DLA MIL-P-2383 H-1986 PINS TENT WOOD.pdf

《DLA MIL-P-2383 H-1986 PINS TENT WOOD.pdf》由会员分享，可在线阅读，更多相关《DLA MIL-P-2383 H-1986 PINS TENT WOOD.pdf（15页珍藏版）》请在麦多课文档分享上搜索。

1、r- MIL-P-2383H 83 = 777770b 0373033 b MIL-P-2383H 26 August 1986 SUPERSEDING . MIL-P-2383G 6 October 1981 MILITARY SPECIFICATION PINS, TENT, WOOD This specification is approved for use by all Departments and Agencies of the Department of Defense. 1. SCOPE 1.1 Scope. This document covers one type and

2、 three sizes of wood tent pins. 1.2 Classification. Wood tent pins shall be of the following sizes as specified (see 6.2). Size 1 - 16 inch Size 2 - 24 inch Size 3 - 36 inch 2. APPLICABLE DOCUMENTS 2.1 Government documents. fc 2.1.1 Documents. The following documents form a part of this document to

3、the extent specified herein. Unless otherwise specified, the issues of these documents shall be those listed in the issue of the Department of Defense Index of Specifications and Standards (DODISS) and supplement thereto, cited in the solicitation. O Beneficial comments (recommendations, additions,

4、deletions) and any pertinent data which may be of use in improving this document should be addressed to: U.S. Army Natick Research, Development, and Engineering Center, Natick, MA 01760-5014 by using the self-addressed Standardization Document Improvement Proposal (DD Form 1426) appearing at the end

5、 of this document or by letter. AMSC N/A FSC 8340 DISTRIBUTION STATEMENT A. Approved for public release; distribution is unlimited , THIS DOCUMENT CONTAIbIS jq- - -. PAGES. ?. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-L - _ - - - - I_.- MIL-P-2

6、383H 83 = 9999906 0373032 B = MIL- P-2 3 8 3H SPEC IF KATIONS FEDERAL QQ-S-78,l - Strapping, Steel And Ceais PPP-B-621 - $mes, Woad, Nailed and Lock-Corner PPP-B-636 - Biaxes, Shipping, Fiberboard STANDMDC MIEZThEY MIL-STD-fTS; - Sampling Procedures and Tables far Inspectian MEL-STB-I29 - Harkfrrg f

7、er Shipment, and Starape L-TD-f4:1: - FaEJ;etiked. Unit Laads. by At Er ibutes IIWrnNGS U,S, AMY NATCK KESEMCE, DEVELOPFEN?: AlW EI%IREE3tIFG CEEEEEXE 5-4-E - PiEs, Tent,. WCFQd: 5-4-4E4 - Pins, Eent, Waad; Cantainers far Domestic -and. matseas Shipnerrt . (Copies af dacuments required by contractor

8、s in connection with specifk acquisition functions shaud .be obtained from the contracting activity or as directed by the cantracting officer.) 2-2 ather publicationsc The iolloning documents form a part of this document to the extent specified herein. Unless otherwise specified, the issues of the d

9、ocuments which are DOD adopted shall be those listed in the issues ofthe DODISS specified in the solicitation. Unless otherwise specified, the issues of docu-ments nut listed in the DODISS shall he the issues of the nangovernment dacuments which are current an the date of the solicitation, AMERICAN

10、SOCIETY FOR TESTING AND MATERIALS (ASTM) A 512 - Cold-Drawn Buttweld Carbon Steel MechnicaI Tubing A 519 - Seamless Carbon and Alloy Steel Mechanical Tubing D 2016 - Moisture Content of Wood 9r D 3951 - Standard Practice for Commercial Packaging (Application for copies should be addressed to the Ame

11、rican Society for Testing and Materials, 1916 Race Street, Phiiadelphia, PA 19103.) (Technical society and technical association documents are generally available for reference from libraries. They are also distributed among technical groups and using Federal agencies,) 2 Provided by IHSNot for Resa

12、leNo reproduction or networking permitted without license from IHS-,-,-MIL-P-2383H 3 U 7379306 O373033 T W MIL-P-2383H fi 2.3 order of precedence. In the event of a conflict between the text of this document and the references cited herein, the text of this document shall take precedence. Nothing in

13、 this document however, shall supersede applicable laws and regulations unless a specific exemption has been obtained. 3. REQUIREMENTS ;t 3.1 First article. When specified in the contract or purchase order, a sample shall be subjected to first article inspection (see 4.3, 6.2, and 6.3). 3.2 Material

14、s (see 6.4). The materials used shall conform to the applicable referenced documents specified herein. Where materials are not definitely specified, they shall be of the quality and type normally used by the manufacturer provided the complete item complies with all the provision of this document. 3.

15、2.1 Wood. - Wood shall be uniformly dried without brashness, honey-combing or casehardening to a moisture content of not less than 8 nor more than 18 percent at time of fabrication when tested as specified in 4.4.1. Wood shall weigh a minimum of 36 pounds per cubic foot at 12 percent moisture conten

16、t when tested as specified in 4.4.1 by any commercial testing method. . The species of wood used shall be any of the following: Ash, white Hickory (true or pecan), Kerving/Apitone Beech Locust, black or honey Birch, sweet or yellow Maple, sugar or black (hard) Elm, rock Oak, red or white, Phillipine

17、 hardwood or Ma 1 ayc i an hardwood 3.2.2 Tube, steel. Steel tube shall conform to MT 1010- 1020, any type or condition of ASTM A 512 or A 519. 3.2.3 Screw, wood. Wood screw shall be of commercial quality zinc plated steel and of the type and size shown on Drawing 5-4-1. 3.3 Construction. Constructi

18、on of tent pins shall conform to Drawing 5-4-1 and as specified herein. 3.3.1 Pins. Pins shall be fabricated of wood specified in 3.2.1, Pins shall be cut in the direction of the grain of the wood as shown on Drawing 5-4-1, exceed 1 inch in 10 inches when tested as specified in 4.4.2.1. The surfaces

19、 on all sides of the pins shall be free from torn grain having a depth greater After cutting the pins to shape, the slope of the wood grain shall not 3 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,- _I_s _I - I MIL-P-233H 3 9999906 0373034 1 MIL-P-

20、2383H than 1/16 inch and skips having an area greater than 1 square inch. Any hole having diameter greater than 1/8 inch will be acceptable provided the hole is completely filled with an epoxy filler, the epoxy filling within the hole is sound and tight, and complies with other requirements herein.

21、Knots shall be sound and tight. Irregular local grain deviations such as birdseye, burl or swirl will be permitted. All pins shall be free from the following: a. Knots or epoxy filled holes less than 3 inches apart b. Heavy stain completely obscuring the grain of the wood c. Wormholes having diamete

22、r greater than 1/16 inch or wormholes closely bunched together exceeding more than 5 in an area of 1/2 square inch on any surface. or spaced closer than 2 inches apart d. e. Splits, loosened grain, larvae channel, bark or gum pocket f. Decay Holes (other than wormholes) having diameter greater than

23、1/8 inch 3.3.1.1 Sizes 1 and 2. Size 1 pin shall be free from any knot or epoxy filled hole within 6 inches from the top or within 3 inches from the bottom. Size 2 pin shall be free from any knot or epoxy filled hole within Il inches from the top or within 3 inches from the bottom. Sizes 1 and 2 pin

24、s shall be free from the following: a. b. C. d. e. f. g. h. Knot or epoxy filled hole having diameter greater than 1/4 inch on the 1-1/16 inch face or diameter greater than 3/8 inch on the 1-1/2 inch face i pin) 2 pin) inches long More than 2 knots or epoxy filled holes per pin (applicable to size M

25、ore than 4 knots or epoxy filled holes per pin (applicable to size Surface check open more than 1/64 inch wide or more than 1-1/2 More than a total of 8 surface checks on the 4 surfaces Surface checks closer than 1/4 inch from any edge More than 4 holes (other than wormholes) on a face (applicable t

26、o More than 6 holes (other than wormholes) on a face (applicable to size i pin) size 2 pin) 3.3.1.2 Size 3. The size 3 pin shall be fitted with a ferrule specified in 3.3.2. The ferrule shall be secured on the pin with a screw specified in 3.2.3. Size 3 pin shall be free from the following: a, Knot

27、or epoxy filled hole on any face having diameter greater than b. Knot or epoxy filled hole within 3 inches for the top or within 12 c. More than 6 knots or epoxy filled holes per pin d. Surface check more than 1/64 inch wide or more than 3 inches long on 1/2 inch inches fromthe bottom any surface of

28、 .pin 4 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-P-2383H 83 W Ob 0373035 3 m MIL-P-2383H e. More than 16 surface checks on the whole pin f. More than 8 holes (other than wormholes) on a single face 3.3.1.2.1 Driving of screw. Screw shall b

29、e screwed in place with head flush with the ferrule. Screw shall not be driven with a hammer. 3.3.2 Ferrule. Ferrule shall be fabricated of steel specified in 3.2.2. The hole in the ferrule shall be countersunk to provide a flush fit for the screw head. 3.4 Finish. Rough or sharp edges, burrs or sli

30、vers on ferrule shall be removed prior to finishing. Ferrule shall then be galvanized in accordance with commercial practice to produce an adherent continuous uniform coating free from scratch, dig, dirt or foreign matter imbedded in coating. 3.5 Workmanship. The finished pins shall conform to the q

31、uality of product established by this document. The occurrence of defects shall not exceed the applicable acceptable quality levels. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for inspection. Unless otherwise specified in the contract or purchase order, the contractor is responsible for the

32、performance of all inspection requirements as specified herein. Except as otherwise specified in the contract or purchase order, the contractor may use his own or any other facilities suitable for the performance of the inspection requirements specified herein, unless disapproved by the Government.

33、The Government reserves the right to perform any of the inspections set forth in the document where such inspections are deemed necessary to assure supplies and services conform to prescribed requirements. f: 4.1.1 Responsibility for compliance. All items must meet all requirements of sections 3 and

34、 5. The inspection set forth in this document shall become a part of the contractors overall inspection system or quality program. absence uf any inspection requirements in the document shall not relieve the contractor of the responsibility of assuring that all products or supplies submitted to the

35、Government for acceptance comply with all requirements of the contract. Sampling in quality conformance does not authorize submission of known defective material, either indicated or actual, nor does it commit the Government to acceptance of defective material. The 4.2 Classification of inspection.

36、The inspection requirements specified herein are classified as follows: a. b. Quality conformance inspection (see 4.4). First article inspection (see 4.3). 5 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-b MIL-P-2383H 4.3 First article inspection.

37、When a first article is required (see 6.21, it shall be examined for the defects specified in table III and 4.4.4. The presence of any defect shall be cause for rejection of the first article. 4.4 Quality conformance inspection. Unless otherwise specified, sampling for inspection shall be performed

38、in accordance with MIL-STD-105. 4.4.1 Component and material inspection. In accordance with 4.1, components and materials shall be inspected in accordance with all the requirements of referenced documents unless otherwise excluded, amended, modified, or qualified in this document or applicable purch

39、ase document. * 4.4.1.1 Component testing, In addition to the quality assurance provisions of the subsidiary documents, testing shall be performed on materials listed in table I for the test characteristics shown. and weight of wood are applicable to the individual unit. The acceptable quality level

40、 (AQL) shall be expressed in terms of percent defective. sample unit of wood tested having less than 8 or more than 18 percent moisture content shall be classified as defective. Any sample of wood tested weighing less than 36 pounds per cubic foot at 12 percent moisture content shall be classified a

41、s defective. Requirements for moisture content Any 6 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-P-233H 3 m 799790b 0373037 7 MIL-P-2383H . a B 8 m o . 4 I m m na E2 mal 4s 4 hl m a incorrect; illegible; of improper size, location, sequence,

42、or method or application Materials Any component missing, damaged, or not as specified Workmanship Inadequate application of components such as: Bulged or distorted container Arrangement of pins within containers not as specified loose strapping on Drawing 5-4-414 11 Provided by IHSNot for ResaleNo

43、reproduction or networking permitted without license from IHS-,-,- _I- - - - MIL-P-23B3H 3 W 777970b 03730q2 O E MIL-P-2383H Examine Defect Content Quantity of pins per container is more or less than More than one size of pin in any container r equ i red * 4.4.6 Palletization examination. The fully

44、packaged and palletized end items shall be examined for the defects listed below. The lot size shall be expressed in units of palletized unit loads. The sample unit shall be one palletized unit load, fully packaged. The inspection level shall be S-1 and the AQL, expressed in terms of defects per hun

45、dred units, shall be 6.5. Examine Defect Fin is hed dimens ion Length, width, or height exceeds specified maximum requirement. Palletization Pallet pattern not as specified. Interlocking of loads not as specified. Load not bonded as Specified. Weight Exceeds maximum load limit. Marking Omitted; inco

46、rrect; illegible; of improper size, location, sequence, or method of application. 4.5 Methods of inspection. 4.5.1 Slope of wood grain. The slope of grain may be determined by combining the grain direction of two adjacent faces of a square or rectangular piece. When one of these faces is straight gr

47、ained, the true slope of grain is shown on the other face. When there is a slope on both faces, the true or combined slope is greater-than the slope on either face. Slope of grain is shown on edge grained faces by the summer wood bands, by the direction in which a free flowing ink or dye spreads, or

48、 by the course taken by a narrow strip lifted by a knife point and torn out. Direction of fiber may also be measured by a slope of grain detector. Any size 1 pin, size 2 pin, or square or rectangular blank of the size 3 pin (see 4.4.2.1) having a slope of wood grain exceeding 1-inch in 10 inches sha

49、ll be classified as defective. 12 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-P-233H 3 = 9999706 0373043 2 MIL-P-2383H 5. PACKAGING : 5.1 Packing. Packing shall be level A, B or Commercial as specified (see 6.2). 5.1.1 Level A packing. Tent pins shall be arranged and packed in containers as shown in Drawing 5-4-414. Quantitie