fig. 3M provide the same information and either can be u

33、sed.5.1.3.4 Plate over 0.375 in. 10 mm in thickness, flat sheet and plate over 60 in. 1500 mm in width or over 200 in. 5000 mmin lengthSame marking as 5.1.3.3 or perimeter marking on one surface. When perimeter marking of two rows is chosen, onerow shall contain the producers name or trademark and t

34、he ordered thickness, and the second row shall contain alloy and temper,and the specification number as shown in Fig. 4 4M.Fig. 4M.NOTE 3If perimeter marking is applied to a full piece as produced but partial sheets or plates are supplied, an arrow shall be applied near one cornerof each partial she

35、et or plate indicating the direction of rolling.5.1.4 Circles:5.1.4.1 Circles 24 in. and over over 600 mm in diameterSpot marking on each circle unless the circle was cut from sheetor plate having continuous marking, and5.1.4.2 Circles less than 24 in. up through 600 mm in diameterTagging or marking

36、 of shipping container.NOTE 4Alclad one side flat sheet, plate, circles, and coiled sheet shall be marked on the bare side.5.1.5 Tread PlateSpot marking near one end on the back side.5.1.6 FoilMarking of this product is not required. Package marking only.5.1.7 Rod, Bar, and Extruded ProfilesContinuo

37、us marking of straight lengths as shown in Fig. 5 5M, Fig. 5M, of sizeshaving an accessible flat surface of 12 in. or more over 12.5 mm in width (with less than 18 in. 3 mm and less indented surface),or a diameter of 12 in. over 12.5 mm or more. Tagging is applicable to smaller sizes, lengths under

38、3 ft 1 m and coils.5.1.8 Structural ProfilesSpot marking near one end as shown in Fig. 6 6M.Fig. 6M.5.1.9 Tube and PipeContinuous marking of non-round straight lengths in a single row of sizes having both a wall thicknessof 0.029 in. and greater over 0.72 mm and a flat surface of 12 in. or more over

39、 12.5 mm in width. Continuous marking of roundstraight lengths in a single row of sizes having both a wall thickness of 0.029 in. and greater over 0.72 mm and a diameter of12 in. or more over 12.5 mm. Tagging is applicable to each coil or bundle of smaller sizes and lengths under 3 ft 1 m.5.1.10 Wir

40、eTagging of coils and straight lengths, and spot marking on one flange of spools.5.1.11 Bus BarSpot marking near one end except that specification number shall not be required to be marked on this product.5.1.12 Forgings:5.1.12.1 Hand ForgingSpot marking on one place of each piece.5.1.12.2 Die Forgi

41、ngMarking in accordance with the requirements of the forging drawing.6. Marking of Cast Aluminum Products6.1 CastingsMarking shall be that as specified by the applicable material specification or as agreed upon between the producerand the purchaser.Fig. 1 Spot Marking for Coiled SheetFIG. 1 M Spot M

42、arking for Coiled SheetB666/B666M 1536.2 Remelt Ingot for Castings:NOTE 1Marking pattern is three staggered rows: two rows contain alloy, temper, and specification number, and every third row contains producersname and ordered thickness. Figure shows spot marking of the lot number.FIG 2 Continuous M

43、arking for Plate Through 0.375 in. and Flat Sheet 0.012 in. and over (for O Temper, 0.020 in. and over) in Thickness, 6 Through 60 in.in Width, and 36 Through 200 in. in LengthNOTE 1Marking pattern is three staggered rows: two rows contain alloy, temper, and specification number, and every third row

44、 contains producersname and ordered thickness. Figure shows spot marking of the lot number.FIG. 2 M Continuous Marking for Plate Through 10 mm and Flat Sheet over 0.30 mm (for O Temper, over 0.50 mm) in Thickness, over150 Through 1500 mm in Width, and 1000 Through 5000 mm in LengthB666/B666M 1546.2.

45、1 Marking of Aluminum IngotThe producers name or trademark (see 4.1.1), alloy designation (see 4.1.2) and cast numbershall be impressioned-stamped or otherwise permanently marked on each ingot or if strapped together, not less than four ingotsin each bundle, two in the top layer and two in the botto

46、m layer. Specification number shall not be required to be marked on thisproduct.NOTE 1Marking pattern is two alternating rows: one row contains alloy, temper, and specification number, and the alternating row contains theproducers name and ordered thickness. Figure shows spot marking of the lot numb

47、er.FIG 3 Continuous Marking for Plate Through 0.375 in. and Flat Sheet 0.012 in. and over (for O Temper, 0.020 in. and over) in Thickness, 6 Through 60 in.in Width, and 36 Through 200 in. in Length.NOTE 1Marking pattern is two alternating rows: one row contains alloy, temper, and specification numbe

48、r, and the alternating row contains theproducers name and ordered thickness. Figure shows spot marking of the lot number.FIG. 3 M Continuous Marking for Plate Through 10 mm and Flat Sheet over 0.30 mm (for O Temper, over 0.50 mm) in Thickness, over150 Through 1500 mm in Width, and 1000 Through 5000

49、mm in Length.B666/B666M 1556.2.2 Marking of Magnesium IngotThe producers name or trademark (see 4.1.1), alloy designation (see 4.1.2), and castnumber shall be impression-stamped or otherwise permanently marked on each ingot or bundle, if strapped together. Specificationnumber shall not be required to be marked on this product.6.3 Ingot or Billet for FabricatingWhen specified in the contract or purchase order, m