FORD ESW-M4G153-A-1988 SEALER RUBBER BASE-FOR RADIAL OIL SEALS《径向油封圈用橡胶基密封剂》.pdf

《FORD ESW-M4G153-A-1988 SEALER RUBBER BASE-FOR RADIAL OIL SEALS《径向油封圈用橡胶基密封剂》.pdf》由会员分享，可在线阅读，更多相关《FORD ESW-M4G153-A-1988 SEALER RUBBER BASE-FOR RADIAL OIL SEALS《径向油封圈用橡胶基密封剂》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONMaterial Name Specification NumberDate Action Changes1988 03 01 CR/CR 132295-P Revised T. P. Koch1978 11 15 Metricated & Retyped PCF RD782440-P31966 10 17 Released CP5-45720WP 3948-a Page 1 of 3 SEALER, RUBBER BASE - FOR RADIAL OIL SEALS ESW-M4G153-A1. SCOPEThe mat

2、erial defined by this sp ecification is a hypalon rubber base, painttype sealer.2. APPLICATIONThis sp ecification was released originally for material applied by sealsuppliers to the O.D. of oil se als to ultimately provide an oil tight sealbetween th e oil seal O.D. and the housing bore of rear whe

3、el bearingassemblies and transmission radial oil seal assemblies.3. REQUIREMENTS3.1 CLEANINGSurfa ces to be coated shall be cleaned free from grease, oil, rustand/or other foreign materials and shall be thoroughly dry beforecoating is applied.3.2 MODE OF APPLICATIONMay be applied electrostatically o

4、r sprayed by the seal suppliers.It shall dry on the seals in 10 min (depending on seal size) whenforce dried as follows:3.2.1 Electrostatic ApplicationIn air circulating convection oven maintained at 183 +/- 5 C.3.2.2 Spray ApplicationUnder infrared lamps located approximately 250 m m from seals.Non

5、 tacky, indicates that two surfaces may be brought intocontact and then separated without injury to either of thesurfaces.3.3 MIXTURE3.3.1 Viscosity 15 - 22 s(FLTM BI 11-2, Ford Cup #4)or3.3.2 Zahn Viscosity at 27 C 18 - 26 s(#2 Cup)ENGINEERING MATERIAL SPECIFICATIONESW-M4G153-AWP 3948-b Page 2 of 3

6、 3.4 TOTAL SOLIDS 14 - 18 %(ASTM D 2834, except heat at 102 +/- 3 C for3 h or until sample reaches constant weight)3.5 DRYNG TIME AT 23 +/- 2 C Tack free in 30 min3.6 SPECIFIC GRAVITY AT 27 C 0.89 - 0.93(ASTM D 891, Method B)3.7 FILM THICKNESSShall be as specified on the engineering drawings.3.8 ADH

7、ESION OF COATINGCut an “X“ in the coate d surface to the metal in several places witha razor blade. Press scotch tape onto the area firmly. After 5 min,remove the tape, pullin g at a direct tangent to the outside diameterof the seal. Regardless of the rate of tape remo val, no coating shalladhere to

8、 the tape.3.9 FLAKING OR POWDERINGScrape the coated surface until clean metal appears. The scrapingsshall be free from flakes or powder.3.10 INFRARED SPECTROPHOTOMETRYFord Motor Company, at its option, may conduct infrared analysis ofmateri al/parts supplied to this specification. The spectraesta bl

9、ished for initial approval shall constitute the referencest andard and shall be kept on file at the designated materiallaboratory. All samples shall produce spectra t hat correspond to thereferen ce standard when tested under the same conditions as thosespecified on the master spectrum.3.11 STATISTI

10、CAL PROCESSSupplie rs must conform to the requirements of Ford Quality SystemStand ard Q-101. A mutually acceptable Control Plan as describedtherein is required for material/source approval. Appropriatestatist ical tools must be used to analyze process/product data sothat variation in the final prod

11、uct is continuously reduced.3.12 SUPPLIERS RESPONSIBILITYAll materials supplied to this specification must be equivalent inal l characteristics to the material upon which approval wasoriginally granted.ENGINEERING MATERIAL SPECIFICATIONESW-M4G153-AWP 3948-b Page 3 of 3 Pri or to making any change in

12、 the properties, composition,constr uction, color, processing or labeling of the materialorig inally approved under this specification, whether or not suchchange s affect the materials ability to meet the specificationrequir ements, the Supplier shall notify Purchasing, Toxicology andthe affected Ma

13、terials Engineering activity of the proposed changesand obtain the written approval of the Materials Engineeringactivity. Test data, t est samples and a new code identification areto be submitted with the request.Substance restrictions imposed by law, regulations or Ford, apply tothe materials addre

14、ssed by this document. The restrictions aredefined in Engineering Material Specification WS S-M99P9999-A1, unlessa different suffix (e.g., A2 or A3) is specified on the engineeringdocument for the application.4. APPROVAL OF MATERIALSMat erials defined by this specification must have prior approval b

15、y theresponsible Materials Engineeri ng activity. Suppliers desiring approval ofthe ir materials shall first obtain an expression of interest from theaffec ted Purchasing, Design and Materials Engineering activity. Uponrequest, the Supplier shall submit to the affected Materials Engineeringactivity

16、its own laboratory rep ort to the specification (test results, notnominal values), the material designation and code number, and testspecim ens for Ford evaluation. Upon approval, the material will be addedto the Engineering Material Approved Source List.5. GENERAL INFORMATIONThe mate rial data incl

17、uded herein is for information only and is not arequirement for the supplier.5.1 FLASH POINT, min -4 C(ASTM D 56)5.2 FLAMMABILITY AND/OR TOXICITYThis material represent s a potential fire and/or health hazard. TheManufacturing Engineering Department shall notify both the PlantSecurity and the Safety Units of its presence in the plant to assurethat proper fire and/or health precautions are p rovided. The locationin which it is used or stored shall be included in the notifications.