SAE AMS 4063E-2008 Aluminum Alloy Clad One Side Sheet 1 25Mn - 0 12Cu (No 11-0 Brazing Sheet) Annealed (UNS A83003)《1 25Mn 0 12Cu(No 11-0铜焊薄板材)退火的铝合金单面涂覆薄板材》.pdf

《SAE AMS 4063E-2008 Aluminum Alloy Clad One Side Sheet 1 25Mn - 0 12Cu (No 11-0 Brazing Sheet) Annealed (UNS A83003)《1 25Mn 0 12Cu(No 11-0铜焊薄板材)退火的铝合金单面涂覆薄板材》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 4063E-2008 Aluminum Alloy Clad One Side Sheet 1 25Mn - 0 12Cu (No 11-0 Brazing Sheet) Annealed (UNS A83003)《1 25Mn 0 12Cu(No 11-0铜焊薄板材)退火的铝合金单面涂覆薄板材》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2013 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS4063E AEROSPACE MATERIAL SPECIFICATION AMS4063 REV. E Issued 1968-05 Revised 2

5、008-06 Reaffirmed 2013-12 Superseding AMS4063D Aluminum Alloy, Clad One Side, Sheet 1.25Mn - 0.12Cu (No. 11-0 Brazing Sheet) Annealed (Composition similar to UNS A83003) RATIONALE AMS4063E has been reaffirmed to comply with the SAE five-year review policy. 1. SCOPE 1.1 Form This specification covers

6、 an aluminum alloy in the form of clad sheet. 1.2 Application This sheet has been used typically for brazed assemblies which are not subject to heat treatment after joining, but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the d

7、ate of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the

8、 last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2355 Quality Assurance Sampling and Testing of Alumin

9、um Alloys and Magnesium Alloys, Wrought Products, Except Forging Stock, and Rolled, Forged, or Flash Welded Rings SAE INTERNATIONAL AMS4063E Page 2 of 5 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585,

10、 www.astm.org. ASTM B 660 Packaging/Packing of Aluminum and Magnesium Products ASTM B 666/666M Identification Marking of Aluminum and Magnesium Products 2.3 ANSI Publications Available from American National Standards Institute, 25 West 43rd Street, New York, NY 10036, Tel: 212-642-4900, www.ansi.or

11、g. ANSI H35.2 Dimensional Tolerances for Aluminum Mill Products ANSI H35.2M Dimensional Tolerances for Aluminum Mill Products (Metric) 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Tables 1 and 2, determined in accordance with AMS2355. TABLE 1 - COMPOS

12、ITION, CORE (3003) Element min maxSilicon Iron Copper Manganese Zinc Other Elements, each Other Elements, total Aluminum - - 0.05 1.0 - - - remainder0.6 0.7 0.201.5 0.100.050.15TABLE 2 - COMPOSITION, CLADDING (4343) Element min maxSilicon Iron Copper Manganese Zinc Other Elements, each Other Element

13、s, total Aluminum 6.8 - - - - - - remainder8.2 0.8 0.250.100.200.050.153.2 Condition Annealed. 3.3 Properties Sheet shall conform to the following requirements, determined in accordance with AMS2355 on the mill product size. SAE INTERNATIONAL AMS4063E Page 3 of 5 3.3.1 Tensile Properties Shall be as

14、 specified in Table 3. TABLE 3A - TENSILE PROPERTIES, INCH/POUND UNITS Nominal Thickness Inch Tensile Strength ksi, max Elongation in 2 Inches %, min 0.006 to 0.007, incl 20.0 12 Over 0.007 to 0.012, incl 20.0 15 Over 0.012 to 0.031, incl 20.0 18 Over 0.031 to 0.050, incl 20.0 20 Over 0.050 to 0.249

15、, incl 20.0 13 TABLE 3B - TENSILE PROPERTIES, SI UNITS Nominal Thickness Millimeters Tensile Strength MPa, max Elongation in 50.8 mm %, min 0.15 to 0.18, incl 138 12 Over 0.18 to 0.30, incl 138 15 Over 0.30 to 0.79, incl 138 18 Over 0.79 to 1.27, incl 138 20 Over 1.27 to 6.32, incl 138 13 3.3.2 Bend

16、ing Sheet shall withstand, without cracking, bending at room temperature flat on itself with axis of bend parallel to the direction of rolling. The clad side may be either the convex or concave side of the sheet for bending tests. 3.3.3 Cladding Shall be applied to only one face of the core. 3.3.3.1

17、 Cladding Thickness After rolling, the average cladding thickness shall be as specified in Table 4. TABLE 4 - MINIMUM AVERAGE CLADDING THICKNESS Total Thickness of Composite Product Inch Total Thickness of Composite Product Millimeters Cladding Thickness % of Total Thickness min Average Up to 0.063,

18、 incl Up to 1.60, incl 8 Over 0.063 to 0.250, excl Over 1.60 to 6.35, excl 4 3.4 Quality Sheet, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the sheet. 3.5 Tolerances Shall conform to all ap

19、plicable requirements of ANSI H35.2 or ANSI H35.2M. SAE INTERNATIONAL AMS4063E Page 4 of 5 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of sheet shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser re

20、serves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the sheet conforms to specified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests Composition (3.1), tensile properties (3.3.1), and tolerances (3.5) are acceptance tests and, except for

21、 composition, shall be performed on each lot. 4.2.2 Periodic Tests Bending (3.3.2) and cladding thickness (3.3.3.1) are periodic tests and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser. 4.3 Sampling and Testing Shall be in accordance w

22、ith AMS2355. 4.4 Reports The vendor of clad sheet shall furnish with each shipment a report stating that the sheet conforms to the composition and showing the results of tests to determine conformance to the other acceptance test requirements and, when performed, to the periodic test requirements. T

23、his report shall include the purchase order number, lot number, AMS4063E, size, and quantity. The report shall also identify the producer, the product form, and the size of the mill product. 4.5 Resampling and Retesting Shall be in accordance with AMS2355. 5. PREPARATION FOR DELIVERY 5.1 Identificat

24、ion Shall be in accordance with ASTM B 666/666M. 5.2 Packaging 5.2.1 Product shall be protected from damage during storage and shipment by a method determined by vendor unless specified by purchaser. Examples of typical protective methods include but are not limited to interleaving with paper or oil

25、ing of the surface. 5.2.2 Sheet shall be prepared for shipment in accordance with ASTM B 660 and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the sheet to ensure carrier acceptance and safe delivery. 6. ACKNOWLEDGMENT A vendor shall

26、 include this specification number and its revision letter in all quotations and when acknowledging purchase orders. SAE INTERNATIONAL AMS4063E Page 5 of 5 7. REJECTIONS Sheet not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.

27、1 A change bar (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of a specification. An (R) symbol to the left of the document title indicates a complete revision of the specifica

28、tion, including technical revision. Change bars and (R) are not used in original publications, nor in specifications that contain editorial changes only. 8.2 This material is occasionally purchased in the as-fabricated condition, similar to the H12 or H14 condition of other aluminum alloys, for ease

29、 of handling or other reasons. When so ordered, the mechanical properties presented in this specification are not applicable. 8.3 Terms used in AMS are clarified in ARP1917. 8.4 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. 8.5 Purchase documents should specify not less than the following: AMS4063E Size of sheet required Quantity of sheet required. PREPARED BY AMS COMMITTEE “D“