ANSI ASTM F1178-2011 Standard Specification for Performance of Enameling System Baking Metal Joiner Work and Furniture《上釉系统、烘干、金属连接件装置和家具的性能规范》.pdf
《ANSI ASTM F1178-2011 Standard Specification for Performance of Enameling System Baking Metal Joiner Work and Furniture《上釉系统、烘干、金属连接件装置和家具的性能规范》.pdf》由会员分享,可在线阅读,更多相关《ANSI ASTM F1178-2011 Standard Specification for Performance of Enameling System Baking Metal Joiner Work and Furniture《上釉系统、烘干、金属连接件装置和家具的性能规范》.pdf(8页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: F1178 11 (Reapproved 2015) An American National StandardStandard Specification forPerformance of Enameling System, Baking, Metal JoinerWork and Furniture1This standard is issued under the fixed designation F1178; the number immediately following the designation indicates the year oforig
2、inal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the performance of a bakingprimer and
3、 enamel on metal for use on fabricated metalproducts, including marine furniture and joiner work.1.2 The values stated in inch-pound units are to be regardedas standard. The metric (SI) units, given in parentheses, are forinformation only.1.3 Painting facilities shall comply with all applicableFeder
4、al and State regulations regarding emissions and wastedisposal.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applic
5、a-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2A1008/A1008M Specification for Steel, Sheet, Cold-Rolled,Carbon, Structural, High-Strength Low-Alloy, High-Strength Low-Alloy with Improved Formability, SolutionHardened, and Bake HardenableA653/A653M Specific
6、ation for Steel Sheet, Zinc-Coated(Galvanized) or Zinc-Iron Alloy-Coated (Galvannealed)by the Hot-Dip ProcessB117 Practice for Operating Salt Spray (Fog) ApparatusB209 Specification for Aluminum and Aluminum-AlloySheet and PlateD522 Test Methods for Mandrel Bend Test of AttachedOrganic CoatingsD1186
7、 Test Methods for Nondestructive Measurement ofDry Film Thickness of Nonmagnetic Coatings Applied toa Ferrous Base (Withdrawn 2006)3D1400 Test Method for Nondestructive Measurement of DryFilm Thickness of Nonconductive Coatings Applied to aNonferrous Metal Base (Withdrawn 2006)3D3359 Test Methods fo
8、r Measuring Adhesion by Tape TestD3363 Test Method for Film Hardness by Pencil Test2.2 American Institute of Steel Construction Manual:4AISC Wire and Sheet Metal Gages Equivalent Thickness inDecimals of an Inch, U.S. Standard Gauge (USSG) forUncoated Hot and Cold Rolled Sheets and GalvanizedSheet Ga
9、ge (GSG) for Hot-Dipped Zinc Coated Sheets2.3 Code of Federal Regulations:540 CFR 60 Subpart EEStandard of Performance for Sur-face Coating of Metal Furniture3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 air dry touch-up enamelan air drying enamel thatmatches the factory app
10、lied enamel in color and gloss and iscompatible with it.3.1.2 baking finishan enamel that requires baking attemperatures above 150F (65C) for the development ofdesired properties.3.1.3 blisteran enclosed raised spot on the paint surfacecaused by moisture or solvent trapped under the surface.3.1.4 cl
11、eaningthe first phase of the metal pretreatmentprior to painting.3.1.5 cureto condense or polymerize a material byheating, resulting in the full development of desired properties.3.1.6 degreasingto remove grease from a surface usingchemical solvent, steam or other method. See cleaning.3.1.7 dry film
12、 thickness (DFT)the actual thickness of thecured paint system. It is measured in mils or thousandths of aninch, that is, 0.001 in. (25.4 m).1This specification is under the jurisdiction of ASTM Committee F25 on Shipsand Marine Technology and is the direct responsibility of Subcommittee F25.01 onStru
13、ctures.Current edition approved Oct. 1, 2015. Published October 2015. Originallyapproved in 1988. Last previous edition approved in 2011 as F1178 11. DOI:10.1520/F1178-11R15.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For
14、Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.4Available from American Institute of Steel Construction (AISC), One E.Wacker Dr., Suite 700, Chicago,
15、IL 60601-2001, http:/www.aisc.org.5Available from U.S. Government Printing Office Superintendent of Documents,732 N. Capitol St., NW, Mail Stop: SDE, Washington, DC 20401, http:/www.access.gpo.gov.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. Uni
16、ted States13.1.8 enamela paint characterized by the ability to form anespecially smooth film.3.1.9 galvanized steelzinc coated steel sheet in confor-mance with Specification A653/A653M, Coating DesignationA1.3.1.10 glossthe degree to which a painted surface reflectslight.3.1.11 joiner workdoors, fra
17、mes, ceilings, bulkheads,window casings, and all trim pieces in accommodation spacesaboard ship.3.1.12 low glossfinish that shows a gloss of 25 to 35 whenmeasured with 60 glossmeter. A ceiling gloss is 6 to 16 whenmeasured the same way.3.1.13 pretreatmentusually restricted to mean the chemi-cal trea
18、tment of unpaired surfaces before painting.3.1.14 smootheven surface finish, glass-like to touch.3.1.15 texturedregular or irregular surface finish.4. Ordering Information4.1 Unless otherwise specified, a smooth, low-gloss enamelfinish will be applied.4.1.1 Color of enamel top coat.4.1.2 Finish:4.1.
19、2.1 Smooth.4.1.2.2 Textured.4.1.3 Gloss (measured with 60 glossmeter):4.1.3.1 Low gloss25 to 35.4.1.3.2 Ceiling gloss6 to 18.5. Materials and Manufacture5.1 Metal substrateThis specification is intended for useon metal furniture and joiner work of either steel or aluminum.5.2 For a smooth, low-gloss
20、 finish, the furniture or joinerwork manufacturer shall follow the procedures in the order andas listed in Sections 6 through 7.5.3 If a textured finish is specified, the furniture or joinerwork manufacturer shall follow the procedures in the order andas listed in Sections 6 through 8.6. Cleaning an
21、d Degreasing6.1 All exterior and interior surfaces, both visible andconcealed, and all joints shall be thoroughly cleaned anddegreased.6.2 The cleaning/rinsing process shall remove dirt, oilgrease, moisture, and other foreign matter.6.3 No detrimental residue from this process shall remaindeposited
22、on any surface.7. Enameling7.1 All surfaces contributing to the appearance of the finalproduct shall be enameled to a smooth, low-gloss finish incolors specified in the ordering documents.7.2 Enamel shall be applied in an amount sufficient toproduce a minimum dry film thickness of 1.5 mils (0.0015 i
23、n.(38.1 m) for joiner doors and frames. For other joinermaterials and furniture, 1 to 1.5 mils (0.001 to 0.0015 in. (25.4to 38.1 m) is acceptable.7.3 The enamel required under this specification shall be athermosetting type, requiring a high baking schedule for propercure. This enamel shall satisfy
24、the requirements of Section 9.8. Texturing (Optional)8.1 If a textured finish is required by ordering documents,the enamel chosen shall be capable of producing a suitableraised textured finish when using equipment and techniquesrecommended by the manufacturer.8.2 All requirements for enameling of th
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
5000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ANSIASTMF11782011STANDARDSPECIFICATIONFORPERFORMANCEOFENAMELINGSYSTEMBAKINGMETALJOINERWORKANDFURNITURE
链接地址:http://www.mydoc123.com/p-432763.html