ASTM B666 B666M-2008 Standard Practice for Identification Marking of Aluminum and Magnesium Products《铝和镁制品的识别标记的标准实施规程》.pdf

《ASTM B666 B666M-2008 Standard Practice for Identification Marking of Aluminum and Magnesium Products《铝和镁制品的识别标记的标准实施规程》.pdf》由会员分享，可在线阅读，更多相关《ASTM B666 B666M-2008 Standard Practice for Identification Marking of Aluminum and Magnesium Products《铝和镁制品的识别标记的标准实施规程》.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B 666/B 666M 08Standard Practice forIdentification Marking of Aluminum and MagnesiumProducts1This standard is issued under the fixed designation B 666/B 666M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of

2、 last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This practice establishes the physi

3、cal item markingrequirements for identification purposes for aluminum andmagnesium products. Package marking for shipment andinspection acceptance is not within the scope of this standard.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The value

4、s stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with it

5、s use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 The following documents of the issue in effect on thedate of material purchase form a p

6、art of this specification to theextent referenced herein:2.2 ASTM Standards:2B 361 Specification for Factory-Made Wrought Aluminumand Aluminum-Alloy Welding FittingsB 404/B 404M Specification for Aluminum and Aluminum-Alloy Seamless Condenser and Heat-Exchanger Tubeswith Integral Fins3B 547/B 547M S

7、pecification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round TubeB 881 Terminology Relating to Aluminum- andMagnesium-Alloy Products2.3 ANSI Standards:H35.1/H35.1(M) Alloy and Temper Designation Systemsfor Aluminum42.4 Military Standards:MIL-STD-409 Alloy Nomenclature and Temper Designa-

8、tion System for Magnesium Base Alloys53. Terminology3.1 DefinitionsRefer to Terminology B 881 for definitionsof product terms used in this specification.3.2 Definitions of Terms Specific to This Standard:3.2.1 Marking:3.2.2 spot markingmarking the identification only onceon the product.3.2.3 continu

9、ous markingrecurring marking of the iden-tification in intervals not greater than 40 in. 1000 mmthroughout the length of the product.3.2.4 perimeter markingmarking continuously the identi-fication in one or two rows adjacent to the four edges of theproduct.3.2.5 taggingattaching tags bearing the req

10、uired identifi-cation markings to coils, bundles, or containers of items whichare too small to mark or whose configuration preclude markingotherwise.4. Basic Marking Requirements and Application4.1 When this practice is required by the material specifi-cation or specified in the contract or purchase

11、 order, wroughtaluminum and magnesium mill products shall be marked foridentification purposes only with the following information onthe product or on tags attached to the product:1This practice is under the jurisdiction of ASTM Committee B07 on LightMetals and Alloys and is the direct responsibilit

12、y of Subcommittee B07.03 onAluminum Alloy Wrought Products.Current edition approved July 15, 2008. Published August 2008. Originallyapproved in 1980. Last previous edition approved in 2001 as B 666/B 666M 01.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Custome

13、r Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn.4Available from Aluminum Association, Inc., 1525 Wilson Blvd., Suite 600,Arlington, VA 22209, http:/www.aluminum.org.5Available from Standardi

14、zation Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.dodssp.daps.mil.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, Unit

15、ed States.4.1.1 Name or Registered Trademark of the Company,which performs the final processing or finishing operation suchas rolling, stretching, thermal treatment, etc., prior to market-ing the product;NOTE 1The company that performs nothing more than a simpleshearing or sawing operation may be ex

16、cluded from marking the productwith its name.4.1.2 Alloy and Temper of the ProductDesignations shallbe in accordance with ANSI H35.1/H35.1M for aluminum andMIL-STD-409 for magnesium;4.1.3 Basic Number of the Specification to which the Prod-uct was ProducedThe basic number does not include therevisio

17、n indicator;4.1.4 Specified (Ordered) Dimensions of the FollowingProducts:4.1.4.1 Sheet and PlateThickness in inches millimetres,4.1.4.2 Coiled Wire and Spooled WireDiameter in inchesmillimetres,4.1.4.3 Tube:(1) Straight LengthsOutside diameter and wall thick-ness, in inches millimetres,(2) CoiledWa

18、ll thickness, in inches millimetres,4.1.4.4 PipeNominal pipe size and ANSI schedule num-ber;4.1.5 Lot number shall be included in the product marking.The definition of lot shall be that as defined in the materialspecification.4.1.6 For magnesium products, the applicable lot numbershall be marked on

19、each piece in at least one location.4.1.7 When required by the material specification, the word“seamless” on certain tube or pipe.NOTE 2The requirements specified in 4.1 are minimum; markingsystems that involve additional information shall be as agreed uponbetween the producer and the purchaser.4.2

20、When this practice is required by the material specifi-cation or specified in the contract or purchase order, marking ofcast aluminum products shall be in accordance with Section 6.4.3 Product marking shall be such that it shall not rub off orbe otherwise obliterated by contact arising from normal h

21、an-dling, exposure to the elements, shipment, and storage. Theheight of the characters shall be commensurate with the size ofthe product being marked; for example, not less than 0.375 in.9 mm for flat sheet and plate, not less than 0.250 in. 6 mmfor hand forgings and not less than 0.125 in. 3 mm for

22、 tubularproducts. Legibility of all markings shall be such as requiredfor ready readability and the required permanency of identifi-cation.4.4 Product marking shall be accomplished in a manner thatwill not adversely affect the subsequent fabrication of thematerial, or produce stresses that would be

23、deleterious to thefunctioning of the finished product. Marking on the productshall be with marking fluid applied by printing, stamping, orstenciling. Ghost images of the characters may remain upon theremoval of marking applied. Impression stamping is consid-ered detrimental and shall not be used exc

24、ept on ingot,castings, forging, and certain tube products, or when requiredby prior agreement between the producer and purchaser.5. Marking of Wrought Aluminum and Magnesium MillProducts5.1 When this practice is required by the material specifi-cation or specified in the contract or purchase order,

25、wroughtaluminum and magnesium mill products shall be marked asfollows:5.1.1 Lot Number, All ProductsSpot marking the product.5.1.2 Coiled SheetSpot marking in one or more rows nearthe outside end as shown in Fig. 1 1M.5.1.3 Flat Sheet and Plate:5.1.3.1 Flat sheet less than 0.012 in. up through 0.30

26、mm(for O temper, less than 0.020 in. up through 0.50 mm) inthicknessSpot marking near one end,5.1.3.2 Plate and flat sheet 0.012 in. and over over 0.30mm (for O temper, 0.020 in. and over over 0.50 mm) inthickness and less than 6 in. up through 150 mm wideContinuous marking in one row,5.1.3.3 Plate

27、up through 0.375 in. 10 mm and flat sheet0.012 in. and over over 0.30 mm (for O temper, 0.020 in. andover over 0.50 mm) in thickness, 6 through 60 in. over 150through 1500 mm in width, and 36 through 200 in. over 1000through 5000 mm in lengthContinuous marking in rowsrunning the direction of rolling

28、 on 6 in. 150 mm centersacross the width on one surface as shown in Fig. 2 2M andFig. 33M. Using the marking pattern of Fig. 2 2M, everythird row shall contain the producers name or trademark andthe ordered thickness. The other two rows shall each containthe alloy and temper and the specification nu

29、mber, and shall bestaggered. Using the marking pattern of Fig. 33M, there aretwo alternating rows. One row shall contain the producersname or trademark and the ordered thickness, and the alternat-ing row shall contain the alloy and temper and the specificationnumber. Both the marking patterns shown

30、in Fig. 22M andFig. 33M provide the same information and either can beused.5.1.3.4 Plate over 0.375 in. 10 mm in thickness, flat sheetand plate over 60 in. 1500 mm in width or over 200 in. 5000mm in lengthSame marking as 5.1.3.3 or perimeter markingFig. 1 Spot Marking for Coiled SheetFIG. 1 M Spot M

31、arking for Coiled SheetB 666/B 666M 082on one surface. When perimeter marking of two rows ischosen, one row shall contain the producers name or trade-mark and the ordered thickness, and the second row shallcontain alloy and temper, and the specification number asshown in Fig. 4 4M.NOTE 3If perimeter

32、 marking is applied to a full piece as produced butpartial sheets or plates are supplied, an arrow shall be applied near onecorner of each partial sheet or plate indicating the direction of rolling.5.1.4 Circles:5.1.4.1 Circles 24 in. and over over 600 mm in diameterSpot marking on each circle unles

33、s the circle was cut fromsheet or plate having continuous marking, andNoteMarking pattern is three staggered rows: two rows contain alloy, temper, and specification number, and every third row contains producers name and orderedthickness. Figure shows spot marking of the lot number.FIG 2 Continuous

34、Marking for Plate Through 0.375 in. and Flat Sheet 0.012 in. and over (for O Temper, 0.020 in. and over) in Thickness, 6 Through 60 in.in Width, and 36 Through 200 in. in LengthNoteMarking pattern is three staggered rows: two rows contain alloy, temper, and specification number, and every third row

35、contains producers name and orderedthickness. Figure shows spot marking of the lot number.FIG. 2 M Continuous Marking for Plate Through 10 mm and Flat Sheet over 0.30 mm (for O Temper, over 0.50 mm) in Thickness, over150 Through 1500 mm in Width, and 1000 Through 5000 mm in LengthB 666/B 666M 0835.1

36、.4.2 Circles less than 24 in. up through 600 mm indiameterTagging or marking of shipping container.NOTE 4Alclad one side flat sheet, plate, circles, and coiled sheet shallbe marked on the bare side.5.1.5 Tread PlateSpot marking near one end on the backside.5.1.6 FoilMarking of this product is not re

37、quired. Pack-age marking only.5.1.7 Rod, Bar, and Extruded ProfilesContinuous mark-ing of straight lengths as shown in Fig. 5 5M, of sizes havingan accessible flat surface of12 in. or more over 12.5 mm inwidth (with less than18 in. 3 mm and less indented surface),NoteMarking pattern is two alternati

38、ng rows: one row contains alloy, temper, and specification number, and the alternating row contains the producers name andordered thickness. Figure shows spot marking of the lot number.FIG 3 Continuous Marking for Plate Through 0.375 in. and Flat Sheet 0.012 in. and over (for O Temper, 0.020 in. and

39、 over) in Thickness, 6 Through 60 in.in Width, and 36 Through 200 in. in Length.NoteMarking pattern is two alternating rows: one row contains alloy, temper, and specification number, and the alternating row contains the producers name andordered thickness. Figure shows spot marking of the lot number

40、.FIG. 3 M Continuous Marking for Plate Through 10 mm and Flat Sheet over 0.30 mm (for O Temper, over 0.50 mm) in Thickness, over150 Through 1500 mm in Width, and 1000 Through 5000 mm in Length.B 666/B 666M 084or a diameter of12 in. over 12.5 mm or more. Tagging isapplicable to smaller sizes, lengths

41、 under 3 ft 1 m and coils.5.1.8 Structural ProfilesSpot marking near one end asshown in Fig. 6 6M.NoteFigure shows spot marking of the lot number. Arrow indicates the rolling direction.FIG 4 Perimeter Marking for Plate over 0.375 in. in Thickness, Flat Sheet and Plate over 60 in. in Width or over 20

42、0 in. in Length.NoteFigure shows spot marking of the lot number. Arrow indicates the rolling direction.FIG. 4 M Perimeter Marking for Plate over 10 mm in Thickness, Flat Sheet and Plate over 1500 mm in Width or over 5000 mm inLength.FIG 5 Continuous Marking for Rod, Bar, Profiles, and Tube in Straig

43、ht LengthsFIG. 5 M Continuous Marking for Rod, Bar, Profiles, and Tube in Straight LengthsB 666/B 666M 0855.1.9 Tube and PipeContinuous marking of non-roundstraight lengths in a single row of sizes having both a wallthickness of 0.029 in. and greater over 0.72 mm and a flatsurface of12 in. or more o

44、ver 12.5 mm in width. Continuousmarking of round straight lengths in a single row of sizeshaving both a wall thickness of 0.029 in. and greater over 0.72mm and a diameter of12 in. or more over 12.5 mm. Taggingis applicable to each coil or bundle of smaller sizes and lengthsunder 3 ft 1 m.5.1.10 Wire

45、Tagging of coils and straight lengths, and spotmarking on one flange of spools.5.1.11 Bus BarSpot marking near one end except thatspecification number shall not be required to be marked on thisproduct.5.1.12 Forgings:5.1.12.1 Hand ForgingSpot marking on one place of eachpiece.5.1.12.2 Die ForgingMar

46、king in accordance with therequirements of the forging drawing.6. Marking of Cast Aluminum Products6.1 CastingsMarking shall be that as specified by theapplicable material specification or as agreed upon between theproducer and the purchaser.6.2 Remelt Ingot for Castings:6.2.1 Marking of Aluminum In

47、gotThe producers name ortrademark (see 4.1.1), alloy designation (see 4.1.2) and castnumber shall be impressioned-stamped or otherwise perma-nently marked on each ingot or if strapped together, not lessthan four ingots in each bundle, two in the top layer and two inthe bottom layer. Specification nu

48、mber shall not be required tobe marked on this product.6.2.2 Marking of Magnesium IngotThe producers nameor trademark (see 4.1.1), alloy designation (see 4.1.2), and castnumber shall be impression-stamped or otherwise permanentlymarked on each ingot or bundle, if strapped together. Specifi-cation nu

49、mber shall not be required to be marked on thisproduct.6.3 Ingot or Billet for FabricatingWhen specified in thecontract or purchase order, marking shall include the produc-ers name or trademark, alloy and cast number. Specificationdata shall not be required to be marked on these products.7. Marking of Unalloyed Aluminum and MagnesiumIngot7.1 When specified in the contract or purchase order,unalloyed aluminum ingot shall be marked as