FORD WSK-M4D665-A-2006 POLYAMIDE (PA) 6 15% GLASS FIBER REINFORCED TO BE USED WITH FORD WSS-M99P1111-A (Use WSK-M4D665-A2)《15%玻璃纤维增强的聚酰胺6 与标准FORD WSS-M99P1111-A一起使用 使用WSK-M4D66.pdf

《FORD WSK-M4D665-A-2006 POLYAMIDE (PA) 6 15% GLASS FIBER REINFORCED TO BE USED WITH FORD WSS-M99P1111-A (Use WSK-M4D665-A2)《15%玻璃纤维增强的聚酰胺6 与标准FORD WSS-M99P1111-A一起使用 使用WSK-M4D66.pdf》由会员分享，可在线阅读，更多相关《FORD WSK-M4D665-A-2006 POLYAMIDE (PA) 6 15% GLASS FIBER REINFORCED TO BE USED WITH FORD WSS-M99P1111-A (Use WSK-M4D665-A2)《15%玻璃纤维增强的聚酰胺6 与标准FORD WSS-M99P1111-A一起使用 使用WSK-M4D66.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 05 02 N-STATUS Replaced by WSK-M4D665-A2; Inserted 3.0; Deleted 3.1, 3.2, 3.8, 3.9, 4A. Reaume/M. Masserant1989 08 31 SM/EQ7118 TP Released M. Siewert Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of

2、 5 POLYAMIDE (PA) 6, 15% GLASS FIBER REINFORCED WSK-M4D665-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a glass fiber reinforced polyamide 6 molding compound. 2. APPLICATION This specification was released originally for material used for plugs. NOTICE: This

3、 material absorbs and retains moisture. Part design and tolerances must accommodate changes in part dimensions and physical properties due to moisture absorption or loss in the service/assembly environment. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and par

4、t producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 CONDITIONING AND TEST CONDITIONS All test values indicated herein are based on material and specimens with moisture content not exceeding 0.2% (test according to ISO 960, Method B/ASTM D 789

5、). All test materials immediately after processing have to be sealed in containers that are impermeable to water vapor. If the moisture content exceeds 0.2%, condition the material for a minimum of 16 h at 40 - 50 C at a reduced pressure below 133 Pa. Conduct tests in a controlled atmosphere of 23 +

6、/- 2 C and 50 +/- 5% relative humidity. Individual specimens shall not be removed from closed containers until immediately before testing. 3.4 MOLDING COMPOUND 3.4.1 Glass Fiber Content 12.5 - 17.5% (ISO 3451/4, test temperature 600 +/- 25 C, test portion 1 g) 3.4.2 Melt Temperature 215 - 225 C (ISO

7、 1218, Method B/ASTM D 789) 3.5 MOLDED TEST SPECIMEN 3.5.1 Preparation of Test Specimens Unless otherwise specified all tests shall be carried out on injection molded one-end gated test specimens. ENGINEERING MATERIAL SPECIFICATIONWSK-M4D665-A Printed copies are uncontrolled Copyright 2006, Ford Glo

8、bal Technologies, LLC Page 2 of 5 The following dimensions are required: A. 150 min x 10 x 4.0 +/- 0.2 mm (Tensile Bar, ISO 3167) B. 120 x 10 x 4.0 +/- 0.2 mm Specimens with shorter dimensions shall be cut from the center portion of the test specimen A and/or B. The specimens shall be prepared accor

9、ding to ISO 294. No annealing allowed. 3.5.2 Density 1.20 - 1.28 g/cm3(ISO 1183, Method A/ASTM D 792, Method A1) 3.5.3 Tensile Strength at Max Load, min 110 MPa (ISO R 527/ASTM D 638M, 150 x 10 x 4.0 +/- 0.2 mm specimen, 5 mm/minute test speed) 3.5.4 Flexural Modulus, min 4.5 GPa (ISO 178/ASTM D 790

10、M, Method I, Procedure A, 80 x 10 x 4.0 +/- 0.2 mm specimen, 64 mm support span) 3.5.5 Shear Modulus at 23 C 1.11 - 1.85 GPa (ASTM D 4065, forced constant amplitude, fixed frequency of 1 Hz +/- 15%, strain level below 1 %. Specimen approx. 60 x 10 x 4.0 +/- 0.2 mm cut from the center of specimen A).

11、 Additionally, a Shear Modulus vs. Temperature curve shall be plotted for -50 to +210 C temperature range, at 5 C minimum intervals. The plotted curve must be within tolerance range shown on page 5. 3.5.6 Impact Strength, Izod, min (ISO 180, Method A/ASTM D 256, Method A, 63.5 x 10 x 4.0 +/- 0.2 mm

12、specimen, 10 specimens for each test) 3.5.6.1 At 23 +/- 2 C 4.5 kJ/m23.5.6.2 At - 40 +/- 2 C 4.0 kJ/m2The test specimens must be conditioned for minimum of 6 h at the above specified temperature prior to impact test. Low temperature testing shall be done within the cold box, if not possible, test ca

13、n be conducted outside, but within 5 s. 3.5.7 Heat Deflection Temperature, min (ISO 75/ASTM D 648, 120 x 10 x 4.0 +/- 0.2 mm specimen) 3.5.7.1 At 1.82 MPa 180 C 3.5.7.2 At 0.45 MPa 200 C ENGINEERING MATERIAL SPECIFICATIONWSK-M4D665-A Printed copies are uncontrolled Copyright 2006, Ford Global Techno

14、logies, LLC Page 3 of 5 3.5.8 Heat Aging Performance (ISO 188/ASTM D 573, 150 +/- 50 air changes/h, 1000 h at 140 +/- 2 C. After heat aging test specimens are to be conditioned in a desiccator for 3 - 5 h at 23 +/- 2 C. Unaged property values shall be determined at the time of the aged properties de

15、termination) 3.5.8.1 Impact Strength, Izod Change +/- 25 % (Test Method per para 3.5.6.1, specimens to be notched before heat aging) 3.6 FLAMMABILITY (ISO 3795) Burn Rate, max 100 mm/minute The specimen size required for material approval is 355 x 100 x 1.0 +/- 0.1 mm with a smooth surface. 3.7 FOGG

16、ING (FLTM BO 116-3) Fog Number, min TBD Formation of excessive amounts of clear film or droplets is cause for rejection. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 COEFFICIENT OF LINEAR THERMA

17、L EXPANSION 3 - 6-5/C (ASTM D 696) 5.2 MOLD SHRINKAGE (ISO 2577, approx. 150 x 100 x 3.2 +/- 0.2 mm injection molded specimen) 5.2.1 Molding Shrinkage After 48 h at 23 +/- 2 C 0.3 - 1.0% 5.2.2 Post Shrinkage (Separate specimens required for each test) After 48 h at 80 C 0.01 - 0.12% After 30 minutes

18、 at 120 C 0.01 - 0.13% ENGINEERING MATERIAL SPECIFICATIONWSK-M4D665-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 4 of 5 5.3 WATER ABSORPTION 1.3 - 1.8% (ISO 62, 24 h/ASTM D 570, 24 h, 50 +/- 1 mm diameter, 3.2 +/- 0.2 mm thick specimen) 5.4 IMPACT STRENGTH, IZ

19、OD, min (ISO 180, Method A/ASTM D 256, Method A, 63.5 x 10 x 4.0 +/- 0.2 mm specimen, 10 specimens minimum) 5.4.1 After Moisture Conditioning 18 kJ/m2The notched specimens shall be immersed for 48 h in distilled water at 50 +/- 1 C and subsequently conditioned for 1 h at 23 +/- 2 C and 50 +/- 5% relative humidity prior to test and tested under the same conditions within 1 h. ENGINEERING MATERIAL SPECIFICATIONWSK-M4D665-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 5 of 5