《SAE AMS 3906 5B-1992 Glass Non-Woven Fiber Tape and Flat Sheet Epoxy Resin Impregnated for Hand and Machine Layup GL-I-36 - 150 (302)《手工和机器铺叠用环氧树脂浸渍的玻璃非机织纤维带和平板GL-I-36-150(302)》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 3906 5B-1992 Glass Non-Woven Fiber Tape and Flat Sheet Epoxy Resin Impregnated for Hand and Machine Layup GL-I-36 - 150 (302)《手工和机器铺叠用环氧树脂浸渍的玻璃非机织纤维带和平板GL-I-36-150(302)》.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、SAE-AMS3906/5ADOPTION NOTICESAE-AMS3906/5, “GLASS NON-WOVEN FIBER TAPE AND FLAT SHEET EPOXYRESIN IMPREGNATED, FOR HAND AND MACHINE LAYUP GL-I-36 - 150(302)“, was adopted on 30-SEP-89 for use by the Department ofDefense (DoD). Proposed changes by DoD activities must besubmitted to the DoD Adopting Ac

2、tivity: Commander, Naval AirWarfare Center, Aircraft Division, Code 414100B120-3, Highway547, Lakehurst, NJ 08733-5100. Copies of this document may bepurchased from the Society of Automotive Engineers 400Commonwealth Drive Warrendale, Pennsylvania, United States,15096-0001. http:/www.sae.org/_Custod

3、ians: Adopting Activity:Navy - ASArmy - MRNavy - ASAREA CMPSDISTRIBUTION STATEMENT A: Approved for public release; distributionis unlimited.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-SAE Technical

4、 Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and enginee ring sciences. The use of this report is entirelyvoluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefrom, is the so

5、le responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invit es your written comments and suggestions.Copyright 1997 Society of Automotive Engineers, Inc.All rights reserved. Printed in U.S.A.QUESTIONS

6、 REGARDING THIS DOCUMENT: (412) 772-7154 FAX: (412) 776-0243TO PLACE A DOCUMENT ORDER: (412) 776-4970 FAX: (412) 776-0790400 Commonwealth Drive, Warrendale, PA 15096-0001AEROS PACE MATERIAL SPECIFIC ATIONSubmitted for recognition as an American National StandardAMS 3906/5BIssued JUN 1975Revised JUL

7、1992Reaffirmed OCT 1997Superseding AMS 3906/5AGlass Non-Woven Fiber T ape and Flat SheetEpoxy Resin Impregnated, For Hand and Machine LayupGL-I-36 - 150 (302)1. SCOPE:1.1 Form: This specification covers one type of epoxy-resin-impregnated, non-woven, glass fiber in the form of tape for hand or machi

8、ne layup and of flat sheet.1.2 Application: These products have been used typically in structural and electrical composites requiring strength up to 150 C (302 F), but usage is not limited to such applications.1.3 Classification: GL-I-36 - 150 (302), non-woven “E” glass fiber impregnated with epoxy

9、resin for service from -55 to +150 C (-67 to +302 F).2. APPLICABLE DOCUMENTS: See AMS 3906.3. TECHNICAL REQUIREMENTS: 3.1 Basic Specification: The complete requirements for procuring the product described herein shall consist of this document and the latest issue of the basic specification, AMS 3906

10、.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3906/5B SAE AMS 3906/5B- 2 -3.2 Product: Shall be a non-woven, general purpose, “E” glass fiber meeting the requirements of MIL-R-60346, Type I, imp

11、regnated with epoxy resin formulated to meet the requirements specified herein.3.3 Properties of Uncured Product: Shall be as shown in Table 1, 3.3.6, and 3.3.7. Tests shall be performed on the product as-received, after warming to above the dew point prior to sampling.3.3.6 Total weight per unit ar

12、ea, determined in accordance with 4.5.3 of AMS 3906, shall be 386 grams per square yard 28 (462 g/m 2 33).3.3.7 Ply thickness, uncured, determined in accordance with 4.5.4 of AMS 3906, shall be 0.011 inch 0.003 (0.28 mm 0.08).3.4 Properties of Cured Laminate: Shall be as follows, determined on speci

13、mens cut from a test panel prepared and tested as specified in the basic specification.3.4.1 Mechanical Properties: Shall be as specified in Table 2.TABLE 1 - PropertiesParagraph Property Requirement Test Method3.3.1 Volatile Content byweight, maximum 2%ASTM D 3530165 C 5 (329 F 9)15 minutes 13.3.2

14、Total Nonfiber Contentby weight 36% 3ASTM D 35293.3.3 Resin Flow by weight 22% 10 ASTM D 3531165 C 5 (329 F 9)3.3.4 Gel Time 3 minutes 2 ASTM D 3532165 C 5 (329 F 9)3.3.5 Tack Shall adhere for30 minutes, minimum4.5.2 of AMS 3906Copyright SAE International Provided by IHS under license with SAENot fo

15、r ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3906/5B SAE AMS 3906/5B- 3 -3.4.2 Density: Shall be determined in accordance with ASTM D 792 on the test laminate used to determine mechanical properties; values for each test laminate shall be reported. Cured resin densi

16、ty shall also be reported.3.4.3 Void Content: Shall be not greater than 4%, determined in accordance with ASTM D 2734.3.4.4 Fiber Volume: Shall be determined in accordance with 4.5.5 of AMS 3906 on the test laminate used to determine mechanical properties; values for each laminate shall be reported.

17、 The fiber density to be used shall be 2.54 g/cm 3 .4. QUALITY ASSURANCE PROVISIONS: See AMS 3906.5. PREPARATION FOR DELIVERY: See AMS 3906.6. ACKNOWLEDGMENT: See AMS 3906.7. REJECTIONS: See AMS 3906.8. NOTES:See AMS 3906.Copyright SAE International Provided by IHS under license with SAENot for Resa

18、leNo reproduction or networking permitted without license from IHS-,-AMS 3906/5B SAE AMS 3906/5B- 4 -TABLE 2A - Minimum Average Mechanical Properties(A), Inch-Pound UnitsPropertyValue, Testedat -67 F 9ksiValue, Testedat 68 to 86 FksiValue, Testedat 302 F 9ksiTestMethodTensile Strength (B) ASTM D 303

19、9Longitudinal 120 110 75.0Transverse TBR TBR TBRTensile Modulus (B) ASTM D 3039Longitudinal 5.0 x 10 3 5.0 x 10 3 4.0 x 10 3Transverse TBR TBR TBRCompressive Strength (B) ASTM D 695Longitudinal 90.0 75.0 40.0Transverse NA TBR NACompressive Modulus (B) ASTM D 695Longitudinal TBR 4.8 x 10 3 TBRTransve

20、rse NA TBR NAFlexural Strength (B) ASTM D 790Longitudinal 160 130 80.0Flexural Modulus (B) ASTM D 790Longitudinal 5.0 x 10 3 4.8 x 10 3 4.0 x 10 3Short Beam Shear Strength TBR 7.5 TBR ASTM D 2344Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networ

21、king permitted without license from IHS-,-AMS 3906/5B SAE AMS 3906/5B- 5 -TABLE 2B - Minimum Average Mechanical Properties(A), SI UnitsPropertyValue, Testedat -55 C 5MPaValue, Testedat 20 to 30 CMPaValue, Testedat 150 C 5MPaTestMethodTensile Strength (B) ASTM D 3039Longitudinal 827 758 517Transverse

22、 TBR TBR TBRTensile Modulus (B) ASTM D 3039Longitudinal 34.5 x 10 3 34.5 x 10 3 27.6 x 10 3Transverse TBR TBR TBRCompressive Strength (B) ASTM D 695MLongitudinal 621 517 276Transverse NA TBR NACompressive Modulus (B) ASTM D 695MLongitudinal TBR 33.1 x 10 3 TBRTransverse NA TBR NAFlexural Strength (B

23、) ASTM D 790MLongitudinal 1103 896 552Flexural Modulus (B) ASTM D 790MLongitudinal 34.5 x 10 3 33.1 x 10 3 27.6 x 10 3Short Beam Shear Strength TBR 52 TBR ASTM D 2344Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without licens

24、e from IHS-,-AMS 3906/5B SAE AMS 3906/5B- 6 -NOTES: (A) Average of three determinations per test. No individual value shall be less than 90%of the average value specified. Test after not less than 30 minutes exposure at the test temperature.(B) Property values are based on a test laminate with a fib

25、er volume of 50% 3. Certainproperty values may be adjusted for other fiber volumes of the test laminate by multiplyingthe listed requirement by the ratio: Actual Fiber Volume, %/50. When such adjustment is used, report the actual fiber volume of the test laminate.TBR - To be reported.NA - Not applicable.PREPARED UNDER THE JURISDICTION OF AMS COMMITTEE “P”Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-