SAE AMS 4442G-2012 Magnesium Alloy Sand Castings 3 2 Rare Earths - 2 5Zn - 0 70Zr (EZ33A-T5) Precipitation Heat Treated (UNS M12330)《镁合金砂模铸件3 2稀土族2 5Zn 0 70Zr (EZ33A-T5)沉积热处理》.pdf

《SAE AMS 4442G-2012 Magnesium Alloy Sand Castings 3 2 Rare Earths - 2 5Zn - 0 70Zr (EZ33A-T5) Precipitation Heat Treated (UNS M12330)《镁合金砂模铸件3 2稀土族2 5Zn 0 70Zr (EZ33A-T5)沉积热处理》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 4442G-2012 Magnesium Alloy Sand Castings 3 2 Rare Earths - 2 5Zn - 0 70Zr (EZ33A-T5) Precipitation Heat Treated (UNS M12330)《镁合金砂模铸件3 2稀土族2 5Zn 0 70Zr (EZ33A-T5)沉积热处理》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2012 SAE International All rights reserved. No part of this publication m

3、ay be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside U

4、SA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS4442G AEROSPACE MATERIAL SPECIFICATION AMS4442 REV. G Issued 1956-07 Reaffirmed 2000-09 Re

5、vised 2012-06 Superseding AMS4442F Magnesium Alloy Sand Castings 3.2 Rare Earths - 2.5Zn - 0.70Zr (EZ33A-T5) Precipitation Heat Treated (Composition similar to UNS M12330) RATIONALE AMS4442G revises Composition (3.1) and Sampling for Chemical Analysis (4.3.1), removes the requirement for determinati

6、on of soluble zirconium (Table 1, 3.1.2), and results from a Five Year Review and update of this specification, 1. SCOPE 1.1 Form This specification covers a magnesium alloy in the form of sand castings. 1.2 Application These castings have been used typically for parts operating up to 500 F (260 C),

7、 and have good pressure tightness, but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision

8、 of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. SAE AMS4442G Page 2 of 8 2.1 SAE Publications Available from SAE International, 400 Com

9、monwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2360 Room Temperature Tensile Properties of Castings AMS2361 Elevated Temperature Tensile Properties of Castings AMS2475 Protective Treatments, Magnesium Alloys AMS269

10、4 In-Process Welding of Castings AMS2750 Pyrometry AMS2804 Identification, Castings 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM B 557 Tension Testing Wrought and Cast Aluminum a

11、nd Magnesium-Alloy Products ASTM B 660 Packaging/Packing of Aluminum and Magnesium Products ASTM B 953 Sampling Magnesium and Magnesium Alloys for Spectrochemical Analysis ASTM B 954 Analysis of Magnesium and Magnesium Alloys by Atomic Emission Spectrometry ASTM E 21 Elevated Temperature Tension Tes

12、ts of Metallic Materials ASTM E 155 Reference Radiographs for Inspection of Aluminum and Magnesium Castings ASTM E 1417 Liquid Penetrant Testing ASTM E 1742 Radiographic Examination 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determined by s

13、pectrochemical methods in accordance with ASTM B 954, or by other analytical methods acceptable to purchaser. TABLE 1 - COMPOSITION Element min max Total Rare Earths (3.1.1) 2.5 4.0 Zinc 2.0 3.1 Zirconium, total 0.40 1.0 Copper (3.1.2) - 0.10 Nickel (3.1.2) - 0.01 Other Elements, each - 0.10 Other E

14、lements, total - 0.30 Magnesium remainder SAE AMS4442G Page 3 of 8 3.1.1 Total Rare Earths (TRE) are principally a mixture of Cerium, Lanthanum, Neodymium and Praseodymium. The Cerium content shall not be less than 45% of TRE. 3.1.2 Determination not required for routine acceptance. 3.2 Condition Pr

15、ecipitation heat treated. 3.3 Casting Castings shall be produced from metal conforming to 3.1. Furnace or ladle additions of grain-refining elements or alloys shall be added to the melt. Molten metal taken from alloying furnaces, with or without addition of foundry operating scrap (gates, sprues, ri

16、sers, and rejected castings), shall not be poured into castings unless first converted to ingot, analyzed, and remelted or unless the composition of a sample taken after the last addition to the melt conforms to 3.1. 3.3.1 A melt shall be the metal withdrawn from a batch-furnace charge of 2000 pound

17、s (907 kg) or less as melted for pouring castings or, when permitted by purchaser, a melt shall be 4000 pounds (1814 kg) or less of metal withdrawn from one continuous furnace in not more than eight consecutive hours. 3.3.2 A lot shall be all castings poured from a single melt in not more than eight

18、 consecutive hours and precipitation heat treated in the same heat treatment batch. 3.4 Cast Test Specimens Chemical analysis specimens and tensile specimens shall be cast as follows and, when requested, shall be supplied with the castings: 3.4.1 Chemical Analysis Specimens Shall be cast from each m

19、elt and shall be of any suitable size, shape, and form. 3.4.2 Tensile Specimens Shall be cast with each lot of castings, shall be of standard proportions conforming to ASTM B 557 with 0.500 inch (12.70 mm) diameter at the reduced parallel gage section, and shall be cast to size in molds made with th

20、e regular foundry mix of sand without using chills. Metal for the specimens shall be part of the melt that is used for the castings and shall be subjected to the same grain refining or alloying treatment given the metal for casting. The temperature of the metal during pouring of the specimens shall

21、be not lower than that during pouring of the castings. 3.5 Heat Treatment Castings and representative tensile specimens shall be precipitation heat treated by heating to a temperature not higher than 475 F (246 C), except as specified in 3.5.1, holding at the selected temperature within 15 F (8 C) f

22、or the proper time for precipitation heat treatment, and cooling in air. At least one set of tensile specimens shall be put into a batch-type furnace with each load of castings or into a continuous furnace at intervals of not longer than 3 hours. Pyrometry shall be in accordance with AMS2750. 3.5.1

23、When specified by purchaser for applications where high-temperature creep properties are not important, castings and representative tensile specimens shall be precipitation heat treated by heating to a temperature not higher than 650 F (346 C), holding at the selected temperature within 15 F (8 C) f

24、or not longer than 2 hours, and cooling in air. 3.6 Properties Castings and separately-cast tensile specimens produced in accordance with 3.4.2 shall conform to the following requirements: SAE AMS4442G Page 4 of 8 3.6.1 Tensile Properties Conformance to the requirements of 3.6.1.1.1 shall be used as

25、 the basis for acceptance of castings except when purchaser specifies that the requirements of 3.6.1.1.2 apply. 3.6.1.1 At Room Temperature Shall be as shown in 3.6.1.1.1 or 3.6.1.1.2, determined in accordance with ASTM B 557. 3.6.1.1.1 Separately-Cast Specimens TABLE 2 - MINIMUM TENSILE PROPERTIES

26、Property Value Tensile Strength 20.0 ksi (138 MPa) Yield Strength at 0.2% Offset 14.0 ksi ( 96 MPa) Elongation in 2 inches (50.8 mm) or 4D 2.0% 3.6.1.1.2 Specimens Cut From Castings or From Integrally-Cast Coupons Specimens as in 4.3.4 shall meet the requirements of Table 3. TABLE 3 - MINIMUM TENSIL

27、E PROPERTIES Property Value Tensile Strength 13.0 ksi (90 MPa) Yield Strength at 0.2% Offset 11.0 ksi (76 MPa) Elongation in 2 inches (50.8 mm) or 4D 1.5% 3.6.1.2 At 500 F (260 C) Shall be as shown in 3.6.1.2.1 or 3.6.1.2.2, determined in accordance with ASTM E 21 on specimens heated to 500 F 5 (260

28、 C 3), held at heat for 10 to 20 minutes before testing, and tested at 500 F 5 (260 C 3). 3.6.1.2.1 Separately-Cast Specimens TABLE 4 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength 13.0 ksi (90 MPa) Yield Strength at 0.2% Offset 8.0 ksi (55 MPa) 3.6.1.2.2 Specimens Cut From Castings or

29、 From Integrally-Cast Coupons Specimens as in 4.3.4 shall meet the requirements of Table 5. TABLE 5 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength 10.0 ksi (69 MPa) Yield Strength at 0.2% Offset 6.0 ksi (41 MPa) 3.6.1.3 When properties other than those specified in 3.6.1.1.2 and 3.6.1.

30、2.2 are required, tensile specimens as in 4.3.4 taken from locations indicated on the drawing, from a casting or castings chosen at random to represent the lot, shall have the properties indicated on the drawing for such specimens. Property requirements at room temperature may be designated in accor

31、dance with AMS2360 and at elevated temperature in accordance with AMS2361. SAE AMS4442G Page 5 of 8 3.7 Quality Castings, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the castings. 3.7.1 Cas

32、tings shall have smooth surfaces sufficiently cleaned to permit fluorescent penetrant inspection. 3.7.1.1 Castings cleaned by blasting shall be pickled in a sulfuric or sulfuric/nitric acid solution to remove not less than 0.002 inch (0.05 mm) of metal prior to protective treatment as in 5.2. 3.7.2

33、Castings shall be produced under radiographic control. This control shall consist of radiographic examination of castings in accordance with ASTM E 1742 or other radiographic procedure acceptable to purchaser until proper foundry technique, which will produce castings free from harmful internal impe

34、rfections, is established for each part number and of production castings as necessary to ensure maintenance of satisfactory quality. 3.7.3 When specified, castings shall be subjected to fluorescent penetrant inspection in accordance with ASTM E 1417. 3.7.4 Radiographic, fluorescent penetrant, and o

35、ther quality standards shall be as agreed upon by purchaser and vendor. ASTM E 155 may be used to define radiographic acceptance standards. 3.7.5 Castings shall not be peened, plugged, impregnated, or welded unless authorized by purchaser. 3.7.5.1 When authorized by purchaser, welding in accordance

36、with AMS2694 or other welding program approved by the purchaser may be used. 3.7.6 Castings shall not be impregnated, chemically treated, or coated to prevent leakage unless specified or allowed by written permission of purchaser designating the method to be used. 4. QUALITY ASSURANCE PROVISIONS 4.1

37、 Responsibility for Inspection The vendor of castings shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the castings conform to

38、specified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests Except as specified in 4.2.1.1, tests for composition (3.1), tensile properties at room temperature (3.6.1.1), and quality (3.7) are acceptance tests and shall be performed to represent each melt or lot as applicable. 4.2.1.1

39、 Tensile properties of specimens cut from castings or from integrally-cast coupons shall be determined only when specified by purchaser or when separately-cast specimens are not available. Tensile properties of separately-cast specimens need not be determined when tensile properties of specimens cut

40、 from castings or from integrally-cast coupons are determined. 4.2.2 Periodic Tests Tensile properties at 500 F (260 C) (3.6.1.2) is a periodic test and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser. 4.2.3 Preproduction Tests Tests for

41、 all technical requirements are preproduction tests and shall be performed prior to or on the first-article shipment of a casting to a purchaser, when a change in material and/or processing requires reapproval as in 4.4.2, and when purchaser deems confirmatory testing to be required. SAE AMS4442G Pa

42、ge 6 of 8 4.3 Sampling and Testing Shall be in accordance with the following: 4.3.1 One chemical analysis specimen in accordance with 3.4.1 and ASTM B 953 from each melt or a casting from each lot. 4.3.2 One separately-cast tensile specimen in accordance with 3.4.2 from each lot. 4.3.3 Two preproduc

43、tion castings in accordance with 4.4.1 of each part number. 4.3.4 Except as permitted by 4.3.4.1, one or more castings from each lot when tensile properties of specimens machined from castings are required. Specimens shall conform to ASTM B 557 and shall be either 0.500 inch (12.70 mm) diameter at t

44、he reduced parallel gage section, subsize specimens proportional to the standard, or standard sheet-type specimens. For determining conformance to the requirements of 3.6.1.1.2, 3.6.1.2.2, or 3.6.1.3, if specimen locations are not shown on the drawing, not less than four tensile specimens, two from

45、the thickest section and two from the thinnest section, shall be cut from a casting or castings from each lot. 4.3.4.1 When permitted by purchaser, tensile specimens conforming to ASTM B 557 excised from integrally-cast coupons may be used in lieu of separately-cast specimens (4.3.2) or specimens cu

46、t from a casting or castings (4.3.4). Size, number, and location of integrally-cast coupons shall be as specified by purchaser. 4.4 Approval 4.4.1 Sample castings from new or reworked patterns and the casting procedure shall be approved by purchaser before castings for production use are supplied, u

47、nless such approval is waived by purchaser. 4.4.2 Vendor shall establish, for production of sample castings of each part number, parameters for the process control factors that will produce acceptable castings; these shall constitute the approved casting procedure and shall be used for producing pro

48、duction castings. If necessary to make any change in parameters for the process control factors, vendor shall submit for reapproval a statement of the proposed changes in processing and when requested, test specimens, sample castings, or both. Production castings incorporating the revised operations

49、 shall not be shipped prior to receipt of reapproval. 4.4.2.1 Process control factors include, but are not limited to, the following: Type of furnace Furnace atmosphere Fluxing or oxide removal procedure Gating and risering practices Metal pouring temperature; variation of 50 F (28 C) from established limit is permissible Solidification and cooling procedures Precipitation heat treatment cycle Cleaning op